CN102011467A - Cement, mortar or concrete photoluminescent board and photoluminescent wall surface or ground and preparation methods thereof - Google Patents
Cement, mortar or concrete photoluminescent board and photoluminescent wall surface or ground and preparation methods thereof Download PDFInfo
- Publication number
- CN102011467A CN102011467A CN 201010532249 CN201010532249A CN102011467A CN 102011467 A CN102011467 A CN 102011467A CN 201010532249 CN201010532249 CN 201010532249 CN 201010532249 A CN201010532249 A CN 201010532249A CN 102011467 A CN102011467 A CN 102011467A
- Authority
- CN
- China
- Prior art keywords
- mortar
- cement
- concrete
- luminous
- ground
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to building materials and relates to a cement, mortar or concrete photoluminescent board. Photoluminescent substance particles are filled in the board, are exposed on the surface of the board and form the same flat and smooth surface with the surface of the board; or the outer surface of the cement, mortar or concrete board is at least provided with a photoluminescent substance layer, wherein the photoluminescent substance particles are filled inside the photoluminescent substance layer, are exposed and form the same flat and smooth surface with the surface of the photoluminescent substance layer. The invention also relates to a preparation method of the cement, mortar or concrete photoluminescent board. The invention has the advantages that: the photoluminescent board can conduct a function of illumination in a dark environment, saves electric energy, also can be adjusted into various colors to emit colored light, can be used as stair treads, toilet walls or floors, inner wallboards or floor tiles of sitting rooms, windowsills and wall decorative plates, and also can be used as outer wall adhesion plates for buildings and can be used for paving road surfaces.
Description
(1) technical field
The invention belongs to building materials, relate to a kind of cement, mortar or concrete luminous plate, noctilucence metope or ground and method for making thereof.
(2) background technology
At present, the place that all there are ground, metope, stair in worker China Democratic National Construction Association and will use the cement treatment surface, under the situation that does not adopt light source, all be very dark evening.For solving lighting problem, on stair or body of wall, electric light is installed, but can be wasted a large amount of electric energy like this.
(3) summary of the invention
The present invention is in order to remedy the deficiencies in the prior art, and a kind of simple in structure, easy to use, cement in dark place good illumination effect, mortar or concrete luminous plate, noctilucence metope or ground are provided, with and preparation method thereof.
The present invention is achieved through the following technical solutions:
Cement of the present invention, mortar or concrete luminous plate, its special character is: plate body inside has the luminous substance particle, and the luminous substance particle appears on the plate body surface and constitutes same smooth smooth surface with the plate body surface; Perhaps, have at least one to wear the luminous substance layer and constitute, the luminous substance particle is arranged in the luminous substance layer, and this particle is exposed outside with the luminous substance laminar surface and constitutes same smooth smooth surface by the plate body appearance of cement, mortar or concrete slab.
Cement of the present invention, mortar or concrete luminous plate, preferred version be, plate body inside also has a large amount of color pebbles, and color pebble appears on the plate body surface and constitutes same smooth smooth surface with the plate body surface; Perhaps, also have a large amount of color pebbles in the luminous substance layer of cement, mortar or concrete slab, and color pebble is exposed outside with the luminous substance laminar surface and constitutes same smooth smooth surface.
Cement of the present invention, mortar or concrete luminous plate, luminous substance particle are the luminous material particle of rare-earth alumo silicate.
Cement of the present invention, mortar or concrete luminous plate, the length of this plate and/or width are during greater than 60 centimetres, and there is reinforcing bar its inside.
Cement of the present invention, mortar or concrete noctilucence ground or metope, ground or metope inside have the luminous substance particle, and the luminous substance particle is on ground or the metope surface appears and constitute same smooth smooth surface with ground or metope surface.
Cement of the present invention, mortar or concrete noctilucence ground or metope, ground or metope inside also have a large amount of color pebbles, and color pebble is on ground or the metope surface appears and constitute same smooth smooth surface with ground or metope surface; The luminous substance particle is the luminous material particle of rare-earth alumo silicate.
The preparation method of cement of the present invention, mortar or concrete luminous plate, a-1 forms by step, perhaps is made up of successively step a, b, c:
A-1. prepare cement, mortar or concrete slurry, and add the luminous substance particle in the slurry and stir, then it is poured into plate, after drying reaches the above intensity of C30 firmly admittedly, smoothly and expose luminescent substance surface finish;
A. prepare cement, mortar or concrete slurry, then it is poured into plate;
B. go into the luminous substance particle at cement, mortar or the concrete slab surface arsis of ot-yet-hardened, and casting cement, mortar or concrete slurry are used for levelling between particle;
C. after the plate drying after the levelling reaches the above intensity of C30 firmly admittedly, that the surface finish of levelling is level and smooth and expose luminescent substance.
