CN101908796A - 一种高频电机的非晶合金定子铁芯的制备方法 - Google Patents

一种高频电机的非晶合金定子铁芯的制备方法 Download PDF

Info

Publication number
CN101908796A
CN101908796A CN 201010211940 CN201010211940A CN101908796A CN 101908796 A CN101908796 A CN 101908796A CN 201010211940 CN201010211940 CN 201010211940 CN 201010211940 A CN201010211940 A CN 201010211940A CN 101908796 A CN101908796 A CN 101908796A
Authority
CN
China
Prior art keywords
adhesive
amorphous alloy
iron core
stator iron
amorphous
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201010211940
Other languages
English (en)
Other versions
CN101908796B (zh
Inventor
李振
李季霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201010211940 priority Critical patent/CN101908796B/zh
Publication of CN101908796A publication Critical patent/CN101908796A/zh
Application granted granted Critical
Publication of CN101908796B publication Critical patent/CN101908796B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及电机制造技术领域，具体是指一种高频电机的非晶合金定子铁芯的制备方法，所述定子铁芯以常规非晶合金粉末为原料，将非晶合金粉末与粘合剂充分均匀混合；再将混合粘合剂后的非晶合金粉末置于模具中加压成型。非晶合金粉末与粘合剂按100∶5至100∶20混合；粘合剂为环氧树脂等绝缘材料；非晶合金粉末与粘合剂混合过程中的温度为120℃至180℃；加压成型过程中的压力为70MPa至90MPa；加压成型过程中的保压时间为5分钟至10分钟。本发明的优点在于，制造简单、方便，产品一致性和稳定性好，有利于批量生产；高频工作时大大减少了定子铁芯产生的涡流损耗、空载损耗和磁滞损耗，达到了节能高效的目的。

Description

一种高频电机的非晶合金定子铁芯的制备方法
技术内容：
本发明涉及电机制造技术领域，具体是指一种高频电机的非晶合金定子铁芯的制备方法。
背景技术：
高频电机是通过高于50HZ的频率来实现的，而一般的定子采用的是高导磁材料来保证单位时间内的总磁通量，但是这种高导磁材料(如硅钢片)制成的定子会产生较大的涡流损耗和磁滞损耗，造成能源的浪费，从而难以符合人们的使用需求。随着科技的进步，人们发现非晶合金具有高饱和磁感应强度和低损耗的特点，于是非晶合金在电子、航空、航天等领域得到了越来越广泛地应用，因此也可以实现其在高频电机中的应用。
专利CN200810007282.2公布了一种高速电机用非晶合金定子铁芯的制备方法，是将非晶合金带材进行切割，形成具有预定长度的多个非晶合金片，叠片后形成层叠棒，对叠棒进行退火、粘结固化后切割所述层叠棒，形成所需形状和尺寸的定子铁芯。
由于非晶合金材料的硬度很高，用常规工具难以剪切，且非晶合金对机械应力非常敏感，因此设计时出于节约制造成本，方便批量生产和降低废品率考虑，应减少剪切量。其次，非晶合金单片厚度较薄，厚度仅为0.03mm材料表面不是很平坦，所以其叠片系数也只能达到82％至86％，因此叠片之间的气隙增加了磁路的磁阻和运行电机所需的电流。
发明内容：
本发明为了克服现有技术中不足，而提供一种低损耗的高频电机的非晶合金定子铁芯的制备方法。
本发明采用以下技术实现，所述定子铁芯以常规非晶合金粉末为原料，将非晶合金粉末与粘合剂充分均匀混合；再将混合粘合剂后的非晶合金粉末置于模具中加压成型，形成所需形状和尺寸的定子铁芯。所述非晶合金粉末与粘合剂按100∶5至100∶20混合；所述粘合剂为环氧树脂、清漆、丙烯酸树脂、氰基丙烯酸酯等绝缘材料；所述非晶合金粉末与粘合剂混合过程中的温度为120℃至180℃；所述加压成型过程中的压力为70MPA至90MPA；所述加压成型过程中的保压时间为5分钟至10分钟。
本发明的优点在于，制造简单、方便，产品一致性和稳定性好，有利于批量生产，高频工作时大大减少了定子铁芯产生的涡流损耗、空载损耗和磁滞损耗，达到了节能高效的目的。
附图说明：
图1为本发明结构图
具体实施方式：
本发明以常规非晶合金粉末为原料，将非晶合金粉末与粘合剂充分均匀混合；再将混合粘合剂后的非晶合金粉末置于模具中加压成型，形成所需形状和尺寸的定子铁芯。非晶合金粉末与粘合剂按100∶5至100∶20混合；粘合剂为环氧树脂、清漆、丙烯酸树脂、氰基丙烯酸酯等绝缘材料；非晶合金粉末与粘合剂混合过程中的温度为120℃至180℃；加压成型过程中的压力为70MPA至90MPA；加压成型过程中的保压时间为5分钟至10分钟。
如图1所示，本发明的实施例如下，由于目前非晶合金粉末的生产已经有了一套成熟的工艺，因此可直接从市场上获得所需形状和尺寸的非晶合金粉末原材料。将非晶合金粉末与粘合剂环氧树脂在温度180℃的环境下，按100∶5的比例充分均匀地混合；再将混合后的非晶合金粉末置于已成型的模具之中，施加压力70MPA，并保持5分钟左右，一定形状和尺寸的定子铁芯即制作完成。

Claims (6)

1.一种高频电机的非晶合金定子铁芯的制备方法，所述定子铁芯以常规非晶合金粉末为原料，其特征在于：
将非晶合金粉末与粘合剂充分均匀混合；
将混合粘合剂后的非晶合金粉末置于模具中加压成型，形成所需形状和尺寸的定子铁芯。
2.根据权利要求1所述的一种高频电机的非晶合金定子铁芯的制备方法，其特征在于：所述非晶合金粉末与粘合剂按100∶5至100∶20混合。
3.根据权利要求1所述的一种高频电机的非晶合金定子铁芯的制备方法，其特征在于：所述粘合剂为环氧树脂、清漆、丙烯酸树脂、氰基丙烯酸酯等绝缘材料。
4.根据权利要求1所述的一种高频电机的非晶合金定子铁芯的制备方法，其特征在于：所述非晶合金粉末与粘合剂混合过程中的温度为120℃至180℃。
5.根据权利要求1所述的一种高频电机的非晶合金定子铁芯的制备方法，其特征在于：所述加压成型过程中的压力为70MPA至90MPA。
6.根据权利要求1所述的一种高频电机的非晶合金定子铁芯的制备方法，其特征在于：所述加压成型过程中的保压时间为5分钟至10分钟。
CN 201010211940 2010-06-22 2010-06-22 一种高频电机的非晶合金定子铁芯的制备方法 Expired - Fee Related CN101908796B (zh)