CN102041374B - 大直径整体莱氏体钢冷轧辊的差温淬火法 - Google Patents

大直径整体莱氏体钢冷轧辊的差温淬火法 Download PDF

Info

Publication number
CN102041374B
CN102041374B CN 201110021699 CN201110021699A CN102041374B CN 102041374 B CN102041374 B CN 102041374B CN 201110021699 CN201110021699 CN 201110021699 CN 201110021699 A CN201110021699 A CN 201110021699A CN 102041374 B CN102041374 B CN 102041374B
Authority
CN
China
Prior art keywords
temperature
cold roll
quenching
cooling
steel cold
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 201110021699
Other languages
English (en)
Other versions
CN102041374A (zh
Inventor
张玉力
杨立凤
杜晓强
杨旭东
景群社
刘瑞明
曹敏
刘国庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANXI BUYEASY MACHINERY MANUFACTURE CO Ltd
Original Assignee
SHANXI BUYEASY MACHINERY MANUFACTURE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANXI BUYEASY MACHINERY MANUFACTURE CO Ltd filed Critical SHANXI BUYEASY MACHINERY MANUFACTURE CO Ltd
Priority to CN 201110021699 priority Critical patent/CN102041374B/zh
Publication of CN102041374A publication Critical patent/CN102041374A/zh
Application granted granted Critical
Publication of CN102041374B publication Critical patent/CN102041374B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及莱氏体钢冷轧辊的热处理方法,具体为一种大直径整体莱氏体钢冷轧辊的差温淬火法,解决了现有大直径整体莱氏体钢冷轧辊淬火后易发生开裂倾向的问题。大直径整体莱氏体钢冷轧辊的差温淬火法,选取预热温度进行等温预热,然后快速加热至淬火温度后保温;接着选取冷却温度进行等温冷却,最后再在空气中冷却,预热温度的范围为大于完全奥氏体化温度临界转变点且小于实际淬火温度30℃,冷却温度的范围为大于马氏体转变点且小于马氏体转变点

Description

大直径整体莱氏体钢冷轧辊的差温淬火法
技术领域
本发明涉及莱氏体钢冷轧辊的热处理方法,具体为一种大直径整体莱氏体钢冷轧辊的差温淬火法。
背景技术
对于具有共晶碳化物组织的莱氏体钢,经过锻造热处理后,较非莱氏体钢具有更高的硬度和耐磨性,主要用于制造大负荷冷轧机的工作辊。但随着直径的增加,加工所需坯料的钢锭尺寸也必然增大,其中心碳化物的堆积也会越来越严重,熔点相对较低,在锻造或热处理加热时易产生过热组织。尤其是其合金元素含量高——其淬透性指数较高,对于大直径(有效尺寸超过200毫米)整体莱氏体钢冷轧辊工件,淬火后中心组织依然会获得高碳马氏体组织,进而增加的工件的开裂倾向。
发明内容
本发明为了解决现有大直径整体莱氏体钢冷轧辊淬火后易发生开裂倾向的问题,提供了一种大直径整体莱氏体钢冷轧辊的差温淬火法。
本发明是采用如下技术方案实现的:大直径整体莱氏体钢冷轧辊的差温淬火法,选取预热温度进行等温预热,然后快速加热至淬火温度后保温;接着选取冷却温度进行等温冷却,最后再在空气中冷却,预热温度的范围为大于完全奥氏体化温度临界转变点                                                
Figure 2011100216996100002DEST_PATH_IMAGE001
Figure 928417DEST_PATH_IMAGE002
且小于实际淬火温度30℃,冷却温度的范围为大于马氏体转变点
Figure 2011100216996100002DEST_PATH_IMAGE003
且小于马氏体转变点
Figure 119621DEST_PATH_IMAGE003
+100℃。采用该差温淬火法通过对预热温度和冷却温度的控制是通过多次试验测得的,保证大直径整体莱氏体钢冷轧辊表层与中心形成适当的温度梯度,避免冷轧辊淬火开裂。
等温预热后加热至淬火温度的升温速度为大于30℃/h,且加热至淬火温度后保温时间大于0.5h,该数量亦是通过大量试验得出的,进一步保证了大直径整体莱氏体钢冷轧辊淬火后整体皆为马氏体组织,冷轧辊表面与其中心的硬度梯度较小,能够满足大负荷轧机工况的条件。
本发明通过合理的设计克服了现有大直径整体莱氏体钢冷轧辊淬火后易发生开裂倾向的问题,整体淬透全硬化,工作层硬度可达60-67HRC,冷轧辊中心与表层的硬度梯度小于10HRC。
具体实施方式
实施例1
大直径整体莱氏体钢冷轧辊是直径为300mm、坯料低倍组织为4级的模具钢Cr12MoV,选取预热温度进行等温预热,然后快速加热至淬火温度后保温;接着选取冷却温度进行等温冷却,最后再在空气中冷却,预热温度为950℃,冷却温度为250℃。等温预热后加热至淬火温度的升温速度为100℃/h,且加热至淬火温度后保温时间1.5h。具体实施过程中,淬火温度为1050℃,且等温预热和等温冷却的时间分别为3h和1.2h。
实施例2
大直径整体莱氏体钢冷轧辊是直径为250mm、坯料低倍组织为3.5级的高速钢W2Mo8Cr4V,选取预热温度进行等温预热,然后快速加热至淬火温度后保温;接着选取冷却温度进行等温冷却,最后再在空气中冷却,预热温度为1100℃,冷却温度为250℃。等温预热后加热至淬火温度的升温速度为100℃/h,且加热至淬火温度后保温时间1.2h。具体实施过程中,淬火温度为1180℃,且等温预热和等温冷却的时间分别为2.5h和1h。
实施例3
大直径整体莱氏体钢冷轧辊是直径为350mm、坯料低倍组织为3级的半高速钢Cr8MoWSiV3,选取预热温度进行等温预热,然后快速加热至淬火温度后保温;接着选取冷却温度进行等温冷却,最后再在空气中冷却,预热温度为1070℃,冷却温度为250℃。等温预热后加热至淬火温度的升温速度为100℃/h,且加热至淬火温度后保温时间2h。具体实施过程中,淬火温度为1130℃,且等温预热和等温冷却的时间分别为3.5h和1.5h。

Claims (1)

1.一种大直径整体莱氏体钢冷轧辊的差温淬火法,其特征在于:选取预热温度进行等温预热,然后快速加热至淬火温度后保温;接着选取冷却温度进行等温冷却,最后再在空气中冷却,预热温度的范围为大于完全奥氏体化温度临界转变点 
Figure 211859DEST_PATH_IMAGE002
且小于实际淬火温度30℃,冷却温度的范围为大于马氏体转变点
Figure 2011100216996100001DEST_PATH_IMAGE003
且小于马氏体转变点
Figure 354258DEST_PATH_IMAGE003
+100℃,等温预热后加热至淬火温度的升温速度为大于30℃/h,且加热至淬火温度后保温时间大于0.5h。
CN 201110021699 2011-01-19 2011-01-19 大直径整体莱氏体钢冷轧辊的差温淬火法 Active CN102041374B (zh)