CN101999781A - One-step forming manufacturing method of bracelet - Google Patents
One-step forming manufacturing method of bracelet Download PDFInfo
- Publication number
- CN101999781A CN101999781A CN2009101697835A CN200910169783A CN101999781A CN 101999781 A CN101999781 A CN 101999781A CN 2009101697835 A CN2009101697835 A CN 2009101697835A CN 200910169783 A CN200910169783 A CN 200910169783A CN 101999781 A CN101999781 A CN 101999781A
- Authority
- CN
- China
- Prior art keywords
- wax
- bracelet
- pattern
- patterns
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a one-step forming manufacturing method of a bracelet, comprising the following steps of: enabling a manually carved water channel to pass through two designed bracelet silver frame accessories, forming a glue film with a wax injecting port in the middle of a surface through gluing pressure, and taking out silver frames; placing the glue film into a double-faced clamp plate with a through hole in the middle of the surface, injecting liquid wax, condensing and then taking out formed wax patterns, splicing the wax patterns together to form an integral bracelet wax pattern; repeating the front two steps to produce the bracelet wax pattern with multiple pattern types, and welding liquid wax channels of a plurality of bracelet wax patterns together by using an electric soldering iron; sleeving the plurality of bracelet wax patterns with iron bell models, injecting liquid gypsum, and carrying out vacuum condensation; placing the gypsum models into a high temperature furnace for thorough burning so as to form hollow gypsum models; placing the hollow gypsum models into an air suction machine, injecting liquid metal, cooling, and then forming; and smashing gypsum to obtain finished products. The method has the advantage that the bracelet is cast in one step, thereby not only saving time and cost, but also manufacturing bracelets with uniform patterns.
Description
Technical field
The present invention relates to a kind of preparation method of bracelet disposal molding.
Background technology
Liking to be beautiful is people's nature, raising along with people's living standard, various ornaments go out thereupon, bracelet is favored by the women always, and bracelet different modeling, the materials sold on the market are extensive, generally all is to carve with artificial, the pattern of carving out can be not of uniform size, integral body is not very attractive in appearance, and is therefore not only consuming time, and cost is also higher simultaneously.
Summary of the invention
The preparation method that the purpose of this invention is to provide a kind of bracelet disposal molding, described bracelet is disposable casting, not only saves time and cost, and the bracelet feature size unanimity of producing, integral body is more attractive in appearance.
The preparation method of a kind of bracelet disposal molding of the present invention may further comprise the steps:
(1) gets two the bracelet silver version accessories of the good water route of hand engraving through design, wherein the water route is located at the inboard of bracelet silver version accessory, across and infall projection, put into the mould that is full of glue, form the rubber moulding that there is the casting mouth at the middle part, surface by glue laminated, then glued membrane is dug dimidiation from the side, take out the silver version;
(2) glued membrane that step (1) is produced is put into the two-sided clamping plate that there is through hole at the middle part, surface, uses the special-purpose wax injector of jewellery to inject wax water from the casting mouth, takes out the wax-pattern that is shaped behind the cold junction, and wax-pattern is stitched together forms a complete bracelet wax-pattern;
(3) repeating step (1) and step (2) are produced the bracelet wax-pattern of multiple types of patterns, weld together with the wax water route of electric iron with a plurality of bracelet wax-patterns;
(4) a plurality of bracelet wax-patterns that step (3) is produced put the iron fluid model, inject parget water, carry out vacuum and condense, and the pigment mass fraction of described parget water is: water 30-40, and powder 100 stirred 2.5-3 minute;
(5) plaster cast that step (4) the is produced high temperature furnace of putting into the 1000-1200 degree is grilled thoroughly, and makes the wax-pattern outflow of being heated, and forms empty plaster cast;
(6) the red empty plaster cast of burning that step (5) is produced is put into lift pump, injects metal water, and the cooling aftershaping blends gypsum, takes out a plurality of metal bracelets that link together, and its separation is obtained finished product, and described metal is metal materials such as gold, silver, copper.