The preparation method of cement of the present invention, mortar or concrete luminous plate in step a-1, also will add color pebble when adding the luminous substance particle in the slurry and stirs; In step b, the color pebble of also will beating in when beating in the luminous substance particle; Luminous substance is the rare-earth alumo silicate luminescent material.
The preparation method of cement of the present invention, mortar or concrete noctilucence ground or metope, form by following steps: preparation cement, mortar or concrete slurry, and adding the luminous substance particle in the slurry stirs, then it is poured on ground matrix or the wall matrix, after drying reaches the above intensity of C30 firmly admittedly, that surface finish is level and smooth and expose luminescent substance.
The preparation method of cement of the present invention, mortar or concrete noctilucence ground or metope also will add color pebble when adding the luminous substance particle in the slurry and stirs; Luminous substance is the rare-earth alumo silicate luminescent material.
The invention has the beneficial effects as follows, illuminating effect can not played in luminous plate and noctilucence metope and noctilucence ground in having the environment of light, save electric energy, all right furnishing multicolour, send colourama, luminous plate can be used for broadstep (reinforcing bar is arranged), lavatory wall or floor, parlor inner wall panel or wood floor bolck, windowsill (reinforcing bar is arranged), wall fitting plate, can be used as also that external wall sticks plate and with this plate road surface pavement, also can be used as the outer panel of ornament.The luminous plate size will have reinforcing bar in inside during greater than 60 centimetres.
(4) description of drawings
Fig. 1 is the structural representation that plate body of the present invention, metope or inside, ground have the luminous substance particle.Fig. 2 has the structural representation of luminous substance layer for plate body appearance of the present invention.
Among the figure, 1 cement, mortar or concrete slab, 2 luminous substance layers, 3 luminous substance particles, 4 color pebbles.
(5) specific embodiment
Accompanying drawing is a kind of specific embodiment of the present invention.
Cement of the present invention, mortar or concrete luminous plate, plate body inside has luminous substance particle 3, and the luminous substance particle appears on the plate body surface and constitutes same smooth smooth surface with the plate body surface; Perhaps, have at least one to wear luminous substance layer 2 and constitute, luminous substance particle 3 is arranged in the luminous substance layer, and this particle is exposed outside with the luminous substance laminar surface and constitutes same smooth smooth surface by the plate body appearance of cement, mortar or concrete slab 1.Plate body inside also has a large amount of color pebble 4, and color pebble appears on the plate body surface and constitutes same smooth smooth surface with the plate body surface; Perhaps, also have a large amount of color pebble 4 in the luminous substance layer 2 of cement, mortar or concrete slab 1, and color pebble is exposed outside with the luminous substance laminar surface and constitutes same smooth smooth surface.The luminous substance particle is the luminous material particle of rare-earth alumo silicate.The length of this plate and/or width are during greater than 60 centimetres, and there is reinforcing bar its inside.
The preparation method of cement of the present invention, mortar or concrete luminous plate, a-1 forms by step, perhaps is made up of successively step a, b, c:
A-1. prepare cement, mortar or concrete slurry, and add the luminous substance particle in the slurry and stir, then it is poured into plate, after drying reaches the above intensity of C30 firmly admittedly, smoothly and expose luminescent substance surface finish;
A. prepare cement, mortar or concrete slurry, then it is poured into plate;
B. go into the luminous substance particle at cement, mortar or the concrete slab surface arsis of ot-yet-hardened, and casting cement, mortar or concrete slurry are used for levelling between particle;
C. after the plate drying after the levelling reaches the above intensity of C30 firmly admittedly, that the surface finish of levelling is level and smooth and expose luminescent substance.
The preparation method of cement of the present invention, mortar or concrete luminous plate in step a-1, also will add color pebble when adding the luminous substance particle in the slurry and stirs; In step b, the color pebble of also will beating in when beating in the luminous substance particle; Luminous substance is the rare-earth alumo silicate luminescent material.
Cement of the present invention, mortar or concrete noctilucence ground or metope, ground or metope inside have the luminous substance particle, and the luminous substance particle is on ground or the metope surface appears and constitute same smooth smooth surface with ground or metope surface.Ground or metope inside also have a large amount of color pebbles, and color pebble is on ground or the metope surface appears and constitute same smooth smooth surface with ground or metope surface; The luminous substance particle is the luminous material particle of rare-earth alumo silicate.
The preparation method of cement of the present invention, mortar or concrete noctilucence ground or metope, form by following steps: preparation cement, mortar or concrete slurry, and adding the luminous substance particle in the slurry stirs, then it is poured on ground matrix or the wall matrix, after drying reaches the above intensity of C30 firmly admittedly, that surface finish is level and smooth and expose luminescent substance.Also to add color pebble when adding the luminous substance particle in the slurry and stir; Luminous substance is the rare-earth alumo silicate luminescent material.
