CN101874455B - 凹凸棒绒毛浆插花泥及其生产方法 - Google Patents

凹凸棒绒毛浆插花泥及其生产方法 Download PDF

Info

Publication number
CN101874455B
CN101874455B CN201010132640XA CN201010132640A CN101874455B CN 101874455 B CN101874455 B CN 101874455B CN 201010132640X A CN201010132640X A CN 201010132640XA CN 201010132640 A CN201010132640 A CN 201010132640A CN 101874455 B CN101874455 B CN 101874455B
Authority
CN
China
Prior art keywords
attapulgite
fluff pulp
inserting flowers
concave
pulp mud
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201010132640XA
Other languages
English (en)
Other versions
CN101874455A (zh
Inventor
吴宏敬
朱勇
蒋文兰
许庆华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Jinmao Explosion-proof Electrical Co., Ltd.
Original Assignee
蒋文兰
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 蒋文兰 filed Critical 蒋文兰
Priority to CN201010132640XA priority Critical patent/CN101874455B/zh
Publication of CN101874455A publication Critical patent/CN101874455A/zh
Application granted granted Critical
Publication of CN101874455B publication Critical patent/CN101874455B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种凹凸棒绒毛浆插花泥及其生产方法，其技术方案的要点是，凹凸棒绒毛浆插花泥由高粘凹凸棒石粘土粉、膨润土粉、绒毛浆散料、尿素、磷酸二氢钾、羧甲基纤维素钠和去离子水组成。当尿素和磷酸二氢钾溶于去离子水后，将高粘凹凸棒石粘土粉、膨润土粉和绒毛浆散料加入去离子水中，搅拌为凹凸棒绒毛浆插花泥的混合物，将羧甲基纤维素钠水溶液加入混合物中进行搅拌为凹凸棒绒毛浆插花泥的半成品，将半成品加入模具中，使用压力机压制成凹凸棒绒毛浆插花泥的成品。凹凸棒绒毛浆插花泥的生产工艺简单、废物利用成本低廉、有较强的市场竞争力。凹凸棒绒毛浆插花泥适用于花店、宾馆、写字楼及家庭鲜花的保鲜。

