CN101864216A - 一种淋涂用氟碳快干罩面漆 - Google Patents

一种淋涂用氟碳快干罩面漆 Download PDF

Info

Publication number
CN101864216A
CN101864216A CN 201010203032 CN201010203032A CN101864216A CN 101864216 A CN101864216 A CN 101864216A CN 201010203032 CN201010203032 CN 201010203032 CN 201010203032 A CN201010203032 A CN 201010203032A CN 101864216 A CN101864216 A CN 101864216A
Authority
CN
China
Prior art keywords
fluorocarbon
combination
ingredient
fluorocarbon resin
curtain coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010203032
Other languages
English (en)
Inventor
陆勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taicang Polymer Material Research And Development Center Co Ltd
Original Assignee
Taicang Polymer Material Research And Development Center Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taicang Polymer Material Research And Development Center Co Ltd filed Critical Taicang Polymer Material Research And Development Center Co Ltd
Priority to CN 201010203032 priority Critical patent/CN101864216A/zh
Publication of CN101864216A publication Critical patent/CN101864216A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种淋涂用氟碳快干罩面漆,它含有单独包装的组分A和组分B。其中组分A有组合氟碳树脂、助剂和混合溶剂;组分B为固化剂;使用时各组分的重量比为:组分A∶组分B=100∶5~15。本发明优点是可以淋涂施工,用机械代替手工作业,操作简单、效率高、节省人力;成膜速度快、平滑均匀、无横向条纹、涂料损失小;特殊的原料选择组合,干燥速度快;漆膜机械性能优异,自洁性、丰满度、保护性佳;漆膜耐老化性能优异;制备方法简单,易于流水线工业化大规模生产。本发明可以广泛用于所有表面平整或小弯曲的板材,如有机片、木地板、铝塑板、人造花岗岩(大理石)等平板(或小弯曲)基材等的罩面保护,起到延续其使用寿命的作用。

