CN102002178B - Continuous long fiber reinforced polyolefin plastic wood composite material and preparation method thereof - Google Patents
Continuous long fiber reinforced polyolefin plastic wood composite material and preparation method thereof Download PDFInfo
- Publication number
- CN102002178B CN102002178B CN2010105829751A CN201010582975A CN102002178B CN 102002178 B CN102002178 B CN 102002178B CN 2010105829751 A CN2010105829751 A CN 2010105829751A CN 201010582975 A CN201010582975 A CN 201010582975A CN 102002178 B CN102002178 B CN 102002178B
- Authority
- CN
- China
- Prior art keywords
- plastic composite
- wood plastic
- preparation
- polyolefine
- fortifying fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a plastic wood composite material and a preparation method and a co-extrusion die thereof, in particular to a continuous long fiber reinforced polyolefin plastic wood composite material and a preparation method thereof. The composite material consists of the following components in percentage by weight: 20 to 80 percent of polyolefin plastic, 0 to 80 percent of wood fiber, 0 to 80 percent of mineral filler, 0 to 10 percent of lubricating agent, 0 to 5 percent of antioxidant, 0 to 5 percent of ultraviolet absorbent, 0 to 10 percent of coupling agent, 0 to 10 percent of pigment and 0 to 30 percent of reinforcing fibers; the reinforcing fibers are surface modified or unmodified glass fibers, jute fibers or hemp palm fibers; and the reinforcing fibers are continuously extended along the length direction of the polyolefin plastic wood composite material, and the number of the reinforcing fibers is at least one beam. The reinforcing fibers are continuously extended and distributed in the polyolefin plastic wood profile; and when the plastic wood profile is forced during use, the continuous extended fibers can quickly transfer the local force to the whole profile so as to greatly improve the strength and the impact resistance of the plastic wood profile.
Description
Technical field
The present invention relates to a kind of Wood plastic composite and preparation method thereof, a kind of specifically continuous fiber strengthens polyolefine Wood plastic composite and preparation method thereof.
Background technology
Wood plastic composite is a kind of emerging environmental protection, the matrix material of low-carbon (LC).Main recovery plastics and the agriculture and forestry organic waste material of adopting is processed into bed board, guardrail fence or indoor and outdoor and decorates as raw material.But, can't be widely used in building field, particularly stressed member or structural part because the mechanical property of Wood plastic composite is lower.
For fibre reinforced plastics a lot of reports and related patent U.S. Patent No. have been arranged both at home and abroad, but the distribution of glass in product is discontinuous phase, remains local pressure when product is stressed.Like long glass fiber reinforced polypropylene material and preparation method thereof (application number: 200810020936.5); Be long glass fibres to be immersed in the Vestolen PP 7052 use after the pelletizing; Its shortcoming is that spun glass remains discontinuous state; Reinforced effects for product is relatively poor with respect to the continuous fibre enhancing, and spun glass can be continued to cut off in product following process process, simultaneously there are wearing and tearing in processing units.In addition, common glass fibre reinforcement difficulty when reclaiming is bigger, and spun glass is difficult to from material, separate.
Summary of the invention
Technical problem to be solved by this invention is: to the shortcoming of above prior art existence; Propose a kind of continuous fiber and strengthen polyolefine Wood plastic composite and preparation method thereof; Can significantly strengthen the mechanical property of Wood plastic composite, expand the Application Areas of Wood plastic composite.
The technical scheme that the present invention solves above technical problem is:
A kind of continuous fiber strengthens the polyolefine Wood plastic composite, and is composed of the following components by weight percentage: polyolefin plastics 20-80%, xylon 0-80%; Mineral-filled thing 0-80%, lubricant 0-10%, inhibitor 0-5%; UV light absorber 0-5%; Coupling agent 0-10%, pigment 0-10%
Fortifying fibre 0-30%; Fortifying fibre is surface-treated or unmodified spun glass, flaxen fiber or monkey grass; Fortifying fibre extends along polyolefine Wood plastic composite length direction continuously, and quantity is at least a branch of.
