CN101838434A - Elastomeric product for modifying common soil and production method thereof - Google Patents

Abstract

The invention discloses an elastomeric product for modifying common soil and a production method thereof. The production method comprises the steps of: removing impurities in soil, drying, crushing and screening to obtain soil particles; then dynamically heating common soil particles, adding a surface modifying agent, drying to obtain modified soil, wherein the surface modifying agent comprises a coupling agent, polyorganosiloxane with reactive functional groups, organosilicon, fatty amine emulsifying bodies and water; and finally, preparing an elastic runway surface layer, a sports ground floor, synthetic leather, household and commercial floors, household and commercial wall decorating materials and the like by using the modified soil and crylic acid cementing agents as main components and doping with a compound prepared by a cross-linking agent, a softening agent, the coupling agent, a foaming agent or defoaming agent and the like. The product has no toxic and harmful gas volatilization in the whole production and use processes, has compression deformation ratio, rebound resilience and durability reaching or exceeding properties of rubber or some plastics, and is an elastic plane material with low cost, high performance and environment protection.

Description

The elastomer product of modifying common soil and production method thereof

Technical field

The present invention relates to a kind of polymer composite and production method thereof, particularly a kind ofly will be used to make the method for elastomer product after the common soil modification.

Background technology

In the process of making materials such as plastics, rubber, paper, coating, cable, add the performance that filler can be saved cost and improve material, be common sense, key is the filler of what material of employing as certain material, so the cooperation between research filler and the organic compound is a more scabrous problem in the materialogy.Earth is the most cheap a kind of in the filler, at present earth is used for filler and mainly adopts nonmetalliferous ore soil, for example kaolin, attapulgite, wilkinite, china clay, coal gangue etc.Not influencing or obviously improve the performance of material after nonmetalliferous ore soil is added, is the focus of research.The modification of much introducing relevant nonmetalliferous ore soil is arranged in the open source literature, takes passages as follows by retrieval:

1, influence [author] leaf of [autograph] modified calcinated kaolin on properties of EPDM is unfolded the old forint of Zhou Yanhao [mechanism] Guangdong University of Technology's material and energy institute, [periodical name] rubber industry .2006,53 (12) .-723-726[digests] adopt silane coupling agent that calcined kaolin is carried out surface modification, research silane coupling agent kind and consumption are filled the influence of EPDM properties of rubber to calcined kaolin.The result shows.Time of scorch and sulfurizing time influence that silane coupling agent is filled the EPDM sizing material to calcined kaolin are little; The modifying function of coupling agent A-17Z is comparatively obvious, can significantly improve the tear strength of EPDM cross-linked rubber; Coupling agent A-172 consumption is excessive, and is unfavorable to EPDM cross-linked rubber solvent resistance.

2, [autograph] Yichang appositional pattern calcined kaolin surface modification and applied research [author] Zhang Wangchi [1,2] graduate school of Hu Mingan [1] Li Jinfa [2] Chen Yanbo [2] [mechanism] [1] China University of Geosciences, [2] Yichang Institute of Geology and Mineral Resources, [periodical name] chemical industry mineral and processing .2006,35 (3) .-10-12,18[digest] appositional pattern kaolin is Chinese distinctive kaolin resource.Application test proves, the high mountain range scholar of Yichang appositional pattern after superfine grinding, calcining, ultra-fine ore grinding and silane coupling agent surface treatment, as the filler of high performance cable sizing material, filling properties be improved significantly.

3, preparation [author] Wang Yuansun [mechanism] of the recessed native reinforced rubber material of [autograph] a kind of surface modification not quite clear [periodical name] rubber and plastic technology and equipment .2006,32 (1) .-66-66[digests] this preparation method is by carrying out organic modification to recessed native surface, improves its consistency and filler effect in rubber.It is characterized in that tensile strength, 300% tensile modulus and tear strength all are significantly improved, and curing time is short, vulcanization crosslinking is effective.This product can be widely used in produces the rubber item (number of applying for a patent 02158227.0) that various high strength require.

