CN102080171A - 一种用于制作电真空器件的复合材料 - Google Patents
一种用于制作电真空器件的复合材料 Download PDFInfo
- Publication number
- CN102080171A CN102080171A CN 201110040858 CN201110040858A CN102080171A CN 102080171 A CN102080171 A CN 102080171A CN 201110040858 CN201110040858 CN 201110040858 CN 201110040858 A CN201110040858 A CN 201110040858A CN 102080171 A CN102080171 A CN 102080171A
- Authority
- CN
- China
- Prior art keywords
- copper
- aluminum
- composite material
- vacuum device
- electric vacuum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是一种用于制作电真空器件的复合材料，其特征在于包括有如下质量百分比组分：铝：0～20%，铜：80～100%。本发明复合材料具有如下优点：因所有金属中，铝的电阻率、热导率最接近于铜，铝替代部分铜而形成的合金不会影响铜的导电、导热性能，而且部分铝原子会溶解于铜晶格而产生固溶强化，使铜铝合金的强度与硬度高于无氧铜，另外，铜铝合金与玻璃、陶瓷真空密封性能良好；由本发明复合材料制作的电真空器件，具有优异的导电、导热性能与真空密封性能，而且强度与硬度高，不易变形。
Description
技术领域
本发明涉及一种用于制作电真空器件的复合材料，属于用于制作电真空器件的复合材料的改进技术。
背景技术
现有电真空器件如磁控管、行波管、大功率发射管、X射线管等均采用无氧铜制作而成，无氧铜具有电阻率低、导热性能与真空密封性能好等优点，但是无氧铜价格持续上升导致了电真空器件生产成本不断增加，而且无氧铜强度与硬度较低，使磁控管、行波管、大功率发射管、X射线管等电真空器件易变形，导致电真空器件修复成本增加，严重变形会使电真空器件产生报废。
发明内容
本发明的目的在于考虑上述问题而提供一种不仅具有无氧铜的优点，而且强度与硬度高，避免变形的用于制作电真空器件的复合材料。
本发明的技术方案是：一种用于制作电真空器件的复合材料，其特征在于包括有如下质量百分比组分：铝：0～20%，铜：80～100%。
本发明复合材料具有如下优点：因所有金属中，铝的电阻率、热导率最接近于铜，铝替代部分铜而形成的合金不会影响铜的导电、导热性能，而且部分铝原子会溶解于铜晶格而产生固溶强化，使铜铝合金的强度与硬度高于无氧铜，另外，铜铝合金与玻璃、陶瓷真空密封性能良好；由本发明复合材料制作的电真空器件，具有优异的导电、导热性能与真空密封性能，而且强度与硬度高，不易变形。
具体实施方式
实施例1：
本发明用于制作磁控管零部件的复合材料，包括有如下质量百分比组分：铝：0～20%，铜：80～100%。
本实施例中，铝为5%，铜为95%；制作磁控管零部件过程如下：
1、将纯铝锭5%与纯铜锭95%置入真空熔炼炉，通电后熔化、搅拌、冷却，得到杂质含量总和低于0.01%的铜铝合金锭；
2、将步骤1中得到的铜铝合金锭冷轧、拉拨、冲压，并进一步定型成为磁控管零部件。
实施例2：
本发明用于制作行波管的复合材料，包括有如下质量百分比组分：铝为10%，铜为90%；制作行波管过程如下：
1、将纯铝锭10%与纯铜锭90%置入真空熔炼炉，通电后熔化、搅拌、冷却，得到杂质含量总和低于0.01%的铜铝合金锭；
2、将步骤1中得到的铜铝合金锭冷轧、拉拨、冲压，并进一步定型成为行波管部件。
实施例3：
本发明用于制作大功率发射管的复合材料，包括有如下质量百分比组分：铝为20%，铜为80%；制作大功率发射管过程如下：
1、将纯铝锭20%与纯铜锭80%置入真空熔炼炉，通电后熔化、搅拌、冷却，得到杂质含量总和低于0.01%的铜铝合金锭；
2、将步骤1中得到的铜铝合金锭冷轧、拉拨、冲压，并进一步定型成为大功率发射管部件。
Claims (1)
1.一种用于制作电真空器件的复合材料，其特征在于包括有如下质量百分比组分：铝：0～20%，铜：80～100%。