CN101959826A - 适用于声学基体的整理复合物 - Google Patents
适用于声学基体的整理复合物 Download PDFInfo
- Publication number
- CN101959826A CN101959826A CN2009801063522A CN200980106352A CN101959826A CN 101959826 A CN101959826 A CN 101959826A CN 2009801063522 A CN2009801063522 A CN 2009801063522A CN 200980106352 A CN200980106352 A CN 200980106352A CN 101959826 A CN101959826 A CN 101959826A
- Authority
- CN
- China
- Prior art keywords
- product
- present
- mixture
- arrangement
- product according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种整理复合物,其具有声学性能,且包含相对于产品的总重量以重量百分比计的至少如下物质:25%至80%的水;0.1%至5%的增稠剂;0.01%至0.8%的分散剂;10%至60%的单颗粒填料,其中D50大于或等于100微米;0.5%至6%的粘合剂;且该整理复合物不包含起泡剂;并在水蒸发后显示800至6000mks瑞利的透气率。
Description
技术领域
本发明涉及具有声学性能的整理复合物。
背景技术
整理复合物(compound),也称为装饰复合物或者整理或装饰涂料,通常用于涂布基体(support)以赋予该基体对应于设定的美学标准的所需修饰。
当装饰或改进具有声学性能的基体的美感时,合适的是使用不妨碍或改变它们的基体的声学性能的特定的整理复合物。特别地,合适的是不妨碍具有声学性能的基体的多孔性。换言之,若要保持施用整理复合物的基体的声学性能,则所有的整理复合物均不合适。特别地,在用于制备吊顶的吸音板的情况中,必须使用特定的整理复合物。
为了符合工业要求,必须找到具有改进声学性能的整理复合物。
因此,本发明要解决的问题是提供具有声学性能并可用作整理复合物的产品。
发明内容
为了该目的,本发明提供了一种产品,其包含相对于产品的总重量以重量百分比计的至少如下物质:
-25%至80%的水;
-0.1%至5%的增稠剂;
-0.01%至0.8%的分散剂;
-10%至60%的单颗粒填料,其中D50大于或等于100微米;
-0.5%至6%的粘合剂;
且不包含起泡剂。
本发明还提供了一种包含上述产品的整理复合物。
本发明还提供了一种施用本发明的整理复合物的糊墙纸板(plasterboard)。
最后,本发明涉及本发明的整理复合物用于制备建筑领域的构件的用途。
本发明提供了决定性的优点,特别是本发明的产品保持了施用该产品的基体的声学性能。
有利地,本发明的产品可用作用于所有类型的天花板、特别是天花板的糊墙纸板的整理复合物。
本发明提供的另一优点在于可利用本发明的产品的声学性能和/或美学性能。
本发明的另一优点是所述复合物包含高含量的水,这确保了该复合物的良好加工性,并促进了在现场施工过程中该复合物的施用。
本发明的另一优点是本发明的产品可以单层施用,这意味着本发明产品的单层施用就足以获得必需的声学性能和/或美学性能。
此外,本发明的产品的优点在于具有良好的覆盖或衬里能力,这使得有可能遮盖由密封剂(jointing compound)形成的接头。
极有利地,本发明的产品适合用作单片天花板(monolithic ceilings)的整理复合物。根据本发明,术语“单片天花板”应理解为由单个构件制得的天花板。例如,其可为包含由接头接合并由整理复合物覆盖的几个糊墙纸板的提供总体的单片外观的天花板,即由单个构件制得。
