CN102008206B - Bamboo bowl and production method - Google Patents
Bamboo bowl and production method Download PDFInfo
- Publication number
- CN102008206B CN102008206B CN2010105653612A CN201010565361A CN102008206B CN 102008206 B CN102008206 B CN 102008206B CN 2010105653612 A CN2010105653612 A CN 2010105653612A CN 201010565361 A CN201010565361 A CN 201010565361A CN 102008206 B CN102008206 B CN 102008206B
- Authority
- CN
- China
- Prior art keywords
- bowl
- bamboo
- veneer plywood
- rotary cutting
- wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a bamboo bowl which has a simple processing method and high product strength, and is difficult to deform. The bamboo bowl comprises a bowl wall (1) and a bowl bottom (2), wherein the bowl wall (1) is adhered to the bowl bottom (2). The bamboo bowl is characterized in that: the bowl wall (1) is a laminated layer of circular rings processed by bamboo rotary cut veneer plywood; and the bowl bottom (2) is formed by processing a laminated layer of circular boards processed by the bamboo rotary cut veneer plywood or coiled materials formed by winding the bamboo rotary cut veneer plywood. A production method for the bamboo bowl comprises the following steps of: preparing the bamboo rotary cut veneer plywood; making blanks; assembling; and performing surface treatment. In the production method, by forming combinations of the bamboo rotary cut veneer plywood in different fiber directions, compared with the textures of natural materials, the produced products have incomparable textures and have high manufacturability and appreciation, and the utilization rate of bamboos is high; simultaneously, the tensile strength of the products in the traverse and longitudinal directions is complementary; moreover, bamboo wood is a green fast-growing resource and the products are environmentally-friendly, so the aims of saving resources and protecting environment are fulfilled.
Description
Technical field
The present invention relates to a kind of daily living article, specifically a kind of bamboo bowl and production method, particularly a kind of bamboo bowl and production method that adopts the bamboo rotary cutting veneer plywood to process.
Background technology
Existing commercially available bowl or the utensil that holds dessert, dry fruit are generally pottery, glass, plastics and metal etc. and process.Allegro urban life, densely covered reinforced concrete urban forests goes short of people's life, constrains and cold and detached.Bowl must contact articles for use as daily life; The ice-cold sense of pottery, glass, plastics; Make fall not mood of people more can increase a little disconsolately, and pottery, glass, plastics resource is non-renewable, more can increase people will continue to use resource to future a worry.Natural, fast living, bamboo wood making that the bamboo bowl adopts, and have practicality and appreciation double grading concurrently, when people use, can feel more cordiality and warm, feel to get close to nature, merge nature, unfold people's mood.
At present, the production of existing bamboo bowl generally adopts bamboo board to make, and is about to that bamboo chip is perpendicular to be pieced together or horizontal assembly adds the glue heating and is pressed into sheet material, afterwards sheet material is cut into the dimensional requirement size of bowl.The thickness of plate is confirmed by the height of bowl, stays under the allowance after the length and width size of plate is confirmed by the diameter of bowl and cuts out.Cut out the inner surface that good sheet material mills out bowl after with clamps earlier down, the rim of a bowl with the outer surface that mills out bowl after the clamps, is well-thought-out plan bowl finished product behind sand milling and top finishing down more then.After perhaps bamboo chip being processed sheet material, cut into the annulus of different sizes by the big young pathbreaker's sheet material of dimensional requirement of bowl, connect into a bowl wall with glue, the bowl wall is connected well-thought-out plan bowl base with glue again with a bowl end, bamboo bowl base through the turning sand milling and after surface treatment the well-thought-out plan bowl.Problems such as above method exists bamboo board surfaces externally and internally milling amount big, and the sheet material utilization rate is not high, and processing is inconvenient, and intensity is not high, and easy deformation and texture composition are simple.
The patent No. is 91232950.5; The applying date is 91.12.14; Denomination of invention is that a kind of patent of bamboo bowl discloses a kind of bamboo section that adopts more piece thin bamboo strips used for weaving bag to tie adhesion-molded hollow garden tube and splices the hollow of back turning moulding mutually and throw the face thing, at the bottom of the garden of turning sheet bamboo clappers is done bowl, adopt interference fit to socket-connect with one again after reface well-thought-out plan bowl.This method processed complex, labour intensity is big, and intensity is not high.
