CN102108257A - 自硬型橡胶沥青涂料 - Google Patents

自硬型橡胶沥青涂料 Download PDF

Info

Publication number
CN102108257A
CN102108257A CN 201010617853 CN201010617853A CN102108257A CN 102108257 A CN102108257 A CN 102108257A CN 201010617853 CN201010617853 CN 201010617853 CN 201010617853 A CN201010617853 A CN 201010617853A CN 102108257 A CN102108257 A CN 102108257A
Authority
CN
China
Prior art keywords
latex
asphalt
air
pitch
rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010617853
Other languages
English (en)
Inventor
田凤兰
段文锋
栾斌
常英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jinzhou Dongfang Yuhong Building Materials Co., Ltd.
Beijing Oriental Yuhong Waterproof Technology Co Ltd
Original Assignee
Beijing Oriental Yuhong Waterproof Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Oriental Yuhong Waterproof Technology Co Ltd filed Critical Beijing Oriental Yuhong Waterproof Technology Co Ltd
Priority to CN 201010617853 priority Critical patent/CN102108257A/zh
Publication of CN102108257A publication Critical patent/CN102108257A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种自硬型橡胶沥青涂料,其以重量百分比计包括沥青50%-65%、阳离子性乳化剂3%-6%、非离子性乳化剂3%-6%、改性胶乳25%-35%、稳定剂1%-3%、填料5%-10%;本发明还提供其制备方法,本发明提出的橡胶沥青涂料用常温自交联乳液进行改性,可具有常温喷涂、手工刮涂、瞬间成性、完美贴合、高弹力、无接缝等突出特点,从根本上解决了边角、缝隙、不规则结构的连接处渗漏等技术难题,彻底更新了传统防水材料的施工工艺和方法。