最后,本发明的优点在于能够用于所有工业,特别是建筑工业和所有建筑市场(建筑、土木工程或预制工厂)、用于建筑领域的构件的工业、灰泥构件的建筑工业中。
具体实施方式
在阅读如下说明书和用于非限制性说明和非限定性目的的实施例之后,本发明的其他优点和特性将清楚显示。
术语“声学性能”应理解为:
-吸收声波的能力,
-耗散声波能量的能力,
-使声波通过的能力,
-对声波的可透过性,
-对声波的透明性,
-降低或去除声波的混响的能力,或者
-最小化声波的反射的能力。
根据本发明,术语“粘合剂”应理解为具有提供给掺入该粘合剂的制剂粘结力的性能的任何复合物。该粘合剂旨在粘合如纤维或粒状填料的惰性构件。
根据本发明,术语“消泡剂”应理解为具有防止或避免在液体、半液体、半固体或固体中形成气相分散的性能,特别是防止或避免形成泡沫的性能的任何复合物。
根据本发明,术语“润湿剂”应理解为具有改变液体的表面张力以促进纤维的分散或避免纤维絮凝的性能的任何复合物。
根据本发明,术语“增稠剂”应理解为提供或促进平衡下的不均匀物理相的保持的任何复合物。
根据本发明,术语“胶质”应理解为植物渗出物或微生物源的胞外分泌物。
根据本发明,术语“D50”应理解为由体积累计的粒度分布的粒子的中位直径(中位直径将分布分为两个相等部分,50体积%的粒子具有小于D50的尺寸,且50体积%的粒子具有大于D50的尺寸)。
根据本发明,术语“单颗粒填料”应理解为单分散填料。术语“单分散”应理解为一种填料,其包含的所有粒子具有相同的尺寸。也就是说,这意指粒子尺寸的粒度分布(根据尺寸的体积百分比)的图形表示仅显示一个单峰(一个单群)。“单颗粒填料”的该定义排除了具有不同尺寸的粒子的混合物或排除了具有不同尺寸的几种粒子的颗粒包(granular packing)。
优选地,本发明的产品不含有微细填料。根据本发明,本发明的术语“微细填料”应理解为中位直径D50严格小于100微米的粒子。
根据本发明,术语“用于建筑领域的构件”应理解为作为建筑的部件的任何构件,例如地板、准条、地基、墙壁、隔断墙、天花板、横梁、工作台(work top)、柱子、桥墩、混凝土块、管道、杆、檐口、道路工程的构件(例如人行道边界)、屋瓦。
首先,本发明提供了一种产品,其包含相对于产品的总重量以重量百分比计的至少如下物质:
-25%至80%的水;
-0.1%至5%的增稠剂;
-0.01%至0.8%的分散剂;
-10%至60%的单颗粒填料,其中D50大于或等于100微米;
-0.5%至6%的粘合剂;
且不包含起泡剂。
优选地,本发明的产品在干燥后为多孔产品或可透气。
优选地,本发明的产品在水蒸发后为多孔产品或可透气。
优选地,本发明的产品在水蒸发后具有800至6000mks瑞利(Rayls)的透气率。
本发明的产品包含相对于产品的总重量以重量百分比计25%至80%的水,优选30%至70%,更优选35%至60%,甚至更优选40%至50%的水。根据本发明合适的水为自来水。
根据本发明的一个变体,所述产品可包含相对于产品的总重量以重量百分比计0.001%至10%的消泡剂,优选0.1%至5%的消泡剂。
本发明的产品包含相对于产品的总重量以重量百分比计0.1%至5%的增稠剂,优选0.5%至2.5%的增稠剂,甚至更优选0.5%至1.5%的增稠剂。
根据本发明的合适的增稠剂优选为树胶、纤维素及其衍生物(如纤维素醚或羧甲基纤维素)、淀粉及其衍生物、明胶、琼脂、角叉菜聚糖。优选地,本发明的产品包含树胶作为增稠剂。根据本发明,合适的作为增稠剂的树胶优选选自阿拉伯胶、黄蓍胶、角豆树胶、葡聚糖胶、迪优坦(Diutan)胶、结冷胶、瓜尔豆胶、硬葡聚糖(Scleroglucan)胶、呫吨(Xanthene)胶、文莱胶。根据本发明,作为增稠剂的优选的树胶为呫吨胶。
本发明的产品包含相对于产品的总重量以重量百分比计0.01%至0.8%的分散剂,优选0.1%至0.5%的分散剂,甚至更优选0.1%至0.25%的分散剂。
