CN101914326A - Aqueous pigment dispersion color paste composition and preparation method thereof - Google Patents
Aqueous pigment dispersion color paste composition and preparation method thereof Download PDFInfo
- Publication number
- CN101914326A CN101914326A CN2010102852328A CN201010285232A CN101914326A CN 101914326 A CN101914326 A CN 101914326A CN 2010102852328 A CN2010102852328 A CN 2010102852328A CN 201010285232 A CN201010285232 A CN 201010285232A CN 101914326 A CN101914326 A CN 101914326A
- Authority
- CN
- China
- Prior art keywords
- acid
- color paste
- pigment dispersion
- component
- aqueous pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an aqueous pigment dispersion color paste composition and a preparation method thereof and belongs to the technical field of decorative base paper body coloring. The composition comprises components A, B, C, D, E and F: 25 to 70 parts of one or mixture of organic dye and inorganic dye, 5 to 20 parts of dispersant, 0.5 to 2 parts of wetting agent, 3 to 20 parts of hydrotropic substance, 0.01 to 1 part of additive generally applied to water-containing paint color paste and 30 to 70 parts of water. The invention also provides a method for preparing the aqueous pigment dispersion color paste composition. Compared with the conventional aqueous color paste, the aqueous pigment dispersion color paste has excellent cellulose-affinity fiber and high stability of high-shear resistance; the generated floccules are uniform and the coloring rate is improved by 5 to 20 percent; and foam is not generated in the application of the composition and the color of the paper board is uniform without aberration basically.
Description
Technical field
The invention belongs to the technical field of decorating base paper mass pigmentation, particularly a kind of aqueous pigment dispersion color paste composition and preparation method thereof.
Background technology
In recent years, in China colorful pigment dyestuff/mineral dye decorative paper dye technology that is used to manufacture paper with pulp is used, in other words hydrophobic pigment dyestuff is combined interaction with different types of tensio-active agent and various associated additives, be dispersed in the medium of water, form pigment dispersion color paste, carry out thorough mixing with the mixture of the water of wanting papermaking to manufacture paper with pulp, paper pulp, titanium dioxide.But used pigment is because itself character, cellulosic fibre is not had affinity, and under the condition of not using tensio-active agent, this dispersible pigment color paste can water-washed away from the fibrous reticulum that forms on the screen cloth of paper machine, and enrichment in the circulation loop of paper machine causes problems.Importantly pigment must be flocculated thus, and the conventional auxiliary agent that adds of papermaking mainly to be resin cation (R.C.), retention aid, Wet Strength Resin etc. be used to realizes flocculating and the pigment of more leave strip anionic charges, they form the throw out of band cationic charge with pigment by so-called bridging.Retention aid can also make titanium dioxide and fine fiber fraction flocculation, and the throw out of generation is retained to cellulosic fiber by interionic interaction and hydrogen bonded, and decorative paper fiber and solid additive are colored.So rationally select for use the mill base and the whole flocculation process to being formed of dispersion agent play an important role.In the technology in paper mill, the operation speed of machine of paper machine promoting, is used for the also corresponding increase of shear loading of the throw out of pigment rapidly on the screen cloth of paper machine, the possible part of throw out is destroyed, its tinctorial strength is descended, form aberration, cause the paper color inconsequent; The color burn of circulation loop plain boiled water (mixing water) is wasted resource simultaneously, pollutes.So, choose the pigment dispersion color paste composition that dispersion agent is formed, the paper machine high workload speed of a motor vehicle is caused the high shear rate of paper pulp and makes the flocculation shear stable of generation particularly important.
The painted water-based of decorative paper that is used to manufacture paper with pulp disperses the aqueous pigment dispersion color paste well known in the prior art of slurry can't satisfy the paper industry requirement, these water-based pigment colour pastes often include the anionic/nonionic tensio-active agent, under the intensive shear loading, except that the firmness deficiency of dispersed component adsorption pigment, also more foam can occur, cause paper wet end moulding process wet paper surface color point-like wadding poly-; Need to add more relatively defoamer, carry out froth breaking, easily cause to remain in to form the depression of refusing water on the dried paper, the deep processing follow-up to decorating base paper produces detrimentally affect.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art, a kind of painted aqueous pigment dispersion color paste composition of decorative paper and preparation method thereof that is used to manufacture paper with pulp is provided, it is stable and produce the foamy problem effectively to solve in paper-making process the anti-high-shear aspect painted.
