CN102127791B - 一种az91镁合金表面厚层处理方法 - Google Patents
一种az91镁合金表面厚层处理方法 Download PDFInfo
- Publication number
- CN102127791B CN102127791B CN2011101015000A CN201110101500A CN102127791B CN 102127791 B CN102127791 B CN 102127791B CN 2011101015000 A CN2011101015000 A CN 2011101015000A CN 201110101500 A CN201110101500 A CN 201110101500A CN 102127791 B CN102127791 B CN 102127791B
- Authority
- CN
- China
- Prior art keywords
- magnesium alloy
- treatment
- oxygen
- concentration
- thick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种AZ91镁合金表面厚层处理方法,属于AZ91镁合金表面厚层处理研究领域,本发明在交流等离子体微弧氧化处理方法基础上,通过向处理液中喷入氧气以增强和改善对保护层的烧结作用,并在氟化钾浓度为262~264g/L、氢氧化钾浓度为93~95g/L、工频交流电压为130~132V、每升处理液氧气喷入量为0.01~0.016L/s条件下,对AZ91镁合金进行106~138秒的交流等离子体微弧氧化表面处理,可在AZ91镁合金表面形成55~65μm厚的组织致密、均匀的厚保护层。
Description
技术领域
本发明涉及一种AZ91镁合金表面厚层处理方法。
背景技术
公开号:CN1900383A,发明名称:“一种AZ91镁合金表面处理方法”上,阐述了AZ91镁合金交流等离子体微弧氧化处理方法,即,采用含有氟化钾和氢氧化钾的处理液,由调压器控制的工频交流电源提供电能,在每个工频交流电压周期内,利用处理液中的阴、阳离子在AZ91镁合金表面进行等离子体微弧放电产生的瞬时高温在AZ91镁合金表面形成保护层。利用这种交流等离子体微弧氧化处理方法,在专利CN1900383A中公开的氟化钾浓度为500~979g/L、氢氧化钾浓度为300~349g/L、工频交流电压为68~80V条件下,可在60~90秒内,使AZ91镁合金表面原位生长出15~30μm厚、组织均匀而完整的乳白色保护层。但是,采用CN1900383A专利方法在AZ91镁合金表面形成的厚度在30μm以上的厚层,存在较为严重的沙化现象即保护层变疏松、起球团的现象,这种出现沙化现象的镁合金表面厚层对镁合金基体几乎没有保护作用,也就是说,采用CN1900383A专利方法在AZ91镁合金表面形成的具有保护作用的保护层的最大厚度为30μm。
对于AZ91镁合金表面的具有保护作用的组织致密、均匀的保护层,其厚度越大,对基体的保护作用越强、越持久,因此,AZ91镁合金的表面保护层在出现沙化现象以前的厚度越大越好。
发明内容
本发明所要解决的技术问题是,克服现有交流等离子体微弧氧化处理方法“组织致密、均匀的表面保护层最大厚度小”的不足,提供一种能够在AZ91镁合金表面形成组织致密、均匀的厚保护层的交流等离子体微弧氧化处理方法,进一步提高具有保护作用的AZ91镁合金表面厚层的最大厚度。
本发明解决其技术问题所采用的技术方案是:在交流等离子体微弧氧化处理方法基础上,向处理液中喷入氧气以增强和改善对保护层的烧结作用,并在氟化钾浓度为262~264g/L、氢氧化钾浓度为93~95g/L、工频交流电压为130~132V、每升处理液氧气喷入量为0.01~0.016L/s条件下,对AZ91镁合金进行106~138秒的交流等离子体微弧氧化表面处理。
本发明的有益效果是:在对镁合金进行表面处理时,对于镁合金的表面保护层,当其达到一定厚度后,在处理液中的离子击穿放电冲击下,会产生迅速变疏松、起球团的沙化现象,要想延迟沙化现象的发生即进一步提高具有保护作用的表面厚层的最大厚度,必须增强和改善对保护层的烧结作用。如果在进行表面处理时向处理液中喷入氧气,则处理液中的离子击穿放电时产生的高温会造成喷入处理液中的氧气形成大量的氧等离子体,这些氧等离子体对保护层具有助烧结作用,可大大增强和改善对保护层的烧结作用,本发明就是利用各表面处理参数优化组合后产生的氧等离子体对保护层的助烧结作用,延迟了沙化现象的发生,进一步增大了具有保护作用的表面厚层的最大厚度。利用本发明,对AZ91镁合金进行表面处理,可在106~138秒内得到55~65μm厚的组织致密、均匀的厚保护层,比采用CN1900383A专利方法得到的最大厚度30μm至少增厚了83%。