4, [autograph] modification dolomite attapulgite feasibility of filling in rubber is inquired into [author] gold leaf tinkling of pieces of jade Qian Yunhua [mechanism] Huaiyingong College chemical industry system, [periodical name] Institutes Of Technology Of Nanjing's journal: natural science edition .2005,29 (6) .-720-723[digests] this article has been inquired into the feasibility of natural compounded mix rhombspar attapulgite filled rubber galosh after surface modification, and sample has carried out mechanical test and microscopic appearance is investigated to filling.Result of study shows that the rhombspar attapulgite loading level in sizing material after stearic acid modified increases substantially, and can reach the 110g/100g sizing material, and have good consistency, and can shorten mixing time, the sizing material drawability is good, film is smooth smooth, and glossiness is good.Compare with light calcium carbonate, the rhombspar attapulgite after the modification can significantly improve tensile strength, 300% tensile modulus, elongation at break and the adhesion strength of filling the glue sample, fills the glue sample than fine particle calcium carbonate respectively and has improved 57.8%, 100%, 5.5%, 16%.

5, [autograph] Calcined Kaolin from Coal Bearing Strata surface modification and application [author] Li Baozhi [1] Wang Wenli [2] [mechanism] [1] Baotou, the Inner Mongol auspicious intelligence surface-modifying agent factory in high molecular products, [2] Chinese building material Office of Technical Services, [periodical name] nonmetalliferous ore .2005,28 (B09) .-49-51[digest] mainly introduced the character of coal series kaolin rock. the surface modification mechanism after calcining, method, equipment are selected, and calcined earth is at the effect of aspects such as plastics, rubber, coating.

6, [autograph] wilkinite/polyacrylic acid high-absorbent material preparation and modification [author] Wei Yue beautiful jade Wu Ji bosom Huang Yunfang [mechanism] Huaqiao University, [periodical name] Huaqiao University's journal: natural science edition .2005,26 (4) .-365-368[digests] adopt high temperature aqueous solution polymerization method fast.Synthetic swelling soil/polyacrylic acid high water absorptive matrix material. inquire into various factors in the Composite Preparation process, as the influence to matrix material suction multiple such as dosage of crosslinking agent and wilkinite ultrafine powder consumption. also matrix material is carried out surface-crosslinked modification in the literary composition. the result shows that modification helps improving the suction multiple and the rate of water absorption of matrix material.

7, [autograph] calcined kaolin surface modification and the applied research in the cable sizing material [author] Cheng Xianzhong [1] Jin Can [1] Liu Xinhai [2] [mechanism] [1] Yichang Institute of Geology and Mineral Resources thereof, [2] Zhengzhou mineral resources comprehensive utilization institute, [periodical name] Chinese powder industry .2005 (4) .-34-37[digest] Coaseries kaolin is Chinese distinctive kaolin resource, through technologies such as superfine grinding, calcining, surface modifications, can be used as the filler of high performance cable sizing material, filling properties is significantly improved.

8, surface modification of [autograph] recessed soil and application [author] the Qian Yunhua gold leaf tinkling of pieces of jade [mechanism] the Huaiyingong College chemical industry in galosh face glue thereof system, [periodical name] nonmetalliferous ore .2005,28 (1) .-17-18, the 43[digest] with stearic acid attapulgite clay (recessed soil) is carried out modification, the top condition of modification is that stearic acid dosage is 2%, modification temperature is that 80 ℃, modification time are 30min, and the activation index of gained modified attapulgite reaches 0.95.The filling test of modified attapulgite in galosh face glue shows that modified attapulgite can substitute fine particle calcium carbonate fully.

9, preliminary study [author] Liu Zhuo of [autograph] nano kaoline surface modification admire PiZhenBang Tian Xike [mechanism] China University of Geosciences's Materials science and chemical engineering institute, [periodical name] chemical industry mineral and processing .2005,34 (5) .-18-20[digests] with different properties-correcting agent nano kaoline has been carried out surface treatment, inquired into the mechanism of action that the tensio-active agent adding raises activation index when modification.Infrared analysis shows: particle surface has really joined coupling agent molecule; The filled rubber test shows: composite modified nano kaoline has good reinforcing effect.

