CN101885879B - 一种用于生产抗静电空调风叶的材料 - Google Patents
一种用于生产抗静电空调风叶的材料 Download PDFInfo
- Publication number
- CN101885879B CN101885879B CN2010101702709A CN201010170270A CN101885879B CN 101885879 B CN101885879 B CN 101885879B CN 2010101702709 A CN2010101702709 A CN 2010101702709A CN 201010170270 A CN201010170270 A CN 201010170270A CN 101885879 B CN101885879 B CN 101885879B
- Authority
- CN
- China
- Prior art keywords
- fan blade
- conditioning fan
- percent
- air
- antistatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种用于生产抗静电空调风叶的材料，按重量百分比包括以下组分：苯乙烯树脂58％-68％，玻璃纤维20-30％，相容剂2-8％，阴离子型抗静电剂3-10％，润滑剂0.2-0.7％，抗氧剂0.2-0.7％。本发明的目的是为了克服现有技术中的不足之处，提供一种相容性较好，力学性能较好，成本比较低的用于生产抗静电空调风叶的材料。
Description
技术领域
本发明涉及一种用于生产抗静电空调风叶的材料。
背景技术
增强增韧稳定的功能材料：ASGF材料广泛用于制造空调以及某些场合排风系统的风叶，在日常环境下的空调使用技术已经非常成熟，但是某些特殊环境下使用的空调风叶，发展仍处于起步阶段，例如在易燃易爆的环境下，要求风叶转动的时候要避免产生静电，因此具有抗静电能力的空调风叶就迎韧而生。
空调及排风系统风叶对ASGF材料的性能要求很高，以应付在高速环境以及冷热交替环境下的使用，所以抗静电ASGF同样需要符合这样的要求，目前使用导电碳黑生产的抗静电ASGF材料，导电碳黑添加量较大，材料性能下降很严重，材料根本无法达到风叶在高速环境下的使用要求，另外由于碳黑添加量比较大，导致价格也比较高昂，同时对生产环境造成较大影响，
而使用内部抗静电剂生产的ASGF材料，力学性能相对较好，但抗静电效果相对较差，另外价格向相对比较昂贵。
发明内容
本发明的目的是为了克服现有技术中的不足之处，提供一种相容性较好，力学性能较好，成本比较低的用于生产抗静电空调风叶的材料。
为了达到上述目的，本发明采用以下方案：
一种用于生产抗静电空调风叶的材料，按重量百分比包括以下组分：
苯乙烯树脂 58％-68％ 玻璃纤维 20-30％
相容剂 2-8％ 阴离子型抗静电剂 3-10％
润滑剂 0.2-0.7％ 抗氧剂 0.2-0.7％
如上所述的一种用于生产抗静电空调风叶的材料，按重量百分比包括以下组分：
苯乙烯树脂 58％-68％ 玻璃纤维 20-30％
相容剂 5％ 阴离子型抗静电剂 6％
润滑剂 0.5％ 抗氧剂 0.5％
如上所述的一种用于生产抗静电空调风叶的材料，其中所述的相容剂为HF-01、HF-02、HF-04中的一种。
如上所述的一种用于生产抗静电空调风叶的材料，其中所述的阴离子型抗静电剂为Ciba ATMER190。
如上所述的一种用于生产抗静电空调风叶的材料，其特征在于所述的润滑剂为硬脂酸锌。
如上所述的一种用于生产抗静电空调风叶的材料，其特征在于所述的抗氧剂为AT-225。
本发明中所述的相容剂HF-01、HF-02 HF-04均为上海华富化工有限公司生产的产品；
