CN101914354B - 一种环保水性氯丁胶粘合剂的制作方法 - Google Patents

一种环保水性氯丁胶粘合剂的制作方法 Download PDF

Info

Publication number
CN101914354B
CN101914354B CN201010245974.8A CN201010245974A CN101914354B CN 101914354 B CN101914354 B CN 101914354B CN 201010245974 A CN201010245974 A CN 201010245974A CN 101914354 B CN101914354 B CN 101914354B
Authority
CN
China
Prior art keywords
component
water
neoprene
high speed
necked flask
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201010245974.8A
Other languages
English (en)
Other versions
CN101914354A (zh
Inventor
裴强
张升喜
金春雪
陈豪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xinyang Normal University
Original Assignee
Xinyang Normal University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xinyang Normal University filed Critical Xinyang Normal University
Priority to CN201010245974.8A priority Critical patent/CN101914354B/zh
Publication of CN101914354A publication Critical patent/CN101914354A/zh
Application granted granted Critical
Publication of CN101914354B publication Critical patent/CN101914354B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种粘合剂的制作方法，特别是一种环保水性氯丁胶粘合剂的制作方法。其特征在于：它包括如下三个步骤：a，氯丁胶乳(组分A)的制作；b，水相分散体系(组分B)的制作；c，水性氯丁胶黏合剂的制备。采用该方法得到的水性氯丁胶黏合剂具有绿色环保、稳定性强、价格低廉等优点。本发明提供的水性氯丁胶黏合剂能在制鞋、家具、手袋等行业被广泛运用。