附图说明
图1为本发明方法对AZ91镁合金进行表面处理装置的主视图。
图中,工频交流电源1,导线2,调压器3,导线4,AZ91镁合金工件5,处理液6,氧气喷嘴7,氧气泵8,处理槽9。
图2为采用本发明方法对AZ91镁合金进行表面处理后得到的处理界面的微观组织。
具体实施方式
结合附图对本发明方法对AZ91镁合金进行表面处理装置的具体说明如下:
对AZ91镁合金进行表面处理装置主要包括:工频交流电源1,调压器3,氧气喷嘴7,氧气泵8,处理槽9。
调压器3的输入端与工频交流电源1通过导线2相连,调压器2的输出端与AZ91镁合金工件5通过导线4相连。氧气喷嘴7采用聚四氟乙烯密封连接方式固定在处理槽9的下部,其一端伸入处理液6内,另一端与氧气泵8相连。
工频交流电源1为工业常用的工频交流电源。调压器3可以采用市场上购买的能够提供镁合金表面处理所需电能的任何型号的调压器。氧气喷嘴7与处理槽9的材质为聚四氟乙烯。AZ91镁合金工件5需要进行除油、打磨和清洗预处理。
一种AZ91镁合金表面厚层处理方法,采用交流等离子体微弧氧化处理方法对AZ91镁合金进行表面处理,在进行表面处理前1分钟开始向处理液中喷入氧气,并在氟化钾浓度为262~264g/L、氢氧化钾浓度为93~95g/L、工频交流电压为130~132V、每升处理液氧气喷入量为0.01~0.016L/s条件下,对AZ91镁合金进行106~138秒的交流等离子体微弧氧化表面处理。
实施方式一,在氟化钾浓度为262g/L、氢氧化钾浓度为93g/L、工频交流电压为130V、每升处理液氧气喷入量为0.01L/s条件下,交流等离子体微弧氧化表面处理106秒后,可在AZ91镁合金工件表面形成55μm厚的组织致密、均匀的厚保护层。
实施方式二,在氟化钾浓度为262g/L、氢氧化钾浓度为93g/L、工频交流电压为132V、每升处理液氧气喷入量为0.01L/s条件下,交流等离子体微弧氧化表面处理106秒后,可在AZ91镁合金工件表面形成58μm厚的组织致密、均匀的厚保护层。
实施方式三,在氟化钾浓度为264g/L、氢氧化钾浓度为93g/L、工频交流电压为130V、每升处理液氧气喷入量为0.016L/s条件下,交流等离子体微弧氧化表面处理138秒后,可在AZ91镁合金工件表面形成62μm厚的组织致密、均匀的厚保护层。
实施方式四,在氟化钾浓度为264g/L、氢氧化钾浓度为95g/L、工频交流电压为132V、每升处理液氧气喷入量为0.016L/s条件下,交流等离子体微弧氧化表面处理138秒后,可在AZ91镁合金工件表面形成65μm厚的组织致密、均匀的厚保护层。
实施方式五,在氟化钾浓度为262g/L、氢氧化钾浓度为95g/L、工频交流电压为132V、每升处理液氧气喷入量为0.016L/s条件下,交流等离子体微弧氧化表面处理106秒后,可在AZ91镁合金工件表面形成59μm厚的组织致密、均匀的厚保护层。
可见,在氟化钾浓度为262~264g/L、氢氧化钾浓度为93~95g/L、工频交流电压为130~132V、每升处理液氧气喷入量为0.01~0.016L/s条件下,对AZ91镁合金进行106~138秒的交流等离子体微弧氧化表面处理,可在AZ91镁合金表面形成55~65μm厚的组织致密、均匀的厚保护层。
附图2为采用本发明方法对AZ91镁合金进行表面处理后得到的处理界面的微观组织。图中上部呈浅色的区域为保护层,下部呈深色的区域为AZ91镁合金基体,可见,厚保护层的组织非常致密、均匀。可见,本发明可在AZ91镁合金表面形成厚度更大的厚保护层。
Claims (1)
1.一种AZ91镁合金表面处理方法,采用交流等离子体微弧氧化处理方法对AZ91镁合金进行表面处理,其特征在于,在进行表面处理前1分钟开始向处理液中喷入氧气,并在氟化钾浓度为262~264g/L、氢氧化钾浓度为93~95g/L、工频交流电压为130~132V、每升处理液氧气喷入量为0.01~0.016L/s条件下,对AZ91镁合金进行106~138秒的交流等离子体微弧氧化表面处理。