Summary of the invention
It is simple to the purpose of this invention is to provide a kind of processing method, and product strength is high, on-deformable bamboo bowl and production method.
The present invention adopts following technical scheme to realize its goal of the invention; A kind of bamboo bowl; It comprises a bowl wall, the bowl end; On at the bottom of the bowl wall is adhesive in bowl, described bowl wall be the lamination by the annulus of bamboo rotary cutting veneer plywood processing, and the described bowl end is the lamination of the plectane processed by the bamboo rotary cutting veneer plywood.
A kind of production method of the bowl of bamboo as stated, it comprises the following steps:
⑴ the preparation of bamboo rotary cutting veneer plywood;
⑵ base: the thickness of bamboo bowl diameter during by differing heights and bowl wall cuts out the blank of the annulus of different sizes as the bowl wall with the bamboo rotary cutting veneer plywood, and the bamboo rotary cutting veneer plywood is cut into the blank of plectane at the bottom of as bowl;
⑶ assembly: after earlier plectane being added the glue ageing, by the height at the bowl end from bottom at the bottom of the bowl to bowl top, the end order, plectane was stacked as a bowl end, again annulus is added the glue ageing after, at the bottom of by bowl-type the annulus of different-diameter size being overlayed bowl on, pressurizeing is shaped into a bowl base;
⑷ surface treatment: bowl base inwall and outer wall respectively through turnning and milling, sanding, full-filling aqueous putty, are coated water paint again and promptly processed the bamboo bowl.
A kind of bamboo bowl, it comprises a bowl wall, the bowl end, at the bottom of a bowl wall is adhesive in bowl on, described bowl wall be the lamination by the annulus of bamboo rotary cutting veneer plywood processing, the described bowl of end, is for to become coiled material to process by bamboo rotary cutting veneer plywood spooling.
A kind of production method of the bowl of bamboo as stated, it comprises the following steps:
⑴ the preparation of bamboo rotary cutting veneer plywood;
⑵ base: the thickness of bamboo bowl diameter during by differing heights and bowl wall cuts out the blank of the annulus of different sizes as the bowl wall with the bamboo rotary cutting veneer plywood, the blank at the bottom of becoming coiled material as bowl bamboo rotary cutting veneer plywood spooling;
⑶ assembly: earlier by the height at the bowl end and size cutting coiled material as bowl at the bottom of, again annulus is added the glue ageing after, at the bottom of by bowl-type the annulus of different-diameter size being overlayed bowl on, pressurization is shaped into a bowl base;
⑷ surface treatment: bowl base inwall and outer wall respectively through turnning and milling, sanding, full-filling aqueous putty, are coated water paint again and promptly processed the bamboo bowl.
The present invention in step ⑶, earlier by the height at the bowl end and size cutting coiled material as bowl at the bottom of, again annulus is added the glue ageing after, at the bottom of by bowl-type the annulus of different-diameter size being mounted on bowl on, pressurization is shaped into a bowl base.
Owing to adopt technique scheme; The present invention has realized goal of the invention preferably; It becomes veneer to carry out the formation combination of different machine directions through using bamboo rotary cutting; The product of producing has been created the unrivaled texture composition of a kind of natural material texture, has manufacturability and appreciating, and utilization rate of bamboo is high; Combination through different machine direction veneers simultaneously; Overcome the extremely weak defective of bamboo wood transverse tensile strength, made laterally, endwise tensile strength is complementary and realize the harmony of product mechanical property, thereby realized the requirement of product function of use; Bamboo wood is green fast production-goods source in addition; The Product Green environmental protection has realized economizing on resources, the purpose of protection environment.
Description of drawings
Fig. 1 is a structural representation of the present invention;
Fig. 2 is the vertical view of Fig. 1;
Fig. 3 is the A place amplification view of Fig. 1;
Fig. 4 is the structural representation of embodiment 2;
Fig. 5 is the structural representation of embodiment 3;
Fig. 6 is a product sketch map of the present invention.
The specific embodiment
Below in conjunction with accompanying drawing and embodiment the present invention is described further.
