CN102002320A - 一种环保型隔热纳米涂料及其制备方法 - Google Patents

一种环保型隔热纳米涂料及其制备方法 Download PDF

Info

Publication number
CN102002320A
CN102002320A CN 201010563980 CN201010563980A CN102002320A CN 102002320 A CN102002320 A CN 102002320A CN 201010563980 CN201010563980 CN 201010563980 CN 201010563980 A CN201010563980 A CN 201010563980A CN 102002320 A CN102002320 A CN 102002320A
Authority
CN
China
Prior art keywords
nanometer
agent
titanium oxide
nano
color stuffing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010563980
Other languages
English (en)
Inventor
谢锋
向明
李雄益
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHA HUARUN PAINT Co Ltd
Original Assignee
CHANGSHA HUARUN PAINT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHA HUARUN PAINT Co Ltd filed Critical CHANGSHA HUARUN PAINT Co Ltd
Priority to CN 201010563980 priority Critical patent/CN102002320A/zh
Publication of CN102002320A publication Critical patent/CN102002320A/zh
Pending legal-status Critical Current

Abstract

一种环保型隔热纳米涂料及其制备方法,所述一种环保型隔热纳米涂料包括以下组份:纳米颜填料浆料、合成水性树脂、成膜助剂、偶联剂、消泡剂、流平剂和润湿剂,所述一种环保型隔热纳米涂料的制备方法是:先将纳米颜填料浆料加入到合成水性树脂中,然后依次加入成膜助剂、偶联剂、消泡剂、流平剂和润湿剂,快速搅拌,即得到一种环保型隔热纳米涂料。本发明加工工艺简单,组分配比合理,具有热阻大、反射率高,辐射传热性能好的功能。

Description

一种环保型隔热纳米涂料及其制备方法
技术领域
本发明涉及纳米涂料,具体为一种环保型隔热纳米涂料及其制备方法。
背景技术
目前的纳米涂料存在的主要问题是涂层较厚,施工要求高,隔热效果差,涂层的空隙率高,防水性能差涂层的耐沾污性和耐候性都较差,对于环境有害。
发明内容
本发明所解决的技术问题在于提供一种环保型隔热纳米涂料及其制备方法,以解决上述背景技术中的缺陷。
本发明所解决的技术问题采用以下技术方案来实现:
一种环保型隔热纳米涂料及其制备方法,所述一种环保型隔热纳米涂料包括以下质量百分比的组份:
合成水性树脂48-52%,
纳米颜填料浆料30-50%,
成膜助剂0.5-5%,
偶联剂0.1-5%,
消泡剂0.1-2%,
流平剂0.1-2%,
润湿剂0.1-2%,
其中,纳米颜填料浆料包括以下质量百分比的组份:
纳米二氧化钛1-5%,
纳米二氧化钛包覆的空心玻璃微珠1-5%,
纳米掺锑二氧化锡1-5%,
去离子水30-40%,
乙醇7-13%,
IPA7-13%,
丁醇7-13%,
丙二醇甲醚醋酸酯7-13%,
分散剂0.065-0.125%,且固含量纳米浆料的30-50%,固含量的纳米材料粒径在20-50纳米之间。
本发明中,所述一种环保型隔热纳米涂料的制备方法,包括下述步骤:
第一步:按纳米颜填料浆料中各组份的质量百分比称取纳米二氧化钛、纳米二氧化钛包覆的空心玻璃微珠、纳米掺锑二氧化锡、去离子水,乙醇,IPA,丁醇,丙二醇甲醚醋酸酯和分散剂,首先,将作为介质的去离子水、乙醇、IPA、丁醇和丙二醇甲醚醋酸酯加入分散机中,然后,加入分散剂,最后加入纳米二氧化钛、纳米二氧化钛包覆的空心玻璃微珠和纳米掺锑二氧化锡分散2小时,即得到所需质量份的纳米颜填料浆料。
第二步:按合成水性树脂、纳米颜填料浆料、成膜助剂、偶联剂、消泡剂、流平剂和润湿剂的质量百分比称取各组分,首先,将第一步制得的纳米颜填料浆料缓慢加入合成水性树脂中,然后再加入成膜助剂、偶联剂、润湿剂、消泡剂和流平剂,搅拌10-30分钟。
有益效果
本发明加工工艺简单,组分配比合理,具有热阻大,反射率高,辐射传热性能好的功能。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面通过实施例对本发明进行具体描述:
实施例1
首先称取纳米二氧化钛、纳米二氧化钛包覆的空心玻璃微珠和纳米掺锑二氧化锡各50克,去离子水400克,乙醇100克,IPA100克,丁醇100克,丙二醇甲醚醋酸酯100克和分散剂1克,然后将水、乙醇、IPA、丁醇和丙二醇甲醚醋酸酯加入分散机中,然后,再加入分散剂,最后加入纳米二氧化钛、纳米二氧化钛包覆的空心玻璃微珠和纳米掺锑二氧化锡,分散2小时之后,即可得到1001克分散性良好的纳米颜填料浆料,纳米颜填料浆料中的固体含量大约为30%;称取合成水性树脂7500克,成膜助剂200克,偶联剂200克,消泡剂100克,流平剂100克和润湿剂100克,然后将制得的纳米颜填料浆料缓慢加入到合成水性树脂中,再加入成膜助剂、偶联剂、润湿剂、消泡剂和流平剂,搅拌30分钟,即得到一种环保型隔热纳米涂料。在生产过程中,可以添加微量的水,调整所述一种环保型隔热纳米涂料的粘度。
实施例2
首先称取纳米二氧化钛、纳米二氧化钛包覆的空心玻璃微珠和纳米掺锑二氧化锡各50克,去离子水300克,乙醇80克,IPA80克,丁醇80克,丙二醇甲醚醋酸酯80克和分散剂1克,然后将去离子水、乙醇、IPA、丁醇和丙二醇甲醚醋酸酯加入分散机中,然后,再加入分散剂,最后加入纳米二氧化钛、纳米二氧化钛包覆的空心玻璃微珠和纳米掺锑二氧化锡,分散2小时,即可得到1001克分散性良好的纳米颜填料浆料,纳米颜填料浆料中的固体含量大约为40%;称取合成水性树脂3000克,成膜助剂200克,偶联剂200克,消泡剂100克,流平剂100克和润湿剂100克,然后将制得的纳米颜填料浆料缓慢加入到合成水性树脂中,再加入成膜助剂、偶联剂、润湿剂、消泡剂和流平剂,搅拌20分钟,即得到一种环保型隔热纳米涂料。在生产过程中,可以添加微量的水,调整所述一种环保型隔热纳米涂料的粘度。
实施例3
首先称取纳米二氧化钛、纳米二氧化钛包覆的空心玻璃微珠和纳米掺锑二氧化锡各50克,去离子水200克,乙醇60克,IPA60克,丁醇60克,丙二醇甲醚醋酸酯60克和分散剂2克,然后将去离子水、乙醇、IPA、丁醇和丙二醇甲醚醋酸酯加入分散机中,然后,再加入分散剂,最后加纳米入二氧化钛、纳米二氧化钛包覆的空心玻璃微珠和纳米掺锑二氧化锡,分散2小时,即可得到1001克分散性良好的纳米颜填料浆料,纳米颜填料浆料中的固体含量大约为50%;称取合成水性树脂1400克,成膜助剂100克,偶联剂50克,消泡剂50克,流平剂50克和润湿剂50克,然后将制得的纳米颜填料浆料缓慢加入到合成水性树脂中,再加入成膜助剂、偶联剂、润湿剂、消泡剂和流平剂,搅拌10分钟,即得到一种环保型隔热纳米涂料。在生产过程中,可以添加微量的水,调整所述一种环保型隔热纳米涂料的粘度。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (2)

