CN101851455A - 无溶剂环氧导电涂料 - Google Patents

无溶剂环氧导电涂料 Download PDF

Info

Publication number
CN101851455A
CN101851455A CN200910131435A CN200910131435A CN101851455A CN 101851455 A CN101851455 A CN 101851455A CN 200910131435 A CN200910131435 A CN 200910131435A CN 200910131435 A CN200910131435 A CN 200910131435A CN 101851455 A CN101851455 A CN 101851455A
Authority
CN
China
Prior art keywords
percent
paint
epoxy
conductive paint
pigment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200910131435A
Other languages
English (en)
Inventor
殷启明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN200910131435A priority Critical patent/CN101851455A/zh
Publication of CN101851455A publication Critical patent/CN101851455A/zh
Pending legal-status Critical Current

Abstract

一种无溶剂环氧导电涂料，其特征是所述涂料组分由环氧树脂、助剂、颜料、导电云母粉、稀释剂、填料和固化剂组成，所占质量百分比范围为：环氧树脂20～25％，助剂0.8～1.5％，颜料5～6.7％，云母粉34～36％，活性稀释剂1～2％，固化剂10～12％，填料为余量。本发明的优点是：符合环保要求、防腐性能优异、施工工艺简单，且涂料层形成后表面平整、光滑，色彩均匀。

Description

无溶剂环氧导电涂料
技术领域
本发明涉及一种涂料，尤其涉及无溶剂环氧导电涂料。
背景技术
采用导电云母粉做为导电介质的溶剂型导电涂料含有较多的有机溶剂，这些有机溶剂在涂料的生产和施工阶段排入大气，污染环境，同时危害人类的健康。
发明内容
本发明的目的是克服现有技术的不足，提供一种符合环保要求、防腐性能优异、施工工艺简单且具有较高性价比的一种一种无溶剂环氧导电涂料。
本发明的具体技术方案如下：
一种无溶剂环氧导电涂料，其特征是所述涂料组分由环氧树脂、助剂、颜料、导电云母粉、稀释剂、填料和固化剂组成，所占质量百分比范围为：环氧树脂20～25％.助剂0.8～1.5％，颜料5～6.7％，云母粉34～36％，活性稀释剂1～2％，固化剂10～12％，填料为余量。
本发明的优点是：符合环保要求、防腐性能优异、施工工艺简单，且涂料层形成后表面平整、光滑，色彩均匀。
具体实施方式
一种无溶剂环氧导电涂料，其特征是所述涂料组分由环氧树脂、助剂、颜料、导电云母粉、稀释剂、填料和固化剂组成，所占质量百分比范围为：环氧树脂20～25％.助剂0.8～1.5％，颜料5～6.7％，云母粉34～36％，活性稀释剂1～2％，固化剂10～12％，填料为余量。

Claims (1)

1.一种的无溶剂环氧导电涂料，其特征是所述涂料组分由环氧树脂、助剂、颜料、导电云母粉、稀释剂、填料和固化剂组成，所占质量百分比范围为：环氧树脂20～25％.助剂0.8～1.5％，颜料5～6.7％，云母粉34～36％，活性稀释剂1～2％，固化剂10～12％，填料为余量。
CN200910131435A 2009-03-30 2009-03-30 无溶剂环氧导电涂料 Pending CN101851455A (zh)