CN101905856B - Method for preparing plane hollow microneedle for transdermal administration - Google Patents
Method for preparing plane hollow microneedle for transdermal administration Download PDFInfo
- Publication number
- CN101905856B CN101905856B CN 201010204623 CN201010204623A CN101905856B CN 101905856 B CN101905856 B CN 101905856B CN 201010204623 CN201010204623 CN 201010204623 CN 201010204623 A CN201010204623 A CN 201010204623A CN 101905856 B CN101905856 B CN 101905856B
- Authority
- CN
- China
- Prior art keywords
- metal substrate
- micropin
- preparing
- cut mark
- cutting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a method for preparing a plane hollow microneedle for transdermal administration, which comprises the following steps of: defining a microneedle flow channel pattern on one surface of a first metal substrate to form a trench, and defining a microneedle pattern on the other surface to form a cutting sign, wherein the central axis of the flow channel pattern is aligned with that of the microneedle pattern; bonding a second metal substrate with a trench surface of the first metal substrate; thinning a non-bonding surface of the second metal substrate, and allowing the cutting sign on the first metal substrate to align with and transfer to the non-bonding surface of the second metal substrate; and thinning a non-bonding surface of the first metal substrate, and cutting by aligning with the cutting sign on the second metal substrate to form the plane hollow microneedle. Based on the micromachining technology and by combining the conventional technology of machining and cutting at the same time, the method reduces the process difficulty, increases the using reliability of the microneedle, and is favorable for quantity production.
Description
Technical field
The present invention relates to micromachining technology, particularly be used for the method for preparing of the plane hollow microneedle of transdermal administration.
Background technology
Main administering mode is oral and injection at present.Oral drugs are because the absorption in the intestines and stomach and the first pass effect of liver have influenced the practical effect of medicine to site of action greatly.Injection not only can bring tangible pain to the patient, also needs the professional to operate simultaneously, even the local damage even the infection of skin can occur, and not being suitable for long-term reaching needs the accurately sustained-release administration of control.
Percutaneous dosing is a reasonable solution.Skin is divided into three layers from outside to inside: horny layer, epidermal area and skin corium.About 10~20 microns of cutin bed thickness is that one deck is extremely organized, and does not have blood vessel and nerve; Epidermal area is positioned at outer subcutaneous about 50~100 microns places, contains a small amount of living cells and nerve, does not contain blood vessel; More also have a large amount of living cells, nerve and blood vessel in the corium of depths.It is thus clear that horny layer is the maximum barrier that the medicine percutaneous absorbs.People have adopted the method for multiple physics, chemistry to absorb with the percutaneous that promotes medicine for this reason.Such as physical methods such as iontophoresis, ultrasonic importing, electroporation and hot piercings, the percutaneous assimilation effect is remarkable, but majority need rely on the automatically controlled property equipment that energy source is arranged, and is bigger to the damage of skin, and medication person can't independently voluntarily use.Chemical penetrating agent is then not obvious to the percutaneous assimilation effect of macromolecular drug, and generally has than strong and stimulating.
Comparatively speaking, microneedle cutaneous is a kind of administering mode between subcutaneous injection and transdermal patch.Micropin also belongs to the short technology of oozing of physics; It is that the acicular texture of a kind of size of difformity that Micrometer-Nanometer Processing Technology processes and material in micron dimension arranged; Handle through skin being carried out painless pore; Produce the permeability that medicine is improved in small duct at keratodermatitis, thereby improve the especially percutaneous absorbtivity of macromolecular drug of medicine greatly; Because the needle point size is minimum, skin is not almost damaged simultaneously, and easy to use, do not need professional training, be fit to individual independent operation.
Distinguish according to manufacturing materials, micropin mainly contains three kinds on silicon, polymer and metal.Silicon materials have sophisticated micro fabrication technology, be easy to produce in batches, but its bio-compatibility is relatively poor, and easy fracture are stranded in the skin, and this is its development key factor of restriction.Polymer micro needle has good bio-compatibility and degradable, but its intensity is relatively poor, on new material excavation and processing technique, all has much room for improvement.Metal micro-needle is cheap, technology is simple, is fit to mass production, and needle point is sharp-pointed, hardness is bigger, is easy to pierce and easy fracture not.Such as metals such as the titanium with bio-compatibility, nickel, rustless steels, be the good material of making micropin.
