CN101962703A - 不锈钢冶炼用后耐火材料的再利用方法 - Google Patents

不锈钢冶炼用后耐火材料的再利用方法 Download PDF

Info

Publication number
CN101962703A
CN101962703A CN2010105295218A CN201010529521A CN101962703A CN 101962703 A CN101962703 A CN 101962703A CN 2010105295218 A CN2010105295218 A CN 2010105295218A CN 201010529521 A CN201010529521 A CN 201010529521A CN 101962703 A CN101962703 A CN 101962703A
Authority
CN
China
Prior art keywords
smelting
stainless steel
steel
molten steel
refractory material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2010105295218A
Other languages
English (en)
Other versions
CN101962703B (zh
Inventor
赵海泉
史永林
罗胜
刘明生
叶文成
严文明
马达
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanxi Taigang Stainless Steel Co Ltd
Original Assignee
Shanxi Taigang Stainless Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanxi Taigang Stainless Steel Co Ltd filed Critical Shanxi Taigang Stainless Steel Co Ltd
Priority to CN2010105295218A priority Critical patent/CN101962703B/zh
Publication of CN101962703A publication Critical patent/CN101962703A/zh
Application granted granted Critical
Publication of CN101962703B publication Critical patent/CN101962703B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

不锈钢冶炼用后耐火材料的再利用方法，属于废物再利用，它包括破碎、筛分、添加到炼钢炉、兑钢水、冶炼、出渣、出钢7个工艺环节，其特征是将不锈钢冶炼用后的耐火材料进行破碎；筛分出粒度不大于5mm的颗粒，称之为钙镁砖颗粒；按1吨钢水添加15～20公斤钙镁砖颗粒的比例将钙镁砖颗粒添加到氩氧脱氮精炼炉中；倒入不锈钢水并按一般炼钢要求加入石灰——吹氧——吹氩——添加硅和萤石进行合金化还原冶炼。本发明能够将不锈钢冶炼用后的耐火材料的侵蚀层、渗透层、原质层全部进行再利用，其利用率为吨钢水大于15kg。

Description

不锈钢冶炼用后耐火材料的再利用方法
技术领域：
本发明属于废物利用领域，具体涉及不锈钢冶炼用后耐火材料的再利用方法。
背景技术：
不锈钢冶炼用后的耐火材料被钢水侵蚀后，耐火材料被分为侵蚀层、渗透层、原质层。每100克用后耐火材料中含有三氧化二铁1.35克、三氧化二铝0.81克、二氧化硅3.58克、氧化钙24.105克、氧化镁69.91克、氧化锰0.085克、氧化镍0.01克、三氧化二铬0.15克。目前，人们采用返回法对用后耐火材料进行再利用，其仅能将原质层进行利用，不能对渗透层和侵蚀层进行再利用，故返回法对用后的耐火材料的再利用率较低。
发明内容：
本发明旨在提供能够对全部的不锈钢冶炼用后的耐火材料进行再利用的方法。
本发明包括破碎、筛分、添加到炼钢炉、兑钢水、冶炼、出渣、出钢7个工艺环节，其特征是将不锈钢冶炼用后的耐火材料进行破碎；筛分出粒度不大于5mm的颗粒，称之为钙镁砖颗粒；按1吨钢水添加15～20公斤钙镁砖颗粒的比例将钙镁砖颗粒添加到氩氧脱氮精炼炉中；兑入不锈钢水并按一般炼钢要求加入石灰——吹氧——吹氩——添加硅和萤石进行合金化还原冶炼；冶炼结束，出渣、出钢。
所述石灰为氧化钙。
本发明能够将不锈钢冶炼用后的耐火材料的侵蚀层、渗透层、原质层全部进行再利用，其利用率为吨钢水大于15kg。
具体实施方式：
实施例：冶炼45吨不锈钢水。
1、将不锈钢冶炼用后的耐火材料进行破碎；
2、筛分出粒度不大于5mm的颗粒，称之为钙镁砖颗粒；
3、将700公斤的钙镁砖颗粒添加到AOD炉中；
4、兑入45吨不锈钢水；
5、按一般炼钢要求加入石灰2.65吨，吹氧30分钟，吹氩40分钟，添加硅铁1～1.5吨/炉和萤石0.55吨；
6、进行合金化还原冶炼，冶炼时间为60分钟；
7、出渣(均为现有技术，省略其描述)；
8、出钢(均为现有技术，省略其描述)。
所述石灰为氧化钙。

Claims (1)

1.不锈钢冶炼用后耐火材料的再利用方法，包括破碎、筛分、添加到炼钢炉、兑钢水、冶炼、出渣、出钢7个工艺环节，其特征是将不锈钢冶炼用后的耐火材料进行破碎；筛分出粒度不大于5mm的颗粒，称之为钙镁砖颗粒；按1吨钢水添加15～20公斤钙镁砖颗粒的比例将钙镁砖颗粒添加到氩氧脱氮精炼炉中；倒入不锈钢水并按一般炼钢要求加入石灰——吹氧——吹氩——添加硅和萤石进行合金化还原冶炼。
CN2010105295218A 2010-10-30 2010-10-30 不锈钢冶炼用后耐火材料的再利用方法 Active CN101962703B (zh)