Embodiment 1:
Can know by Fig. 1, Fig. 2, Fig. 3; A kind of bamboo bowl, it comprises bowl wall 1, the bowl end 2, at the bottom of a bowl wall 1 is adhesive in bowl on 2; Described bowl wall 1 is the lamination by the annulus of bamboo rotary cutting veneer plywood processing, and the described bowl end 2 is the lamination by the plectane of bamboo rotary cutting veneer plywood processing.
A kind of production method of the bowl of bamboo as stated, it comprises the following steps:
⑴ the preparation of bamboo rotary cutting veneer plywood;
Choose do not have go mouldy rotten, the free from insect pests fission, unmanned be hurt, does not have obvious aberration and does not promptly have the negative and positive two sides, the brows diameter is more than 10 ㎝, nearly bamboo 130 ㎝ to 430 ㎝ perfectly straight bamboo wood partly is subsequent use.
The bamboo wood chosen cut out be cut into the long thick bamboo tube of 340 ㎜-350 ㎜ (present embodiment is 340 ㎜), cut out that every section thick bamboo tube keeps a ring at least when cutting, be peeled into veneer longitudinal cracking behind the veneer with minimizing.
Boiling, rotary-cut.With get through joint at a distance from after thick bamboo tube put into iron cage and put in the distilling kettle water submergence hot digestion into softening.After heating water to boiling; Boost to 0.15MPa and pressurize 40 minutes, step-down is then driven still bamboo cage is moved in another pond; Keep 70 ℃ of water temperatures--80 ℃, take out afterwards that bamboo axially is peeled into the bamboo chip that thickness is 0.35 ㎜-0.80 ㎜ (present embodiment is 0.44 ㎜) in the peeler upper edge.
With the drying of the bamboo chip after the rotary-cut, assembly, hot-forming one-tenth bamboo wood rotary cut venner glued board.The double-deck guipure conveying drier of the forward and backward equal warp of bamboo chip gluing is dry; Dry rear piece moisture content is controlled to be 12%-16%; The chip moisture content is controlled to be 10%-14%; Then with 2 layers-9 layers (present embodiment is 5 layers) bamboo chip in length and breadth broken pattern arrange assembly hot pressing so that fiber checks and balance, avoid modification behind the plate forming.The bamboo rotary cutting veneer plywood of processing is of a size of 320 ㎜ * 320 ㎜ * 2.20 ㎜.
⑵ base: the thickness of diameter during by bamboo bowl differing heights and bowl wall cuts out the blank of the annulus of different sizes as bowl wall 1 with the bamboo rotary cutting veneer plywood, with the bamboo rotary cutting veneer plywood cut into plectane as bowl at the bottom of 2 blank;
⑶ assembly: after earlier plectane being added the glue ageing; Height 2 bottoms to bowl top, the ends 2 order at the bottom of the bowl by the bowl end 2 stacks plectane as a bowl end 2, again annulus is added the glue ageing after; On 2, pressurization is shaped into a bowl base at the bottom of by bowl-type the annulus of different-diameter size being overlayed bowl;
By maximum processing the rim of a bowl diameter 300 ㎜ bamboo bowls; High 120 ㎜ of jorum, minimum process the rim of a bowl diameter 125 ㎜ bamboo bowls, high 55 ㎜ of minimum bowl; The thickness of each bowl bowl wall 1 is that 8 ㎜ calculate; Adopt 53 bamboo rotary cutting veneer plywoods that are of a size of 320 ㎜ * 320 ㎜ * 2.20 ㎜, every glued board is cut out the annulus and plectane of different sizes after, 8 bamboo bowl bases that one-tenth diameter capable of being combined is different.Like the thickness by the bowl wall is that 5 ㎜ calculate 11 bamboo bowl bases that one-tenth diameter capable of being combined is different.The thickness of each bowl of present embodiment bowl wall is 8 ㎜.
⑷ surface treatment: bowl base inwall and outer wall respectively through turnning and milling, sanding, full-filling aqueous putty, are coated water paint again and promptly processed the bamboo bowl, be i.e. bamboo matter cover bowl.