10, [autograph] appositional pattern calcined kaolin surface modification and application test research [author] Liu Xin Haili one ripple [mechanism] Zhengzhou Institute of Multipurpose Utilization of Mineral Resources, CAGS, [periodical name] Chinese powder technology .2005,11 (2) .-6-8[digests] appositional pattern kaolin is Chinese distinctive kaolin resource.Application test proves that appositional pattern kaolin is after superfine grinding, calcining, ultra-fine ore grinding and silane coupling agent surface treatment, and as the filler of high performance cable sizing material, filling properties is significantly improved.

11, the modification of [autograph] activation of bentonite and application [author] Zhao Liying in rubber, the mineral products comprehensive utilization .2004 (2) of Jiang Yinshan [mechanism] Jilin University [periodical name] .-23-27[digest] the method activated bentonite that adopts thermal treatment to combine with mechanical-chemical modification, can prepare rubber-reinforcing filler.The fugitive constituent and the combination water of mineral can be effectively driven away in thermal treatment, and the activation structure guarantees and raising dry process mechanical force and chemical surface modification effect, makes the properties-correcting agent consumption just can obtain desirable index below 1%.The wilkinite that adopts this kind method to make substitutes the semi-reinforcing hydrocarbon black amount and reaches 30%, and the every physicals of rubber item meets standard GB 3778-94; 100% substitutes high abrasion furnace black(HAF), and the rubber mechanical property satisfies the GB318-98 technical requirements.

12, [autograph] kaolin Research on Surface Modification progress [author] king Xu Hailu rising sun morning [mechanism] Chinese Academy Of Sciences Process Engineering Research Institute's energy and investigation of materials center, [periodical name] chemical industry mineral and processing .2004,33 (3) .-1-3, the 10[digest] summarized the present Research of kaolin surface modification and the purposes of modified kaolin, research direction has from now on been proposed.

13, Chinese patent, application (patent) number: 200480036156.X, title: preparation contains method application (patent right) people of kaolinic rubber composition: Dow Corning Corp., address: Michigan, United States invention (design) people: MG Procktor; Taylor RM enters date: the 2006.06.05 of country summary: a kind of kaolinic rubber composition that contains processing, and said composition is made up of following basically: organopolysiloxane, the kaolin of processing; Solidifying agent; With the optional additive that is selected from one or more rheology modifiers, pigment, tinting material, antiadhesives, softening agent, adhesion promotor, whipping agent, fire retardant and the siccative.Said composition is substantially free of reinforcing filler.These are final contain kaolinic rubber composition can be used for such as the siloxanes section bar extrude, wire rod and cable coating, glass assembling and be used for the purposes of structure packing ring.

14, Chinese patent, application (patent) number: 200410047914.X, title: decoration of exterior wall is with fluorocarbon coating and manufacture method applicant: China National Petroleum Corporation (CNPC); China Petroleum Group Engineering and Technology Research Institute, address: No. 6, Liupukang, Xicheng District, Beijing City, summary: the present invention relates to a kind of decoration of exterior wall with fluorocarbon coating and manufacture method, by vinylidene fluoride water-based fluorine emulsion, Natvosol, poly carboxylic acid sodium, alkylphenol polyoxyethylene, polyether-modified dimethyl polysiloxane, 2-amino-2-methyl-1-propanol, titanium dioxide, talcum powder, kaolin, 2,2,4-trimethylammonium-1, the 3-pentanediol mono isobutyrate, sodium polyacrylate, polyurethane-modified polyethers, the aerosil powder is through certain heating, stir, grinding is made.Characteristics with environmental protection ambient cure, it is filmed and has good weathering resistance, solvent resistance and contamination resistance.