Description

自硬型橡胶沥青涂料
技术领域
[0001] 本发明涉及一种涂料,特别是用于防水防腐领域的自硬型橡胶浙青涂料。
背景技术
[0002] 近些年国家加强了基础设施的投入并一直在强调环保、节能减排等,而高固含量 自硬型橡胶浙青涂料是国际一流多用途环保防水产品,具有常温喷涂、瞬间成性、完美贴 合、高弹力、无接缝等突出特点,从根本上解决了边角、缝隙、不规则结构的连接处渗漏等技 术难题,彻底更新了传统防水材料的施工工艺和方法,高固含量自硬型橡胶浙青涂料必将 引领防水领域技术更新换代的新潮流。
[0003] 但是,高固含量自硬型橡胶浙青产品对于组分选择则非常严苛,如果组分,特别是 乳化剂,选择不当,容易产生浊点过低、或者浙青颗粒粗大等问题。这些问题使得自硬型橡 胶浙青涂料无法达到施工工艺要求,大大限制了其发展。如何找到合适配方的高固含量自 硬型橡胶浙青产品,已经成为业界研究的焦点。
发明内容 [0004] 本发明旨在解决前述技术问是 1,提供 一种适宜的自硬型橡胶浙青涂料。[0005] 本发明所提供的一种自硬型_ 良胶浙ΐ ί涂料,其以重量百分比计包括如下组分:[0006] 浙青 50% -65% » [0007] 阳离子性乳化剂3% -6% ; [0008] 非离子性乳化剂3% -6% ; [0009] 改性胶乳 25% -35% [0010] 稳定剂 1% -3% ; [0011] 填料: 5% -10%。 [0012] 优选以重量百分比计包括如下组分: [0013] 浙青 55% -60% » [0014] 阳离子性乳化剂3% -6% ; [0015] 非离子性乳化剂3% -6% ; [0016] 改性胶乳 25% -30% [0017] 稳定剂 1% -3% ; [0018] 填料: 5% -10%。 [0019] 所述的浙1 ί选自天然浙青、石油浙青 、煤浙青或其混合物;优选为石油浙青,且其针入度为60-100(1/ xIOmm)。
[0020] 所述阳离子性浙青乳化剂选自十二烷基胺、十四烷基胺、十六烷基胺、二十二烷基 胺、椰子油胺、牛脂胺、氢化牛脂胺、油胺、大豆油胺、1-氨乙基-2-十七烷基咪唑啉-2、木质 素胺、十二烷基二甲基苄基氯化铵、十四烷基二甲基氯化铵、十六烷基二甲基苄基氯化铵或 其混合物。[0021] 所述非离子性浙青乳化剂选自十二酸单乙醇酰胺、十二酸二乙醇酰胺、椰油酸单 乙醇酰胺、椰油酸二乙醇酰胺、聚氧乙烯山梨醇单月桂酸酯、聚氧乙烯山梨醇单油酸酯、壬 基酚聚氧乙烯醚或其混合物。
[0022] 所述改性胶乳选自阳离子氯丁胶乳、自交联羧基胶乳、阳离子丁苯胶乳、苯丙胶 乳、天然胶乳、丁腈胶乳、丁基胶乳、聚异戊二烯胶乳、乙烯-醋酸乙烯乳胶、三元乙丙胶乳、 二元乙丙胶乳、氯化丁基胶乳、氯磺化聚乙烯胶乳或其混合物;所述的填料选自碳酸钙、滑 石粉、硅灰石粉、高岭土、膨润土或其混合物。
[0023] 所述稳定剂选自无机盐、无机酸或有机酸、聚乙烯醇、纤维素或其混合物;所述无 机盐选自硫酸盐、硝酸盐或盐酸盐;所述无机酸或有机酸选自脂肪酸、醋酸、盐酸或酒石酸。
[0024] 本发明还提供一种自硬型橡胶浙青涂料制备工艺,其包括如下步骤:
[0025] A、称取如下重量百分比的组分:
[0026]浙青 50%-65%;
[0027] 阳离子性乳化剂3% -6% ;
[0028] 非离子性乳化剂3% -6% ;
[0029]改性胶乳: 25%-;35%
[0030]稳定剂
[0031]填料: 5% -10%。
[0032] B、将浙青先在110°C _130°C脱水1小时_2小时,然后温和加热到130°C _160°C, 计量后备用;
[0033] C、将水加热到45°C -65°C,计量后备用;
[0034] D、将乳化剂、稳定剂加入到备用热水中,搅拌均勻,制成乳化水溶液,控制温度为 45 0C _65°C,备用;
[0035] E、开启乳化机系统,将前述所得的乳化水溶液与热浙青混合,制得乳化浙青备 用;
[0036] F、将所得乳化浙青与改性胶乳和填料在搅拌器中搅拌混合,搅拌20分钟,静止1 小时后过滤得成品。
[0037] 申请人经研究发现,单一乳化剂无法满足自硬型橡胶浙青涂料对乳化浙青的要 求,因为单一乳化剂有固定的HLB值,它不能满足复杂的浙青乳化所需要HLB范围。因此本 发明特别选择了阳离子性和非离子性两种乳化剂,按特定的比例进行复配,形成复合乳化 剂。
