CN102071392A - 链条、齿轮、轴承表层处理工艺 - Google Patents

链条、齿轮、轴承表层处理工艺 Download PDF

Info

Publication number
CN102071392A
CN102071392A CN2009102239425A CN200910223942A CN102071392A CN 102071392 A CN102071392 A CN 102071392A CN 2009102239425 A CN2009102239425 A CN 2009102239425A CN 200910223942 A CN200910223942 A CN 200910223942A CN 102071392 A CN102071392 A CN 102071392A
Authority
CN
China
Prior art keywords
gear
chain
bearing
spare part
reach
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2009102239425A
Other languages
English (en)
Inventor
缪建良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MIU JIANLIANG
Original Assignee
MIU JIANLIANG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MIU JIANLIANG filed Critical MIU JIANLIANG
Priority to CN2009102239425A priority Critical patent/CN102071392A/zh
Publication of CN102071392A publication Critical patent/CN102071392A/zh
Pending legal-status Critical Current

Abstract

一种链条、齿轮、轴承表层处理工艺，将链条、齿轮或轴承进行表面抛光，将抛光后的零件用夹具夹紧其非摩擦受力表面，放入真空中然后充入氮气，在-1个大气压下加热至900℃，充入甲醇裂解气进行渗入炭族元素，然后将裂解气排出，重新充入氮气并达到1个大气压，然后降温至200℃，保持该温度12h后，在将温度自然降至室温即可。本发明的优点在于，可以达到均匀的渗透过程，并可以将零件内部的结构应力合理的分散，其渗透层一致，保证零件在工作的过程中不受到内部应力影响。此外，零件的表面光滑度和硬度都可以达到较高的水准，普通的灰尘或沙粒不能造成表面划伤，不会影响传动过程中的摩擦。

Description

链条、齿轮、轴承表层处理工艺
技术领域
本发明涉及一种链条、齿轮、轴承等表层的处理工艺，具体的说是一种用渗透炭族元素的方式达到加强表面的硬度、耐磨度的技术方案。
背景技术
对于链条、齿轮、轴承等长期承压并且产生摩擦的零件，其耐磨性和硬度的要求比普通的工作条件的零件要高很多，所以链条、齿轮、轴承等零件一般都采用特殊的工艺来加强其耐磨性和硬度，比较常见的就是渗碳、表面电镀、淬火处理等。对于齿轮、轴承、和链条这样的零件一旦传动过程中有灰尘或沙粒进入其传动摩擦表面，将会对其使用寿命产生影响。
本发明就是根据实际应用进行研究，提供一种产生更高的耐磨性和硬度的工艺方法，满足更加恶劣工作条件的需要。
发明内容
本发明的目的是提供一种链条、齿轮、轴承表层处理工艺，使其可以再恶劣的环境下长时间的使用而不需要更换零部件。
本发明的目的是通过以下技术方案来实现：
一种链条、齿轮、轴承表层处理工艺，包括以下步骤，
一、将链条、齿轮或轴承进行表面抛光，
二、将抛光后的零件用夹具夹紧其非摩擦受力表面，放入真空中然后充入氮气，
三、在-1个大气压下加热至900℃，
四、充入甲醇裂解气进行渗入炭族元素，然后将裂解气排出，重新充入氮气并达到1个大气压，然后降温至200℃，保持该温度12h后，在将温度自然降至室温即可。
本发明的优点在于，可以达到均匀的渗透过程，并可以将零件内部的结构应力合理的分散，其渗透层一致，保证零件在工作的过程中不受到内部应力影响。此外，零件的表面光滑度和硬度都可以达到较高的水准，普通的灰尘或沙粒不能造成表面划伤，不会影响传动过程中的摩擦。
具体实施方式
本发明实施例所述的链条、齿轮、轴承表层处理工艺，包括以下步骤，
一、将链条、齿轮或轴承进行表面抛光，
二、将抛光后的零件用夹具夹紧其非摩擦受力表面，放入真空中然后充入氮气，
三、在-1个大气压下加热至900℃，
四、充入甲醇裂解气进行渗入炭族元素，然后将裂解气排出，重新充入氮气并达到1个大气压，然后降温至200℃，保持该温度12h后，在将温度自然降至室温即可。
此时零件的各项指标可以达到的标准为，表面硬度HV05超过550，表面渗透层的厚度可以达到0.1mm，渗透浓度可以达到1C％以上。
本发明的优点在于，可以达到均匀的渗透过程，并可以将零件内部的结构应力合理的分散，其渗透层一致，保证零件在工作的过程中不受到内部应力影响。此外，零件的表面光滑度和硬度都可以达到较高的水准，普通的灰尘或沙粒不能造成表面划伤，不会影响传动过程中的摩擦。

Claims (1)

1.一种链条、齿轮、轴承表层处理工艺，包括以下步骤，
一、将链条、齿轮或轴承进行表面抛光，
二、将抛光后的零件用夹具夹紧其非摩擦受力表面，放入真空中然后充入氮气，
三、在-1个大气压下加热至900℃，
四、充入甲醇裂解气进行渗入炭族元素，然后将裂解气排出，重新充入氮气并达到1个大气压，然后降温至200℃，保持该温度12h后，在将温度自然降至室温即可。
CN2009102239425A 2009-11-20 2009-11-20 链条、齿轮、轴承表层处理工艺 Pending CN102071392A (zh)