CN102086356A - Sticking film for wood composition floor - Google Patents
Sticking film for wood composition floor Download PDFInfo
- Publication number
- CN102086356A CN102086356A CN 201010567106 CN201010567106A CN102086356A CN 102086356 A CN102086356 A CN 102086356A CN 201010567106 CN201010567106 CN 201010567106 CN 201010567106 A CN201010567106 A CN 201010567106A CN 102086356 A CN102086356 A CN 102086356A
- Authority
- CN
- China
- Prior art keywords
- floor
- bonding film
- solid wooden
- wooden compound
- compound floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a sticking film for wood composition floor, and the sticking film is prepared from the following raw materials, by weight, 35-45 parts of HDPE 6098; 35-45 parts of high density polyethylane 5000S; 1-2 parts of anti-aging agent UV; 10-20 parts of LLDPE 7042; and 5-20 parts of EVA260 resin. The sticking film for wood composition floor in the invention possesses strong bonding force, and the obtained wood composition floor possesses high shearing intensity, good temperature resistance and waterproof property; because raw materials used to produce the sticking film contain no formaldehyde, the obtained finished product sticking film contains no formaldehyde, the wood composition floor made by using the sticking film contains no formaldehyde, is environment-friendly floor, generates no pollution to indoor environment, is good for health, and is suitable to be applied and popularized in decoration wood floor industry.
Description
Technical field
The present invention relates to the plastics film technical field, specifically, relate to and a kind ofly be used for adjacent plank layer is carried out bonding bonding film when producing solid wooden compound floor.
Background technology
Solid wooden compound floor is mainly used in the flooring finishing, is the important wooden finishing materials of occasion such as family, hotel, hotel.At present, the production of solid wooden compound floor mostly adopts wood single-plate to form substrate by urea formaldehyde resin adhesive gummed, is plane materiel coated with high-grade decorative veneer on substrate again, and hot-press gluing forms the finished product floor.Because employed urea formaldehyde resin adhesive is by urea and the formaldehyde linear urea aldehyde oligopolymer that polycondensation makes under the catalysis of acid or alkali in the production process, the floor is in production and use, the formaldehyde that has a large amount of unbound states discharges, according to test, the volatilization of formaldehyde is for up to 3-15, and serious environment pollution, harm people's is healthy.
Based on above present situation, press for a kind of formaldehydeless environmental-friendly adhesion material of development and substitute urea formaldehyde resin adhesive, be used for the production of solid wooden compound floor, make the solid wooden compound floor of production formaldehydeless, environmental protection, be of value to the healthy of people.
Summary of the invention
Technical problem to be solved by this invention is: provide a kind of solid wooden compound floor that does not contain formaldehyde, environmental protection bonding film, be used for carrying out adjacent plank layer bonding.
For solving the problems of the technologies described above, technical scheme of the present invention is: the bonding film of solid wooden compound floor, described solid wooden compound floor are to be made by the raw material of following weight part with bonding film
HDPE?6098 35～45
High density polyethylene(HDPE) 5000S 35～45
Antiaging agent UV 1～2
LLDPE?7042 10～20
EVA260 resin 5～20.
As optimized technical scheme, described solid wooden compound floor is to be made by the raw material of following weight part with bonding film
HDPE?6098 40
High density polyethylene(HDPE) 5000S 40
Antiaging agent UV 2
LLDPE?7042 15
EVA260 resin 13.
As optimized technical scheme, described solid wooden compound floor is made with blow moulding with bonding film, and prepared solid wooden compound floor is 170 ℃～195 ℃ with the melt temperature of bonding film.
Owing to adopted technique scheme, the invention has the beneficial effects as follows: because solid wooden compound floor of the present invention is to be that raw material is made with blow moulding by HDPE 6098, high density polyethylene(HDPE) 5000S, antiaging agent UV, LLDPE 7042, EVA260 resin 5-19 with bonding film, do not contain formaldehyde in the raw material of production usefulness, therefore the finished product solid wooden compound floor that makes does not contain formaldehyde with bonding film yet; When using the bonding film that does not contain formaldehyde of the present invention to produce solid wooden compound floor, lay the bonding film of one deck solid wooden compound floor between the adjacent two layers wood single-plate, utilize pressing machine, under High Temperature High Pressure under the condition, the wood single-plate that lays is exerted pressure, when temperature reaches 170 ℃～195 ℃, bonding film is in molten state, adjacent wood single-plate is bonded together, behind the naturally cooling, bonding film is condensed into solid-state, and adjacent wood single-plate is bonded together tightly, promptly makes solid wooden compound floor.Solid wooden compound floor of the present invention is strong with bonding film bonding force, the shearing resistance height of the solid wooden compound floor that makes, and the test proof even wood single-plate is destroyed, also is difficult to the two-layer wood single-plate that bonds together by this bonding film is separated; Solid wooden compound floor of the present invention owing to have higher melt temperature, makes the solid wooden compound floor of production have good high temperature resistant and water resistance with bonding film; Because solid wooden compound floor of the present invention does not contain formaldehyde with bonding film; being a kind of bonding film of environmental protection environment-friendly type, utilizing the solid wooden compound floor of this bonding film production that does not contain formaldehyde also not contain formaldehyde, is a kind of environmental protection floor; can not pollute indoor environment, be of value to the healthy of people.
