CN102009423A

CN102009423A - Production method of double-layer solid wood flooring

Info

Publication number: CN102009423A
Application number: CN 201010507136
Authority: CN
Inventors: 刘贤继
Original assignee: Individual
Current assignee: Individual
Priority date: 2010-10-14
Filing date: 2010-10-14
Publication date: 2011-04-13
Anticipated expiration: 2030-10-14
Also published as: CN102009423B

Abstract

The invention discloses a production method of a double-layer solid wood flooring. The method comprises the following steps of: radially cutting China fir into a veneer serving as a blank plate of a bottom plate; radially cutting acokanthera venenata wood or german oak wood or irko wood or castanopsis chinensis hance wood into a veneer serving as a blank plate of a faceplate; cooking and degreasing the sawed faceplate blank plate; baking and making the strength of the faceplate equal to or less than that of the bottom plate by changing the thickness of the blank plate according to the different bending strengths of the two kinds of blank plates, coating a hot pressing glue on the China fir blank plate and the faceplate blank plate with the same deflexion, and compressing and moulding the blank plates in a press, and controlling the temperature to be between 90 and 100 DEG C, wherein the pressure is 16 to 20kg per square centimeter; and planning and sanding the hot-pressed moulded plate. In the method, two kinds of different woods are adopted to mould the double-layer solid wood flooring at a high temperature under a high pressure, so that the advantages of the two kinds of woods complement each other. The double-layer solid wood flooring is fully dried through ultraviolet light irradiation. Horizontal bends and warps are removed by planning without pressure and are subjected to difference match and stress balance treatment, so that the problem which is difficult to solve by bowing deformation is effectively solved.

Description

The production method of dual-layer wood floor

Technical field

The present invention relates to a kind of timber floor production method, particularly a kind of dual-layer wood floor production method.

Background technology

Because wood floors have the untouchable many excellent specific properties of other floor decorative materials, and are comfortable as feel, fine setting environment humidity, harmless to health, thereby enjoy people to favor; At present, timber floor is broadly divided into former timber floor and multiple field timber floor two big classes.

Though former timber floor has kept self characteristics and pure natural property fully, a kind of material can not satisfy the many specification requirements to the floor; The easement distortion can't overcome, and the monolithic plank is thicker, and parching property of influence is had relatively high expectations to environment for use, and changing slightly is easy to generate distortion, influences attractive in appearance and service life.

Though the multiple field timber floor has crisscross level, unordered distortion is wayward, still can not overcome easement distortion, no matter be quarter sawing or rotary-cut, always the internal layer space has; These spaces have increased glue consumption, and harmful substance is also corresponding to be increased.

Summary of the invention

The objective of the invention is to overcome the shortcoming of prior art, provide a kind of usefulness two kinds of different timber, be bonded through HTHP, it is wear-resisting to have a panel, and negative is soft, on-deformable dual-layer wood floor of stable performance and production method thereof.

The production method of dual-layer wood floor of the present invention comprises the steps:

1, getting China fir radially is cut into veneer and makes the base plate blanket and use, get China fir do negative be because China fir can finely tune self humidity with environmental change, make it to produce moisture-proof function, immortal in the certain environment following centuries of condition, China fir is the length fibre structure, and bending strength is good, belongs to the less excellent material of a kind of deflection, be commonly called as the king in the wood, China fir also has the characteristic strong with the glue adhesion; Experiment showed, China fir and chinquapin wood behind hot pressing, gummed, boiling can not be ftractureed in one hour in pressure cooker;

2, get chinquapin wood and radially be cut into veneer, it is stand-by to make the panel blanket, and getting chinquapin wood, to make panel be because chinquapin wood has the natural anticorrosion function, the unavoidable and boiling water as the total surface on floor, and the contact of liquid such as children's urine is so the moisture-proof anticorrosive on floor is absolutely necessary; Chinquapin wood also has density height, wear-resisting, withstand voltage, fire-retardant characteristics; Making panel with chinquapin wood is one of best material, and the certainly also iron jujube of available this locality, blue or green firm etc., or the disk beans of import etc. is cooked the panel material, but can't compare favourably with chinquapin wood on comprehensive function;

3, will saw good panel wood blanket and carry out the boiling degreasing;

4, the panel blanket after China fir blanket and the degreasing is contained in respectively in two different drying rooms dries; Material is put and is adopted goods-shelf type built on stilts, divide three phases to heat up, environment temperature～30 ℃ are the I stage, 30 ℃～60 ℃ is the II stage, ultraviolet illumination is the III stage, the ultraviolet ray facility is 5 each ultraviolet light generators of 1 kilowatt, be distributed in the drying room, adopting this technology is in order to allow blanket fully parch, and because of the water evaporates of ultraviolet illumination energy quick active deep layer, wooden baking needed time of chinquapin and temperature Duo 15～20% than China fir, the three phases time spent equates, panel blanket oven dry total time is 5～9 days, and material goes out drying room needs emphasis parching property of check and uniformity, and only the parching property of guaranteed material and uniformity could guarantee the indeformable or small deformation of product;

5, the above-mentioned blanket that will dry does not have the pressure planing, removes lateral bending (horizontal curved) and song and sticks up, and looks its degree if any the blanket of natural flaw and carries out traceless repair, and the just remaining easement of the blanket of having planed is not so handled;