本发明的产品包含相对于产品的总重量以重量百分比计10%至60%的单颗粒填料,其中D50大于或等于100微米,特别是包含20%至55%的单颗粒填料,优选30%至50%的单颗粒填料,更优选35%至50%的单颗粒填料,且最终甚至更优选40%至45%的单颗粒填料。
根据本发明的合适的单颗粒填料优选为碳酸钙、白云石(碳酸钙和碳酸镁)、二氧化硅、滑石、云母、无水或脱水硫酸钙、硫酸钡或其混合物。根据本发明的一个变体,根据本发明的合适的单颗粒填料可为碳酸钙和玻璃珠的混合物,应理解玻璃珠的百分比相对于产品的总重量以重量百分比计为小于或等于14%。根据本发明的另一变体,根据本发明的合适的单颗粒填料不包含玻璃珠。
优选地,根据本发明的合适的单颗粒填料为碳酸钙。更特别地,根据本发明的合适的碳酸钙具有大于或等于100微米,优选100微米至2毫米,更优选110微米至500微米,甚至更优选120微米至250微米的D50。根据本发明的最终优选的碳酸钙具有等于200微米的D50。所述数值通过激光衍射,优选使用Malvern MS2000粒度计型装置并使用干法测得。
本发明的产品可进一步包含相对于产品的总重量以重量百分比计0.1%至5%的合成或动物纤维,优选包含1%至3%的合成或动物纤维。根据本发明的合适的合成纤维可为聚酰胺纤维、聚丙烯纤维、聚酯纤维、聚丙烯腈纤维。根据本发明的优选的纤维为合成纤维,特别是聚酰胺纤维。
优选地,本发明的产品不含有植物纤维。
本发明的产品包含相对于产品的总重量以重量百分比计0.5%至6%的粘合剂,优选包含1.0%至5%的粘合剂,更优选1.5%至4%,甚至更优选1.5%至2%的粘合剂。所述粘合剂使得有可能确保本发明的产品的粘结力。根据本发明的合适的粘合剂可为丙烯酸聚合物、苯乙烯丙烯酸聚合物(styrene acrylic polymer)、乙烯基聚合物,其混合物和衍生物。根据本发明的优选的粘合剂为丙烯酸聚合物,特别是苯乙烯丙烯酸聚合物。
本发明的产品可进一步包含另外的添加剂,例如润湿剂、聚结剂、流化剂、杀细菌剂、杀真菌剂、重溶剂、颜料、光催化颜料。
根据本发明的一个变体,所述产品可进一步包含0.05%至1%的润湿剂。根据本发明的合适的润湿剂优选为醇、多元醇,特别是二醇。
根据本发明的另一变体,所述产品可进一步包含0.01%至5%的聚结剂。根据本发明的合适的聚结剂优选为二醇醚。
本发明的产品可进一步包含重溶剂。根据本发明的合适的重溶剂优选为己二醇或碳酸丁烯酯(butylene carbonate)。
根据本发明的另一变体,所述产品可进一步包含一种或多种单独的颜料或组合的颜料。根据本发明的合适的颜料优选为二氧化钛。
本发明的产品可进一步包含一种或多种光催化颜料。根据本发明的合适的光催化颜料可为光催化二氧化钛。
优选地,本发明的产品不包含粘土。
优选地,本发明的产品不包含吡啶硫酮锌(zinc pyrithione)。
本发明的产品可通过在混合器中将产品的各种组分连续与水混合而制得。
本发明的产品可在一次施用中进行施用。这意味着不必施用几层本发明的产品以获得令人满意的结果。应注意当在基体上的本发明的产品的量为0.7至3.5千克/平方米时认为结果是令人满意的。
本发明的产品在一次施用至基体上后具有0.7至3.5千克/平方米,优选1.0至3.0千克/平方米,更优选1.0至2.5千克/平方米,甚至更优选1.5至2.0千克/平方米的产品量。
本发明的产品的优点在于能够通过不同的方法进行施用,例如泥刀施用法、辊子施用法、喷雾施用法。优选的施用方法为喷雾法,特别是使用软管喷枪或使用大体积低压喷雾装置或使用“无气”装置的施用方法。
当所述产品以一层(称为施用层)施用在其基体上时,该层的厚度为0.5毫米至2毫米,优选0.7毫米至1.5毫米,甚至更优选0.8毫米至1.3毫米。