The present invention makes fortifying fibre being distributed in the polyolefine plastic-wood section of extension continuously; When plastic-wood section is in use stressed; The fiber that extends continuously can be passed to section bar integral body rapidly with local pressure, thereby significantly improves the intensity and the shock resistance of plastic-wood section.In addition, fortifying fibre uses flaxen fiber or monkey grass, and the feature of environmental protection is stronger; Monkey grass particularly can guarantee the intensity of fiber can guarantee the feature of environmental protection again.
Continuous fiber of the present invention strengthens the preparation method of polyolefine Wood plastic composite, carries out according to the following steps:
(1) batch mixing: with polyolefin plastics particle, xylon, mineral-filled, lubricant, inhibitor, UV light absorber, coupling agent and pigment were poured the mixer mixing into 3-5 minute in proportion;
(2) granulation: the raw material after will mixing adds parallel double-screw extruder and carries out the compounding granulation, obtains moulding wood aggregate;
(3) extrude: will mould wood aggregate and add forcing machine, fusion after mould extrude; In the step (3), mould the wood aggregate fusion after mould when extruding in die side to adding continuous fortifying fibre, control forcing machine body temperature, die temperature and extruded velocity make plastic-wood material in moulding, coat glass and extrude together; Body temperature is 100-200 ℃, and die temperature is 100-200 ℃, and extruded velocity is 100-1000mm/min.
This bright science with fortifying fibre in die side to adding simultaneously; It is extruded with moulding wood aggregate; Form " co-extrusion ", can guarantee that fortifying fibre extends continuously and do not cut off in plastic-wood material, reach the intensity that improves plastic-wood section and the purpose of shock resistance.In addition, body temperature is controlled at 100-200 ℃, and die temperature is controlled at 100-200 ℃; Extruded velocity is controlled at 100-1000mm/min, and the setting of body temperature mainly is based on the fusing point of Wood plastic composite, makes the abundant fusion of Wood plastic composite; Promote the dispersion of xylon in plastics, the control through die temperature makes Wood plastic composite when mould is extruded, and has good structure hold facility on the one hand; Can coat continuous fiber again on the other hand; Macrofiber is dispersed in the plastic-wood section uniformly, improves reinforced effects, guarantee the continuity that product is extruded.Extruded velocity is slow excessively, and production efficiency is low, extruded velocity is too fast then cause continuous fiber and plastic-wood material combine not closely, be easy in use occur the running phenomenon.
The technical scheme that the present invention further limits is:
Aforesaid continuous fiber strengthens the polyolefine Wood plastic composite, and xylon is poplar powder, powdered rice hulls or bamboo powder, is mainly derived from the waste abrasive dust in timber, bamboo processing factory and the rice source mill, and fineness is 20 orders-200 orders; Mineral-filled is lime carbonate or talcum powder, derives from chemical plant or processing of stone field, and fineness is 100 orders-2000 orders.
Aforesaid continuous fiber strengthens the polyolefine Wood plastic composite, and fiber dimensious is 200-4800Tex.
Aforesaid continuous fiber strengthens the polyolefine Wood plastic composite, fortifying fibre be arranged in the polyolefine Wood plastic composite near surface layer, can improve reinforced effects like this.Specifically can be following technical scheme: polyolefine Wood plastic composite section bar cross section is a rectangle, and fortifying fibre is along section bar width at least one row that arranges; Can be according to the arrangement mode of section bar cross section adjustment fiber.Less like section bar thickness, can along the section bar width arrange one row fiber; Bigger like section bar thickness, can be along the section bar width number row's fibers of arranging.Polyolefine Wood plastic composite section bar cross section is an abnormity (non-rectangle), and fortifying fibre is the shape arrangement along the section bar outer.Polyolefine Wood plastic composite section bar is a hollow body, and fortifying fibre is arranged in section bar top layer or brace rod.
