CN102069140B - Novel film coating sand - Google Patents
Novel film coating sand Download PDFInfo
- Publication number
- CN102069140B CN102069140B CN2011100390865A CN201110039086A CN102069140B CN 102069140 B CN102069140 B CN 102069140B CN 2011100390865 A CN2011100390865 A CN 2011100390865A CN 201110039086 A CN201110039086 A CN 201110039086A CN 102069140 B CN102069140 B CN 102069140B
- Authority
- CN
- China
- Prior art keywords
- sand
- percent
- film coating
- iron
- coating sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses film coating sand, which comprises the following components in percentage by weight: 2.0 to 2.1 percent of resin, 0.03 to 0.05 percent of coupling agent, 0.2 to 0.32 percent of urotropine, 0.1 to 0.15 percent of calcium stearate, 0.08 to 0.1 percent of iron oxide red, 6 to 8 percent of iron sand and the balance of silica sand. Compared with the conventional film coating sand, the film coating sand has the performance of delaying the gas forming velocity by 3 to 5 seconds and inhibiting the generation of nitrogen besides the performance of the conventional film coating sand, can effectively reduce nitrogen pores generated on castings, and greatly improves the yield of high-nickel austenitic ductile iron castings.
Description
Technical field
The present invention relates to the making of precoated sand, especially make the low anti-nitrogen precoated sand of getting angry.
Background technology
Along with the progress of science and technology, the development of society; The consumer is increasingly high to the quality requirement of product, and corresponding high-end product can not meet the demands with common raw material, falls behind gradually, eliminates; And then through the prescription, technology adjustment improve raw-material serviceability; Be used to produce high-end product, this material of high-nickel austenite magnesium iron is because the particularity of its material (flowability is poor, setting temperature is high, be prone to produce nitrogen pore etc.) uses the foundry goods of conventional this kind of precoated sand making core production material can cause a lot of insurmountable defectives; Therefore just must improve the performance of precoated sand, it is satisfied the demands.
Make core with precoated sand, have the production efficiency height, characteristics such as coremaking is convenient, core up time length; Arriving widely in casting used, but its weak point is also arranged, and be bigger such as its gas forming amount; Be prone to produce nitrogen pore; When especially core was used to produce the high-nickel austenite magnesium iron, pin hole, nitrogen pore defective were a lot, adjust other process meanses and also produce little effect.
Summary of the invention
The present invention is intended to overcome the deficiency of above prior art, provides a kind of foundry goods that can effectively prevent to produce the novel precoated sand of nitrogen pore.
Technical solution problem of the present invention adopts following technical scheme:
A kind of novel precoated sand, each component proportioning by weight is following: resin 2.1%, coupling agent 0.05%, methenamine 0.25%, calcium stearate 0.126%, iron oxide red 0.08%, iron sand 8%, surplus are silica sand.
Beneficial effect of the present invention is following: compare with conventional precoated sand; This precoated sand also has the raising rate of delaying 3-5S except that the performance with conventional precoated sand, suppress the performance of nitrogen gas generation; Can effectively reduce foundry goods and produce nitrogen pore, improve the yield rate of high-nickel austenite iron casting greatly.
The specific embodiment
Embodiment 1
A kind of novel precoated sand, each component proportioning by weight is following:
Resin 2.1%, coupling agent 0.05%, methenamine 0.25%, calcium stearate 0.126%, iron oxide red 0.08%, iron sand 8%.
Embodiment 2
A kind of novel precoated sand, each component proportioning by weight is following:
Resin 2.0%, coupling agent 0.03%, methenamine 0.2%, calcium stearate 0.15%, iron oxide red 0.1%, iron sand 7%, surplus are silica sand.
Embodiment 3
A kind of novel precoated sand, each component proportioning by weight is following:
Resin 2.0%, coupling agent 0.04%, methenamine 0.3%, calcium stearate 0.13%, iron oxide red 0.09%, iron sand 6%, surplus are silica sand.
Claims (1)
1. a precoated sand is characterized in that, each component proportioning by weight is following: resin 2.1%, coupling agent 0.05%, methenamine 0.25%, calcium stearate 0.126%, iron oxide red 0.08%, iron sand 8%, surplus are silica sand.