CN101858190A - Method for producing liquid wood integral door - Google Patents
Method for producing liquid wood integral door Download PDFInfo
- Publication number
- CN101858190A CN101858190A CN201010206327A CN201010206327A CN101858190A CN 101858190 A CN101858190 A CN 101858190A CN 201010206327 A CN201010206327 A CN 201010206327A CN 201010206327 A CN201010206327 A CN 201010206327A CN 101858190 A CN101858190 A CN 101858190A
- Authority
- CN
- China
- Prior art keywords
- parts
- liquid wood
- wood
- integral door
- raw materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for producing a liquid wood integral door, which comprises the following steps of: 1) preparing liquid wood, namely (1) drying and grinding raw materials; (2) mixing the raw materials to obtain a mixture; and (3) generating the liquid wood, wherein the liquid wood comprises the following raw materials in part by weight: 100 parts of polyvinyl chloride, 40 parts of calcium carbonate, 60 parts of wood fiber powder, 4.5 parts of stabilizer, 8 parts of chlorinated polyethylene (CPE), 5 parts of acrylamide (ACR), 3 parts of H530, 0.5 part of polyethylene (PE) wax, 0.6 part of stearic acid, and 1 part of pigment; and 2) performing extrusion molding on the liquid wood at one time to obtain the integral door. In the method, the raw materials are molded at one time at a high temperature and under high pressure, do not contain formaldehyde, and are subjected to surface treatment by adopting thermal transfer technology; the integral door is free of paint, has no any toxic harmful gas and smell release in the production and use process, is environmental-friendly and has practicality.
Description
Technical field
The present invention relates to a kind of production method of liquid wood integral door.
Background technology
Along with the economic sustained, stable growth of China, the realty industry fast development, people's living standard improves rapidly, and house decoration is persistently overheating, the bulk product that market must be used finishing--and the demand of door sharply increases.
Along with quickening of urbanization process, the house first, the expansion of secondary decoration and office commercial location, rural market, also will discharge the market space on a large scale.For the house door of one family, bedroom door, kitchen door, lavatory door, balcony door are arranged ... five or six fan door at least, go up ten fan doors at most.
In the market, the production method of common house door is more, but mostly technology is loaded down with trivial details, and cost costliness, and inflammablely at the aspect of performance ubiquity is afraid of tide, and is yielding, easily problem such as release formaldehyde.
Pursue constant rule durable, healthy, that the environmental protection household is market comsupton, people occur at the class product of calling a kind of not only green low-carbon but also economic fashion.
Summary of the invention
The technical issues that need to address of the present invention just are to overcome the defective of prior art, a kind of production method of liquid wood integral door is provided, the used raw material of the present invention are in the moulding next time of high temperature, condition of high voltage, material does not contain formaldehyde, adopt hot transfer technique during surfacing, exempt from paint, no any toxic and harmful and smell discharge in production, use, environmental protection, the tool practicality.
For addressing the above problem, the present invention adopts following technical scheme:
The production method of a kind of liquid wood integral door of the present invention comprises the following steps:
1), the preparation of liquid wood;
2) be integral door, with an extrusion modling of liquid wood.
The parts by weight of raw materials of described liquid wood is provided as: 100 parts of polyvinyl chloride, 40 parts in calcium carbonate, 60 parts of wood fiber powders, 4.5 parts of stabilizing agents, 5 parts of 8 parts of CPE, ACR, 3 parts of H530,0.5 part in PE wax, 0.6 part of stearic acid, 1 part of pigment;
The preparation process of liquid wood is:
(1) raw material drying milled processed;
(2) batch mixing system material: all raw materials of handling are carried out secondary plasticizing processing handle;
(3) generate liquid wood: material at high temperature is fused into mobile lenticular material, generates liquid wood.
Also carry out shaping cutting, printing or hot transfer printing, moulding or engraving and assembling edge sealing step after the extrusion modling.
The present invention adopts wood fiber powder resources such as stalk, wood dust without timber, converts it into liquid wood, and bubble is not afraid of in an extrusion modling, and finished product can also recycling after the several years.Effectively save the forest reserves, sexual valence caters to huge numbers of families, already develops a circular economy for China's type gate and has opened a fan gate.
Products characteristics of the present invention has:
1. environmental protection:
The present invention is that material does not contain formaldehyde in the moulding next time of high temperature, condition of high voltage, and biological sensitive transfer technology is adopted in surfacing, exempts from paint, and no any pernicious gas and smell discharge in the production use, and environmental-protecting performance is remarkable especially.