The product that the present invention produces is as shown in Figure 6, and it has following characteristics:
Bamboo bowl of the present invention adopts crisscross bamboo rotary cutting veneer plywood sheet material to make through thermocompression forming, and add to coat and carry out surface treatment, moisture absorption or apply certain external force and make the possibility of its distortion minimum, dimensional stability is superior to existing bamboo bowl.
The present invention forms every annulus and the plectane diameter of bamboo bowl wall through calculating; And the method for taking to cut out a piece of cloth in a way with the minimum material to make two or more articles of clothing making cover bowl; After promptly a sheet material cuts out the blank of several annulus as bowl wall 1 from big to small; Core cut again plectane as bowl at the bottom of 2 blank, sheet material is fully used, improved utilization rate of bamboo widely.
Reconfigure through bamboo wood, it is beautiful to have created material texture unrivaled in a kind of bamboo and wood materials native texture.The bowl wall 1 of this bamboo bowl appears deep mixed; Thickness uniform circular striped; It had both embodied a kind of exquisite beyond compare skin texture composition; Not losing the natural beauty of natural material again, is the handicraft that integrates the not only practical of natural beauty and technology U.S.A but also have enjoying value, makes the bamboo added value of product obtain greatly to promote.
Bamboo bowl of the present invention also can adopt slicing bamboo veneer processing and preparing.
Embodiment 2:
Can know by Fig. 4, for 2 consistent at the bottom of making bowl with the texture of bowl wall 1, appear deep mixed, thickness uniform circular striped.A kind of bamboo bowl, it comprises bowl wall 1, the bowl end 2, and on 2, described bowl wall 1 be the lamination by the annulus of bamboo rotary cutting veneer plywood processing at the bottom of a bowl wall 1 was adhesive in bowl, and the described bowl of end 2, is for to become coiled material to process by bamboo rotary cutting veneer plywood spooling.
A kind of production method of the bowl of bamboo as stated, it comprises the following steps:
⑴ the preparation of bamboo rotary cutting veneer plywood;
Present embodiment is in the preparation of step ⑴ bamboo rotary cutting veneer plywood; Prepare two kinds of bamboo rotary cutting veneer plywoods, a kind of is that 3 layers of bamboo chip of 0.35 ㎜ are prepared into three layers of bamboo rotary cutting veneer plywood with thickness, is of a size of 320 ㎜ * 320 ㎜ * 1.00 ㎜; Another kind of is that 5 layers of bamboo chip of 0.44 ㎜ are prepared into five layers of bamboo rotary cutting veneer plywood with thickness, is of a size of 320 ㎜ * 320 ㎜ * 2.20 ㎜.
⑵ base: the thickness of bamboo bowl diameter during by differing heights and bowl wall cuts out the blank of the annulus of different sizes as bowl wall 1 with the bamboo rotary cutting veneer plywood, become coiled material as bowl bamboo rotary cutting veneer plywood spooling at the bottom of 2 blank;
In step ⑵ base, the thickness of bamboo bowl diameter when selecting five layers of bamboo rotary cutting veneer plywood by differing heights for use and bowl wall cuts out the blank of the annulus of different sizes as bowl wall 1 with the bamboo rotary cutting veneer plywood; 2 blank during spooling, is closely knit coiled material at the bottom of selecting for use three layers of bamboo rotary cutting veneer plywood spooling to become coiled material as bowl, and the bosom part is done inner core with the bamboo bar.
⑶ assembly: earlier by the height at the bowl end 2 and size cutting coiled material as bowl at the bottom of 2, again annulus is added the glue ageing after, on 2, pressurization is shaped into a bowl base at the bottom of by bowl-type the annulus of different-diameter size being overlayed bowl;
During spooling, also can with three layers of bamboo rotary cutting veneer plywood by bowl at the bottom of 2 height cut into spooling behind the strip bamboo chip, during assembly, annulus added the glue ageing after, on 2, pressurization is shaped into a bowl base at the bottom of by bowl-type the annulus of different-diameter size being overlayed bowl.
Surplus with embodiment 1.
Embodiment 3:
Can know by Fig. 5, for 2 consistent at the bottom of making bowl with the texture of bowl wall 1, appear deep mixed, thickness uniform circular striped.