Description

一种淋涂用氟碳快干罩面漆
技术领域
本发明涉及一种涂料,具体地说,是涉及一种可淋涂施工用于表面平整的板材的氟碳快干罩面漆及其制备方法。
背景技术
目前,淋涂机越来越广泛地应用于涂料行业的施工作业中,其用机械的方法使油漆或UV漆产生瀑布式的漆膜,被涂复的物件以恰当的速度从瀑布式的漆膜底下穿过,从而达到漆成膜的目的。该淋涂机适用于所有平面固件的淋涂,特别适合于在镜片、有机片、木地板、铝塑板、人造花岗岩(大理石)等平板(或小弯曲)基材的表面淋涂一层或多层保护漆膜或其它功能漆膜,具有成膜速度快、节省时间、无污染,膜层牢固、均匀、平滑、光亮等优点,由于其可以不用人工,替代了传统的手扫漆工艺或喷漆工艺。但是,现今可用于淋涂机的漆大多为UV漆,PU漆等,还未出现可以淋涂的氟碳漆,氟碳漆是目前综合性能最优异的涂料之一,其中有一种为氟碳罩面漆,此氟碳罩面漆现今多采用喷涂的施工方法,不但施工麻烦,浪费人力,而且质量不能保证,如会出现色差大,膜厚不均等现象,施工完成后,施工队伍的保护工作量也大,因为喷雾,所以更费原料。因此,可淋涂的氟碳罩面漆成为社会的亟需。
发明内容
本发明正是为了克服上述不足,提供一种烘烤氟碳罩面漆,其不仅可以淋涂施工,而且具有快干、耐候、附着力优异及防腐蚀性强的特点。
本发明还要解决的一个技术问题是提供上述罩面漆的制备方法。
为解决上述技术问题,本发明所采用的技术方案如下:
一种淋涂用氟碳快干罩面漆,它含有单独包装的组分A、组分B;其中组分A有组合氟碳树脂、助剂和混合溶剂,所述组合氟碳树脂是由三氟氯乙烯树脂(如大连振邦氟涂料股份有限公司生产的ZB-F-100、ZB-F-200)和四氟乙烯树脂(如阜新瑞氟隆涂料有限责任公司生产的RF-100、日本大金公司生产的GK-570)按重量比例1~4.5∶1.5组合而成,其固含量为40%~60%,氟含量为25%~45%;组分A中各种原料的重量比为:组合氟碳树脂∶助剂∶混合溶剂=62~86∶7~26∶5~20;组分B为固化剂;组分A与组分B的重量比=100∶5~15。
固化剂为HDI三聚体,优选用己二异氰酸酯。
助剂是下面六种助剂的混合物:
(1)润湿分散剂:成分为含亲和颜料基团的高分子量嵌段共聚物溶液,用量为组合氟碳树脂的0.006~0.01倍,优选用德国毕克化学公司的BYK-161,苏州兴泰国光化学助剂有限公司生产的TA-100-50;
(2)流平剂:成份为有机改性硅氧烷,用量为组合氟碳树脂的0.003~0.007倍,优选用嘉智信诺化学有限公司生产的WE-D8975和WE-D8900;
(3)消泡剂:成份为聚硅氧烷溶液,用量为组合氟碳树脂的0.003~0.007倍,优选用德国毕克化学公司的BYK-066;
(4)白炭黑:用量为组合氟碳树脂的0.045~0.2倍;
(5)光稳定剂:用量为组合氟碳树脂的0.003~0.008倍,优选用上海耐阳洁净技术有限公司生产的UV-3100;
(6)醋酸纤维素浆:用量为组合氟碳树脂的0.045~0.1倍。
混合溶剂为醋酸丁酯与二甲苯按1~10∶2~8的混合物。
上述淋涂用氟碳快干罩面漆的制备方法,按配方要求的重量比进行称量,加入部分(20%~30%)组合氟碳树脂和润湿分散剂以及部分混合溶剂搅拌均匀,予分散,研磨,达到规定细度,按配方量加入剩余组合氟碳树脂,剩余混合溶剂,固化剂和各种助剂,调节粘度,过滤,检验后计量包装;
烘烤条件为二级烘烤:初级烘烤温度:60~120℃,烘烤时间4~9分钟;二级烘烤温度:80~100℃,烘烤时间6~8分钟,适合低温烘烤。
有益效果:本发明所述的淋涂用氟碳快干罩面漆主要应用于表面平整或小弯曲板材的罩面保护,具有以下优点:
1、组合树脂由三氟氯乙烯树脂和四氟乙烯树脂按重量比例1~4.5∶1.5组合而成,其具备了三氟树脂和四氟树脂的优点,克服了其缺点,配制成的氟碳漆具有非常好的光泽度、溶解性、相容性、流平性及施工性;
2、可以淋涂,用机械代替手工作业,操作简单、效率高、节省人力;
3、成膜速度快、光滑均匀、无横向条纹、涂料损失小;
4、特殊的原料选择组合,干燥速度快;
5、漆膜机械性能优异,自洁性、丰满度佳;
6、漆膜耐老化性能优异;
7、具有很强的保护性,由于金属铝浆等材料的不规则性,在氟碳油漆面漆中,极易与空气发生氧化反应,会导致漆面发黑的现象,本发明所述的罩面漆将会阻止这种现象发生,使漆面保持长久。
8、制备方法简单,易于流水线工业化大规模生产。
具体实施方式:
下面列举七个实施例对本发明加以进一步说明,但本发明不只限于这些实施例。
实施例1
在1000ml的容器中,加入组合氟碳树脂15g(固含量为46%),分散剂BYK-1610.5g,混合溶剂3g,搅拌均匀,予分散,研磨,达到规定细度15μm时,按配方量加入剩余的组合氟碳树脂47g和流平剂WE-D8975 0.35g、消泡剂BYK-066 0.35g、白炭黑15g、光稳定剂UV-3100 0.4g、醋酸纤维浆7.0g及混合溶剂11.4g,搅拌均匀后调节粘度,过滤,取样,组分A、组分B按100∶5~15重量配比成漆,经各项技术指标检验,检验合格后计量包装。
实施例2~7
操作步骤和反应条件同实施例1,原料具体用量如表1。
表1.实施例1~7原料配比wt/wt
 原料名称   实施例1   实施例2   实施例3   实施例4   实施例5   实施例6   实施例7
 组合氟碳树脂(固含量46%),g   62   70   70   75   80   80   86
  BYK-161,g   0.5   0.5   0.4   0.8   0.6   0.6   0.5
  WE-D8975,g   0.35   0.30   0.35   0.35   0.30   0.30   0.35
  BYK-066,g   0.35   0.30   0.35   0.35   0.30   0.30   0.35
  白炭黑,g   15   6   7   10   4   4   3
  UV-3100,g   0.4   0.3   0.4   0.4   0.5   0.4   0.3
  醋酸纤维浆,g   7   8   3   6   3   5   4
  混合溶剂   14.4   14.6   18.5   7.1   11.3   9.4   5.5
  固化剂   7.8   7.8   7.8   7.8   7.8   7.8   7.8
以上实施例1~7所制得的淋涂用氟碳快干罩面漆,通过淋涂机(市面有售)进行淋涂施工,施工机械使用时,粘度调整为8″~15″(涂4#杯),在表面平整的板材表面形成一层漆膜,对此漆膜进行性能测试,测试结果如表2和表3。
表2.实施例1~4漆膜性能测试数据
Figure BSA00000167054200041
表3.实施例5~7漆膜性能测试数据
Figure BSA00000167054200051