The invention provides a kind of aqueous pigment dispersion color paste composition, said composition comprises: count by weight
Component A: pigment dyestuff, mineral dye a kind of or their mixture 25-70 part
B component: dispersion agent 5-20 part
Component C: wetting agent 0.5-2 part
Component D: hydrotrophy material 3-20 part
Component E: one is used for additive 0.01-1 part of aqueous coating mill base
Component F: water 30-70 part.
Preferably, described pigment dyestuff is selected from one or more mixtures that monoazo class, tetrazo class, azo condensation class, naphthols AS class, the blue or green serial class of phthalein, dione pyrrolo-pyrrole pigment, benzopyrazoles ketone or isoindole drench ketone; As: CI Pigment Yellow 73 1, CI Pigment Yellow 73 3, CI pigment Yellow 14, CI pigment yellow 17, CI Pigment Yellow 73 18, CI Pigment Yellow 73 62, CI Pigment Yellow 73 65, CI Pigment Yellow 73 74, CI pigment yellow 81, CI pigment yellow 83, CI Pigment Yellow 73 95, CI Pigment Yellow 73 110, CI pigment Yellow 12 0, CI pigment yellow 13 9, CI pigment yellow 147, CI Pigment Yellow 73 151, CI pigment yellow 154, CI Pigment Yellow 73 180 etc.; CI pigment Orange 13, CI pigment orange 34, CI pigment orange 36, CI pigment orange 73 etc.; CI Pigment red 5, CI pigment Red 8, CI Pigment red 22, CI Pigment red 23, CI pigment red 31, CI Pigment Red 112, CI pigment red 122, CI Pigment red 144, CI pigment red 146, CI Pigment red 166, CI Pigment red 170, CI Pigment red 176, CI Pigment red 185, CI Pigment red 187, CI Pigment red 254 etc.; CI pigment violet 19, CI pigment Violet 23 etc.; CI pigment Blue 15: 0, CI pigment Blue 15: 1, CI pigment Blue 15: 3, CI pigment Blue 15: 6, CI pigment blue 60 etc.; CI pigment Green 7, CI Pigment green 8, CI pigment green 36 etc.One or more mixtures of the oxide compound of oxide compound, titanyl compound or the antimony of the oxide compound of described mineral dye chosen from Fe, the oxide compound of chromium, cobalt are as iron oxide yellow, red iron oxide, Hua Lan, ultramarine, chromoxide green, titanium dioxide, lithopone or other mixed phase metal oxide, carbon black etc.
Preferably, B component is that at least a or two above mixtures are formed among following (b1), (b2), (b3), (b4):
(b1): one or more mixtures in naphthalenesulfonate formaldehyde condensation compound, phenol sulfonic formaldehyde condensation compound or naphthene sulfonic acid-phenol sulfonic formaldehyde condensation compound; The commodity that are suitable for: as, sodium methylene bis-naphthalene sulfonate, sulfonated lignin, alkyl naphthalene sulfonic acid formaldehyde condensation products etc.
(b2): sulfonated alkyl naphathalene; As sodium butylnaphthalenesulfonate, sodium dibutyl naphthalene sulfonate, octyl group sodium naphthalene sulfonate, dioctyl sodium naphthalene sulfonate etc.
(b3): vinylbenzene-phenol polyoxyethylene polyoxypropylene compound, chemical formula is:
F-O-(CHCH
3CH
2O)
m-(CH
2CH
2O)
n-XM
In the formula: F=vinylbenzene-phenolic groups, m=3-12, n=10-40, X=CH
2COO
-, SO
3 -, M=K
+, Na
+, NH
4 +Deng;
No matter m, n, X and M are selected from what value in the specialized range, and its represented product all is can buy from the market to obtain, and applied in the specific embodiment of the present invention all is to buy the corresponding product that obtains from the market.
(b4): water-soluble poly styrene-propene acid copolymer; Dissolved polystyrene-acrylic copolymer form by alkali neutralization of ethylene base acid unit, be preferably the resin aqueous solution of 25-40% weight, preferably, used resin essentially consist is by 40-60% weight aromatic unsaturated compound and multipolymer that 40-60% vinylformic acid/methacrylic acid/(methyl) acrylate is formed, the number-average molecular weight M=1000-10000g/mol of described multipolymer.