Distinguish according to processing technology, micropin mainly contains from face and plane two kinds, and the former needle shaft is perpendicular to substrate surface, and the latter's axle then is parallel to substrate surface.From the face micropin, especially for large ratio of height to width from the face micropin, complex process is wayward, difficulty is more with high costs.Then technology is simple relatively for the plane micropin, and the convenient control of micropin pattern combines integrated fluid channel, pick off etc. to form the microinjection control system easily with other technologies.
Distinguish according to internal structure, micropin mainly contains solid and hollow two kinds, and the former can produce skin physics through hole, and the mode of medicine with infiltration is transferred in the body; The latter then can be stored in medicine in the cavity, treats to be released in the body after needle point thrusts skin.It is thus clear that empty micropin more is similar to conventional syringe, transdermal administration is more efficient.
People such as Chen in 1997 utilize the anisotropy etch stop technology of silicon to process the silicon-base plane of fluid channel empty micropin is arranged (CHEN J; Et al.A multichannel neural probe for selective chemical Delivery at the Cellular Level [J] .IEEE Transactions on Biomedical Engineering; 1997,44 (8): 760-769.).Lin in 1999 etc. utilize similar techniques to process silicon nitride micropin (LIN L, PISANO A P.Silicon-Processed Microneedles [J] .IEEE Journal of Microelectmmechanical Systems, 1999,8 (1): 78-84.).People such as Oka in 2002 utilize the corrosive liquid undercutting to make silicon form zigzag; In conjunction with silicon-silicon bond close, plasma etching and copolymerization pyrophosphate ion bundle bombardment lithographic technique processed plane hollow silicon micropin (OKAK; Et al.Fabrication of a microneedle for a trace blood test [J] .Sensors and Actuators A; 2002,97-98:478-485).People such as Paik in 2004 utilize dry etching and raceway groove to recharge technology and have processed monocrystal silicon plane hollow microneedle array (PAIK S J; Et al.A novel microneedle array integrated with a PDMS biochip for microfluid systems [A] .The 12th International Conference on Solid State Sensors, Actuators and Microsystems [C] .Boston:2003.146-1449; PAIK S J; Et al.In-plane single-crystal-silicon microneedles for minimally invasive microfluid systerns [J] .Sensors and Actuators A:Physical; 2004,114 (2-3): 276-284).Because the use of silica-base material, the silicon process technology of majority of mature all can use, but the silicon materials built-in problem can't be avoided simultaneously.Except the crisp easy fracture of silicon micropin matter, silicon face also can adsorbed proteins, makes leukocyte stick to the micropin surface, possibly produce the inflamed stress of Denging, so the suitable human body therapy that directly is used for of silicon micropin.Even in subsequent technique, add gold thin film etc., owing to a little less than surface film technology combines reliability, be difficult to from changing this problem in essence.