Claims (6)

1.一种淋涂用氟碳快干罩面漆,其特征在于:它含有单独包装的组分A和组分B;其中组分A有组合氟碳树脂、助剂和混合溶剂,所述的组合氟碳树脂是由三氟氯乙烯树脂和四氟乙烯树脂按重量比例1~4.5∶1.5组合而成,其氟含量为45%~55%;组分A中各种原料的重量比为:组合氟碳树脂∶助剂∶混合溶剂=62~86∶7~26∶5~20;组分B为固化剂;组分A与组分B的重量比=100∶5~15。
2.根据权利要求1所述的一种淋涂用氟碳快干罩面漆,其特征在于:所述固化剂为HDI三聚体。
3.根据权利要求1所述的一种淋涂用氟碳快干罩面漆,其特征在于:所述助剂是下面六种助剂的混合物:
(1)润湿分散剂:成分为含亲和颜料基团的高分子量嵌段共聚物溶液,用量为组合氟碳树脂的0.006~0.01倍;
(2)流平剂:成份为有机改性硅氧烷,用量为组合氟碳树脂的0.003~0.007倍;
(3)消泡剂:成份为聚硅氧烷溶液,用量为组合氟碳树脂的0.003~0.007倍;
(4)白炭黑:用量为组合氟碳树脂的0.045~0.2倍;
(5)光稳定剂:用量为组合氟碳树脂的0.003~0.008倍;
(6)醋酸纤维素浆:用量为组合氟碳树脂的0.045~0.1倍。
4.根据权利要求1所述的一种淋涂用氟碳快干罩面漆,其特征在于:所述混合溶剂为醋酸丁酯与二甲苯按1~10∶2~8的混合物。
5.制备如权利要求1所述的一种淋涂用氟碳快干罩面漆的方法,其特征在于:按配方要求的重量比进行称量,加入部分组合氟碳树脂和润湿分散剂以及部分混合溶剂搅拌均匀,予分散,研磨,达到规定细度,按配方量加入剩余组合氟碳树脂,剩余混合溶剂,固化剂和各种助剂,调整粘度,过滤,检验后计量包装。
6.根据权利要求5所述的一种淋涂用氟碳快干罩面漆的制备方法,其特征在于:烘烤条件为二级烘烤:初级烘烤温度:60~120℃,烘烤时间4~9分钟;二级烘烤温度:80~100℃,烘烤时间6~8分钟。
CN 201010203032 2010-06-18 2010-06-18 一种淋涂用氟碳快干罩面漆 Pending CN101864216A (zh)