CN101935447B - 一种透明水溶性树脂 - Google Patents
一种透明水溶性树脂 Download PDFInfo
- Publication number
- CN101935447B CN101935447B CN 201010251492 CN201010251492A CN101935447B CN 101935447 B CN101935447 B CN 101935447B CN 201010251492 CN201010251492 CN 201010251492 CN 201010251492 A CN201010251492 A CN 201010251492A CN 101935447 B CN101935447 B CN 101935447B
- Authority
- CN
- China
- Prior art keywords
- soluble resin
- transparent water
- solution
- water soluble
- transparent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供了一种透明水溶性树脂，其制备方法是：先将聚乙二醇与聚乙烯吡咯烷酮按重量比为1∶0.25～0.35混合，保持温度25～30℃时，搅拌待其完全溶解后得到溶液，再将该溶液与透明脲醛树脂液按体积比为1∶3～4混合得到胶液，按胶液体积的5～15％加入凝固剂冰醋酸，充分搅拌，并用真空泵抽气2～5min至无大量气泡产生，静置待表面再无气泡即得到透明水溶性树脂；其中所述聚乙二醇的分子量为600。使用该透明水溶性树脂包埋生物标本的优点是成功率高、不易开裂、透明且具备一定的硬度，可用于打磨抛光及造型等的后期处理，更能长久保持生物标本的原貌。
Description
技术领域
本发明涉及一种包埋生物标本的树脂，特别涉及一种透明水溶性树脂。
背景技术
目前，制作包埋生物标本常用的方法有如下几种：第一种是采用脲醛树脂包埋生物标本，其优点是成本低；缺点是胶体含水量高，且在制作过程中由于水分的蒸发极易开裂，成功率极低，所制树脂无韧性且易碎。第二种是在脲醛树脂中加入聚乙烯醇，该方法虽成功率较第一种稍高，但成功率总的来说还是相对较低。第三种是中国专利CN 100569854C提供的用于小型生物标本包埋的透明水溶性树脂，使用该产品包埋的生物标本具有不易开裂，具柔性，透明度好成功率高的优点，但由于使用的树脂成型后的硬度不够，不便于打磨抛光及造型等的后期处理。
发明内容
针对现有技术的不足，本发明提供了一种透明水溶性树脂，使用该透明水溶性树脂制备的包埋标本成功率高、具备一定的硬度，后期处理时可以进行打磨抛光等后期处理过程。
这一种透明水溶性树脂，其制备方法是：先将聚乙二醇与聚乙烯吡咯烷酮按重量比为1∶0.25～0.35混合，保持温度25～30℃时，搅拌待其完全溶解后得到溶液，再将该溶液与透明脲醛树脂液按体积比为1∶3～4混合得到胶液，按胶液总重量的5～15％加入凝固剂冰醋酸，充分搅拌，并用真空泵抽气2～5min至无大量气泡产生，静置待表面再无气泡即得到透明水溶性树脂；其中所述聚乙二醇的分子量为600。
制备本发明所述的各种原料均在市场有出售，并且价格低廉。
本发明与现有技术不同之处在于加入了一种新组分——聚乙烯吡咯烷酮，聚乙烯吡咯烷酮是一种非离子型高分子化合物，白色或乳白色粉末或颗粒，是具有吸湿性易流动的粉末，无臭或微臭，溶于水、碱、酸及极性有机溶剂，具有很强的膨胀性能和与多类物质的络合能力。由于聚乙烯吡咯烷酮既溶于水，又溶于大部分有机溶剂、毒性很低、生理相溶性好，通常用于医药、食品、化妆品这些与人们健康密切相关的领域中，从未用于生物标本的制作包埋中，在本发明中首次将聚乙烯吡咯烷酮与其它组分按一定的重量配比关系后更能发挥其特有的作用，不仅能增加产品的硬度，还可使包埋后成型的树脂能在后期加工时进行打磨抛光等处理，大大提高了标本的观赏价值。
本发明适用来包埋小型生物标本，使用时包括如下工序：a.底胶的制备：将本发明透明水溶性树脂注入模具的底部，放入50～55℃温箱中凝固；b.包埋标本：将处理后的生物标本放在凝固后的底胶上，注入本发明透明水溶性树脂，使其浸没标本，并置入50～55℃温箱中凝固；c.面胶的制作：将本发明透明水溶性树脂注入b工序凝固后的胶面，置于50～55℃温箱中凝固后，从模具中取出，再次放在50～55℃温箱直至完全固化；待其完全固化后，从温箱中取出，经打磨抛光，标本制作完成。
本发明的有益效果是该透明水溶性树脂流动性强，透明度好，便于生物标本的包埋；使用该树脂包埋的生物标本不仅具备一定的韧性，兼具一定的硬度，不易开裂，能有效防虫，防霉，并能长久保持标本原色，同时能增加产品的硬度，包埋后仍然可以在后期加工时进行打磨抛光，提高观赏价值，是一种成功率较高的适用于小型生物标本包埋的透明水溶性树脂。
具体实施例(共2例)
实施例1
先将分子量为600的聚乙二醇750克与聚乙烯吡咯烷酮250克混合，保持温度25～30℃时，搅拌、待其完全溶解后得到溶液，再取该溶液20毫升与透明脲醛树脂液80毫升混合成胶液，按胶液100毫升总体积的10％加入凝固剂冰醋酸即10毫升，充分搅拌并用真空泵抽气2～5min至无大量气泡产生，静置待表面再无气泡即得透明水溶性树脂，即可用来包埋小型生物标本。
实施例2
先将分子量为600的聚乙二醇800克与聚乙烯吡咯烷酮200克混合，保持温度25～30℃时，搅拌、待其完全溶解后得到溶液，再取该溶液25毫升与透明脲醛树脂液75毫升混合成胶液，按胶液100毫升总体积的5％加入凝固剂冰醋酸即5毫升，充分搅拌并用真空泵抽气2～5min至无大量气泡产生，静置待表面再无气泡即得透明水溶性树脂，即可用来包埋小型生物标本。
Claims (1)
1.一种透明水溶性树脂，其制备方法是：先将聚乙二醇与聚乙烯吡咯烷酮按重量比为1∶0.25～0.35混合，保持温度25～30℃时，搅拌待其完全溶解后得到溶液，再将该溶液与透明脲醛树脂液按体积比为1∶3～4混合得到胶液，按胶液体积的5～15％加入凝固剂冰醋酸，充分搅拌，并用真空泵抽气2～5min至无大量气泡产生，静置待表面再无气泡即得到透明水溶性树脂；其中所述聚乙二醇的分子量为600。