People such as last century Mo Frazier adopt the surface micro processing technique to combine cryogenic conditions to process the hollow palladium micropin in isoplanar (Paputsky; Et a l.A low temperature IC compatable process for fabricating surfacemicromachined metallic microchannels.IEEE J Microelectromech Sys; 1998,7 (2): 267-273; J.Brazzle, et al.Fluid-coupled metallic micromachined needle arrays.20thinter.ConeIEEE.Med&Bio Society, Hong Kong, 1998.1837-1840; J.Brazzle, et al.Hollow metallic micromachined needle arrays.J.Micro Biomed Devices, 2000,2:197-205.).Its colleague Chandrasekaran etc. has also processed similar micropin (S.Chandrasekaran, et al.Surface micromachined metallic microneedles, J Microelectromech Sys, 2003, (12): 281-288.).Above-mentioned micropin preparation technology designs machining at low temperature, and its technology difficulty expends high more greatly, and architectural characteristic and quality control also are difficult for guaranteeing.2006; People such as Parker utilize deep erosion and golden gold bonding to produce titanio micropin (E.R.Parker; Et al.Bulk Titanium Microneedles with Embedded Microfluidic Networks for Transdermal Drug Delivery.IEEEMEMS 2006; Istanbul, Turkey, 22-26January 2006:498-501.).This is all having bigger improvement and raising aspect material and the processing technique.But since golden gold bonding bond strength a little less than, wait test as the micropin security reliability of inserting device.Simultaneously, too much use the deep etching technique of titanium, very high to technical process requirement itself, difficulty is bigger, and the also corresponding raising of cost is many.Be exactly its little machining process that adopts in addition, or not be not suitable for volume production with traditional silicon disk processing technique coupling.2009; People such as Xiao Yan Xiao of Shanghai Communications University utilize electroplating technology to prepare the thick nickel plane micropin of 50 μ m; Afterwards again deposit 2 microns compatible (the YAN Xiao-xiao of polymer proliferation; Et al.MEMS In-Plane Metallic Microneedle for Drug Delivery.Nanotechnology and Precision Engineering, Sep.2009, Vol.7No.5:419-422).Its micropin of electroplating preparation and substrate caking power a little less than, the polymer of while deposit also is prone to come off, global reliability and ease for use all have much room for improvement.
Summary of the invention
The purpose of this invention is to provide a kind of method for preparing that is used for the plane hollow microneedle of transdermal administration; This method combines traditional machining and cutting technique simultaneously based on micromachining technology, strengthens the dependability of micropin; Reduce technology difficulty, and realize producing in batches.
Technical scheme of the present invention is following:
A kind of method for preparing of plane hollow microneedle may further comprise the steps:
1) at the one side definition micropin runner figure of first metal substrate, forms raceway groove, aim at raceway groove location definition micropin figure at another side then, form cut mark; Perhaps, at the one side definition micropin figure of first metal substrate, form cut mark earlier, aim at micropin graphical definition micropin runner figure at another side then, form raceway groove;
2) get one second metal substrate, the raceway groove face of itself and first metal substrate is bonded together;
3) the nonbonding face of attenuate second metal substrate, and the cut mark on first metal substrate aimed at transfer on the nonbonding face of second metal substrate;
4) the nonbonding face of attenuate first metal substrate is aimed at the cut mark cutting on second metal substrate then, forms plane hollow microneedle.
Above-mentioned steps 1) formation of raceway groove and cut mark is adjustable in proper order in, as long as micropin figure and runner figure are aimed at each other, and the central axial alignment of ordinary circumstance lower flow channel figure and micropin figure.The mode of definition figure can be photoetching, laser marking, silk screen printing etc.; The mode that forms raceway groove and cut mark can be that substrate is carried out wet etching or dry etching etc., and wherein the mode of wet etching comprises that again being soaked in the corrosive liquid corrosion and spray corrodes.
Preferably use following method to form raceway groove for step 1): at a resist coating of first metal substrate, lithographic definition goes out micropin inner flow passage figure, is that mask etching first metal substrate forms raceway groove then with the photoresist.The photoresist that uses in etching process as mask, the negative photoresist of anti-etchings such as preferred SU8; Dry etching is generally adopted in the formation of raceway groove, for example adopts reactive ion etching (RIE) technology, and etching depth depends on the size design of raceway groove and micropin.
For the preferred following method of the formation of cut mark in the step 1): at the another side resist coating of first metal substrate, lithographic definition goes out that the expose portion of wet etching first metal substrate forms cut mark behind the micropin figure, removes photoresist again.The photoresist that uses can be the eurymeric photoresist; Wet etching forms cut mark, and the corrosive liquid that is adopted is decided according to the material of substrate.Etching time is very short, and general 1-2min is so even if form raceway groove earlier, corrosion process is also little to the influence of raceway groove.Be the protection raceway groove, also can form the back it is protected (as coating protection glue), form cut mark again at raceway groove.