Recognize from above-mentioned open source literature, adopt properties-correcting agent that nonmetalliferous ore soil is carried out modification, can make itself and other macromolecular material have good consistency, can shorten the mixture mixing time, also can significantly improve tensile strength, tensile modulus, elongation at break and the adhesion strength etc. of materials such as filled plastics, rubber, paper, coating, cable.But in the existing document not about common soil (for example common yellow mud, common red soil, common black mud or common white clay) being carried out be used for after the modification report of polymer mineral filler.

Elastomer product comprises elastic sports floor, flexibly wall brick, synthetic leather etc.Present being seen elastomer product is mainly rubber and thermoplastic elastomer.The major defect that rubber exists is to distribute toxic and harmful in the sulfidation, and environment is produced detrimentally affect.Thermoplastic elastomer has the physical and mechanical properties of vulcanized rubber and the performance of technical process of nonrigid plastic, but its thermotolerance is not so good as rubber, and along with temperature rises, rerum natura declines by a big margin, thereby the scope of application is restricted.Simultaneously, compression set, rebound resilience, that weather resistance is equal to rubber phase is poor, also often is higher than similar rubber on the price.Above elastomerics is very big to the dependence of Chemicals, promptly uses mineral filler to reduce cost, and the content of its mineral filler is not higher than 60% yet.

Having some documents to mention employing in recent years is that raw material is made elastomer material with the acrylate, for example:

1, virgin fast tinkling of pieces of jade Li Yuan friend's Zhang Xinghua [mechanism] Guangdong University of Technology's material of the preparation of [autograph] butyl acrylate copolymer elastomer and performance study [author] thereof and energy institute, [periodical name] Guangdong rubber .2004 (7) .-2-4[digest] this paper synthesized the butyl acrylate elastomer material, and adding vinyl cyanide and vinylformic acid is that comonomer carries out modification.The hardness and the second-order transition temperature of product have been tested.The result shows: under butyl acrylate and vinylformic acid and acrylonitrile compolymer, along with vinyl cyanide and acrylic acid content increase, the hardness of polymkeric substance and second-order transition temperature also increase with it, and wherein vinylformic acid is more obvious to the effect that hardness improves.

2, [autograph] anti-phase concentrated emulsion method prepares porous polypropylene acid butyl ester elastomer material [author] Chen Hong Du Zhongjie in beautiful morning and encourages preparation of Hang Quan [mechanism] Beijing University of Chemical Technology Beijing's novel high polymer material and processing key lab, [periodical name] China Synthetic Rubber Industry .2006,29 (3) .-186-188[digests] be monomer with the butyl acrylate.Vinylstyrene is a linking agent.Diisopropyl azodicarboxylate is an initiator, sorbitan monooleate is an emulsifying agent, water is disperse phase, polyacrylic acid fourth aigret (PBA) elastomer material that has prepared abscess type structure with anti-phase concentrated emulsion method, investigated the influence of polymeric reaction temperature, emulsifying agent consumption, disperse phase volume fraction, and foam structure has been characterized by scanning electron microscope to PBA elastomer material foam structure.The result shows that polymeric reaction temperature should be controlled to be 50～60 ℃; Along with the emulsifying agent massfraction is increased to 30% from 10%, the elastomeric aperture of PBA reduces gradually, and the number of channels between abscess increases; Along with the increase of disperse phase volume fraction, the cell diameter of PBA elastomer material and channel diameter speed are cumulative big, and porosity increases, and density reduces.

The disclosed acrylic ester copolymer elastomerics of above-mentioned document has solved the part weak point of rubber and thermoplastic elastomer existence, and the Application Areas of novel material is provided.But with the acrylic ester copolymer elastomerics apply to industry and daily life yet there are no report; ACRYLIC EMULSION multipolymer and modifying common soil are combined into resilient material not to appear in the newspapers yet.

Summary of the invention

The objective of the invention is to overcome the shortcoming that prior art exists, a kind of method of modifying common soil is provided, reaching with modifying common soil, acrylic acid emulsion copolymers is the manufacture method of the composite mud elastic product of main material production.This composite mud elastic product is all nonhazardous gas volatilizations in whole production, use.Its compression deformation rate, rebound resilience, weather resistance can both meet or exceed the performance of rubber.30%-80% is an earth in its finished product, is the elastic face material of a kind of low cost, high-performance, environmental protection.