6, difference coupling reaches by the thickness that changes blanket according to the different bending strength of above-mentioned two kinds of blankets that intensity equates or panel is weaker than base plate, and the thickness of base plate and panel is than being 2.5-4: 1;

7, press shown in the accompanying drawing, the easement deflection of two kinds of blankets is represented with amount of deflection 1,2,3,4,5, because every compact plate all can have certain flexibility, we are defined as the A face to bandy face, and aduncate face is defined as the B face.And defining one meter long blanket, crooked arc apex is amount of deflection 1 to the distance of string for the 0-1 millimeter; Distance is an amount of deflection 2 for the 1-2 millimeter; Distance is an amount of deflection 3 for the 2-3 millimeter; Distance is an amount of deflection 4 for the 3-4 millimeter; Distance is an amount of deflection 5 for the 4-5 millimeter;

8, the B of China fir blanket that two amounts of deflection is identical and panel blanket coats hot pressing glue and press solidly moulding in press in the face of the B face, and temperature is controlled at 90 ℃～100 ℃; 16～20 kilograms every square centimeter of pressure, pressure is excessive or too small all unsuitable, and this method is called stress equilibrium;

9, the profiled sheeting that hot pressing is good also has a spot of easement distortion, all can eliminate after adjustable cast iron planes and sanding.

The present invention adopts the dual-layer wood floor of two kinds of different timber through the HTHP moulding, and the mutual supplement with each other's advantages of two kinds of materials of collection fully parches through ultraviolet lighting again; No pressure planing is removed horizontal bending with song and is stuck up, and through the difference coupling, stress equilibrium is handled again, efficiently solves the problem that the easement distortion is difficult to capture.

Description of drawings

Accompanying drawing is a floor of the present invention amount of deflection schematic diagram.

The specific embodiment

Below in conjunction with specific embodiment the present invention is described in further details.

1, getting China fir radially is cut into veneer and makes the base plate blanket and use;

2, get chinquapin wood and radially be cut into veneer, it is stand-by to make the panel blanket;

3, will saw good chinquapin wood blanket and carry out the boiling degreasing;

4, the wood of the chinquapin after China fir blanket and degreasing blanket is contained in respectively in two different drying rooms dries; Material is put and is adopted goods-shelf type built on stilts, divide three phases to heat up, environment temperature～30 ℃ are the I stage, 30 ℃～60 ℃ is the II stage, ultraviolet illumination is the III stage, the ultraviolet ray facility is 5 each ultraviolet light generators of 1 kilowatt, be distributed in the drying room, adopting this technology is in order to allow blanket fully parch, because of the water evaporates of ultraviolet illumination energy quick active deep layer, chinquapin wood baking needed time and temperature Duo 20% than China fir, and China fir blanket total time is 5 days, material goes out drying room needs emphasis parching property of check and uniformity, and only the parching property of guaranteed material and uniformity could guarantee the indeformable or small deformation of product;

5, the blanket with oven dry does not have the pressure planing, removes lateral bending (horizontal curved) and song and sticks up, and looks its degree if any the blanket of natural flaw and carries out traceless repair;

6, difference coupling reaches by the thickness that changes blanket according to two kinds of different bending strengths of blanket exactly that intensity equates or panel slightly is weaker than base plate, and both thickness ratios are 3.1: 1.9;

7, press shown in the accompanying drawing, the easement deflection of two kinds of blankets represented with amount of deflection 1,2,3,4,5,

8, China fir is identical with chinquapin wood amount of deflection blanket B coats hot pressing glue and press solidly moulding in press in the face of the B face, and temperature is controlled at 90 ℃; 16 kilograms every square centimeter of pressure;

Claims

1. the production method of a dual-layer wood floor is characterized in that: comprise the steps:

(1), getting China fir radially is cut into veneer and makes the base plate blanket and use;

(2), get the iron jujube or blue or green just or disk beans or chinquapin wood radially be cut into veneer, make the panel blanket;

(3), will saw good panel blanket and carry out the boiling degreasing;

(4), the panel blanket after China fir blanket and the degreasing is contained in respectively in two different drying rooms dries; Material is put and is adopted goods-shelf type built on stilts, divide three phases to heat up, environment temperature～30 ℃ are the I stage, 30 ℃～60 ℃ is the II stage, ultraviolet illumination is the III stage, the three phases time spent equates that panel blanket baking needed time and temperature Duo 15～20% than China fir, and China fir blanket oven dry total time is 5～9 days;

(5), the above-mentioned blanket that will dry do not have the pressure planing, removes lateral bending and song and sticks up, and carries out traceless repair if any the blanket of natural flaw;

(6), reach by the thickness that changes blanket according to the different bending strength of above-mentioned two kinds of blankets that intensity equates or panel is weaker than base plate, the thickness of base plate and panel is than being 2.5-4: 1;

(7), the B of China fir blanket that two amounts of deflection is identical and panel blanket is in the face of the B face, coats hot pressing glue and press solidly moulding in press, temperature is controlled at 90 ℃～100 ℃; 16～20 kilograms every square centimeter of pressure;

(8), the profiled sheeting that hot pressing is good is through adjustable cast iron planes and sanding.

2. the production method of dual-layer wood floor according to claim 1, it is characterized in that: described panel blanket is the veneer that chinquapin wood radially is cut into.