CN102010737A - 一种1/3焦煤参与的炼焦配煤方法 - Google Patents
一种1/3焦煤参与的炼焦配煤方法 Download PDFInfo
- Publication number
- CN102010737A CN102010737A CN2010105992306A CN201010599230A CN102010737A CN 102010737 A CN102010737 A CN 102010737A CN 2010105992306 A CN2010105992306 A CN 2010105992306A CN 201010599230 A CN201010599230 A CN 201010599230A CN 102010737 A CN102010737 A CN 102010737A
- Authority
- CN
- China
- Prior art keywords
- coal
- coking
- coking coal
- blending
- accounts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种1/3焦煤参与的炼焦配煤方法,它包括以下步骤:第一步、对参与炼焦配煤的1/3焦煤进行检测的步骤;第二步、对1/3焦煤进行分类的步骤;第三步、将各单种炼焦煤混配的步骤;所述各单种煤中至少包括1/3焦煤;所述1/3焦煤为1/3焦煤1#、1/3焦煤2#、1/3焦煤3#中的一种或几种;上述各类1/3焦煤的重量占配煤总重量的百分配比分别为:所述1/3焦煤1#:25~35%、所述1/3焦煤2#:10~30%、所述1/3焦煤3#:1~10%;且上述1/3焦煤总重量占配煤总重量的1~40%。本发明方法可以稳定提高焦炭质量,降低配煤成本。
Description
技术领域
本发明涉及炼焦配煤技术领域,具体涉及炼焦配煤方法,特别是有1/3焦煤参与的炼焦配煤方法。
背景技术
我国煤资源丰富,但炼焦煤资源紧缺,而且在有限的炼焦煤资源中分布不均衡。在已经探明的煤炭储量中,炼焦煤储量仅占煤炭总储量的26%,焦煤仅占炼焦煤储量的17.57%,肥煤占10%。而在配煤炼焦中,焦肥煤一般应占50%-60%,炼焦煤资源与炼焦配煤的需求之间矛盾严重。
为了能够提高焦炭质量并且降低生产成本,各国炼焦工作者逐渐开始重视对非主焦煤的应用研究上来,而1/3焦煤作为我国煤资源储备中含量较高的煤种,如何使用1/3焦煤已成为炼焦工作者必需面临的问题。1/3焦煤作为一种变质程度介于焦煤与肥煤之间的煤种,其复杂程度比焦肥煤复杂得多,而我国对1/3炼焦煤的使用主要依赖于传统的煤质指标和煤岩指标的镜质组反射率及其分布,这两种指标以及这两种指标的组合指标均存在一定缺陷,不能全面地对1/3焦煤做到合理使用。
发明内容
本发明所要解决的技术问题是:提供一种1/3焦煤参与的炼焦配煤方法,该炼焦配煤方法可以稳定提高焦炭质量,降低配煤成本。
本发明解决上述技术问题所采用的技术方案是:
一种1/3焦煤参与的炼焦配煤方法,其特征在于:它包括以下步骤:
第一步、对参与炼焦配煤的1/3焦煤进行检测的步骤,它包括:
对1/3焦煤进行基氏流动度测定以测定1/3焦煤的最大流动度MF指标、
对1/3焦煤进行镜质组反射率测定以测定1/3焦煤的最大反射率Rmax;
第二步、对1/3焦煤进行分类的步骤,
1/3焦煤1#:MF≥1300DDPM且Rmax≥0.85;
1/3焦煤2#:MF≥500DDPM且0.85>Rmax≥0.78;
1/3焦煤3#:MF<500DDPM;
第三步、将各单种炼焦煤混配的步骤;
所述各单种煤中至少包括1/3焦煤;所述1/3焦煤为1/3焦煤1#、1/3焦煤2#、1/3焦煤3#中的一种或几种;
上述各类1/3焦煤的重量占配煤总重量的百分配比分别为:
所述1/3焦煤1#:25~35%、所述1/3焦煤2#:10~30%、所述1/3焦煤3#:1~10%;且上述1/3焦煤总重量占配煤总重量的1~40%。
上述方案中,各单种煤中还包括焦煤、气肥煤和/或肥煤;
气肥煤和肥煤的重量总和占配煤总重量的5~15%;焦煤重量占配煤总重量的30~50%;
上述方案中,各单种煤中还包括瘦煤,瘦煤重量占配煤总重量的1~15%。
本发明方法克服了现有技术不能对1/3焦煤煤质进行准确评定和合理使用的缺点,使1/3焦煤资源得到合理使用,科学配煤,提高焦炭质量。
具体实施方式
本发明炼焦配煤方法实施例1包括以下步骤:
第一步、对参与炼焦配煤的1/3焦煤进行检测的步骤,它包括:
对1/3焦煤进行基氏流动度测定以测定1/3焦煤的最大流动度MF指标、
对1/3焦煤进行镜质组反射率测定以测定1/3焦煤的最大反射率Rmax;