In the technical scheme of the present invention, the common soil modification of the first step is achieved in that

The earth drying, pulverize, sieve, remove sandstone, foreign material, the mud powder; Perhaps add water and mix, sieve and make mud, drying, pulverizing again gets the mud powder.Then the common soil powder is carried out dynamic heat, under its at a high speed dynamic situation, add surface-modifying agent, drying obtains modification earth.

The mechanism of common soil modification of the present invention is: utilize the surface chemistry method, functional group in the organic molecule is produced absorption or chemical reaction at the common soil particle surface, its particle surface is coated, make the surface organic of common soil, the original physico-chemical property in common soil surface is changed, reach the purpose of modification.Common soil powder through surface modification is distributed in the organic polymer material, makes to produce a kind of " molecule bridge " with specific function between common soil particle and organic polymer, and the effect of this " bridge " depends primarily on surface-modifying agent.The preparation method of the common soil particle surface modifier that the present invention adopts is: coupling agent, polysiloxane, organosilicon are mixed stirring with the emulsified body and the water of fatty amine, promptly get common soil surface-modifying agent of the present invention.

The composition and the mass content of described common soil surface-modifying agent are as follows:

Coupling agent 0.6-6 part;

Polysiloxane 1-12 part with reactive functional groups;

Emulsified body 0-2 part of organosilicon and fatty amine;

All the other are water.

Above-described coupling agent is selected silane coupling agent for use, for example the modified amido silane coupling agent, contain the silane coupling agent of peroxy, silane coupling agent with diazonium and nitrine structure, its molecular formula is RsiXn, wherein Xn is a hydrolysising group, generally be alkoxyl group, generate SiOH after this class group hydrolysis.

The used silane coupling agent of the present invention can be following kind:

Above-described polysiloxane with reactive functional groups comprise hydroxyl alkyl polysiloxane, carboxyl polysiloxane, dimethyl siloxane or cyclohexyl methyl siloxanes derivative and modifier, polysiloxane polyether copolymer, contain the polysiloxane of vinyl or epoxide group, polydimethylsiloxane (PDMS), poly-propyl group methylsiloxane (PPMS), poly-octyl group methylsiloxane (POMS) and polyphenyl methyl siloxane (PPhMS) etc.

Research to Functional Organic Polysiloxane mainly is from macromolecular molecule synthesis design in recent years, with anionic ring-opening polymerization method or condensation polymerization, adopt the synthetic organopolysiloxane of organosilane monomer that has functional groups or have special construction with specific function, controlled architecture.From the synthetic organopolysiloxane that has controlled microcosmic molecule and condensed state structure and have functional functional group of the relation of polymer architecture and performance.

As everyone knows, polysiloxane has organic and two-fold advantage inorganic materials concurrently, for example (,) Heat stability is good, second-order transition temperature is low, ventilation property is high, dielectricity is good, with good biocompatibility and special surface property.Yet a little less than the Intermolecular Forces of polysiloxane, when using as a kind of exotic materials, mechanical property is poor, has limited its range of application to a certain extent.Active group is introduced the siloxanes segment as side group or end group, make it to become reactive polysiloxanes; With the block or the graft copolymer of other polymer formation polysiloxane, be the effective means that improves the polysiloxane mechanical property and the advantage of polysiloxane is brought into other polymkeric substance again.

The characteristics that the common soil particle has surface energy height, hydrophilic oleophobic, very easily reunites are difficult to homodisperse in the polymer of nonpolar or low-pole, these feature limits its application in polymer, therefore must carry out surface modification to it.With polysiloxane-modified purpose is to make the common soil particle surface coat the last layer organism, improve the consistency and the bonding force of common soil and macromolecule matrix, thereby reach the purpose that improves the Polymer Physics performance, reduces production costs, the present invention adopts silane coupling agent that common soil is carried out modification.Compare with the unmodified common soil of filling, filling silane coupler modified its hardness of argillous matrix material, stress at definite elongation and tear strength increases, thereby slow down or stop crackle or breach in the material when stressed, to enlarge cracking, silane coupling agent makes the common soil surface organic, has improved the dispersiveness of common soil in matrix.