Above-mentioned steps 2) material of second metal substrate is identical with first metal substrate usually, and selectable metal material includes but not limited to titanium, rustless steel, nickel or their alloy, is preferably titanium.The all metal substrates of the present invention are all selected smooth thin slice usually, and thickness is generally 50~2000 μ m.Most preferred, said first metal substrate and second metal substrate all use four cun titanio disks.First metal substrate is twin polishing; Second metal substrate can be the single or double polishing; The bonding face of second metal substrate and first metal substrate is a burnishing surface, and the bonding mode can adopt surperficial Direct Bonding (for example diffusion welding (DW) bonding), also can adopt intermediate layer bonding etc.The diffusion welding (DW) bonding is normally 1 * 10
-4Under the vacuum environment of Pa, temperature is about 1000~1200 ℃, and pressurization kept 1~2 hour, wherein, and pressure and the time relation of being inversely proportional to.
Above-mentioned steps 3) method of transfer cut mark figure can be to aim at photoetching, laser marking, silk screen printing etc., and wet etching or dry etching second metal substrate obtain cut mark at its nonbonding face then.Preferred resist coating at attenuate and after polishing the nonbonding face of second metal substrate; And the cut mark of aiming on first metal substrate carries out photoetching; Through wet etching second metal substrate cut mark is transferred on second metal substrate from first metal substrate then, removed photoresist again.Employed photoresist generally is the eurymeric photoresist, and wet etching shifts cut mark, and the corrosive liquid that is adopted is looked the material of metal substrate and decided.
Above-mentioned steps 3) and can use methods such as wet etching (comprise spray corrosion) or chemically mechanical polishing that metal substrate is carried out attenuate in the step 4).The thickness of the plane micropin that forms at last depends on bonding pad thickness and thickness thinning.
Above-mentioned steps 4) cutting mode can be cut, line cutting, ion beam cutting, the cutting of water cutter etc. in; Can adopt method cleaning micropin surface and cut edge residues such as pickling processes after the cutting, general use is carried out like the mixed diluting solution of Fluohydric acid., nitric acid and vitriolic mixed liquor or hydrogen peroxide and water.
The plane hollow microneedle structure of the present invention's preparation is made up of the needle body array of front end and the supporting mass and the reservoir one of rear end usually, and said needle body is parallel with the substrate direction, and pattern is determined by layout design.
Plane hollow microneedle of the present invention can be widely used in the transdermal administration device, and micropin produces the physics hole through the pierce horny layer and strengthens operational efficiency, to macromolecular drug, is the painless transdermal administration mode of a kind of safety particularly.Owing to have fluid channel, micropin of the present invention can extract with partly integrated painless microinjection and the body fluid that is applied to accurately control of syringe; Through the adjustable reservoir of capacity, can combine to reach the purpose of medicament slow release simultaneously, thereby realize more efficient, accurate, the secular conveying of medicine with patch or heeling-in.
The present invention combines multiple technologies such as micromachined, traditional mechanical processing and cutting, has reduced technology difficulty with respect to prior art, has strengthened the dependability of micropin, and can realize producing in batches.Concrete advantage is for example: 1. introduce Pervasion Weld Technology and make two substrate fusion bondings, strengthened joint dynamics and sealing between two tracts of runners, improved the reliability that micropin uses; 2. adopt cutting formation pin types such as laser, reduced process complexity preferably, also saved costs such as preparation reticle simultaneously with respect to dry etching; 3. preferably adopt hardness, toughness and the bio-compatibility of titanium base material, and adopt body titanium processing technique, avoided micropin and the caducous shortcoming of substrate adhesiveness difference with the assurance micropin; 4. introduce four cun titanio disks, making traditional mechanical processing combine with the MEMS process technology becomes possibility, has expanded preparation means greatly.
Description of drawings
Fig. 1 a~1k is the process chart that the embodiment of the invention prepares the titanio plane hollow microneedle.
Fig. 2 is the runner figure and the micropin pattern sketch map of plane hollow microneedle of the present invention.