Beneficial effect of the present invention is: bracelet is disposable casting, not only save time and cost, and the bracelet feature size unanimity of producing, integral body is more attractive in appearance.
The specific embodiment
Embodiment:
The preparation method of the described a kind of bracelet disposal molding of the present invention of the embodiment of the invention may further comprise the steps: (1) gets two the bracelet silver version accessories of the good water route of hand engraving through design, wherein the water route is located at the inboard of bracelet silver version accessory, across and infall projection, put into the mould that is full of glue, form the rubber moulding that there is the casting mouth at the middle part, surface by glue laminated, then glued membrane is dug dimidiation from the side, take out the silver version; (2) glued membrane that step 1 is produced is put into the two-sided clamping plate that there is through hole at the middle part, surface, uses the special-purpose wax injector of jewellery to inject wax water from the casting mouth, takes out the wax-pattern that is shaped behind the cold junction, and wax-pattern is stitched together forms a complete bracelet wax-pattern; (3) repeating step 1 and step 2 are produced the bracelet wax-pattern of multiple types of patterns, weld together with the wax water route of electric iron with a plurality of bracelet wax-patterns; (4) a plurality of bracelet wax-patterns that step 3 is produced put the iron fluid model, inject parget water, carry out vacuum and condense, and described parget water restrains powder by 30 ml waters and 100, stir to form in 2.5-3 minute; (5) plaster cast that step 4 the is produced high temperature furnace of putting into the 1000-1200 degree is grilled thoroughly, and makes the wax-pattern outflow of being heated, and forms empty plaster cast; (6) the red empty plaster cast of burning that step 5 is produced is put into lift pump, injects metal water, and the cooling aftershaping blends gypsum, takes out a plurality of metal bracelets that link together, and its separation is obtained finished product, and described metal is metal materials such as gold, silver, copper.
In the preparation method step 1 of the described bracelet disposal molding of the present invention of the embodiment of the invention, the casting mouth is located at the middle part, surface of glued membrane, and common glued membrane casting mouth is located at the side of glued membrane.
Claims (2)
1. the preparation method of a bracelet disposal molding is characterized in that, may further comprise the steps:
(1) gets two the bracelet silver version accessories of the good water route of hand engraving through design, wherein the water route is located at the inboard of bracelet silver version accessory, across and infall projection, put into the mould that is full of glue, form the rubber moulding that there is the casting mouth at the middle part, surface by glue laminated, then glued membrane is dug dimidiation from the side, take out the silver version;
(2) glued membrane that step (1) is produced is put into the two-sided clamping plate that there is through hole at the middle part, surface, uses the special-purpose wax injector of jewellery to inject wax water from the casting mouth, takes out the wax-pattern that is shaped behind the cold junction, and wax-pattern is stitched together forms a complete bracelet wax-pattern;
(3) repeating step (1) and step (2) are produced the bracelet wax-pattern of multiple types of patterns, weld together with the wax water route of electric iron with a plurality of bracelet wax-patterns;
(4) a plurality of bracelet wax-patterns that step (3) is produced put the iron fluid model, inject parget water, carry out vacuum and condense, and the pigment mass fraction of described parget water is: water 30-40, and powder 100 stirred 2.5-3 minute;
(5) plaster cast that step (4) the is produced high temperature furnace of putting into the 1000-1200 degree is grilled thoroughly, and makes the wax-pattern outflow of being heated, and forms empty plaster cast;
(6) the red empty plaster cast of burning that step (5) is produced is put into lift pump, injects metal water, and the cooling aftershaping blends gypsum, takes out a plurality of metal bracelets that link together, and its separation is obtained finished product.
2. the preparation method of bracelet disposal molding according to claim 1 is characterized in that: the described metal in the step (6) is gold, silver or copper.