[0038] 本发明所用的阳离子性浙青乳化剂选择了十二烷基胺、十四烷基胺、十六烷基胺、 二十二烷基胺、椰子油胺、牛脂胺、氢化牛脂胺、油胺、大豆油胺、1-氨乙基-2-十七烷基咪 唑啉-2盐酸盐、木质素胺、十二烷基二甲基苄基氯化铵、十四烷基二甲基氯化铵、十六烷基 二甲基苄基氯化铵中的一种或多种。本发明对非离子性浙青乳化剂为十二酸单乙醇酰胺、 十二酸二乙醇酰胺、椰油酸单乙醇酰胺、椰油酸二乙醇酰胺、聚氧乙烯山梨醇单月桂酸酯、 聚氧乙烯山梨醇单油酸酯、壬基酚聚氧乙烯醚中的一种或多种。采用上述乳化剂进行复合, 有利于消除单用非离子性乳化剂易产生浊点低的问题,也可以避免单用阳离子性乳化剂, 浙青颗粒粗大的问题。使用上述复配乳化剂,可以缩小油水两者之间的相对密度差值及粘 度的差值,增强浙青微粒的电势,易于形成双电层,增加颗粒之间的相互排斥力,阻碍浙青微粒的聚合倾向。
[0039] 本发明提出的橡胶浙青涂料用常温自交联乳液进行改性,可具有常温喷涂、手工 刮涂、完美贴合、高弹力、无接缝等突出特点,从根本上解决了边角、缝隙、不规则结构的连 接处渗漏等技术难题,彻底更新了传统防水材料的施工工艺和方法。
具体实施方式
[0040] 实施例1
[0041] 将发明产品中的乳化浙青原材料按下述(表1)进行配比(重量比,下同):
[0042] 表1乳化浙青配方表(100份乳化浙青)
[0043]
Figure CN102108257AD00061
[0044] 乳化浙青制造工艺如下:
[0045] A、将浙青先在110°C _130°C脱水1小时_2小时,然后温和加热到130°C _160°C, 计量后备用;
[0046] B、将自来水加热到45°C _65°C,计量后备用;
[0047] C、将乳化剂、稳定剂加入到备用热水中,搅拌均勻,制成乳化水溶液,控制温度为 45 0C _65°C,备用;
[0048] D、开启乳化机系统,将符合温度要求的乳化水溶液倒入乳化中,立即倒入符合温 度要求的热浙青,符合要求的乳化浙青制备完成。
[0049] 再将发明产品中的原材料按下述(表2)进行配比(重量比,下同):
[0050] 表2自硬型橡胶浙青涂料(100份涂料)
[0051]
Figure CN102108257AD00062
[0052] 自硬型橡胶浙青涂料的制造工艺如下:
[0053] 将乳化浙青、改性胶乳、填料加入到搅拌缸中高速搅拌,搅拌20分钟,静止1小时 后过滤。[0054] 实施例2
[0055] 将乳化浙青原材料按下述(表3)进行配比(重量比,下同):
[0056] 表3乳化浙青配方表(100份乳化浙青)
[0057]
Figure CN102108257AD00071
[0058] 实施例2的乳化浙青制造工艺如实施例1
[0059] 再将涂料中的原材料按下述(表4)进行配比(重量比,下同):
[0060] 表4自硬型橡胶浙青涂料(100份涂料)
[0061]
Figure CN102108257AD00072
[0062] 实施例2的自硬型橡胶浙青涂料的制造工艺如实施例1
[0063] 实施例3
[0064] 将乳化浙青原材料按下述(表5)进行配比(重量比,下同):
[0065] 表5乳化浙青配方表(100份乳化浙青)
[0066]
Figure CN102108257AD00073
[0067] 实施例3的乳化浙青制造工艺如实施例1
[0068] 再将涂料中的原材料按下述(表6)进行配比(重量比,下同):
[0069] 表6自硬型橡胶浙青涂料(100份涂料)
[0070]
Figure CN102108257AD00081
[0071]
[0072] 实施例3的自硬型橡胶浙青涂料的制造工艺如实施例1
[0073] 实施例4
[0074] 将乳化浙青原材料按下述(表7)进行配比(重量比,下同):
[0075] 表7乳化浙青配方表(100份乳化浙青)
[0076]
Figure CN102108257AD00082
[0077] 实施例4的乳化浙青制造工艺如实施例1
[0078] 再将涂料中的原材料按下述(表8)进行配比(重量比,下同):
[0079] 表8自硬型橡胶浙青涂料(100份涂料)
[0080]
Figure CN102108257AD00083
[0081] 实施例4的自硬型橡胶浙青涂料的制造工艺如实施例1
[0082] 该发明提出的橡胶浙青涂料用常温自交联乳液进行改性,具有可常温喷涂、手工刮涂、完美贴合、高弹力、无接缝等突出特点,从根本上解决了边角、缝隙、不规则结构的连 接处渗漏等技术难题,其物性指标可达到下述(表9)要求,达到并超过住建部标准JCT 408-2005《水乳型浙青防水涂料》的相应要求(表10)。
[0083] 表9自硬型橡胶浙青涂料物性指标
[0084]
Figure CN102108257AD00091
[0085] 表10JCT 408-2005水乳型浙青防水涂料
[0086]
Figure CN102108257AD00092