The micropin pattern photo that Fig. 3 obtains for cut, wherein B is the enlarged drawing of a needle body shown in the A.
The specific embodiment
Bottom combines accompanying drawing, further the present invention is elaborated through embodiment, but the scope that does not limit the present invention in any way.
Through machining, utilize the mode of line cutting to prepare four cun titanio disks to chemical pure titanium material.Carry out cryogenic vacuum annealing and chemically mechanical polishing, obtain the titanio disk of thick four cun two-sided or single-sided polishings of 200 μ m.Utilize and should prepare plane hollow microneedle according to following step by middle titanio disk:
1, forms the micropin runner
The titanio disk of getting a slice twin polishing is as the first titanio sheet 1, and the thick SU83010 photoresist 2 of spin coating 15 μ m left standstill 24 hours on one of which side burnishing surface.(stopped 2 minutes through baking before the hot plate from 45 ℃ of per 10 degree; Stopped 10 minutes to 95 ℃; Naturally be cooled to room temperature then), be printed on four cun chromium plate exposure 28s of micropin runner figure, carry out the hot plate after bake then and (stopped 1 minute from 45 ℃ of per 10 degree; To 95 ℃ of stops 5 minutes, be cooled to room temperature then naturally).Use the special-purpose developer solution of SU8 that it is carried out developing in 8 minutes to the reticle figure at last and occur fully, shown in Fig. 1 a.Utilize the ICP/RIE dry etching technology, adopt chlorine-based gas, the etching 30 μ m degree of depth.Etching parameters is: coil power 300-500W, and dull and stereotyped power 50W-200W, gas flow 30-70sccm forms raceway groove 3, shown in Fig. 1 b.
2, form cut mark
At the even eurymeric photoresist 4 that is coated with of the opposite side burnishing surface of the first titanio sheet; Thickness is 1 μ m, be printed on the runner figure one by one four cun reticle of corresponding pattern cut aim at the exposure 4s, carried out 120 ℃ of hot plate post bakes then 1 minute; Developing to figure occurs fully, shown in Fig. 1 c.Immerse HF: HNO
3: H
2O=1: in the solution of 1: 30 (volume ratio) 1~2 minute, erode away cut mark 5, shown in Fig. 1 d.Immerse afterwards and remove photoresist in the acetone soln, see Fig. 1 e.
3, diffusion welding (DW) bonding
Get another sheet list and throw (or two throwing) titanio disk, shown in Fig. 1 f, make the runner face of its burnishing surface and the first titanio sheet 1 carry out the diffusion welding (DW) bonding as the second titanio sheet 6.Diffusion welding (DW) is 1 * 10
-4Under the vacuum environment of Pa, temperature is about 1000~1200 ℃, and pressurization kept 1~2 hour.Wherein, pressure and the time relation of being inversely proportional to.Bonding pressure can reach more than the 18.18MPa.
4, attenuate and transfer cut mark
Nonbonding face to the second titanio sheet 6 carries out attenuate CMP polishing, makes it to reduce 150 μ m thickness, shown in Fig. 1 g.The even above that afterwards eurymeric photoresist 7 that is coated with uses the existing cut mark in the pattern cut domain and the back side to aim at exposure imaging (seeing Fig. 1 h).Then photoetching face is carried out wet etching, reach the purpose of metastatic marker.Concrete processing step erodes away cut mark 8 on the nonbonding face of the second titanio sheet 6, shown in Fig. 1 i with above-mentioned step 2.The first titanio sheet, 1 nonbonding face is carried out CMP polishing attenuate, make whole bonding pad thickness reach 100~150 μ m, see Fig. 1 j.
5, cutting forms needle point
Utilize ultraviolet nanosecond or psec green (light) laser to aim at bonding pad cut mark 8 and carry out the micropin cutting, form needle body and medicine storage pool, the plane hollow microneedle that obtains designing.The preferred power of laser is 3~50w.The gained micropin is immersed HF: HNO
3: H
2O=1: pickling is 1~2 minute in the solution of 1: 30 (volume ratio), removes the cut residue, improves its surfacing fineness.