Description

凹凸棒绒毛浆插花泥及其生产方法
技术领域
本发明涉及插花泥，具体涉及一种凹凸棒绒毛浆插花泥及其生产方法。
背景技术
室内外扦插鲜花或是用花篮扦插鲜花，都需要使用插花泥，插花泥是一种固定和支撑鲜花的插花专用品，大多采用塑料发泡制成，外观形状有长方形、正方形、圆柱形和圆锥形，质轻如泡沫塑料，让其自然吸足水沉入水底后取出重如铅块，再置于花篮或其它容器中，将鲜花扦插在插花泥的四周，鲜花得到固定，又可起到保湿和保鲜的作用。
塑料发泡制成的插花泥不足之处是：(1)扦插在插花泥上的鲜花保鲜期较短，鲜花和枝叶很快就会凋谢，影响观赏效果；(2)插花泥内的水分蒸发比较快，造成插花泥的外观形状容易变形，致使扦插的鲜花和枝叶产生移位，直接影响到鲜花和枝叶的外观；(3)插花泥使用1～2次后，扦插的孔洞太多，易破碎，不能重复使用；(4)由于生产成本较高，难以推广应用。
生产卫生巾、尿不湿和卫生护理垫时，需要使用的主要原材料有绒毛浆和高吸水树脂，在生产卫生巾的过程中，有一部分质地较轻的绒毛浆和高吸水树脂微粒会被引风机抽出，造成很大的浪费。
发明内容
本发明的目的是克服现有技术中不足之处，提供一种凹凸棒绒毛浆插花泥及其生产方法。
凹凸棒绒毛浆插花泥由高粘凹凸棒石粘土粉、膨润土粉、绒毛浆散料、尿素、磷酸二氢钾、羧甲基纤维素钠和去离子水组成。当尿素和磷酸二氢钾溶于去离子水后，将高粘凹凸棒石粘土粉、膨润土粉和绒毛浆散料加入去离子水中，搅拌为凹凸棒绒毛浆插花泥的混合物，将羧甲基纤维素钠水溶液加入混合物中进行搅拌为凹凸棒绒毛浆插花泥的半成品，将半成品加入模具中，使用压力机压制成凹凸棒绒毛浆插花泥的成品。
凹凸棒石粘土在含水的情况下具有较高的可塑性，稳定性好，凹凸棒石粘土的硬度为莫氏2～3度；凹凸棒石粘土潮湿时呈粘性，粘度可达到3000mPa·s以上，凹凸棒石粘土干燥后收缩率小，且不产生龟裂。高粘凹凸棒石粘土粉是采用提高凹凸棒石粘土粘度的加工工艺生产的粉状凹凸棒石粘土。
膨润土具有强的吸湿性和膨胀性，可吸附8～15倍于自身体积的水量，体积膨胀可达数倍至30倍，在水介质中能分散成胶凝状和悬浮状。
绒毛浆是一种生产卫生巾、尿不湿和卫生护理垫用作吸水介质的纸浆，绒毛浆纤维长、柔软性能好、白度高和保水性能优越，绒毛浆散料是生产卫生巾过程中产生的边角废料，绒毛浆散料中含有绒毛浆和高吸水树脂。
尿素外观呈白色晶体或粉末，易溶于水，是一种高浓度氮肥。
磷酸二氢钾是一种速效磷钾复合肥，其外观为白色晶体，性质稳定，易溶于水，极易被植物吸收利用。
羧甲基纤维素钠为白色或乳白色纤维状粉末或颗粒，易于分散在水中成澄明胶状液，具有粘合、增稠、增强、乳化、保水、悬浮等作用。
本发明通过下述技术方案予以实现：
1、凹凸棒绒毛浆插花泥的配料按重量百分比由下列组分组成：高粘凹凸棒石粘土粉45～65％、膨润土粉5～20％、绒毛浆散料2～15％、尿素0.01～1％、磷酸二氢钾0.01～1％、羧甲基纤维素钠水溶液1～15％和去离子水5～35％；
所述羧甲基纤维素钠水溶液的配料按重量百分比由下列组分组成：羧甲基纤维素钠0.1～10％和去离子水90～99.9％；
所述膨润土粉的颗粒细度小于0.074毫米。
2、凹凸棒绒毛浆插花泥的生产方法：(1)先将去离子水、尿素和磷酸二氢钾加入已经运转的搅拌机内，当尿素和磷酸二氢钾溶于去离子水后，将高粘凹凸棒石粘土粉、膨润土粉和绒毛浆散料加入溶有尿素、磷酸二氢钾的去离子水中，搅拌为凹凸棒绒毛浆插花泥的混合物；(2)将羧甲基纤维素钠水溶液加入凹凸棒绒毛浆插花泥的混合物中进行搅拌，搅拌混合均匀后为凹凸棒绒毛浆插花泥的半成品；(3)将凹凸棒绒毛浆插花泥的半成品加入模具中，使用压力机压制成凹凸棒绒毛浆插花泥的成品。
所述高粘凹凸棒石粘土粉是采用提高凹凸棒石粘土粘度的加工工艺生产的凹凸棒石粘土，其特征在于，从矿区开采的凹凸棒石粘土，需要经过30～120天的自然风化；改性处理方法是：以重量百分比计算，取自然风化后的凹凸棒石粘土94～98％，均匀加入2～6％碳酸钠，共同输入浸泡池中，加入清水进行浸泡陈化，浸泡时间为72～120小时；取浸泡后的凹凸棒石粘土，输入搅拌机中进行搅拌，并将搅拌后的凹凸棒石粘土，经挤压机挤成薄片，其厚度控制在0.5～2毫米，将凹凸棒石粘土薄片，进行晾晒，晾晒后的凹凸棒石粘土薄片，其含水量≤15％；配料以重量百分比计算：晾晒后的凹凸棒石粘土94～98％、高吸水树脂0.5～5％和纤维素0.5～3％，将上述配料进行搅拌，搅拌均匀后输入磨机中进行磨粉，颗粒细度≤0.074毫米。
上述生产工艺是采用由本发明人于2005年6月20日申请的“提高凹凸棒石粘土粘度的加工工艺”，中国专利授权公告号为：CN 1317067C，授权公告日：2007年5月23日。
将高粘凹凸棒石粘土粉、膨润土粉和绒毛浆散料加入溶有尿素、磷酸二氢钾的去离子水后，有利于提高了凹凸棒石粘土和膨润土的粘度，使绒毛浆散料中的绒毛浆和高吸水树脂吸水后膨胀，储蓄了大量的尿素和磷酸二氢钾的水溶液，以确保鲜花所需要的营养，有利于枝叶的正常生长和延长花期，扦插在插花泥上的鲜花保鲜期长，色泽艳丽。
凹凸棒绒毛浆插花泥粘度高，柔软可塑性强，光泽和弹性好，可以设计成多种不同形状的插花泥，具有保水性强、收缩率小、不变形、不变硬和不产生龟裂的特点。
凹凸棒绒毛浆插花泥的生产工艺简单、废物利用成本低廉、有较强的市场竞争力。
凹凸棒绒毛浆插花泥适用于花店、宾馆、写字楼及家庭鲜花的保鲜，还用于各种大型节日活动、婚丧礼庆及各种花篮和花车的设计。
具体实施方式
下面结合实施例对本发明作进一步的描述：
1、凹凸棒绒毛浆插花泥的配料按重量百分比由下列组分组成：高粘凹凸棒石粘土粉48％、膨润土粉12％、绒毛浆散料6.7％、尿素0.2％、磷酸二氢钾0.1％、羧甲基纤维素钠水溶液8％和去离子水25％；
所述羧甲基纤维素钠水溶液的配料按重量百分比由下列组分组成：羧甲基纤维素钠4％和去离子水96％；
所述膨润土粉的颗粒细度小于0.074毫米。
2、凹凸棒绒毛浆插花泥的生产方法：(1)先将去离子水、尿素和磷酸二氢钾加入已经运转的搅拌机内，当尿素和磷酸二氢钾溶于去离子水后，将高粘凹凸棒石粘土粉、膨润土粉和绒毛浆散料加入溶有尿素、磷酸二氢钾的去离子水中，搅拌为凹凸棒绒毛浆插花泥的混合物；(2)将羧甲基纤维素钠水溶液加入凹凸棒绒毛浆插花泥的混合物中进行搅拌，搅拌混合均匀后为凹凸棒绒毛浆插花泥的半成品；(3)将凹凸棒绒毛浆插花泥的半成品加入模具中，使用压力机压制成凹凸棒绒毛浆插花泥的成品。