Preferably, be used for preparing one or more mixtures of aromatic unsaturated compound vinylbenzene, a-vinyl toluene, Vinyl toluene or the benzyl acrylate of above-mentioned multipolymer; Vinylformic acid/methacrylic acid/(methyl) acrylate monomer is following acid, or following acid and ester composition, described acid is vinylformic acid, methacrylic acid, MALEIC ANHYDRIDE, methylene-succinic acid, one or more of hydroxyethyl methacrylate propanesulfonic acid sodium, described ester are maleic acid mono-esterification thing, maleic acid ester, FUMARIC ACID TECH GRADE (diester), glycidyl acrylate, methyl acrylate, ethyl propenoate, butyl acrylate, Octyl acrylate, 2-EHA, vinylformic acid 2-hydroxyl ethyl ester, Propylene glycol monoacrylate, methyl methacrylate, Jia Jibingxisuanyizhi, butyl methacrylate, Octyl methacrylate, glycidyl acrylate, methacrylic acid 2-hydroxyl ethyl ester, one or more of (methyl) Propylene glycol monoacrylate.
Preferably, being used for neutral alkali is organic bases or mineral alkali.Organic bases is preferably ammonia, as Monoethanolamine MEA BASF, diethanolamine, trolamine, N, and N-dimethylethanolamine, diisopropanolamine (DIPA), amino methyl propyl alcohol etc.Mineral alkali is preferably sodium hydroxide, potassium hydroxide, lithium hydroxide, aqua ammonia etc.
Preferably, component C is the terminal fatty alcohol-polyoxyethylene ether that contains acid groups, and chemical formula is R (CH
2CH
2O)
n-XM, wherein R=C
4-C
20, n=3-10, X=CH
2COO
-, SO
3 -, M=K
+, Na
+, NH
4 +, (no matter R, n, X and M are selected from what value in the specialized range, and its represented product all is can buy from the market to obtain, and applied in the specific embodiment of the present invention all is to buy the corresponding product that obtains from the market).Or component C is succsinic acid fat acid esters sodium sulfonate, wherein fatty acid ester selection C
4-C
20Lipid acid.
Preferably, component D is ethylene glycol, propylene glycol, glycerine, glycol ether, triglycol, polyoxyethylene glycol, butyl glycol ether, Diethylene Glycol butyl ether, propylene glycol monomethyl ether, propylene glycol butyl ether, one or more mixtures in ethanol, the Virahol.
Preferably, component E is the additive that is usually used in the aqueous coating mill base, as: one or more mixtures of sanitas, mould inhibitor, defoamer.Sanitas commonly used has: Sodium Benzoate, magnificent section 981, mould inhibitor commonly used has: mould inhibitor GXL, mould inhibitor DC-2011, defoamer commonly used has: defoamer F-111, defoamer AE-203E.
Preferably, component F is distilled water, softening water, also available tap water.
Above-mentioned water-based paint disperses paste composition to prepare by the following method:
Mix according to described parts by weight by said components B, C, D, E, F, add described parts by weight component A and mix making beating, homogenizing, under the cooling water temperature condition, use sand mill or ball mill to grind, be ground to 0.5-2 μ m, separate grinding medium and get aqueous pigment dispersion color paste.Wherein grinding medium uses quartz silica bead or the Zirconium oxide bead of size d=0.4-8mm.
The beneficial effect that the present invention had:
The ordinary method that this aqueous pigment dispersion color paste is manufactured paper with pulp by decorating base paper, the cardboard water is pulled an oar at a high speed, add titanium dioxide or mineral filler, add aqueous pigment dispersion color paste of the present invention, can be miscible with the water arbitrary proportion, making beating mixes, add paper making additive, has excellent close cellulosic fibre with the aqueous color paste contrast of routine, good anti-high shear stability, the flocs unit of generation is even, makes dye uptake improve 5-20%, in application, do not produce foam, the cardboard color even that is ferreted out, basic no color differnece.The water that leaches is clear colourless, has reduced the pollution of the three wastes, has reduced consumption, has improved product competitiveness.
Embodiment
In order to understand the present invention, further specify the present invention with embodiment below, but do not limit the present invention.