In the such scheme, the runner figure and the micropin pattern of prepared plane hollow microneedle are as shown in Figure 2.The length of needle body is 200~800 microns, and width is 20~80 microns, and thickness is 100~300 microns, and the needle point angle is less than 30 °.Wherein, 30 microns of the inner flow passage degree of depth, width is 10~40 microns; Reservoir is the square of the length of side 1~5mm.
The employed metal substrate material of present embodiment is 99.99% chemical pure titanium, and micropin is parallel with titanium substrate base direction, forms single microneedle array (as shown in Figure 3), and the pin type can be adjusted domain according to needs and set up on their own.
The titanium material is having irreplaceable advantage as a kind of bio-compatibility good metal aspect the making micropin.At first, titanium has enough hardness to make the needle point can pierce, also has good toughness simultaneously, and instant bending also is unlikely to fracture and stays skin.Secondly, the titanium pin thrust the too drastic property reaction that should not cause skin, reduce phenomenons such as the issuable inflammation allergy of administered area.But as the extremely strong metal material of a kind of corrosion resistance, the processing technique difficulty of titanium is big, cost is high also is to limit the biggest obstacle that it is applied always.In order to produce the titanio micropin that reliability is higher, practicality is stronger; We have comprehensively used micromachined and multiple process technology such as traditional machining and cut; Prepared a kind of titanio plane hollow microneedle that is used for transdermal administration; The preparation of wafer level has effectively improved the possibility of volume production, and Pervasion Weld Technology has significantly strengthened the reliability of bonding, and the laser scribing method has increased the motility of microneedle configuration.
Claims (9)
1. the method for preparing of a plane hollow microneedle may further comprise the steps:
1) at the one side definition micropin runner figure of first metal substrate, forms raceway groove, aim at raceway groove location definition micropin figure at another side then, form cut mark; Perhaps, at the one side definition micropin figure of first metal substrate, form cut mark earlier, aim at micropin graphical definition micropin runner figure at another side then, form raceway groove;
2) get one second metal substrate, adopt diffusion welding (DW) to be bonded together in the raceway groove face of itself and first metal substrate;
3) the nonbonding face of attenuate second metal substrate, and the cut mark on first metal substrate aimed at transfer on the nonbonding face of second metal substrate;
4) the nonbonding face of attenuate first metal substrate is aimed at the cut mark cutting on second metal substrate then, forms plane hollow microneedle.
2. method for preparing as claimed in claim 1 is characterized in that: the mode of definition figure is photoetching, laser marking or silk screen printing in the step 1), and the mode that forms raceway groove and cut mark is that first metal substrate is carried out wet etching or dry etching.
3. method for preparing as claimed in claim 2 is characterized in that: adopt reactive ion etching technology to form raceway groove in the step 1), adopt wet etching to form cut mark.
4. method for preparing as claimed in claim 1 is characterized in that: first metal substrate is identical with the material of second metal substrate, is titanium, rustless steel, nickel or their alloy.
5. method for preparing as claimed in claim 1 is characterized in that: the thickness of first metal substrate and second metal substrate is 50~2000 μ m.
6. method for preparing as claimed in claim 1 is characterized in that: step 2) diffusion welding (DW) is bonded under the vacuum environment of 1 * 10-4Pa and carries out, and temperature is 1000~1200 ℃, and pressurization kept 1~2 hour.
7. method for preparing as claimed in claim 1 is characterized in that: use the method for wet etching or chemically mechanical polishing that metal substrate is carried out attenuate in step 3) and the step 4).
8. method for preparing as claimed in claim 1 is characterized in that: step 3) shifts the figure of cut mark through the method for aiming at photoetching, laser marking or silk screen printing, and through wet etching or be dry-etched on second metal substrate and form cut mark.
9. method for preparing as claimed in claim 1 is characterized in that: the cutting mode in the step 4) is cut, line cutting, ion beam cutting or the cutting of water cutter.