Aforesaid continuous fiber strengthens the polyolefine Wood plastic composite, and mineral-filled thing is that in talcum powder, lime carbonate or the wollastonite one or more mix; Lubricant is an ethylene bis stearamide, PE wax, montanic acid, calcium stearate, one or more mixing in the Triple Pressed Stearic Acid; Inhibitor is the composite antioxidant that phosphite ester kind antioxidant and Hinered phenols antioxidant are formed, and wherein phosphite ester kind antioxidant and Hinered phenols antioxidant were formed by weight 1: 0.3~1: 0.7.
Aforesaid continuous fiber strengthens the preparation method of polyolefine Wood plastic composite, in the step (2), and 100-300 ℃ of parallel double-screw processing temperature, rotating speed 100-400r/min.
Embodiment
Embodiment one
A kind of continuous fiber strengthens the polyolefine Wood plastic composite, and is composed of the following components by weight percentage: polyolefin plastics 50%, xylon 10%, mineral-filled thing 12%; Lubricant 1%, inhibitor 5%, UV light absorber 1%; Coupling agent 10%, pigment 1%, fortifying fibre 10%; Fortifying fibre is surface-treated or unmodified spun glass, flaxen fiber or monkey grass; Fortifying fibre extends along polyolefine Wood plastic composite length direction continuously, and quantity is at least a branch of.
Xylon is poplar powder, powdered rice hulls or bamboo powder, is mainly derived from the waste abrasive dust in timber, bamboo processing factory and the rice source mill, and fineness is 20 orders; Mineral-filled is lime carbonate or talcum powder, derives from chemical plant or processing of stone field, and fineness is 100 orders.
Continuous fiber strengthens the polyolefine Wood plastic composite, and fiber dimensious is 200Tex.
Fortifying fibre be arranged in the polyolefine Wood plastic composite near surface layer, can improve reinforced effects like this.Specifically can be following technical scheme: polyolefine Wood plastic composite section bar cross section is a rectangle, and fortifying fibre is along section bar width at least one row that arranges; Can be according to the arrangement mode of section bar cross section adjustment fiber.Less like section bar thickness, can along the section bar width arrange one row fiber; Bigger like section bar thickness, can be along the section bar width number row's fibers of arranging.Polyolefine Wood plastic composite section bar cross section is an abnormity (non-rectangle), and fortifying fibre is the shape arrangement along the section bar outer.Polyolefine Wood plastic composite section bar is a hollow body, and fortifying fibre is arranged in section bar top layer or brace rod.
Mineral-filled thing is that in talcum powder, lime carbonate or the wollastonite one or more mix; Lubricant is an ethylene bis stearamide, PE wax, montanic acid, calcium stearate, one or more mixing in the Triple Pressed Stearic Acid; Inhibitor is the composite antioxidant that phosphite ester kind antioxidant and Hinered phenols antioxidant are formed, and wherein phosphite ester kind antioxidant and Hinered phenols antioxidant were formed by weight 1: 0.3.
Continuous fiber strengthens the preparation method of polyolefine Wood plastic composite, carries out according to the following steps:
(1) batch mixing: with polyolefin plastics particle, xylon, mineral-filled, lubricant, inhibitor, UV light absorber, coupling agent and pigment are poured mixer in proportion into and were mixed 3 minutes;
(2) granulation: the raw material after will mixing adds parallel double-screw extruder and carries out the compounding granulation, obtains moulding wood aggregate, 300 ℃ of parallel double-screw processing temperatures, rotating speed 100r/min;
(3) extrude: will mould wood aggregate and add forcing machine; Fusion after mould extrude; Mould the wood aggregate fusion after mould when extruding in die side to adding continuous fortifying fibre; Control forcing machine body temperature, die temperature and extruded velocity make plastic-wood material in moulding, coat glass and extrude together; Body temperature is 100 ℃, and die temperature is 100 ℃, and extruded velocity is 100mm/min.
Embodiment two
A kind of continuous fiber strengthens the polyolefine Wood plastic composite, and is composed of the following components by weight percentage: polyolefin plastics 28%, xylon 20%, mineral-filled thing 10%; Lubricant 5%, inhibitor 1%, UV light absorber 5%; Coupling agent 1%, pigment 10%, fortifying fibre 20%; Fortifying fibre is surface-treated or unmodified spun glass, flaxen fiber or monkey grass; Fortifying fibre extends along polyolefine Wood plastic composite length direction continuously, and quantity is at least a branch of.