The emulsified body of above-described organosilicon and fatty amine can select for use carboxylic acid and amido substituted silane to carry out fatty amide alkyl silane, fatty amide alkyltrialkoxysilaneand of condensation etc.

The surface-modifying agent that the present invention joins can produce the chemical physics reaction with the common soil particle surface, forms hydrogen bond, and is condensed into covalent linkage.Because hydrogen bond and covalent linkage are more than the strong interface interaction power of Van der Waals force, and the total bond energy in interface between this surface-modifying agent and common soil powder exceeds the physical adsorption of single purity, so presents there is very strong sticking power at common soil powder interface.The mutual condensation of each intermolecular SiOH of silane during this period, copolymerization forms cancellated film, covers common soil powder granule surface, and exposes the functional group that the R reactive behavior is arranged.These reactive functional can with organic polymer material generation bonding action, make common soil can and the organic polymer base-material between produce strong crosslinkedly, form firm chemical bond.

Common soil particle surface modification method of the present invention is as follows:

Prescription: surface-modifying agent 15%-50%, common mud powder 50%-85%.

The manufacture method of common mud powder: earth can adopt common yellow mud, red soil, black mud or white clay etc.Earth drying, pulverizing, mistake 100-800 mesh sieve are removed stone, gravel and foreign material, get the mud powder; Perhaps add water and mix, cross the 100-800 mesh sieve and make mud, drying, pulverizing again gets the mud powder.

The method of modifying of common mud powder:, it is carried out surface modification according to the mechanism of common soil powder surface modification.At first, the common soil particle is carried out dynamic heat, after certain temperature (80 ℃-130 ℃), add above-mentioned surface-modifying agent, preferably add with atomization.In surface-modifying agent and common soil reaction process, temperature should remain in 100 ℃.Under the high speed dynamic situation, the hold-time should be at 2～6min.Differential responses time common mud powder surface active degree will have difference.

The common soil after the modification and the bridging property of organic polymer material have had improvement, and dispersiveness is greatly improved, and the free area that bears external load has obtained increase, the mechanical property of organic polymer material goods are enhanced, functional significantly improving.Modifying common soil can be widely used in industries such as plastics, rubber, coating.Modifying common soil of the present invention is mainly used in and makes the composite mud elastic product.

The composite mud elastic product of manufacturing of the present invention mainly comprises: elastic sports floor (for example surfacing material in places such as runway, basketball field, volleyball court, tennis court, table tennis court, swimming pool and recreation ground), flexibly wall brick, synthetic leather etc.We have also reported some elastic sports floors in the open source literature that retrieves, wall brick flexibly, elastomer products such as synthetic leather, the urethane of adding respectively that has, polyethylene, polyvinyl chloride, synthetic rubber, nylon, materials such as Resins, epoxy, the solution that has the shortcoming of distributing toxic and harmful in the vulcanization of rubber process, the solution that has the partial properties weak point that exists of rubber and thermoplastic elastomer, the Application Areas of novel material is provided, but also the ubiquity cost is higher for present elastomer product, the product instability, easily bubble, come unstuck, layering, can not recycling, use problems such as extensive not enough.

Common soil after modification can with very strong crosslinked of water-soluble acrylic acid emulsion copolymerization deposits yields, form the long-chain network structure polymer, its physical and chemical performance is highly stable.The elastomer product that the present invention adopts common soil after the modification and acrylic acid emulsion copolymers to make, as elastic sports floor, flexibly wall brick, synthetic leather etc. can overcome the deficiencies in the prior art part, cost is low, physical and chemical performance is stable excellent, more ageing-resistant.

Application in elastomer product describes with regard to modifying common soil below.

The modifying common soil particle has good intensity and elasticity through the elastomer material that acrylic acid emulsion copolymers interlinkage generates.