本发明中所述的阴离子型抗静电剂Ciba ATMER190其化学名称为 烯丙基磺酸钠，适用于苯乙烯聚合物，硬质PVC及TPU，分子量320-335g/mol，其为广州承诚化工有限公司生产的产品；
本发明中所述的润滑剂为汉维新材料科技有限公司生产的硬脂酸锌；
本发明中所述的抗氧剂为AT-225为宁波保税区可比克化工有限公司生产的产品。
本发明的有益效果：
本发明产品中采用阴离子型抗静电剂，利用特殊的相容剂使得抗静电剂与AS基体有较好的相容性，使得力学性能得到加大的保留，符合空调的风叶使用要求，另外抗静电效果也非常出色，只需要添加少量的阴离子抗静电剂就可以满足抗静电要求，材料成本比较低。
具体实施方式
下面结合具体实施方式对本发明做进一步描述：
实施例1
本发明用于生产抗静电空调风叶的材料，按重量百分比包括以下组分：
苯乙烯树脂 58％ 玻璃纤维 30％
相容剂HF-01 8％ Ciba ATMER190 3.6％
硬脂酸锌 0.2％ AT-225 0.2％
将上述各组分放入高速混合机，混合搅拌均匀，并通过双螺杆挤出机混炼，在180℃下挤出，然后牵引，过水槽冷却后造粒，即得本 发明产品。
实施例2
本发明用于生产抗静电空调风叶的材料，按重量百分比包括以下组分：
苯乙烯树脂 68％ 玻璃纤维 20％
相容剂HF-02 2％ Ciba ATMER190 8.6％
硬脂酸锌 0.7％ AT-225 0.7％
将上述各组分放入高速混合机，混合搅拌均匀，并通过双螺杆挤出机混炼，在180℃下挤出，然后牵引，过水槽冷却后造粒，即得本发明产品。
实施例3
本发明用于生产抗静电空调风叶的材料，按重量百分比包括以下组分：
苯乙烯树脂 63％ 玻璃纤维 25％
相容剂HF-04 5％ Ciba ATMER190 6％
硬脂酸锌 0.5％ AT-225 0.5％
将上述各组分放入高速混合机，混合搅拌均匀，并通过双螺杆挤出机混炼，在180℃下挤出，然后牵引，过水槽冷却后造粒，即得本发明产品。
实施例4
本发明用于生产抗静电空调风叶的材料，按重量百分比包括以下组分：
苯乙烯树脂 65％ 玻璃纤维 27％
相容剂HF-02 3％ Ciba ATMER190 4％
硬脂酸锌 0.4％ AT-225 0.6％
将上述各组分放入高速混合机，混合搅拌均匀，并通过双螺杆挤出机混炼，在180℃下挤出，然后牵引，过水槽冷却后造粒，即得本发明产品。
实施例5
本发明用于生产抗静电空调风叶的材料，按重量百分比包括以下组分：
苯乙烯树脂 59％ 玻璃纤维 29％
相容剂HF-04 6％ Ciba ATMER190 5％
硬脂酸锌 0.7％ AT-225 0.3％
将上述各组分放入高速混合机，混合搅拌均匀，并通过双螺杆挤出机混炼，在180℃下挤出，然后牵引，过水槽冷却后造粒，即得本发明产品。
本发明各实施例的性能参数见下表：
| 性能指标 | 实施 例1 | 实施 例2 | 实施 例3 | 实施 例4 | 实施 例5 |
| 弯曲强度(MPa) | 130.0 | 146 | 142 | 143 | 138 |
| 弯曲模量(GPa) | 6.0 | 6.5 | 6.3 | 6.4 | 6.2 |
| 拉伸强度(MPa) | 105.0 | 132 | 121 | 128 | 119 |
| 断裂伸长率(％) | 12.0 | 13.1 | 12.7 | 12.6 | 12.4 |
| 冲击强度(KJ/M2) | 4.5 | 5.6 | 5.3 | 5.5 | 5.2 |
| 热变形温度(℃) | 98 | 102 | 113 | 108 | 110 |
| 表面电阻Ωcm | 108 | 108 | 108 | 108 | 108 |
Claims (1)
1.一种用于生产抗静电空调风叶的材料，其特征在于按重量百分比包括以下组分：
苯乙烯树脂 65％ 玻璃纤维 27％
相容剂HF-02 3％ Ciba ATMER190 4％
硬脂酸锌 0.4％ AT-225 0.6％。