Xylon is poplar powder, powdered rice hulls or bamboo powder, is mainly derived from the waste abrasive dust in timber, bamboo processing factory and the rice source mill, and fineness is 100 orders; Mineral-filled is lime carbonate or talcum powder, derives from chemical plant or processing of stone field, and fineness is 1000 orders.
Continuous fiber strengthens the polyolefine Wood plastic composite, and fiber dimensious is 2000Tex.
Fortifying fibre be arranged in the polyolefine Wood plastic composite near surface layer, can improve reinforced effects like this.Specifically can be following technical scheme: polyolefine Wood plastic composite section bar cross section is a rectangle, and fortifying fibre is along section bar width at least one row that arranges; Can be according to the arrangement mode of section bar cross section adjustment fiber.Less like section bar thickness, can along the section bar width arrange one row fiber; Bigger like section bar thickness, can be along the section bar width number row's fibers of arranging.Polyolefine Wood plastic composite section bar cross section is an abnormity (non-rectangle), and fortifying fibre is the shape arrangement along the section bar outer.Polyolefine Wood plastic composite section bar is a hollow body, and fortifying fibre is arranged in section bar top layer or brace rod.
Mineral-filled thing is that in talcum powder, lime carbonate or the wollastonite one or more mix; Lubricant is an ethylene bis stearamide, PE wax, montanic acid, calcium stearate, one or more mixing in the Triple Pressed Stearic Acid; Inhibitor is the composite antioxidant that phosphite ester kind antioxidant and Hinered phenols antioxidant are formed, and wherein phosphite ester kind antioxidant and Hinered phenols antioxidant were formed by weight 1: 0.5.
Continuous fiber strengthens the preparation method of polyolefine Wood plastic composite, carries out according to the following steps:
(1) batch mixing: with polyolefin plastics particle, xylon, mineral-filled, lubricant, inhibitor, UV light absorber, coupling agent and pigment are poured mixer in proportion into and were mixed 4 minutes;
(2) granulation: the raw material after will mixing adds parallel double-screw extruder and carries out the compounding granulation, obtains moulding wood aggregate, 200 ℃ of parallel double-screw processing temperatures, rotating speed 300r/min;
(3) extrude: will mould wood aggregate and add forcing machine; Fusion after mould extrude; Mould the wood aggregate fusion after mould when extruding in die side to adding continuous fortifying fibre; Control forcing machine body temperature, die temperature and extruded velocity make plastic-wood material in moulding, coat glass and extrude together; Body temperature is 150 ℃, and die temperature is 150 ℃, and extruded velocity is 600mm/min.
Embodiment three
A kind of continuous fiber strengthens the polyolefine Wood plastic composite, and is composed of the following components by weight percentage: polyolefin plastics 20%, xylon 30%, mineral-filled thing 10%; Lubricant 10%, inhibitor 2%, UV light absorber 3%; Coupling agent 5%, pigment 5%, fortifying fibre 15%; Fortifying fibre is surface-treated or unmodified spun glass, flaxen fiber or monkey grass; Fortifying fibre extends along polyolefine Wood plastic composite length direction continuously, and quantity is at least a branch of.
Xylon is poplar powder, powdered rice hulls or bamboo powder, is mainly derived from the waste abrasive dust in timber, bamboo processing factory and the rice source mill, and fineness is 200 orders; Mineral-filled is lime carbonate or talcum powder, derives from chemical plant or processing of stone field, and fineness is 2000 orders.
Continuous fiber strengthens the polyolefine Wood plastic composite, and fiber dimensious is 4800Tex.
