CN102070823A - Aes树脂改性聚丙烯复合材料 - Google Patents
Aes树脂改性聚丙烯复合材料 Download PDFInfo
- Publication number
- CN102070823A CN102070823A CN2009101128406A CN200910112840A CN102070823A CN 102070823 A CN102070823 A CN 102070823A CN 2009101128406 A CN2009101128406 A CN 2009101128406A CN 200910112840 A CN200910112840 A CN 200910112840A CN 102070823 A CN102070823 A CN 102070823A
- Authority
- CN
- China
- Prior art keywords
- modified polypropylene
- resin
- barium sulfate
- composite material
- light calcium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明改性聚丙烯复合材料采用AES树脂改性聚丙烯树脂,能有效提高产品抗老化性能和低温冲击强度;采用轻质碳酸钙与硫酸钡进行复合,并加入钛酸脂偶联剂进行表面改性处理后制成轻质碳酸钙与硫酸钡混合物复合填充剂,不但能提高产品加工过程中的物料流动性能,而且能提高复合填充剂与聚丙烯树脂的相容性。
Description
技术领域
本发明涉及一种改性聚丙烯复合材料,特别是一种采用AES树脂改性聚丙烯复合材料。
背景技术
目前公知的改性聚丙烯复合材料是采用玻璃纤维改性方法,以及添加超细无机粉体(如纳米碳酸钙、蒙脱土)方法来提高聚丙烯树脂的低温冲击强度;采用加抗氧剂方法来提高聚丙烯树脂的抗老化性能。但是,采用玻璃纤维改性聚丙烯树脂,虽然提高了聚丙烯树脂低温冲击强度,可是会降低聚丙烯树脂的抗老化性能,并且会影响生产环境;采用超细无机粉体改性聚丙烯树脂,在实际生产过程中易产生团聚现象,会严重影响产品的物理力学性能;加抗氧剂改性聚丙烯树脂,虽然会提高产品的抗老化性能,可是对聚丙烯树脂长期抗老化稳定性能提高有限。同时,为了降低聚丙烯树脂加工过程中的制造成本,通常采用添加碳酸钙填料,但是加入碳酸钙填料会影响物料加工过程中的流动性能。
发明内容
本发明的目的是提出一种综合性能优异的AES树脂改性聚丙烯复合材料。
本发明所采用的技术方案为:采用AES树脂改性聚丙烯树脂,能有效提高产品抗老化性能和低温冲击强度;采用轻质碳酸钙与硫酸钡进行复合,并加入钛酸脂偶联剂进行表面改性处理,制成轻质碳酸钙与硫酸钡混合物复合填充剂,不但能提高产品加工过程中的物料流动性能,而且能提高复合填充剂与聚丙烯树脂的相容性。
本发明主要生产工艺是按配方用普通聚丙烯树脂、AES树脂(丙烯腈/三元乙丙橡胶/苯乙烯共聚物)和经过钛酸脂偶联剂表面改性处理的轻质碳酸钙与硫酸钡复合填充剂,通过搅拌、熔融塑化、造粒、冷却工艺制造而成。
本发明的轻质碳酸钙和硫酸钡复合填充剂的原料配方为:
材料名称 | 重量比(%) |
轻质碳酸钙(400目) | 50-74 |
硫酸钡(300目) | 24-40 |
钛酸脂偶联剂 | 2-10 |
本发明的的原料配方为:
材料名称 | 重量比(%) |
聚丙烯树脂 | 62-74 |
AES树月旨(UB-500A或HW600G) | 3-5 |
轻质碳酸钙和硫酸钡复合填充剂 | 23-33 |
本发明不但具有普通聚丙烯的优点,而且具有优异的低温冲击强度、抗老化性能和加工流动性能等特点,主要应用于电力电缆护套管、化工管道、建筑排水管、以及汽车保险杆,仪器、仪表盒等领域。
以下结合附图对本发明进行详细描述。
图1为本发明的生产工艺路线图。
具体实施方案
根据图1所示,本发明的一种技术方案为:按重量比用65%的400目轻质碳酸钙与32%的300目硫酸钡进行搅拌复合,并加入3%的钛酸脂偶联剂进行表面改性处理,制成轻质碳酸钙与硫酸钡复合填充剂。然后按重量比用70%的聚丙烯树脂、4%AES树脂(UB-500A)和26%轻质碳酸钙与硫酸钡复合填充剂,通过搅拌、熔融塑化、造粒、冷却工艺制造而成。
Claims (3)
1.一种AES树脂改性聚丙烯复合材料,其特征是按配方用普通聚丙烯树脂、AES树脂(丙烯腈/三元乙丙橡胶/苯乙烯共聚物)和经过钛酸脂偶联剂表面改性处理的轻质碳酸钙与硫酸钡复合填充剂,通过搅拌、熔融塑化、造粒、冷却工艺制造而成。
2.根据权利要求1所述的AES树脂改性聚丙烯复合材料,其特征是轻质碳酸钙与硫酸钡复合填充剂是按重量比用50-74%的400目轻质碳酸钙与24-40%的300目硫酸钡进行搅拌复合,并加入2-10%的钛酸脂偶联剂通过表面改性处理制成。
3.根据权利要求1或2所述的AES树脂改性聚丙烯复合材料,其特征是原料配方(重量比)为:62-74%的聚丙烯树脂、3-5%AES树脂(UB-500A)和23-33%轻质碳酸钙与硫酸钡复合填充剂。