⑴ the preparation of bamboo rotary cutting veneer plywood;
Present embodiment is in the preparation of step ⑴ bamboo rotary cutting veneer plywood; Prepare two kinds of bamboo rotary cutting veneer plywoods, a kind of is that 3 layers of bamboo chip of 0.35 ㎜ are prepared into three layers of bamboo rotary cutting veneer plywood with thickness, is of a size of 320 ㎜ * 320 ㎜ * 1.00 ㎜; Another kind of is that 5 layers of bamboo chip of 0.44 ㎜ are prepared into five layers of bamboo rotary cutting veneer plywood with thickness, is of a size of 320 ㎜ * 320 ㎜ * 2.20 ㎜.
⑵ base: the thickness of bamboo bowl diameter during by differing heights and bowl wall cuts out the blank of the annulus of different sizes as bowl wall 1 with the bamboo rotary cutting veneer plywood, become coiled material as bowl bamboo rotary cutting veneer plywood spooling at the bottom of 2 blank;
In step ⑵ base, the thickness of bamboo bowl diameter when selecting five layers of bamboo rotary cutting veneer plywood by differing heights for use and bowl wall cuts out the blank of the annulus of different sizes as bowl wall 1 with the bamboo rotary cutting veneer plywood; 2 blank during spooling, is closely knit coiled material at the bottom of selecting for use three layers of bamboo rotary cutting veneer plywood spooling to become coiled material as bowl, and the bosom part is done inner core with the bamboo bar.
⑶ assembly: for easy to process, earlier by the height at the bowl end 2 and size cutting coiled material as bowl at the bottom of 2, again annulus is added the glue ageing after, on 2, pressurization is shaped into a bowl base at the bottom of by bowl-type the annulus of different-diameter size being mounted on bowl.
During spooling, also can with three layers of bamboo rotary cutting veneer plywood by bowl at the bottom of 2 height cut into spooling behind the strip bamboo chip, during assembly, annulus added the glue ageing after, on 2, pressurization is shaped into a bowl base at the bottom of by bowl-type the annulus of different-diameter size being mounted on bowl.
Surplus with embodiment 1.
Claims (3)
1. bamboo bowl; It comprises a bowl wall (1), the bowl end (2); At the bottom of bowl wall (1) is adhesive in bowl on (2); It is characterized in that described bowl wall (1) is the lamination by the annulus of bamboo rotary cutting veneer plywood processing, the described bowl end (2) is for to become coiled material to process by bamboo rotary cutting veneer plywood spooling.
2. the production method of bamboo bowl according to claim 1 is characterized in that it comprises the following steps:
⑴ the preparation of bamboo rotary cutting veneer plywood;
⑵ base: the thickness of bamboo bowl diameter during by differing heights and bowl wall cuts out the blank of the annulus of different sizes as bowl wall (1) with the bamboo rotary cutting veneer plywood, become coiled material as bowl bamboo rotary cutting veneer plywood spooling at the bottom of the blank of (2);
⑶ assembly: earlier by the height of the bowl end (2) and size cutting coiled material as bowl at the bottom of (2), again annulus is added the glue ageing after, on (2), pressurization is shaped into a bowl base at the bottom of by bowl-type the annulus of different-diameter size being overlayed bowl;
⑷ surface treatment: bowl base inwall and outer wall respectively through turnning and milling, sanding, full-filling aqueous putty, are coated water paint again and promptly processed the bamboo bowl.
3. the production method of bamboo bowl according to claim 1 is characterized in that it comprises the following steps:
⑴ the preparation of bamboo rotary cutting veneer plywood;
⑵ base: the thickness of bamboo bowl diameter during by differing heights and bowl wall cuts out the blank of the annulus of different sizes as bowl wall (1) with the bamboo rotary cutting veneer plywood, become coiled material as bowl bamboo rotary cutting veneer plywood spooling at the bottom of the blank of (2);
⑶ assembly: earlier by the height of the bowl end (2) and size cutting coiled material as bowl at the bottom of (2), again annulus is added the glue ageing after, on (2), pressurization is shaped into a bowl base at the bottom of by bowl-type the annulus of different-diameter size being mounted on bowl;
⑷ surface treatment: bowl base inwall and outer wall respectively through turnning and milling, sanding, full-filling aqueous putty, are coated water paint again and promptly processed the bamboo bowl.