CN102061464A - 一种新型环保钝化剂 - Google Patents
一种新型环保钝化剂 Download PDFInfo
- Publication number
- CN102061464A CN102061464A CN 200910194012 CN200910194012A CN102061464A CN 102061464 A CN102061464 A CN 102061464A CN 200910194012 CN200910194012 CN 200910194012 CN 200910194012 A CN200910194012 A CN 200910194012A CN 102061464 A CN102061464 A CN 102061464A
- Authority
- CN
- China
- Prior art keywords
- steel
- weight part
- phosphoric acid
- promotor
- active agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种新型环保钝化剂，其特征在于包括硅酸钠30-40g/L、磷酸盐10-20g/L、促进剂5-10g/L、表面活性剂0.5-1g/L，所述的硅酸盐和磷酸盐的质量比为2-3∶1，所述促进剂为氯酸钾，所述的表面活性剂由OP-10、TX-100和NP-5构成，其中，OP-10的重量份为1.8-2.2，TX-100的重量份为0.8-1.2，P-5的重量份为0.8-1.2，混合液最后用磷酸来调节pH值到3-5。本发明与已有技术相比，具有既能使钢铁零件表面快速钝化，同时为又不带来环境污染等问题的优点。
Description
技术领域
本发明涉及一种钢铁快速钝化用的钝化剂。
背景技术
钢铁材料的腐蚀无时无刻不在发生，据统计，每年有10％的钢材因为腐蚀而无法回收。为防止腐蚀，减少因钢铁材料腐蚀造成的巨大损失，就必须采取各种各样的防腐方法，对钢铁表面进行钝化处理就是其中一种手段。目前，用于钢铁钝化处理的钝化剂大概有三类：铬酸盐、钼酸盐和有机钝化剂。用铬酸盐作钝化剂成本低、使用方便、耐腐蚀性能好，但是其毒性高且易致癌，排放后对环境造成极大的污染难以治理，随着环保意识的增强，铬酸盐的使用受到严格的限制。有机钝化剂价格较昂贵，而且会散发出各种刺激性的气味，长期接触有致癌作用，钝化剂容易产生细菌使水体变质而产生环境污染问题。钼酸盐是一种有效的成膜促进剂和缓释剂，因其成本高昂，且钝化后耐腐蚀性能不及铬酸盐，使得大多数企业不能接受。
同时，由于需要钝化的钢铁零件形状多样，钝化后零件表面会残留部分钝化液，这部分水分使得零件在加热烘干过程中极易发生腐蚀，生产厂家不得不在钝化液中加入强氧化性物质来加强其钝化剂的防腐蚀性能。但是，长期接触强氧化性物质会对操作工人的身体造成伤害，而且对工厂生产设备、生产产地等要求更高，生产成本提高。因此，寻找一种简单、快速、经济、实用、环保的钝化剂具有重要意义。
发明内容
本发明的发明目的在于提供一种既能使钢铁零件表面快速钝化，同时为又不带来环境污染等问题的新型环保钝化剂。
本发明是这样实现的：包括
硅酸钠30-40g/L，
磷酸盐10-20g/L
促进剂5-10g/L
表面活性剂0.5-1g/L
所述的硅酸盐和磷酸盐的质量比为2-3∶1，
所述促进剂为氯酸钾，
所述的表面活性剂由OP-10、TX-100和NP-5构成，其中，OP-10的重量份为1.8-2.2，TX-100的重量份为0.8-1.2，P-5的重量份为0.8-1.2，
混合液最后用磷酸来调节PH值到3-5。
使用时，可采用浸涂或喷涂的方法对钢铁进行钝化。经过此钝化液处理的钢材，表面快速的形成一层均匀致密的钝化膜，这种膜是由带负电荷的硅酸根离子或者是二氧化硅胶团与带正电荷的锌离子配位作用所形成的保护膜，耐腐蚀性能强，经过钝化后的钢铁零件不论是吹干还是200℃烘干均有良好的耐腐蚀性能。同时，由于加入了少量的非离子表面活性剂，极大的降低了溶液的表面张力，使得残留在钢铁表面的钝化液可以在极短的时间内脱落。