Claims (10)

1. 一种自硬型橡胶浙青涂料,其特征在于以重量百分比计包括如下组分: 浙青 50% -65% ;阳离子性乳化剂3%-6% ; 非离子性乳化剂3% -6% ; 改性胶乳: 25%-35% 稳定剂 1^-3%;填料: 5%-10%。
2.按照权利要求1所述的自硬型橡胶浙青涂料,其特征在于以重量百分比计包括如下 组分:浙青 55% -60% ;阳离子性乳化剂3%-6% ; 非离子性乳化剂3% -6% ; 改性胶乳: 25%-30% 稳定剂 1^-3%;填料: 5%-10%。
3.按照权利要求1或2所述的自硬型橡胶浙青涂料,其特征在于所述的浙青选自天然 浙青、石油浙青、煤浙青或其混合物。
4.按照权利要求3所述的自硬型橡胶浙青涂料,其特征在于所述的浙青选自石油浙 青,且其针入度为60-100 (l/10mm)。
5.按照权利要求1或2所述的自硬型橡胶浙青涂料,其特征在于所述阳离子性浙青乳 化剂选自十二烷基胺、十四烷基胺、十六烷基胺、二十二烷基胺、椰子油胺、牛脂胺、氢化牛 脂胺、油胺、大豆油胺、1-氨乙基-2-十七烷基咪唑啉_2、木质素胺、十二烷基二甲基苄基氯 化铵、十四烷基二甲基氯化铵、十六烷基二甲基苄基氯化铵或其混合物。
6.按照权利要求1或2所述的自硬型橡胶浙青涂料,其特征在于所述非离子性浙青乳 化剂选自十二酸单乙醇酰胺、十二酸二乙醇酰胺、椰油酸单乙醇酰胺、椰油酸二乙醇酰胺、 聚氧乙烯山梨醇单月桂酸酯、聚氧乙烯山梨醇单油酸酯、壬基酚聚氧乙烯醚或其混合物。
7.按照权利要求1或2所述的自硬型橡胶浙青涂料,其特征在于所述改性胶乳选自阳 离子氯丁胶乳、自交联羧基胶乳、阳离子丁苯胶乳、苯丙胶乳、天然胶乳、丁腈胶乳、丁基胶 乳、聚异戊二烯胶乳、乙烯-醋酸乙烯乳胶、三元乙丙胶乳、二元乙丙胶乳、氯化丁基胶乳、 氯磺化聚乙烯胶乳或其混合物;所述的填料选自碳酸钙、滑石粉、硅灰石粉、高岭土、膨润土 或其混合物。
8.按照权利要求1或2所述的自硬型橡胶浙青涂料,其特征在于:所述稳定剂选自无 机盐、无机酸或有机酸、聚乙烯醇、纤维素或其混合物。
9.如权利要求8所述的自硬型橡胶浙青涂料,其特征在于所述无机盐选自硫酸盐、硝 酸盐或盐酸盐;所述无机酸或有机酸选自脂肪酸、醋酸、盐酸或酒石酸。
10. 一种自硬型橡胶浙青涂料制备工艺,其特征在于包括如下步骤: A、称取如下重量百分比的组分:浙青 50% -65% ;阳离子性乳化剂3% -6% ;非离子性乳化剂3% -6% ; 改性胶乳: 25%-35% 稳定剂 1%-3%;填料: 5%-10%;B、将浙青先在110°C _130°C脱水1小时-2小时,然后温和加热到130°C _160°C,计量 后备用;C、将水加热到45°C _65°C,计量后备用;D、将乳化剂、稳定剂加入到备用热水中,搅拌均勻,制成乳化水溶液,控制温度为 45 0C _65°C,备用;E、开启乳化机系统,将前述所得的乳化水溶液与热浙青混合,制得乳化浙青备用;F、将所得乳化浙青与改性胶乳和填料在搅拌器中搅拌混合,搅拌20分钟,静止1小时 后过滤得成品。
CN 201010617853 2010-12-22 2010-12-22 自硬型橡胶沥青涂料 Pending CN102108257A (zh)