CN101908649A - 一种铅酸蓄电池用胶体电解质配方 - Google Patents
一种铅酸蓄电池用胶体电解质配方 Download PDFInfo
- Publication number
- CN101908649A CN101908649A CN2010102229619A CN201010222961A CN101908649A CN 101908649 A CN101908649 A CN 101908649A CN 2010102229619 A CN2010102229619 A CN 2010102229619A CN 201010222961 A CN201010222961 A CN 201010222961A CN 101908649 A CN101908649 A CN 101908649A
- Authority
- CN
- China
- Prior art keywords
- lead
- percent
- battery
- storage battery
- colloidal electrolyte
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种铅酸蓄电池用胶体电解质配方,包括以下组份,各组份重量百分比为:气相二氧化硅0.8%~10%、聚乙二醇0.4%~0.8%、三氧化二铋0.03%~0.6%、三氧化二锑0.05%~0.3%、硫酸亚锡0.05%~0.5%、磷酸0.3%~1%、无水硫酸钠0.5%~2%、硫酸25%~40%、水50%~60%。本发明的优点是:使用本发明的胶体电解质后,对铅钙合金蓄电池,有效改善了普通胶体电解质不能适应铅钙合金电池的缺点,改善铅钙合金电池的早期容量衰减效应,进一步提高了铅钙电池的深放电循环寿命、低温大电流充放电性能以及过放电后的可再充电性能,提高了电池的使用安全性,降低了电池的综合使用成本。
Description
技术领域
本发明涉及一种铅酸蓄电池用胶体电解质配方。
背景技术
电动车作为未来人类交通工具的重要组成部分已被形成共识,目前电动车辆普遍采用阀控式密封铅酸蓄电池为主要的动力来源,随着电动车产业的快速发展对蓄电池的循环寿命、可在充电能力、免维护性能、使用安全性提出了更高的要求,作为动力型电池为了提供对深循环寿命的可靠性,多以铅锑合金电池为主,但以铅锑合金为材料的蓄电池存在板栅腐蚀速度快,因锑的积累失水速度快,导致热失控变形槽体破裂,维护不当会引起提前寿命终止。为了克服这些缺点,电动车电池在逐步向铅钙合金材料过渡,虽然解决了电池在使用过程失水过快的问题,提高了免维护性能,但铅钙合金由于钙的存在,也带来了电池深循环容量衰减快,寿命短,过放电后的充电可恢复性能差,活性物质容易软化脱落的缺点。而且这些缺点在串联使用的蓄电池中表现的更为突出。
发明内容
本发明专利的目的就是解决现有铅钙合金深放电性能差,循环寿命短,可再充电恢复性能差,可提高蓄电池组的一致性及深放电状态下循环寿命特性的一种新型胶体铅酸蓄电池用胶体电解质的配方组分。
为了解决上述技术问题,本发明是通过以下技术方案实现的:一种铅酸蓄电池用胶体电解质配方,包括以下组份,各组份重量百分比为:气相二氧化硅0.8%~10%、聚乙二醇0.4%~0.8%、三氧化二铋0.03%~0.6%、三氧化二锑0.05%~0.3%、硫酸亚锡0.05%~0.5%、磷酸0.3%~1%、无水硫酸钠0.5%~2%、硫酸25%~40%、水50%~60%。
优选的,各组份重量百分比为:气相二氧化硅4.5%、聚乙二醇0.6%、三氧化二铋0.3%、三氧化二锑0.2%、硫酸亚锡0.3%、磷酸0.8%、无水硫酸钠1.3%、硫酸37%、水55%。
优选的,各组份重量百分比为:气相二氧化硅0.8%、聚乙二醇0.8%、三氧化二铋0.05%、三氧化二锑0.3%、硫酸亚锡0.05%、磷酸1%、无水硫酸钠0.5%、硫酸40%、水56.5%。
优选的,各组份重量百分比为:气相二氧化硅10%、聚乙二醇0.4%、三氧化二铋0.6%、三氧化二锑0.05%、硫酸亚锡0.5%、磷酸0.3%、无水硫酸钠2%、硫酸26.5%、水60%。
优选的,各组份重量百分比为:气相二氧化硅7%、聚乙二醇0.7%、三氧化二铋0.1%、三氧化二锑0.1%、硫酸亚锡0.4%、磷酸0.6%、无水硫酸钠1.1%、硫酸40%、水50%。
优选的,所述磷酸的浓度为75%,所述硫酸的浓度为90%。