Fortifying fibre be arranged in the polyolefine Wood plastic composite near surface layer, can improve reinforced effects like this.Specifically can be following technical scheme: polyolefine Wood plastic composite section bar cross section is a rectangle, and fortifying fibre is along section bar width at least one row that arranges; Can be according to the arrangement mode of section bar cross section adjustment fiber.Less like section bar thickness, can along the section bar width arrange one row fiber; Bigger like section bar thickness, can be along the section bar width number row's fibers of arranging.Polyolefine Wood plastic composite section bar cross section is an abnormity (non-rectangle), and fortifying fibre is the shape arrangement along the section bar outer.Polyolefine Wood plastic composite section bar is a hollow body, and fortifying fibre is arranged in section bar top layer or brace rod.
Mineral-filled thing is that in talcum powder, lime carbonate or the wollastonite one or more mix; Lubricant is an ethylene bis stearamide, PE wax, montanic acid, calcium stearate, one or more mixing in the Triple Pressed Stearic Acid; Inhibitor is the composite antioxidant that phosphite ester kind antioxidant and Hinered phenols antioxidant are formed, and wherein phosphite ester kind antioxidant and Hinered phenols antioxidant were formed by weight 1: 0.7.
Continuous fiber strengthens the preparation method of polyolefine Wood plastic composite, carries out according to the following steps:
(1) batch mixing: with polyolefin plastics particle, xylon, mineral-filled, lubricant, inhibitor, UV light absorber, coupling agent and pigment are poured mixer in proportion into and were mixed 5 minutes;
(2) granulation: the raw material after will mixing adds parallel double-screw extruder and carries out the compounding granulation, obtains moulding wood aggregate, 300 ℃ of parallel double-screw processing temperatures, rotating speed 400r/min;
(3) extrude: will mould wood aggregate and add forcing machine; Fusion after mould extrude; Mould the wood aggregate fusion after mould when extruding in die side to adding continuous fortifying fibre; Control forcing machine body temperature, die temperature and extruded velocity make plastic-wood material in moulding, coat glass and extrude together; Body temperature is 200 ℃, and die temperature is 200 ℃, and extruded velocity is 1000mm/min.
The present invention makes fortifying fibre being distributed in the polyolefine plastic-wood section of extension continuously; When plastic-wood section is in use stressed; The fiber that extends continuously can be passed to section bar integral body rapidly with local pressure, thereby significantly improves the intensity and the shock resistance of plastic-wood section.In addition, fortifying fibre uses flaxen fiber or monkey grass, and the feature of environmental protection is stronger; Monkey grass particularly can guarantee the intensity of fiber can guarantee the feature of environmental protection again.In extruded velocity and the die temperature of die side to adding fiber major control section bar.Extruded velocity is too fast cause easily fortifying fibre with mould wooden base material combine not tight.Temperature is low excessively, and product approval difficulty increases the wearing and tearing of mould, fortifying fibre with mould wooden base material combine not closely, reinforced effects is bad.Die temperature is too high, and the melt strength of plastic-wood material is low, and plastic-wood material can't be extruded by coating reinforced fiber, occurs plastic-wood material and fiber easily and breaks away from, and can't play enhancement.This bright science with fortifying fibre in die side to adding simultaneously; It is extruded with moulding wood aggregate; Form " co-extrusion ", can guarantee that fortifying fibre extends continuously and do not cut off in plastic-wood material, reach the intensity that improves plastic-wood section and the purpose of shock resistance.In addition, body temperature is controlled at 100-200 ℃, and die temperature is controlled at 100-200 ℃; Extruded velocity is controlled at 100-1000mm/min, and the setting of body temperature mainly is based on the fusing point of Wood plastic composite, makes the abundant fusion of Wood plastic composite; Promote the dispersion of xylon in plastics, the control through die temperature makes Wood plastic composite when mould is extruded, and has good structure hold facility on the one hand; Can coat continuous fiber again on the other hand; Macrofiber is dispersed in the plastic-wood section uniformly, improves reinforced effects, guarantee the continuity that product is extruded.Extruded velocity is slow excessively, and production efficiency is low, extruded velocity is too fast then cause continuous fiber and plastic-wood material combine not closely, be easy in use occur the running phenomenon.
The present invention can also have other embodiment, and the technical scheme that equal replacement of all employings or equivalent transformation form all drops within the scope of requirement protection of the present invention.