测得各种1/3焦煤的最大流动度MF指标和最大反射率Rmax见表1:
表1:1/3焦煤性能指标
最大流动度MF/DDPM | 平均最大反射率Rmax | |
1号1/3焦煤 | 2388 | 0.90 |
2号1/3焦煤 | 23880 | 0.91 |
3号1/3焦煤 | 1986 | 0.79 |
4号1/3焦煤 | 227 | 0.66 |
5号1/3焦煤 | 472 | 0.78 |
第二步、对1/3焦煤进行分类的步骤,
1/3焦煤1#:MF≥1300DDPM且Rmax≥0.85;
1/3焦煤2#:MF≥500DDPM且0.85>Rmax≥0.78;
1/3焦煤3#:MF<500DDPM。
4号、5号1/3焦煤为1/3焦煤3#,3号1/3焦煤为1/3焦煤2#,1号、2号1/3焦煤为1/3焦煤1#。
第三步、将各单种炼焦煤混配的步骤;
所述各单种煤中包括1/3焦煤、焦煤、气肥煤、肥煤、瘦煤;
所述1/3焦煤为1/3焦煤1#、1/3焦煤2#、1/3焦煤3#中的一种或几种;
上述各类1/3焦煤的重量占配煤总重量的百分配比分别为:
所述1/3焦煤1#:25~35%、所述1/3焦煤2#:10~30%、所述1/3焦煤3#:1~10%;且上述1/3焦煤总重量占配煤总重量的1~40%。
所述气肥煤和肥煤的重量总和占配煤总重量的5~15%;焦煤重量占配煤总重量的30~50%;瘦煤重量占配煤总重量的1~15%。
各单种煤的重量百分配比为:气肥煤:10%;肥煤:5%、1/3焦煤1#:35%;焦煤:35%;瘦煤:15%。
本发明有1/3焦煤参与的炼焦配煤方法实施例2,它与实施例1基本相同,只是各单种煤的重量百分配比为:气肥煤:10%; 1/3焦煤1#:25%;1/3焦煤2#:10%;1/3焦煤3#:5%;焦煤:50%。
本发明有1/3焦煤参与的炼焦配煤方法实施例3,它与实施例1基本相同,只是各单种煤的重量百分配比为:肥煤:15%、1/3焦煤2#:30%; 1/3焦煤3#:8%;焦煤:32%;瘦煤:15%。
本发明有1/3焦煤参与的炼焦配煤方法实施例4,它与实施例1基本相同,只是各单种煤的重量百分配比为:气肥煤:10%;肥煤:5%、 1/3焦煤1#:35%;焦煤:45%;瘦煤:5%。
本发明有1/3焦煤参与的炼焦配煤方法实施例5,它与实施例1基本相同,只是各单种煤的重量百分配比为:气肥煤:10%;肥煤:5%、1/3焦煤1#:35%;1/3焦煤3#:5%;焦煤:45%。
有1/3焦煤参与的炼焦配煤方法对比例1,它与实施例1基本相同,只是各单种煤的重量百分配比为:气肥煤:5%;肥煤:10%、 1/3焦煤3#:30%;焦煤:45%;瘦煤:10%。
有1/3焦煤参与的炼焦配煤方法对比例2,它与实施例1基本相同,只是各单种煤的重量百分配比为:气肥煤:5%;肥煤:10%、1/3焦煤1#:15%; 1/3焦煤3#:15%;焦煤:45%;瘦煤:10%。
对比实验:
将实施例1~5和对比例1~2生产出的焦炭热性能指标见表2:
表2:焦炭热性能指标
反应性CRI/% | 反应后强度CSR/% | |
实施例1 | 24 | 66 |
实施例2 | 23 | 65 |
实施例3 | 25 | 64 |
实施例4 | 27 | 65 |
实施例5 | 27 | 64 |
对比例1 | 30 | 63 |
对比例2 | 42 | 55 |
从表2可以看出,用本发明炼焦配煤方法可以提高焦炭质量的稳定性。
Claims (3)
1.一种1/3焦煤参与的炼焦配煤方法,其特征在于:它包括以下步骤:
第一步、对参与炼焦配煤的1/3焦煤进行检测的步骤,它包括:
对1/3焦煤进行基氏流动度测定以测定1/3焦煤的最大流动度MF指标、
对1/3焦煤进行镜质组反射率测定以测定1/3焦煤的最大反射率Rmax;
第二步、对1/3焦煤进行分类的步骤,
1/3焦煤1#:MF≥1300DDPM且Rmax≥0.85;
1/3焦煤2#:MF≥500DDPM且0.85>Rmax≥0.78;
1/3焦煤3#:MF<500DDPM;
第三步、将各单种炼焦煤混配的步骤;
所述各单种煤中至少包括1/3焦煤;所述1/3焦煤为1/3焦煤1#、1/3焦煤2#、1/3焦煤3#中的一种或几种;
上述各类1/3焦煤的重量占配煤总重量的百分配比分别为:
所述1/3焦煤1#:25~35%、所述1/3焦煤2#:10~30%、所述1/3焦煤3#:1~10%;且上述1/3焦煤总重量占配煤总重量的1~40%。
2.如权利要求1所述的炼焦配煤方法,其特征在于:各单种煤中还包括焦煤、气肥煤和/或肥煤;
气肥煤和肥煤的重量总和占配煤总重量的5~15%;焦煤重量占配煤总重量的30~50%。
3.如权利要求2所述的炼焦配煤方法,其特征在于:各单种煤中还包括瘦煤,瘦煤重量占配煤总重量的1~15%。