Description

一种环保水性氯丁胶粘合剂的制作方法
技术领域
本发明涉及一种粘合剂的制作方法，特别是一种环保水性氯丁胶粘合剂的制作方法。
背景技术
氯丁胶是第一种被大量生产的合成橡胶化合物。氯丁胶由氯丁烯单体聚合而成，俗称万能胶，是中国大陆传统大宗接着剂，此种接着剂应用范围广，具有初黏力大、黏结强度高等特点，主要用于居家及公共设施的装饰装修、木器工业、制鞋工业等产业上。
最初氯丁胶所使用的溶剂是苯，溶解性极佳，胶粘剂的性能也较容易控制，但是苯的毒性相当大，在多次出现操作使用者中毒死亡事故后改用甲苯作溶剂。甲苯的毒性虽然比苯小多了，但如果措施不当仍可严重毒害操作者和污染环境。20世纪80年代，一度出现用汽油、乙酯等混合溶剂代替大部份甲苯或全部代替甲苯的研究，但因成本增加，胶粘性能不稳定，刺激性气味重，人们不愿意选用。
随着环保要求日趋严苛，溶剂型接着剂的应用亦受到日趋严格的法规规范，大部分发达国家停止或限制使用含三苯溶剂型的氯丁胶，而发展环保型接着剂，其中水溶性氯丁胶是发展的主要趋势。
发明内容
本发明具有如下两个目的：
1、提供一种制备所述水性氯丁胶粘合剂的方法；
2、提供一种价格低廉、性能优良、绿色环保的水性氯丁胶粘合剂(也称“水性万能胶”)。
本发明的技术解决方案是：
一种环保水性氯丁胶粘合剂的制作方法，其特征在于：它包括如下步骤：
a、组分A的制备：
在1500mL的三口烧瓶中依次加入300mL乙酸乙酯、200mL120号溶剂油、500mL碳酸二甲脂、100g碳九树脂、300g氯丁橡胶和50g二辛脂，机械搅拌，高速分散5h，得到浅黄色、半透明的粘稠液体，即得到组分A；
b、组分B的制备：
在1500mL的三口烧瓶中依次加入1000mL去离子水、20g阴离子纤维素钠盐、15g糊精、5g氯丁胶专用乳化剂，5g消泡剂和5g防老化剂，装上回流冷凝管、机械搅拌，加热至80℃，高速分散5h，得到乳白色粘稠液体，即得到组分B；
C、水性氯丁胶黏合剂的制备：
取300份组分A、300份组分B加入到1000mL的三口烧瓶，装上回流冷凝管、机械搅拌，加热至50℃，高速分散3h，得到白色乳状粘稠液体，即水性氯丁胶黏合剂，其固含物可达30g/100mL。
本发明具有如下优点：
1、绿色环保、安全，大限度地降低了有机挥发成分；
2、价格低廉，比普通溶剂型氯丁胶黏合剂成本节省40％；
3、性能优良，其粘度低(30000cps/25℃)、热稳定性好(50～60℃性能不变化)、初粘强度大(10.5N/12mm，温度为25℃)，固化速度快(15-30s)。
具体实施方式：
实施例1
首先，在1500mL的三口烧瓶中依次加入300mL乙酸乙酯、200mL 120号溶剂油、500mL碳酸二甲脂、100g碳九树脂、300g氯丁橡胶、50g二辛脂，得到混合物；
其次，对上述混合物进行机械搅拌，高速分散5h，得到浅黄色、半透明的粘稠液体(组分A)；
再次，在1500mL的三口烧瓶中依次加入1000mL去离子水、20g阴离子纤维素钠盐、15g糊精、5g氯丁胶专用乳化剂、5g消泡剂、5g防老化剂，装上回流冷凝管，得到混合物；
复再次，对上述混合物进行机械搅拌，加热至80℃，高速分散5h，得到乳白色粘稠液体(组分B)；
最后，取300份组分A、300份组分B加入1000mL的三口烧瓶，装上回流冷凝管、机械搅拌，加热至50℃，高速分散3h，得到白色乳状粘稠液体(即水性氯丁胶黏合剂)。
实施例2
首先，在1500mL的三口烧瓶中依次加入1000mL去离子水、20g阴离子纤维素钠盐、15g糊精、5g氯丁胶专用乳化剂、5g消泡剂、5g防老化剂，装上回流冷凝管，得到混合物；
其次，对上述混合物进行机械搅拌，加热至80℃，高速分散5h，得到乳白色粘稠液体(组分B)；
再次，在1500mL的三口烧瓶中依次加入300mL乙酸乙酯、200mL 120号溶剂油、500mL碳酸二甲脂、100g碳九树脂、300g氯丁橡胶、50g二辛脂，得到混合物；
复再次，对上述混合物进行机械搅拌，高速分散5h，得到浅黄色、半透明的粘稠液体(组分A)；
最后，取300份组分A、300份组分B加入1000mL的三口烧瓶，装上回流冷凝管、机械搅拌，加热至50℃，高速分散3h，得到白色乳状粘稠液体(即水性氯丁胶黏合剂)。

Claims (1)

1.一种环保水性氯丁胶粘合剂的制作方法，其特征在于：它包括如下步骤：
a、组分A的制各：
在1500mL的三口烧瓶中依次加入300mL乙酸乙酯、200mL120号溶剂油、500mL碳酸二甲酯、100g碳九树脂、300g氯丁橡胶和50g二辛酯，机械搅拌，高速分散5h，得到浅黄色、半透明的粘稠液体，即得到组分A；
b、组分B的制备：
在1500mL的三口烧瓶中依次加入1000mL去离子水、20g阴离子纤维素钠盐、15g糊精、5g氯丁胶专用乳化剂，5g消泡剂和5g防老化剂，装上回流冷凝管、机械搅拌，加热至80℃，高速分散5h，得到乳白色粘稠液体，即得到组分B；
C、水性氯丁胶黏合剂的制备：
取300份组分A、300份组分B加入到1000mL的三口烧瓶，装上回流冷凝管、机械搅拌，加热至50℃，高速分散3h，得到白色乳状粘稠液体，即水性氯丁胶黏合剂，其固含物可达30g／100mL。
CN201010245974.8A 2010-08-05 2010-08-05 一种环保水性氯丁胶粘合剂的制作方法 Expired - Fee Related CN101914354B (zh)