Embodiment 1
Component A: 40 parts of pigment yellow 83s
B component: 3 parts of naphthalenesulfonate formaldehyde condensation compounds
And vinylbenzene-phenol polyoxyethylene polyoxypropylene compound, chemical formula is:
F-O-(CHCH
3CH
2O)
3-(CH
2CH
2O)
15-SO
3Na, F=vinylbenzene-phenolic groups in the formula.5 parts
Component C: end contains the fatty alcohol-polyoxyethylene ether of acid groups, and chemical formula is: C
9(CH
2CH
2O)
6SO
31 part of Na
Component D: 5 parts of glycerine
Component E: 981 0.2 parts of sanitas China sections
Component F: 45.8 parts of softening waters
Add up to: 100 parts
Said components B, C, D, E, F are mixed according to described parts by weight, add described parts by weight component A and mix making beating, homogenizing, under the cooling water temperature condition, use sand mill to grind, be ground to 0.5-2 μ m, separate grinding medium and get aqueous pigment dispersion color paste.
Embodiment 2
Component A: 170 35 parts of Pigment reds
B component: 5 parts of phenol sulfonic formaldehyde condensation compounds
Vinylbenzene-phenol polyoxyethylene polyoxypropylene compound, chemical formula is:
F-O-(CHCH
3CH
2O)
3-(CH
2CH
2O)
15CH
2COONa, F=vinylbenzene-phenolic groups in the formula.6 parts
Component C: 2 parts of succsinic acid octanoate sodium sulfonates
Component D: 8 parts of propylene glycol
Component E: 0.2 part of defoamer F-111
Component F: 43.8 parts in tap water
Add up to: 100 parts
Said components B, C, D, E, F are mixed according to described parts by weight, add described parts by weight component A and mix making beating, homogenizing, under the cooling water temperature condition, use sand mill to grind, be ground to 0.5-2 μ m, separate grinding medium and get aqueous pigment dispersion color paste.
Embodiment 3
Component A: 35 parts of pigment Blue 15s
B component: 5 parts of dioctyl sodium naphthalene sulfonates
Vinylbenzene-phenol polyoxyethylene polyoxypropylene compound, chemical formula is:
F-O-(CHCH
3CH
2O)
3-(CH
2CH
2O)
15SO
3Na, F=vinylbenzene-phenolic groups in the formula.6 parts
Component C: end contains the fatty alcohol-polyoxyethylene ether of acid groups, and chemical formula is: C
18(CH
2CH
2O)
10SO
31 part of Na
Component D: 8 parts of ethylene glycol
Component E: 0.2 part of anti-enzyme agent DC-2011
Component F: 44.8 parts in tap water
Add up to: 100 parts
Said components B, C, D, E, F are mixed according to described parts by weight, add described parts by weight component A and mix making beating, homogenizing, under the cooling water temperature condition, use sand mill to grind, be ground to 0.5-2 μ m, separate grinding medium and get aqueous pigment dispersion color paste.
Above aqueous pigment dispersion color paste has high tinctorial strength, good flowability and stability in storage; Basic non-foam under the papermaking shear conditions; In papermaking, add 10% this aqueous pigment dispersion color paste through high-shear 1 hour with do not shear paper pulp and compare and only lose 0.3% tinctorial strength.
Method of the present invention is described by specific embodiment.Those skilled in the art can use for reference links such as content appropriate change raw material of the present invention, processing condition and realize corresponding other purpose, its relevant change does not all break away from content of the present invention, all similar replacements and change will become apparent to those skilled in the art that and all be regarded as comprising within the scope of the present invention.
Claims (10)
1. aqueous pigment dispersion color paste composition, it is characterized in that: said composition comprises: meter by weight
Component A: pigment dyestuff, mineral dye a kind of or their mixture 25-70 part,
B component: dispersion agent 5-20 part,
Component C: wetting agent 0.5-2 part,
Component D: hydrotrophy material 3-20 part,
Component E: one is used for the additive of aqueous coating mill base, 0.01-1 part,
Component F: water 30-70 part.
2. a kind of aqueous pigment dispersion color paste composition according to claim 1 is characterized in that: described pigment dyestuff is selected from one or more mixtures that monoazo class, tetrazo class, azo condensation class, naphthols AS class, the blue or green serial class of phthalein, dione pyrrolo-pyrrole pigment, benzopyrazoles ketone or isoindole drench ketone; One or more mixtures in the oxide compound of oxide compound, titanyl compound or the antimony of the oxide compound of described mineral dye chosen from Fe, the oxide compound of chromium, cobalt.