Embodiment
Solid wooden compound floor of the present invention is to be made by the raw material of following weight part with bonding film
HDPE?6098 35～45
High density polyethylene(HDPE) 5000S 35～45
Antiaging agent UV 1～2
LLDPE?7042 10～20
EVA260 resin 5～20.
Described antiaging agent UV can select antiaging agent UV-531, antiaging agent UV-328 or antiaging agent UV-329 for use.
Embodiment one: solid wooden compound floor of the present invention selects for use the raw material of following weight part to make with bonding film
HDPE?6098 40
High density polyethylene(HDPE) 5000S 40
Antiaging agent UV-531 2
LLDPE?7042 15
EVA260 resin 13.
Embodiment two: solid wooden compound floor of the present invention selects for use the raw material of following weight part to make with bonding film
HDPE?6098 35
High density polyethylene(HDPE) 5000S 35
Antiaging agent UV-328 1
LLDPE?7042 10
EVA260 resin 5.
Embodiment three: solid wooden compound floor of the present invention selects for use the raw material of following weight part to make with bonding film
HDPE?6098 45
High density polyethylene(HDPE) 5000S 45
Antiaging agent UV-329 1.5
LLDPE?7042 20
EVA260 resin 20.
This composite floor board of reality of the present invention adopts blow moulding commonly used in the plastics-production field with the raw material of bonding film according to above-mentioned weight part, and for example the stretch-blow method is made, and prepared solid wooden compound floor is 170 ℃～195 ℃ with the melt temperature of bonding film.
Because solid wooden compound floor of the present invention is to be that raw material is made with blow moulding by HDPE 6098, high density polyethylene(HDPE) 5000S, UV, LLDPE 7042, EVA260 resin 5-19 with bonding film, do not contain formaldehyde in the raw material of production usefulness, therefore the finished product solid wooden compound floor that makes does not contain formaldehyde with bonding film yet; When using the bonding film that does not contain formaldehyde of the present invention to produce solid wooden compound floor, lay the bonding film of one deck solid wooden compound floor between the adjacent two layers wood single-plate, utilize pressing machine, under High Temperature High Pressure under the condition, the wood single-plate that lays is exerted pressure, when temperature reaches 170 ℃～195 ℃, bonding film is in molten state, adjacent wood single-plate is bonded together, behind the naturally cooling, solid wooden compound floor is condensed into solid-state with bonding film, adjacent wood single-plate is bonded together tightly, promptly makes solid wooden compound floor.Solid wooden compound floor of the present invention is strong with the bonding force of bonding film, the shearing resistance height of the solid wooden compound floor that makes, shearing resistance is 7.5MPa after testing, the test proof, even wood single-plate is destroyed, also be difficult to the two-layer wood single-plate that bonds together by this bonding film is separated; Solid wooden compound floor of the present invention with bonding film owing to have a higher melt temperature, make the solid wooden compound floor of production have good high temperature resistant and water resistance, under following condition, do the dipping stripping test, the solid wooden compound floor that makes was soaked 6 hours in 10 ℃～25 ℃ cold water, dried by the fire at least 18 hours in 40 ± 3 ℃ baking oven, peeling off or ftractureing does not all appear in arbitrary termination on floor or arbitrary limit again; Because solid wooden compound floor does not contain formaldehyde with bonding film, is a kind of environmental-friendly adhesion film, utilizes the solid wooden compound floor of this bonding film production that does not contain formaldehyde not contain formaldehyde yet, is a kind of environmental protection floor, can not pollute indoor environment, is of value to the healthy of people.
Claims (3)
1. the bonding film of solid wooden compound floor, it is characterized in that: described solid wooden compound floor is to be made by the raw material of following weight part with bonding film
HDPE?6098 35～45
High density polyethylene(HDPE) 5000S 35～45
Antiaging agent UV 1～2
LLDPE?7042 10～20
EVA260 resin 5～20.
2. the bonding film of solid wooden compound floor as claimed in claim 1 is characterized in that: described solid wooden compound floor is to be made by the raw material of following weight part with bonding film
HDPE?6098 40
High density polyethylene(HDPE) 5000S 40
Antiaging agent UV 2
LLDPE?7042 15
EVA260 resin 13.
3. the bonding film of solid wooden compound floor as claimed in claim 1 or 2, it is characterized in that: described solid wooden compound floor is made with blow moulding with bonding film.