本发明的产品在水蒸发之后具有大于或等于800mks瑞利(Nsm-3),优选800至6000mks瑞利,优选950至5000mks瑞利,甚至更优选1000至3500mks瑞利的根据ASTM C522-87标准测得的空气流动阻力。
在将产品施用至其基体上之后,使该产品优选在环境温度下干燥。
在干燥之后,本发明的产品优选为多孔产品或可透气。术语“可透气”应理解为具有大于或等于800mks瑞利(Ns m-3),优选800至6000mks瑞利,甚至更优选1000至3500mks瑞利的根据ASTMC522-87标准测得的空气流动阻力的产品。
本发明也涉及包含如上所述的本发明的产品的整理复合物。
本发明的整理复合物优选为多孔产品或可透气。术语“可透气”应理解为具有大于或等于800mks瑞利(Ns m-3),优选800至6000mks瑞利,优选950至5000mks瑞利,甚至更优选1000至3500mks瑞利的根据ASTM C522-87标准测得的空气流动阻力的复合物。
本发明的整理复合物优选为不改变施用所述整理复合物的所述基体的声学性能的复合物。
本发明的整理复合物优选为不改变施用所述整理复合物的基体的透气率的复合物。
可利用本发明的复合物的声学性能和/或美学性能。
可将本发明的复合物施用在许多基体上,特别是例如地板、墙壁、隔断墙、天花板、横梁、工作台、檐口和其他类型的基体。
本发明也提供了如上所述的其上施用了本发明的整理复合物的基于石膏的板,特别是糊墙纸板。
最后,本发明也涉及本发明的整理复合物用于制备建筑领域的构件的用途。
如下实施例说明了本发明而不限制本发明。
实施例
所用的反应物:
用于本发明的产品的不同制剂中的反应物在如下表I中分组。
表I
设备:
-装有分散叶片的Rayneri实验室混合分散器。
-装有带有变速器的搅拌轴(mixing shaft)的Zanelli牌Argon AI7.5型高速混合分散器。
软管喷枪:Europro牌6P型喷射组装件(Projection ensemble),其包含带有不锈钢整体料斗和容积螺杆泵(包含在与减速器偶联的非同步电动机内)的机器以及压缩机和装有直径为3毫米的喷嘴的软管喷枪。
操作程序:制备本发明的实施例1的复合物:
在混合碗筒(bowl)中,引入43.49份自来水。
在400rpm的搅拌下,在5分钟的时间内连续引入0.13份CoatexP90分散剂,0.11份Envirogem 360润湿剂,0.02份Clerol PLB847消泡剂和0.63份Actigum CS6增稠剂。
搅拌逐渐增加至2500rpm,并同时在20分钟的时间内加入45.01份Durcal 130单颗粒填料,5.00份Tiona 595二氧化钛颜料和2.00份Rhoximat NYL0.8纤维。
搅拌降低至1000rpm,并同时在3分钟的时间内加入3.00份Acronal S790粘合剂,0.31份Dowanol PNB聚结剂和0.31份Mergal723K抗微生物剂(biocide agent)。
成分的量相对于产品的总重量以重量百分比给出。
本发明的复合物:
根据如上所述的实施例1的操作程序制备本发明的不同复合物:复合物2至13。如下表II描述了复合物1至8的化学组成,表III描述了复合物9至15的化学组成,其相对于产品的总重量以重量百分比计。
表II
类 | 复合物 | 1 | 2 | 3 | 4 | 5 |
溶剂 | 水 | 43.49 | 33.34 | 26.86 | 27.99 | 28.08 |
分散剂 | Coatex P90 | 0.13 | 0.04 | 0.11 | 0.25 | 0.11 |
润湿剂 | Envirogem 360 | 0.11 | ||||
消泡剂 | Clerol PLB847 | 0.02 | 0.02 | |||
增稠剂 | Rheo 3000 | 0.77 | 1.78 | 2.01 | ||
Actigum CS 6 | 0.63 | 0.46 | ||||
填料 | Beatite 350-630μm | 38.97 | ||||