3. a kind of aqueous pigment dispersion color paste composition according to claim 1 is characterized in that: described B component is that at least a or two above mixtures are formed among following b1, b2, b3, the b4:
B1: one or more mixtures in naphthalenesulfonate formaldehyde condensation compound, phenol sulfonic formaldehyde condensation compound or naphthene sulfonic acid-phenol sulfonic formaldehyde condensation compound;
B2: sulfonated alkyl naphathalene;
B3: vinylbenzene-phenol polyoxyethylene polyoxypropylene compound, chemical formula is:
F-O-(CHCH
3CH
2O)
m-(CH
2CH
2O)
n-XM
In the formula: F=vinylbenzene-phenolic groups, m=3-12, n=10-40, X=CH
2COO
-, SO
3 -, M=K
+, Na
+, NH
4 +
B4: water-soluble poly styrene-propene acid copolymer is dissolved polystyrene-acrylic copolymer by alkali neutralization of ethylene base acid unit.
4. a kind of aqueous pigment dispersion color paste composition according to claim 1 is characterized in that: described component C is the terminal fatty alcohol-polyoxyethylene ether that contains acid groups, and chemical formula is R (CH
2CH
2O)
n-XM, wherein R=C
4-C
20, n=3-10, X=CH
2COO
-, SO
3 -, M=K
+, Na
+, NH
4 +, or be succsinic acid fat acid esters sodium sulfonate, wherein fatty acid ester is selected C
4-C
20Lipid acid.
5. a kind of aqueous pigment dispersion color paste composition according to claim 1, it is characterized in that: described component D is ethylene glycol, propylene glycol, glycerine, glycol ether, triglycol, polyoxyethylene glycol, butyl glycol ether, Diethylene Glycol butyl ether, propylene glycol monomethyl ether, propylene glycol butyl ether, one or more mixtures in ethanol, the Virahol.
6. a kind of aqueous pigment dispersion color paste composition according to claim 1 is characterized in that: described component E is sanitas, mould inhibitor, one or more mixtures of defoamer.
7. a kind of aqueous pigment dispersion color paste composition according to claim 3, it is characterized in that: the described neutral alkali that is used for is organic bases or mineral alkali, organic bases is Monoethanolamine MEA BASF, diethanolamine, trolamine, N, N-dimethylethanolamine, diisopropanolamine (DIPA) or amino methyl propyl alcohol, mineral alkali are sodium hydroxide, potassium hydroxide, lithium hydroxide or aqua ammonia.
8. a kind of aqueous pigment dispersion color paste composition according to claim 3 is characterized in that: described polystyrene-acrylic copolymer is the resin aqueous solution of 25-40% weight.
9. a kind of aqueous pigment dispersion color paste composition according to claim 8, it is characterized in that: used resin essentially consist is by 40-60% weight aromatic unsaturated compound and multipolymer that 40-60% vinylformic acid/methacrylic acid/(methyl) acrylate is formed, the number-average molecular weight M=1000-10000g/mol of described multipolymer.
Preferably, described aromatic unsaturated compound is one or more mixtures in vinylbenzene, a-vinyl toluene, Vinyl toluene or the benzyl acrylate; Vinylformic acid/methacrylic acid/(methyl) acrylate monomer is preferably following acid, or following acid and ester composition, described acid is vinylformic acid, methacrylic acid, MALEIC ANHYDRIDE, methylene-succinic acid, one or more of hydroxyethyl methacrylate propanesulfonic acid sodium, described ester are maleic acid mono-esterification thing, maleic acid ester, FUMARIC ACID TECH GRADE (diester), glycidyl acrylate, methyl acrylate, ethyl propenoate, butyl acrylate, Octyl acrylate, 2-EHA, vinylformic acid 2-hydroxyl ethyl ester, Propylene glycol monoacrylate, methyl methacrylate, Jia Jibingxisuanyizhi, butyl methacrylate, Octyl methacrylate, glycidyl acrylate, methacrylic acid 2-hydroxyl ethyl ester, one or more of (methyl) Propylene glycol monoacrylate.
10. the preparation method of the described aqueous pigment dispersion color paste composition of claim 1 is characterized in that:
Said components B, C, D, E, F are mixed according to described parts by weight; add described parts by weight component A and mix making beating, homogenizing; under the cooling water temperature condition; use sand mill or ball mill to grind; be ground to 0.5-2 μ m; separate grinding medium and get water-based paint dispersion slurry, wherein grinding medium uses quartz silica bead or the Zirconium oxide bead of size d=0.4-8mm.