CN102357648A - Chill coating for casting - Google Patents
Chill coating for casting Download PDFInfo
- Publication number
- CN102357648A CN102357648A CN2011103093042A CN201110309304A CN102357648A CN 102357648 A CN102357648 A CN 102357648A CN 2011103093042 A CN2011103093042 A CN 2011103093042A CN 201110309304 A CN201110309304 A CN 201110309304A CN 102357648 A CN102357648 A CN 102357648A
- Authority
- CN
- China
- Prior art keywords
- graphite powder
- powder
- chill
- coating
- casting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a chill coating for casting, which is composed of graphite powder, sodium bentonite, iron oxide red, silicon iron powder, colophony and ethyl alcohol. Amorphous graphite powder is combined with flaky-shaped graphite powder in usage. The chill coating for the casting can effectively prevent chill from appearing at chill portions and improve casting quality.
Description
Technical field
The invention belongs to casting technology field, especially relate to a kind of foundry goods and use chill coating.
Background technology
In spheroidal graphite cast-iron was produced, for a change the casting solidification mode guaranteed that shrinkage porosite, shrinkage cavity do not appear in foundry goods inside; Usually place the chill of some; Thereby reach the quality problems that solve shrinkage porosite, shrinkage cavity, but another outstanding quality problems occurred, spoken parts in traditional operas appears in chill position foundry goods; Processing difficulties is simultaneously also with air holes.Aborning, use traditional chill coating, as: 1. rosin 25%, jet-black 15%, system are with oil 60%; 2. graphite powder 94%, potter's clay 6%, water are an amount of.But effect is all not obvious, and particularly the spoken parts in traditional operas at chill position is difficult for eliminating, and has only and adopts heat-treating methods to eliminate again, has increased the castings production cost.
Summary of the invention
The objective of the invention is: provide a kind of foundry goods of avoiding the chill position spoken parts in traditional operas, raising casting quality to occur to use chill coating.
Technical scheme of the present invention is: this coating is made up of following material by weight percentage: graphite powder 86-91%, sodium bentonite 2-4%, ferric oxide red powder 2-3%, ferrosilicon powder 2-3%, rosin 3-4%, ethanol are an amount of; Said graphite powder is that amorphous graphite powder and the combination of flaky graphite powder are used, and is by weight percentage: flaky graphite powder 25-35%, amorphous graphite powder 65-75%.
Preferred version of the present invention is: this coating is made up of following material by weight percentage: graphite powder 88.5%, sodium bentonite 3%, ferric oxide red powder 2.5%, ferrosilicon powder 2.5%, rosin 3.5%, ethanol are an amount of; Said graphite powder is that amorphous graphite powder and the combination of flaky graphite powder are used, and is by weight percentage: flaky graphite powder 30%, amorphous graphite powder 70%.
The invention has the beneficial effects as follows: the present invention chooses graphite powder as the coating skeleton, swashs heat coating cracking down for guaranteeing thick and large casting high temperature, and amorphous graphite and flaky graphite combination are used, and having good temperature resistance can; Simultaneously, for preventing bleb, add the ferric oxide red powder of 2-3%; Select for use an amount of high purity ethanol as carrier, prevent that moisture is too high, produce pore; Select for use sodium bentonite as suspending agent, reduced cost; For preventing the chill pore, select hydrophobic type binding agent-rosin for use; Add ferrosilicon powder and can prevent that spoken parts in traditional operas from appearring in foundry goods.This coating has good wetability, has improved normal temperature, elevated temperature strength and the rigidity of coating, effectively avoids the chill position spoken parts in traditional operas to occur, reduces casting defect.In castings production in enormous quantities, improve casting yield, low cost of manufacture.
The specific embodiment
Embodiment 1: this chill coating is made up of following material by weight percentage: graphite powder 88.5%, sodium bentonite 3%, ferric oxide red powder 2.5%, ferrosilicon powder 2.5%, rosin 3.5%, ethanol are an amount of; Graphite powder is that amorphous graphite powder and the combination of flaky graphite powder are used, and is by weight percentage: flaky graphite powder 30%, amorphous graphite powder 70%.
The collocation method of this coating: 1. rosin is pulverized, cross 200/270 screen size; 2. after rosin being dissolved in ethanol, add bentonite and stir, add flaky graphite powder, amorphous graphite powder, ferric oxide red powder, ferrosilicon powder then, use stirs.During use, evenly brush is on the chill working surface with spread pen, and the about 0.1-0.3mm of thickness lights baking then.
Embodiment 2: this chill coating is made up of following material by weight percentage: graphite powder 89%, sodium bentonite 2%, ferric oxide red powder 3%, ferrosilicon powder 3%, rosin 3%, ethanol are an amount of; The ratio of amorphous graphite powder and flaky graphite powder is 25:75.
Embodiment 3: this chill coating is made up of following material by weight percentage: graphite powder 88%, sodium bentonite 4%, ferric oxide red powder 2%, ferrosilicon powder 2%, rosin 4%, ethanol are an amount of; The ratio of amorphous graphite powder and flaky graphite powder is 35:65.
Embodiment 4: this chill coating is made up of following material by weight percentage: graphite powder 86%, sodium bentonite 4%, ferric oxide red powder 3%, ferrosilicon powder 3%, rosin 4%, ethanol are an amount of; The usage ratio of amorphous graphite powder and flaky graphite powder is 30:70.
Embodiment 5: this chill coating is made up of following material by weight percentage: graphite powder 91%, sodium bentonite 2%, ferric oxide red powder 2%, ferrosilicon powder 2%, rosin 3%, ethanol are an amount of; The usage ratio of amorphous graphite powder and flaky graphite powder is 32:68.
Claims (2)
1. a foundry goods is used chill coating, it is characterized in that: this coating is made up of following material by weight percentage: graphite powder 86-91%, sodium bentonite 2-4%, ferric oxide red powder 2-3%, ferrosilicon powder 2-3%, rosin 3-4%, ethanol are an amount of; Said graphite powder is that amorphous graphite powder and the combination of flaky graphite powder are used, and is by weight percentage: flaky graphite powder 25-35%, amorphous graphite powder 65-75%.
2. foundry goods according to claim 1 is used chill coating, it is characterized in that: this coating is made up of following material by weight percentage: graphite powder 88.5%, sodium bentonite 3%, ferric oxide red powder 2.5%, ferrosilicon powder 2.5%, rosin 3.5%, ethanol are an amount of; Said graphite powder is that amorphous graphite powder and the combination of flaky graphite powder are used, and is by weight percentage: flaky graphite powder 30%, amorphous graphite powder 70%.