CN101967095A - 12-羟基硬脂酸甘油酯及其制备方法和应用 - Google Patents
12-羟基硬脂酸甘油酯及其制备方法和应用 Download PDFInfo
- Publication number
- CN101967095A CN101967095A CN201010262612XA CN201010262612A CN101967095A CN 101967095 A CN101967095 A CN 101967095A CN 201010262612X A CN201010262612X A CN 201010262612XA CN 201010262612 A CN201010262612 A CN 201010262612A CN 101967095 A CN101967095 A CN 101967095A
- Authority
- CN
- China
- Prior art keywords
- preparation
- glyceryl ester
- acid glyceryl
- oxystearic acid
- stearic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及12-羟基硬脂酸甘油酯及其制备方法和应用。所述的12-羟基硬脂酸甘油酯,由以下方法制备:1mol氢化蓖麻油与0.8-3.0mol甘油混合后,加入0.2-1.2%量的强碱性催化剂;温度控制在120℃-200℃,压力控制在-0.09-0.0MPa,进行酯交换保温反应1.0-4.0小时;最后降温到100℃左右出料切片。本发明制备简便,可用于塑料的润滑剂,乳化剂,抗静电剂,滴流剂,由于12-羟基硬脂酸甘油酯中的侧链上带有一个羟基,使得亲水性增加,同时由于有较高的熔点,在塑料中使用时析出慢,有效提高了使用有效期,也提高了薄膜的透明度,使塑料薄膜的抗静电的持效性和流滴剂的持效性都有较好的改善。
Description
技术领域
本发明涉及12-羟基硬脂酸甘油酯及其制备方法和应用。
背景技术
在塑料行业中,应用硬脂酸甘油酯作为润滑剂,抗静电剂,流滴剂使用,已经有很长的历史了,主要由于它价格低廉,材料宜得,很受用户的青睐。但在使用中也确实存在一些不足。如作为抗静电剂使用时,抗静电效果不理想,抗静电的持效性不足。作为薄膜中的流滴剂使用时也有同样的缺陷。
发明内容
本发明主要是针对塑料薄膜中使用的抗静电剂和流滴剂而开发的,提供了一种新的物质12-羟基硬脂酸甘油酯,以及其制备方法和应用。
所述的1.12-羟基硬脂酸甘油酯,其特征在于化学式为
所述12-羟基硬脂酸甘油酯的制备方法,其特征在于用以下化学反应制备
包括以下步骤:
1)1mol氢化蓖麻油与0.8-3.0mol甘油混合后,加入0.2-1.2%量的强碱性催化剂;
2)温度控制在120℃-200℃,压力控制在-0.09-0.0Mpa,,进行酯交换保温反应1.0-4.0小时;
3)最后降温到100℃左右出料切片。
所述12-羟基硬脂酸甘油酯的制备方法,其特征在于步骤1)中所述的强碱性催化剂是指氢氧化钠,氢氧化钾,硬脂酸钠,甲醇钠,乙醇钠,碱金属氧化物等其中的一种或两种以上复配构成。
所述12-羟基硬脂酸甘油酯的制备方法,其特征在于步骤2)中所述的温度控制在120℃-160℃。
所述12-羟基硬脂酸甘油酯的制备方法,其特征在于步骤2)中所述的压力控制在-0.09--0.08Mpa。
所述12-羟基硬脂酸甘油酯的制备方法,其特征在于步骤2)中所述的进行酯交换保温反应时间为1.0-2.0小时;
所述12-羟基硬脂酸甘油酯的制备方法,其特征在于步骤2)中所述的温度从120℃逐步升到160℃。
所述的12-羟基硬脂酸甘油酯,其特征在于熔点,68-72℃,羟值,330-390mgkoH/g。
所述的12-羟基硬脂酸甘油酯,其特征在于用作塑料的润滑剂,乳化剂,抗静电剂。
本发明制备简便,实施方便,可用于塑料的润滑剂,乳化剂,抗静电剂,滴流剂,由于12-羟基硬脂酸甘油酯中的侧链上带有一个羟基,使得亲水性增加,同时由于有较高的熔点,在塑料中使用时析出慢,有效提高了使用有效期,也提高了薄膜的透明度,经实际使用12-羟基硬脂酸甘油酯代替硬脂酸甘油酯,塑料薄膜的抗静电的持效性和流滴剂的持效性都有较好的改善。
附图说明
图1、图2为本发明12-羟基硬脂酸甘油酯气质联用图谱;
图3为本发明12-羟基硬脂酸甘油酯傅立叶远红外色谱图。
具体实施方式
本发明的12-羟基硬脂酸甘油酯,其化学式为
其制备包括以下步骤:
1)1mol氢化蓖麻油与0.8-3.0mol甘油混合后,加入0.2-1.2%量的强碱性催化剂;
2)温度控制在120℃-200℃,压力控制在-0.09-0.0Mpa,,进行酯交换保温反应1.0-4.0小时;
3)最后降温到100℃左右出料切片。
反应方程式为
经试验,本发明可优选采用以下方法制备:1mol氢化蓖麻油与0.8-3.0mol甘油混合后,加入0.2-1.2%量的催化剂(可以是指氢氧化钠,氢氧化钾,硬脂酸钠,甲醇钠,乙醇钠,碱金属氧化物等其中的一种或复配)进行酯交换反应。要求在真空情况下(真空度在-0.09-0.08Mpa),温度从120℃逐步升到160℃,保温反应1.0-2.0小时,最后降温到100℃左右出料切片。经测试,熔点:68-72℃,羟值:330-390mgkoH/g,如图1、图2为本发明气质联用图谱,图3为本发明傅立叶远红外色谱图。本产品12-羟基硬脂酸甘油酯可用于塑料的润滑剂,乳化剂,抗静电剂,滴流剂。
本发明产品应用于农膜上作为流滴剂的成份,在2007年及2008年的越冬棚试验中发现,使用了本产品的膜透明度由原来的89%提高到了91.2%,雾度值也由原来的14.0%降到为11.06%明显好于同类产品。同时应用了本产品后膜的析出情况明显好转,与日本的KF-650同类产品相媲美。流滴有效期也达到了5个月以上。
Claims (9)
1.12-羟基硬脂酸甘油酯,其特征在于化学式为
3.如权利要求书2所述12-羟基硬脂酸甘油酯的制备方法,其特征在于步骤1)中所述的强碱性催化剂是指氢氧化钠,氢氧化钾,硬脂酸钠,甲醇钠,乙醇钠,碱金属氧化物等其中的一种或两种以上复配构成。
4.如权利要求书2所述12-羟基硬脂酸甘油酯的制备方法,其特征在于步骤2)中所述的温度控制在120℃-160℃。
5.如权利要求书2所述12-羟基硬脂酸甘油酯的制备方法,其特征在于步骤2)中所述的压力控制在-0.09--0.08Mpa。
6.如权利要求书2所述12-羟基硬脂酸甘油酯的制备方法,其特征在于步骤2)中所述的进行酯交换保温反应时间为1.0-2.0小时。
7.如权利要求书2所述12-羟基硬脂酸甘油酯的制备方法,其特征在于步骤2)中所述的温度从120℃逐步升到160℃。
8.如权利要求书1所述的12-羟基硬脂酸甘油酯,其特征在于熔点,68-72℃,羟值,330-390mgkoH/g。
9.如权利要求书1所述的12-羟基硬脂酸甘油酯,其特征在于用作塑料的润滑剂,乳化剂,抗静电剂。