与现有技术相比,本发明的优点是:气相二氧化硅为比表面积极大的颗粒状物质,其羟基与水分子结合后为一种触变性极好的凝胶剂;聚乙二醇为凝胶促进剂和稳定剂,可使形成的胶体胶链结构在一定强度下保持稳定,并有很强的锁水作用;三氧化二铋加在胶体电解质中,吸附到电极板的活性物质中,并掺杂在活性物质与板栅界面上,起到消除电极板钝化的作用;三氧化二锑随着电池的充放电,吸附到电极板的活性物质中,由于锑的析氢过电位低于铅钙合金,起到降低铅钙合金的过电位,提高铅钙合金电极板充电接受能力的作用;硫酸亚锡吸附沉积电极板表面及活性物质中,改善了活性物质粒子间的导电性能,提高蓄电池过放电后的可再充电恢复能力;磷酸可使活性物质放电后的硫酸铅晶粒细化,增加充电后的α二氧化铅含量,降低了活性物质软化速度,提高电池在深放电状态下的循环寿命;无水硫酸钠溶解于电解质,增加电解质中不参与反应的硫酸根离子含量,在蓄电池过放电,当硫酸耗尽时,改善因电解液中酸浓度的降低而引起的硫酸铅大量溶出而导致的蓄电池微短路,使用本发明的胶体电解质后,对铅钙合金蓄电池,有效改善了普通胶体电解质不能适应铅钙合金电池的缺点,改善铅钙合金电池的早期容量衰减效应,进一步提高了铅钙电池的深放电循环寿命、低温大电流充放电性能以及过放电后的可再充电性能,提高了电池的使用安全性,降低了电池的综合使用成本。
具体实施方式
实施例一:一种铅酸蓄电池用胶体电解质配方,各组份重量百分比为:气相二氧化硅4.5%、聚乙二醇0.6%、三氧化二铋0.3%、三氧化二锑0.2%、硫酸亚锡0.3%、磷酸0.8%、无水硫酸钠1.3%、硫酸37%、水55%。
实施例二:一种铅酸蓄电池用胶体电解质配方,各组份重量百分比为:气相二氧化硅0.8%、聚乙二醇0.8%、三氧化二铋0.05%、三氧化二锑0.3%、硫酸亚锡0.05%、磷酸1%、无水硫酸钠0.5%、硫酸40%、水56.5%。
实施例三:一种铅酸蓄电池用胶体电解质配方,各组份重量百分比为:气相二氧化硅10%、聚乙二醇0.4%、三氧化二铋0.6%、三氧化二锑0.05%、硫酸亚锡0.5%、磷酸0.3%、无水硫酸钠2%、硫酸26.5%、水60%。
实施例四:一种铅酸蓄电池用胶体电解质配方,各组份重量百分比为:气相二氧化硅7%、聚乙二醇0.7%、三氧化二铋0.1%、三氧化二锑0.1%、硫酸亚锡0.4%、磷酸0.6%、无水硫酸钠1.1%、硫酸40%、水50%。
以上四个实施例中,所述磷酸的浓度为75%,所述硫酸的浓度为90%。将混合好的胶体高速剪切后,通过专用抽真空设备灌入电池中即可。
以上所述仅为本发明的具体实施例,但本发明的技术特征并不局限于此,任何本领域的技术人员在本发明的领域内,所作的变化或修饰皆涵盖在本发明的专利范围之中。
Claims (6)
1.一种铅酸蓄电池用胶体电解质配方,其特征在于:包括以下组份,各组份重量百分比为:气相二氧化硅0.8%~10%、聚乙二醇0.4%~0.8%、三氧化二铋0.03%~0.6%、三氧化二锑0.05%~0.3%、硫酸亚锡0.05%~0.5%、磷酸0.3%~1%、无水硫酸钠0.5%~2%、硫酸25%~40%、水50%~60%。
2.如权利要求1所述的一种铅酸蓄电池用胶体电解质配方,其特征在于:各组份重量百分比为:气相二氧化硅4.5%、聚乙二醇0.6%、三氧化二铋0.3%、三氧化二锑0.2%、硫酸亚锡0.3%、磷酸0.8%、无水硫酸钠1.3%、硫酸37%、水55%。
3.如权利要求1所述的一种铅酸蓄电池用胶体电解质配方,其特征在于:各组份重量百分比为:气相二氧化硅0.8%、聚乙二醇0.8%、三氧化二铋0.05%、三氧化二锑0.3%、硫酸亚锡0.05%、磷酸1%、无水硫酸钠0.5%、硫酸40%、水56.5%。
4.如权利要求1所述的一种铅酸蓄电池用胶体电解质配方,其特征在于:各组份重量百分比为:气相二氧化硅10%、聚乙二醇0.4%、三氧化二铋0.6%、三氧化二锑0.05%、硫酸亚锡0.5%、磷酸0.3%、无水硫酸钠2%、硫酸26.5%、水60%。
5.如权利要求1所述的一种铅酸蓄电池用胶体电解质配方,其特征在于:各组份重量百分比为:气相二氧化硅7%、聚乙二醇0.7%、三氧化二铋0.1%、三氧化二锑0.1%、硫酸亚锡0.4%、磷酸0.6%、无水硫酸钠1.1%、硫酸40%、水50%。
6.如权利要求1至5中任一项所述的一种铅酸蓄电池用胶体电解质配方,其特征在于:所述磷酸的浓度为75%,所述硫酸的浓度为90%。