本发明的钝化液能与钢铁表面快速反应形成钝化膜膜层，且从根本上解决了由于钢铁形状多样而引起的挂水腐蚀的问题，构成钝化液的硅酸钠、磷酸盐、促进剂都是无毒无害、廉价的化工原料，本发明配制简单，钝化后的钢铁零件满足欧洲ROHS指令要求。
本发明与已有技术相比，具有既能使钢铁零件表面快速钝化，同时为又不带来环境污染等问题的优点。
具体实施方式：
现结合实施例对本发明作进一步详细描述：
实施例一：
本发明是这样实现的：包括
硅酸钠30g/L，
磷酸盐10g/L
促进剂5g/L
表面活性剂0.5g/L
所述的硅酸盐和磷酸盐的质量比为3∶1，
所述促进剂为氯酸钾，
所述的表面活性剂由OP-10、TX-100和NP-5构成，其中，OP-10的重量份为1.8，TX-100的重量份为0.8，P-5的重量份为0.8，
混合液最后用磷酸来调节PH值到3。
采用浸涂或喷涂的方法对钢铁进行钝化，经过钝化后的钢铁零件不论是吹干还是200℃烘干均有良好的耐腐蚀性能。
实施例二：
本发明是这样实现的：包括
硅酸钠35g/L，
磷酸盐15g/L
促进剂7g/L
表面活性剂0.7g/L
所述的硅酸盐和磷酸盐的质量比为2.5∶1，
所述促进剂为氯酸钾，
所述的表面活性剂由OP-10、TX-100和NP-5构成，其中，OP-10的重量份为2，TX-100的重量份为1，P-5的重量份为1，
混合液最后用磷酸来调节PH值到4。
采用浸涂或喷涂的方法对钢铁进行钝化，经过钝化后的钢铁零件不论是吹干还是200℃烘干均有良好的耐腐蚀性能。
实施例三：
本发明是这样实现的：包括
硅酸钠40g/L，
磷酸盐20g/L
促进剂10g/L
表面活性剂1g/L
所述的硅酸盐和磷酸盐的质量比为2∶1，
所述促进剂为氯酸钾，
所述的表面活性剂由OP-10、TX-100和NP-5构成，其中，OP-10的重量份为2.2，TX-100的重量份为1.2，P-5的重量份为1.2，
混合液最后用磷酸来调节PH值到5。
采用浸涂或喷涂的方法对钢铁进行钝化，经过钝化后的钢铁零件不论是吹干还是200℃烘干均有良好的耐腐蚀性能。
实施例四：
本发明是这样实现的：包括
硅酸钠40g/L，
磷酸盐15g/L
促进剂10g/L
表面活性剂0.5g/L
所述的硅酸盐和磷酸盐的质量比为8∶3，
所述促进剂为氯酸钾，
所述的表面活性剂由OP-10、TX-100和NP-5构成，其中，OP-10的重量份为2.2，TX-100的重量份为0.8，P-5的重量份为1.2，
混合液最后用磷酸来调节PH值到3。
采用浸涂或喷涂的方法对钢铁进行钝化，经过钝化后的钢铁零件不论是吹干还是200℃烘干均有良好的耐腐蚀性能。
实施例五：
本发明是这样实现的：包括
硅酸钠30g/L，
磷酸盐15g/L
促进剂5g/L
表面活性剂1g/L
所述的硅酸盐和磷酸盐的质量比为2∶1，
所述促进剂为氯酸钾，
所述的表面活性剂由OP-10、TX-100和NP-5构成，其中，OP-10的重量份为1.8，TX-100的重量份为1.2，P-5的重量份为0.8，
混合液最后用磷酸来调节PH值到5。
采用浸涂或喷涂的方法对钢铁进行钝化，经过钝化后的钢铁零件不论是吹干还是200℃烘干均有良好的耐腐蚀性能。
Claims (1)
1.一种新型环保钝化剂，其特征在于包括
硅酸钠30-40g/L、
磷酸盐10-20g/L、
促进剂5-10g/L、
表面活性剂0.5-1g/L，
所述的硅酸盐和磷酸盐的质量比为2-3∶1，
所述促进剂为氯酸钾，
所述的表面活性剂由OP-10、TX-100和NP-5构成，其中，OP-10的重量份为1.8-2.2，TX-100的重量份为0.8-1.2，P-5的重量份为0.8-1.2，
混合液最后用磷酸来调节PH值到3-5。