Durcal 130 | 45.01 | 46.10 | 49.88 | 58.02 | ||
Poraver 0.5-1 | 10.15 | 11.08 | ||||
纤维 | PP Stavon 18/4 | 1.02 | ||||
Rhoximat NYL 0.8 | 2.00 | |||||
颜料 | Tiona 568 | 5.00 | 5.54 | 5.97 | 5.09 | 6.30 |
粘合剂 | Acronal S790 | 3.00 | 3.69 | 4.69 | 5.09 | 4.58 |
聚结剂 | Dowanol PnB | 0.31 | 0.37 | 0.60 | 0.76 | 0.57 |
抗微生物剂 | Mergal 723K | 0.31 | 0.28 | 0.04 | ||
100.00 | 100.00 | 100.00 | 100.00 | 80.63 |
表III
每个复合物的空气渗透性的测量:
空气渗透性由空气阻力的测量进行评估。所述测量使用通常称为欧姆计的阻力计完成。在样品与对照玻璃板之间通过5厘米直径孔测得为17%的以水柱英寸数计的空气流的压差。每次进行对应于5个不同的空气流值的5个测量。所得的值越高,空气通过的阻力越大,则样品多孔性越低,渗透性越低。
(渗透率mks瑞利)=(ΔP英寸H2O×149.4)/1.49×105×(5.10-2)2/4结果示于如下表IV。
表IV
本发明的复合物1至11可透气。
声学测量试验:
将复合物12和13施用至具有声学性能的糊墙纸板上。复合物使用软管喷枪施用(泵速:2.5,雾化压力:30psi)。
组装体称作“系统”。
噪声降低系数(NRC)的测量方法为描述于ASTM C423-02A标准中的使用容积为114立方米的房间的方法。
声学测量在这些系统上完成。
表V
复合物12和13可透气,且不改变或仅仅略微改变其上施用它们的基体的声学性能。当未涂布的糊墙纸板具有0.55的NRC时,涂布有复合物12(系统)的相同的板具有0.55的NRC。类似地,当未涂布的糊墙纸板具有0.80的NRC时,涂布有复合物13(系统)的相同的板具有0.75的NRC。
Claims (15)
1.一种产品,其包含相对于产品的总重量以重量百分比计的至少如下物质:
-25%至80%的水;
-0.1%至5%的增稠剂;
-0.01%至0.8%的分散剂;
-10%至60%的单颗粒填料,其中D50大于或等于100微米;
-0.5%至6%的粘合剂;
且不包含起泡剂。
2.根据权利要求1所述的产品,其特征在于其进一步包含0.001%至10%的消泡剂。
3.根据权利要求1所述的产品,其特征在于其包含0.5%至1.5%的增稠剂。
4.根据权利要求1所述的产品,其特征在于其在水蒸发后具有800至6000mks瑞利的透气率。
5.根据权利要求1所述的产品,其特征在于其包含0.1%至0.5%的分散剂。
6.根据权利要求1所述的产品,其特征在于其包含35%至50%的单颗粒填料。
7.根据权利要求1所述的产品,其特征在于其包含碳酸钙作为单颗粒填料,其中D50为100微米至2毫米。
8.根据权利要求1所述的产品,其特征在于其进一步包含0.1%至5%的合成纤维。
9.根据权利要求1所述的产品,其特征在于所述产品在单次施用至基体上之后具有0.7至3.5千克/平方米的产品量。
10.根据权利要求1所述的产品,其特征在于其进一步包含一种或多种光催化颜料。
11.一种整理复合物,其包含如权利要求1至10任一项所述的产品。
12.根据权利要求11所述的整理复合物,其特征在于其为透气的复合物。
13.根据权利要求12所述的整理复合物,其特征在于其为不改变施用所述整理复合物的基体的透气率的复合物。
14.一种具有石膏基底的板,在其上施用了根据权利要求11至13所述的整理复合物。
15.根据权利要求11至13所述的整理复合物用于制备建筑领域的构件的用途。