Claims (1)

1.一种凹凸棒绒毛浆插花泥，其特征在于，凹凸棒绒毛浆插花泥的配料按重量百分比由下列组分组成：高粘凹凸棒石粘土粉45～65％、膨润土粉5～20％、绒毛浆散料2～15％、尿素0.01～1％、磷酸二氢钾0.01～1％、羧甲基纤维素钠水溶液1～15％和去离子水5～35％；
所述羧甲基纤维素钠水溶液的配料按重量百分比由下列组分组成：羧甲基纤维素钠0.1～10％和去离子水90～99.9％；
所述膨润土粉的颗粒细度小于0.074毫米；
所述凹凸棒绒毛浆插花泥的生产方法：(1)先将去离子水、尿素和磷酸二氢钾加入已经运转的搅拌机内，当尿素和磷酸二氢钾溶于去离子水后，将高粘凹凸棒石粘土粉、膨润土粉和绒毛浆散料加入溶有尿素、磷酸二氢钾的去离子水中，搅拌为凹凸棒绒毛浆插花泥的混合物；(2)将羧甲基纤维素钠水溶液加入凹凸棒绒毛浆插花泥的混合物中进行搅拌，搅拌混合均匀后为凹凸棒绒毛浆插花泥的半成品；(3)将凹凸棒绒毛浆插花泥的半成品加入模具中，使用压力机压制成凹凸棒绒毛浆插花泥的成品；
所述高粘凹凸棒石粘土粉是采用提高凹凸棒石粘土粘度的加工工艺生产的凹凸棒石粘土，其特征在于，从矿区开采的凹凸棒石粘土，需要经过30～120天的自然风化；改性处理方法是：以重量百分比计算，取自然风化后的凹凸棒石粘土94～98％，均匀加入2～6％碳酸钠，共同输入浸泡池中，加入清水进行浸泡陈化，浸泡时间为72～120小时；取浸泡后的凹凸棒石粘土，输入搅拌机中进行搅拌，并将搅拌后的凹凸棒石粘土，经挤压机挤成薄片，其厚度控制在0.5～2毫米，将凹凸棒石粘土薄片，进行晾晒，晾晒后的凹凸棒石粘土薄片，其含水量≤15％；配料以重量百分比计算：晾晒后的凹凸棒石粘土94～98％、高吸水树脂0.5～5％和纤维素0.5～3％，将上述配料进行搅拌，搅拌均匀后输入磨机中进行磨粉，颗粒细度≤0.074毫米。
CN201010132640XA 2010-03-26 2010-03-26 凹凸棒绒毛浆插花泥及其生产方法 Active CN101874455B (zh)