CN102074872B - 一种铜质多股电缆焊接工艺 - Google Patents
一种铜质多股电缆焊接工艺 Download PDFInfo
- Publication number
- CN102074872B CN102074872B CN 200910310163 CN200910310163A CN102074872B CN 102074872 B CN102074872 B CN 102074872B CN 200910310163 CN200910310163 CN 200910310163 CN 200910310163 A CN200910310163 A CN 200910310163A CN 102074872 B CN102074872 B CN 102074872B
- Authority
- CN
- China
- Prior art keywords
- welding
- cable
- end parts
- termination section
- copper stranded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种铜质多股电缆焊接工艺，包括电缆截断、端头部固定绑扎、热压成形、焊接和清理工序，所述的热压成形工序采用高温状态下压力定形工艺、即将绑扎固定的端头部用氧气火焰炬加热至800℃左右，然后采用铁榔头或其他工具锤击的方法施加压力使端头部成为扁圆形或半圆形或其他便于与焊接连接件焊接的形状。采用该工艺可使电缆焊接截面获得较理想的电缆端部形状，从而获得理想的焊接质量，并可节约焊接添料。
Description
【技术领域】
本发明涉及变压器的制造工艺，尤其是涉及一种铜质多股电缆的焊接工艺。
【背景技术】
变压器生产制造过程中有大量的铜质多股电缆焊接问题，如电缆与铜板接线片的焊接，电缆与电缆的焊接，电缆与绕组出头的焊接，按照一般的变压器生产工艺，多采用磷铜气焊方法，其做法是把电缆截断、将端头部固定绑扎后即进行焊接。这种焊接工艺存在以下不足：
1.因为电缆的圆截面影响，与其他焊接连接件的接触面较小(特别是大规格电缆)，容易导致接触面电流密度增大；
2.由于电缆截面为圆形，在截断后端部易于松散，且存有一定应力，焊接时不易定形，容易产生局部突起、毛刺等现象；
3.松散的单根电缆线芯经焊接磷铜渗透，极易脆化折断，产生电位悬浮；
4.由于松散的端头影响，需要消耗较多的焊接添料。
公开号为CN101299356A的发明专利申请公开了一种“电缆绞合导体整芯焊接方法”，该方法采取：在焊接前，选用与电缆绞合导体直径相应的压紧模具，先将电缆绞合导体端头压紧再用大电流加热两个端头、并同时施压进行焊接。该方法主要是解决由多根铜或铝单线绞合而成的电缆绞合导体的对焊的问题，而不适用于电缆与铜板接线片等其他焊接连接件的焊接，另外该方法的压紧需要整套与电缆绞合导体直径相应的压紧模具，导致焊接成本的增加。
【发明内容】
本发明的目的在于提供一种铜质多股电缆焊接工艺，采用该工艺可使电缆焊接截面获得较理想的电缆端部形状，从而获得理想的焊接质量，以克服已有技术存在的上述不足。
为解决上述技术问题，本发明采取的技术方案是：
一种铜质多股电缆焊接工艺，包括电缆截断、端头部固定绑扎、热压成形、焊接和清理工序，所述的热压成形工序采用高温状态下压力定形工艺，即将绑扎固定的端头部用氧气火焰炬加热至800℃左右，然后采用锤击的方法施加压力使端头部成为扁圆形或半圆形。
由于采取上述技术方案，本发明之一种铜质多股电缆焊接工艺具有如下有益效果：
1.通过高温状态下压力定形后，可获得所需要的较理想的电缆端部形状，使其与其他焊接连接件的接触面增大，且有较适配的外形及尺寸，容易达到焊接质量要求；而且可避免接触面电流密度增大；
2.通过高温状态下压力定形后，电缆端头部不会松散，焊接时定形容易，不易产生局部突起、毛刺等现象；
3.通过高温状态下压力定形，使松散的电缆端头热压后成为一整体，消除了单根电缆线芯经焊接磷铜渗透，极易脆化折断，产生电位悬浮的缺陷；
4.通过高温状态下压力定形，使松散的电缆端头热压后成为一整体，可节约焊接添料。
下面结合附图和实施例对本发明之一种铜质多股电缆焊接工艺的技术特征作进一步的说明。
【附图说明】
图1：传统的焊接工艺流程框图：
图2：本发明之一种铜质多股电缆焊接工艺流程框图。
【具体实施方式】
实施例：一种铜质多股电缆焊接工艺，包括电缆截断、端头部固定绑扎、热压成形、焊接和清理工序，所述的热压成形工序在所述端头部固定绑扎工序后、在施行焊接工序之前，该热压成形工序采用高温状态下压力定形工艺，即将绑扎固定的端头部用氧气火焰炬加热至800℃左右，即肉眼观察为暗红色时，然后采用铁榔头或其他工具锤击的方法施加压力使电缆的端头部成为扁圆形或半圆形，再将热压成形的电缆端头与焊接连接件焊接。
上述实施例中，所述端头部固定绑扎工序是采用铜金属线芯将电缆端头部扎紧，作为上述实施例的一种变换，也可用其他金属线芯将电缆端头部扎紧；另外也可根据需要将电缆端头部压成其他便于与焊接连接件焊接的形状。
Claims (2)
1.一种铜质多股电缆焊接工艺，包括电缆截断、端头部固定绑扎、焊接和清理工序，其特征在于：在所述端头部固定绑扎工序后、在施行焊接工序之前还有热压成形工序，所述的热压成形工序采用高温状态下压力定形工艺，即将绑扎固定的端头部用氧气火焰炬加热至800℃左右，然后采用锤击的方法施加压力使端头部成为扁圆形或半圆形。
2.根据权利要求1所述的一种铜质多股电缆焊接工艺，其特征在于：所述的端头部固定绑扎工序是采用铜金属线芯将电缆端头部扎紧。