Claims (9)
1. a continuous fiber strengthens the preparation method of polyolefine Wood plastic composite, and it is composed of the following components by weight percentage that said continuous fiber strengthens the polyolefine Wood plastic composite:
Polyolefin plastics 20-80%
Xylon 0-80%
Mineral-filled thing 0-80%
Lubricant 0-10%
Inhibitor 0-5%
UV light absorber 0-5%
Coupling agent 0-10%
Pigment 0-10%
Fortifying fibre 0-30%;
The weight percent of said xylon, mineral-filled thing, lubricant, inhibitor, UV light absorber, coupling agent, pigment and fortifying fibre all is not 0;
Said fortifying fibre is surface-treated or unmodified spun glass;
Said fortifying fibre extends along polyolefine Wood plastic composite length direction continuously, and quantity is at least a branch of;
Said preparation method, carry out according to the following steps:
⑴ batch mixing: with polyolefin plastics particle, xylon, mineral-filled thing, lubricant, inhibitor, UV light absorber, coupling agent and pigment were poured the mixer mixing into 3-5 minute in proportion;
⑵ granulation: the raw material after will mixing adds parallel double-screw extruder and carries out the compounding granulation, obtains moulding wood aggregate;
⑶ extrude: will mould wood aggregate and add forcing machine, fusion after mould extrude;
It is characterized in that: among the said step ⑶; Mould the wood aggregate fusion after mould when extruding in die side to adding continuous fortifying fibre; Control forcing machine body temperature, die temperature and extruded velocity make plastic-wood material in moulding, coat glass and extrude together; Said body temperature is 100-200 ℃, and die temperature is 100-200 ℃, and extruded velocity is 100-1000mm/min.
2. continuous fiber as claimed in claim 1 strengthens the preparation method of polyolefine Wood plastic composite, and it is characterized in that: said xylon is poplar powder, powdered rice hulls or bamboo powder, and fineness is 20 orders-200 orders; Said mineral-filled thing is lime carbonate or talcum powder, and fineness is 100 orders-2000 orders.
3. continuous fiber as claimed in claim 1 strengthens the preparation method of polyolefine Wood plastic composite, and it is characterized in that: said fortifying fibre specification is 200-4800Tex.
4. continuous fiber as claimed in claim 1 strengthens the preparation method of polyolefine Wood plastic composite, it is characterized in that: said fortifying fibre be arranged in the polyolefine Wood plastic composite near surface layer.
5. continuous fiber as claimed in claim 4 strengthens the preparation method of polyolefine Wood plastic composite, and it is characterized in that: said polyolefine Wood plastic composite cross section is a rectangle, and said fortifying fibre is along section bar width at least one row that arranges.
6. continuous fiber as claimed in claim 4 strengthens the preparation method of polyolefine Wood plastic composite, it is characterized in that: said polyolefine Wood plastic composite cross section is abnormity, and said fortifying fibre is the shape arrangement along the section bar outer.
7. continuous fiber as claimed in claim 4 strengthens the preparation method of polyolefine Wood plastic composite, and it is characterized in that: said polyolefine Wood plastic composite is a hollow body, and said fortifying fibre is arranged in section bar top layer or brace rod.
8. continuous fiber as claimed in claim 1 strengthens the preparation method of polyolefine Wood plastic composite, and it is characterized in that: said mineral-filled thing is one or more mixing in talcum powder, lime carbonate or the wollastonite; Said lubricant is an ethylene bis stearamide, PE wax, montanic acid, calcium stearate, one or more mixing in the Triple Pressed Stearic Acid; Said inhibitor is the composite antioxidant that phosphite ester kind antioxidant and Hinered phenols antioxidant are formed, and wherein phosphite ester kind antioxidant and Hinered phenols antioxidant are formed by weight 1:0.3~1:0.7.
9. continuous fiber as claimed in claim 1 strengthens the preparation method of polyolefine Wood plastic composite, it is characterized in that: among the said step ⑵, and 100-300 ℃ of parallel double-screw processing temperature, rotating speed 100-400r/min.