CN101942219A - 一种工装用高耐氯漂高耐热压牢度的深蓝色还原染料 - Google Patents
一种工装用高耐氯漂高耐热压牢度的深蓝色还原染料 Download PDFInfo
- Publication number
- CN101942219A CN101942219A CN2010102639717A CN201010263971A CN101942219A CN 101942219 A CN101942219 A CN 101942219A CN 2010102639717 A CN2010102639717 A CN 2010102639717A CN 201010263971 A CN201010263971 A CN 201010263971A CN 101942219 A CN101942219 A CN 101942219A
- Authority
- CN
- China
- Prior art keywords
- fastness
- hot pressing
- vat dyes
- chlorine
- high fastness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种工装用高耐氯漂高耐热压牢度的深蓝色还原染料,该染料由以下组分组成:重量分数为12-16%的染料单体A,重量分数为18-22%的染料单体B,重量分数为1-5%的染料单体C,重量分数为60-64%的分散剂和0-2%的防尘油。本发明提供的深蓝色还原染料按照国家标准其耐氯漂牢度可以达到4-5级,耐热压牢度达4-5级,除此之外,该染料的干耐摩擦牢度为4-5级,湿耐摩擦牢度为3-4级,完全可以满足高要求工装系列产品性能。
Description
技术领域
本发明涉及一种深蓝色染料,特别涉及工装专用深蓝色高耐氯漂高耐热压牢度的深蓝色还原染料(还原深蓝W-NBS)。
背景技术
还原染料是一类品种众多、色泽鲜艳、牢度优异的高级染料,由于还原染料具有优良的耐晒、耐气候、耐热、耐溶剂、耐洗性能,能够广泛地应用于棉、毛、丝、麻、合成纤维及其混纺织物、交织物的印染,是棉用染料中的一种高级产品。
近年来,随着社会的发展,工装产品面临耐氯漂牢度、耐热压牢度等要求的提高,同时,欧美市场对涤棉工装面料的各项色牢度也都有很高的要求,尤其是医疗工装面料要求耐氯漂牢度、耐热压牢度AATCC标准4级以上。一般还原染料氯漂牢度都比较优良,例如红F3B、黄G、艳绿FFB、紫2R等都有较高的耐氯漂牢度,但应用较为普遍的还原藏青、还原深蓝、艳蓝等染料,耐氯漂牢度较低,各项指标很难达到要求,特别是用于出口的产品,就更难满足要求,而且在染色的过程中,染色物遇到有效氯时容易受到破坏,而使色泽变暗布面发黑,耐氯漂牢度只有1级,质量严重受损。此外,耐热压牢度也很难满足工作产品的需求,因此,原有产品已经无法满足日益增长的客户要求,迫切需要一种高耐氯漂高耐热压牢度的深蓝色产品来满足市场需要。
发明内容
本发明要解决的技术问题是提供一种适用于工装的高耐氯漂高耐热压牢度的深蓝色还原染料。
为解决上述技术问题,本发明所采用的技术方案是:
一种工装用高耐氯漂高耐热压牢度的深蓝色还原染料,其特征在于该染料由以下组分组成:
重量分数为12-16%的化学结构式(1)的染料单体A,
重量分数为18-22%的如化学式(2)的染料单体B,
重量分数为7-9%的如化学式(3)的染料单体C,
重量分数为60-64%的分散剂和重量分数为0-2%的防尘油。
作为对本发明的进一步限定,本发明所述的分散剂为木质素磺酸钠。
本发明所述的深蓝色还原染料可以按照以下方法制备:将计量比的还原染料单体滤饼、分散剂打浆后,采用湿粉碎技术进行粉碎研磨,研磨72小时后通过管道送达喷雾干燥塔干燥,同时喷入一定量的防尘油,最后成品包装,喷雾干燥中产生的废气由旋风除尘装置通过数次过滤除尘。
本发明采用的染料单体A可选用江苏亚邦染料股份有限公司生产的环保型还原深蓝BO,染料单体B可选用江苏亚邦染料股份有限公司生产的环保型还原蓝BC,染料单体C可选用江苏亚邦染料股份有限公司生产的环保型还原艳绿FFB。
采用上述技术方案后,本发明所取得的有益效果是:本发明提供的藏青色还原染料按照国家标准其氯漂牢度可以达到4-5级,耐热压牢度达4-5级,除此之外,该染料的干摩擦牢度为4-5级,湿摩擦牢度为3-4级,可以完全满足高要求工装系列产品性能。
具体实施方式
下面结合实施例对本发明作进一步详细的说明,但本发明的保护范围并不限于此。
实施例1-5
按表1所示数据,将计量比的还原染料单体A、还原染料单体B和还原染料单体C滤饼、分散剂打浆后,采用湿粉碎技术进行粉碎研磨,研磨72小时后通过管道送达喷雾干燥塔干燥,同时喷入如表1所示量的防尘油,最后成品包装,喷雾干燥中产生的废气由旋风除尘装置通过数次过滤除尘。
表1
将上述实施例制得的深蓝色还原染料进行复合性能测试,分别采用GB/T7069-1997、GB/T6152-1997、GB/T3920-1997测定其各项染色牢度。测定结果见表2。
表2 单位:级
Claims (3)
2.根据权利要求1所述的一种工装用高耐氯漂高耐热压牢度的深蓝色还原染料,其特征在于所述的分散剂为木质素磺酸钠。
3.根据权利要求1所述的一种工装用高耐氯漂高耐热压牢度的深蓝色还原染料,其特征在于该深蓝色还原染料可以按照下述方法制备:将计量比的还原染料滤饼、分散剂打浆后,采用湿粉碎技术进行粉碎研磨,研磨72小时后通过管道送达喷雾干燥塔干燥,同时喷入一定量的防尘油,最后成品包装,喷雾干燥中产生的废气由旋风除尘装置通过数次过滤除尘。