When cement of the present invention, cement mortar or concrete luminous plate, the thickness of plate were 1 centimetre of left and right sides, its inside had the luminous substance particle, plays illuminating effect.When the thickness of plate was thicker, there was the solid inorganic fluorescence coating on its surface, and the luminous substance particle is arranged in the fluorescence coating, played illuminating effect.Noctilucence metope and noctilucence ground are to play illuminating effect equally.At the precast stair plate or pouring in the process of indoor roofing or metope, it (is the luminous substance particle that the surface adds several solid inorganic pigment, adularescent, blueness, green etc.), after intensity reaches C30 after the maintenance, cement, the mortar on surface are ground off, after exposing solid luminescence pigment (being the luminous substance particle), polish its appearance.Do not having under the situation of light source evening, and broadstep and ground, metope send colored points, are particularly useful for stair, washroom and public place etc.
Cement of the present invention, mortar or concrete luminous plate, in each step, when preparation cement, mortar or concrete slurry, the cement that uses is high strength cement.
Claims (10)
1. a cement, mortar or concrete luminous plate, it is characterized in that: plate body inside has the luminous substance particle, and the luminous substance particle appears on the plate body surface and constitutes same smooth smooth surface with the plate body surface; Perhaps, have at least one to wear the luminous substance layer and constitute, the luminous substance particle is arranged in the luminous substance layer, and this particle is exposed outside with the luminous substance laminar surface and constitutes same smooth smooth surface by the plate body appearance of cement, mortar or concrete slab.
2. cement according to claim 1, mortar or concrete luminous plate is characterized in that: plate body inside also has a large amount of color pebbles, and color pebble appears on the plate body surface and constitutes same smooth smooth surface with the plate body surface; Perhaps, also have a large amount of color pebbles in the luminous substance layer of cement, mortar or concrete slab, and color pebble is exposed outside with the luminous substance laminar surface and constitutes same smooth smooth surface.
3. cement according to claim 1 and 2, mortar or concrete luminous plate is characterized in that: the luminous substance particle is the luminous material particle of rare-earth alumo silicate.
4. cement according to claim 1 and 2, mortar or concrete luminous plate is characterized in that: the length of this plate and/or width are during greater than 60 centimetres, and there is reinforcing bar its inside.
5. a cement, mortar or concrete noctilucence ground or metope, it is characterized in that: ground or metope inside have the luminous substance particle, and the luminous substance particle is on ground or the metope surface appears and constitute same smooth smooth surface with ground or metope surface.
6. cement according to claim 5, mortar or concrete noctilucence ground or metope, it is characterized in that: ground or metope inside also have a large amount of color pebbles, and color pebble is on ground or the metope surface appears and constitute same smooth smooth surface with ground or metope surface; The luminous substance particle is the luminous material particle of rare-earth alumo silicate.
7. the preparation method of a cement, mortar or concrete luminous plate, it is characterized in that: a-1 forms by step, perhaps is made up of successively step a, b, c:
A-1. prepare cement, mortar or concrete slurry, and add the luminous substance particle in the slurry and stir, then it is poured into plate, after drying reaches the above intensity of C30 firmly admittedly, smoothly and expose luminescent substance surface finish;
A. prepare cement, mortar or concrete slurry, then it is poured into plate;
B. go into the luminous substance particle at cement, mortar or the concrete slab surface arsis of ot-yet-hardened, and casting cement, mortar or concrete slurry are used for levelling between particle;
C. after the plate drying after the levelling reaches the above intensity of C30 firmly admittedly, that the surface finish of levelling is level and smooth and expose luminescent substance.
8. the preparation method of cement according to claim 7, mortar or concrete luminous plate is characterized in that: in step a-1, also will add color pebble when adding the luminous substance particle in the slurry and stir; In step b, the color pebble of also will beating in when beating in the luminous substance particle; Luminous substance is the rare-earth alumo silicate luminescent material.
9. the preparation method of a cement, mortar or concrete noctilucence ground or metope, it is characterized in that: form: preparation cement, mortar or concrete slurry by following steps, and adding the luminous substance particle in the slurry stirs, then it is poured on ground matrix or the wall matrix, after drying reaches the above intensity of C30 firmly admittedly, that surface finish is level and smooth and expose luminescent substance.
10. the preparation method of cement according to claim 9, mortar or concrete noctilucence ground or metope is characterized in that: also will add color pebble when adding the luminous substance particle in the slurry and stir; Luminous substance is the rare-earth alumo silicate luminescent material.