2, fire-retardant, be not afraid of bubble, anticorrosion, anti-ly go mouldy, anti-ly damage by worms, indeformable:
Be particularly suitable for indoor and outdoor places such as the temperature difference is big, humidity, improper ventilation, as washroom, kitchen, storage room door etc.
3, rational in infrastructure, intensity is high:
The present invention adopts an actor's rendering of an operatic tune structure design, and the technology of a good prescription and an extrusion integral moulding guarantees product quality height unanimity.
4, splicing structure, it is time saving and energy saving to install:
The present invention adopts simple splicing structure, and it is very convenient that door pocket is installed, and door pocket wired-AND gate cover adopts bayonet socket to connect, and need not rifle nail or viscose glue and fixes.
5, insulation, sound insulation value are good:
An actor's rendering of an operatic tune structure of liquid wood integral door and the specific properties of liquid wood have guaranteed that its thermal conductivity is lower than plastics and timber, and heat preservation and energy conservation effects is remarkable, and the noise reduction sound insulation value is good.
6, superiority of effectiveness is remarkable:
The present invention adopts the industrialization manufacturing, steady quality, and cost is low, and extremely strong price advantage is arranged.
The selected wood fiber powder of the present invention is as main raw material(s), adopt world advanced person's liquid wood technology and system door technology, an extrusion molding, thoroughly changed synthetic loaded down with trivial details technology and the workshop-based production model of traditional system door palpus secondary, realized interior door industrialization, standardization, pipelining, product have do not ftracture, indeformable, be not afraid of advantages such as bubble, zero formaldehyde.All kinds of interior door have been remedied on the existing market in the defective of aspects such as material and function.
The present invention has abundant pattern, style and mounting means easily, the distinguishing feature that has possessed all high-grade interior door, and price is well below other interior door, being widely used in house decoration and major works decorates, other category interior door is specially adapted to wet environments such as kitchen, washroom, for far can not reach.
The specific embodiment
1), the preparation of liquid wood:
The parts by weight of raw materials of described liquid wood is provided as: 100 parts of polyvinyl chloride, 40 parts in calcium carbonate, 60 parts of wood fiber powders, 4.5 parts of stabilizing agents, 5 parts of 8 parts of CPE, ACR, 3 parts of H530,0.5 part in PE wax, 0.6 part of stearic acid, 1 part of pigment;
The preparation process of liquid wood is:
(1) raw material drying milled processed;
(2) batch mixing system material: all raw materials of handling are carried out secondary plasticizing processing handle;
(3) generate liquid wood: material at high temperature is fused into mobile lenticular material, generates liquid wood.
2) be integral door, with extrusion modling of liquid wood.
3) packing warehouse-in, also carry out shaping cutting, printing or hot transfer printing, moulding or engraving and assembling edge sealing step after the extrusion modling, at last.
The present invention is applied to extrusion integral environmental protection door one time with liquid wood, has thoroughly overturned the complicated production technology of conventional door industry, has established interior door industry new standard, has realized the producing material miracle on the building materials and ornaments history; Product is once putting goods on the market, and rapidly with its cheap cost, unique quality outclass the functional performance of traditional timber, becomes people's house ornamentation first-selection.
It should be noted that at last: obviously, the foregoing description only is for example of the present invention clearly is described, and is not the qualification to embodiment.For those of ordinary skill in the field, can also make other changes in different forms on the basis of the above description.Here need not also can't give exhaustive to all embodiments.And conspicuous variation of being extended out thus or change still are among protection scope of the present invention.
Claims (3)
1. the production method of a liquid wood integral door, it is characterized in that: described production method comprises the following steps:
1), the preparation of liquid wood;
2) be integral door, with extrusion modling of liquid wood.
2. the production method of liquid wood integral door as claimed in claim 1, it is characterized in that: the parts by weight of raw materials of described liquid wood is provided as: 100 parts of polyvinyl chloride, 40 parts in calcium carbonate, 60 parts of wood fiber powders, 4.5 parts of stabilizing agents, CPE8 part, ACR5 part, 3 parts of H530,0.5 part in PE wax, 0.6 part of stearic acid, 1 part of pigment;
The preparation process of liquid wood is:
(1) raw material drying milled processed;
(2) batch mixing system material: all raw materials of handling are carried out secondary plasticizing processing handle;
(3) generate liquid wood: material at high temperature is fused into mobile lenticular material, generates liquid wood.
3. the production method of liquid wood integral door as claimed in claim 2 is characterized in that: also carry out shaping cutting, printing or hot transfer printing, moulding or engraving and assembling edge sealing step after the extrusion modling.