1.一种环保型隔热纳米涂料及其制备方法,其特征在于,所述一种环保型隔热纳米涂料包括以下质量百分比的组份:
合成水性树脂48-52%,
纳米颜填料浆料30-50%,
成膜助剂0.5-5%,
偶联剂0.1-5%,
消泡剂0.1-2%,
流平剂0.1-2%,
润湿剂0.1-2%,
其中,纳米颜填料浆料包括以下质量百分比的组份:
纳米二氧化钛1-5%,
纳米二氧化钛包覆的空心玻璃微珠1-5%,
纳米掺锑二氧化锡1-5%,
去离子水30-40%,
乙醇7-13%,
IPA7-13%,
丁醇7-13%,
丙二醇甲醚醋酸酯7-13%,
分散剂0.065-0.125%,且固含量纳米浆料的30-50%,固含量的纳米材料粒径在20-50纳米之间。
2.一种环保型隔热纳米涂料及其制备方法,其特征在于,所述一种环保型隔热纳米涂料的制备方法,包括下述步骤:
第一步:按纳米颜填料浆料中各组份的质量百分比称取纳米二氧化钛、纳米二氧化钛包覆的空心玻璃微珠、纳米掺锑二氧化锡、去离子水,乙醇,IPA,丁醇,丙二醇甲醚醋酸酯和分散剂,首先,将作为介质的去离子水、乙醇、IPA、丁醇和丙二醇甲醚醋酸酯加入分散机中,然后,加入分散剂,最后加入纳米二氧化钛、纳米二氧化钛包覆的空心玻璃微珠和纳米掺锑二氧化锡分散2小时,即得到所需质量量份的纳米颜填料浆料。
第二步:按合成水性树脂、纳米颜填料浆料、成膜助剂、偶联剂、消泡剂、流平剂和润湿剂的质量百分比称取各组分,首先,将第一步制得的纳米颜填料浆料缓慢加入合成水性树脂中,然后再加入成膜助剂、偶联剂、润湿剂、消泡剂和流平剂,搅拌10-30分钟。
CN 201010563980 2010-11-29 2010-11-29 一种环保型隔热纳米涂料及其制备方法 Pending CN102002320A (zh)