The present invention passes through to add some auxiliary agents, simultaneously, and by the control mold temperature, and then every performance index of regulation and control goods.

Wherein the parts by weight of each component are as follows:

Modifying common soil 30-80

ACRYLIC EMULSION multipolymer 20-70

Flexibility agent 0-8

Antifreezing agent 0-10

Whipping agent 0-12

Defoamer 0-2

Tinting material 0-6

Water 0-20

The combination of one or more below described acrylic acid emulsion copolymers adopts: 1, methyl acrylate (MA); 2, ethyl propenoate (EA); 3, butyl acrylate (n-BA); 4, ethyl acrylate (Octyl acrylate, 2-EHA); 5, synthetic (styrene-butadiene emulsion) and natural polymer mixed emulsion, 6, acrylic ester high molecular type copolymer emulsion; 7, polyethyl acrylate, butyl polyacrylate, hydroxymethyl acrylamide copolymer; 8, selfing chain acrylate copolymer emulsion (unreacted monomer≤1%); 9, negatively charged ion, nonionic phenotype are from interlinkage acrylate copolymer emulsion (unreacted monomer≤0.5%); 10, the multi-copolymerization emulsion of the acrylate copolymer of tool reactive group; 11, the compound of polyacrylic ester, its main component structure is:

12, compound emulsification system acrylic acid esters co-polymer, its chemical structure is:

13, methyl methacrylate, butyl acrylate, acrylamide ternary copolymer emulsion; 14, butyl acrylate and acrylonitrile copolymer emulsion; 15, the copolymer emulsion of all acrylic ester class; 16, the copolymerized macromolecule compound of vinylformic acid and ester thereof, main component structure is:

R is CH ₃Or C ₂H ₅, C ₄H ₃,

ACRYLIC EMULSION multipolymer of the present invention adopts the commercially available prod, is generally the water-soluble emulsion class, and its solid content requires between 30-50% weight.

Described flexibility agent is mainly used in the elasticity that improves compound mud, regulate its pliability, improve sense of touch, can adopt the general flexibility agent of chemical field, for example the emulsified body of organosilicon and fatty amine, organosilicon emulsion, polysiloxane, two carboxylic acid amide derivative, octadecyl ethylene urea, quaternary sun lotus property promoting agent with reactive functional groups.

Described antifreezing agent is ethyleneamines (ethyleneamines) or quadrol (1,2-2 ethylamine, a kind of water white thick liquid), ethylene glycol and derivative thereof, water-soluble amide and calcium chloride.

The effect of described whipping agent is to make compound mud resilient material produce trickle unicellular structure.Used whipping agent is p-toluene sulfonyl hydrazide, diimide diformamide, azodicarboamide (ADC), dibenzoyl peroxide (BPO) etc.

Described defoamer adopts propanediol polyoxypropylene Soxylat A 25-7 (high molecular type surfactant), polyoxypropylene glyceryl ether, can make mud apply or spraying process in, can eliminate foam effectively, with the density that improves the finished product internal surface, stop abscess.

Described tinting material can select for use the water-based color paste of printing coating black, red, yellow, blue, green, perhaps water miscible inorganic, pigment dyestuff, as other series inorganic pigments such as carbon black, chromium titan yellow, chromium nickel yellow, molybdenum red, Sudan red, ultramarine blue, zirconium system, cobalt series pigments, also can use pigment dyestuff, for example azo pigment, phthalocyanine pigment and heterocycle pigment etc.Fine pigments such as high-weatherability Rutile type Titanium Dioxide, phthalocyanine blue and high temperature resistant coating chrome yellow wherein, product has the raw material guarantee at home, also can be widely used in painted fields such as paint, printing ink, plastics, rubber item, leatheroid.

Selecting for use of whipping agent, antifreezing agent, defoamer, tinting material is particular case according to product.The product requirement elasticity that has is big, as elastic sports floor, needs to add whipping agent to improve the elasticity of product; For making exterior product, add a certain amount of antifreezing agent in the material, can resist subzero 25 ℃ low temperature in winter; The synthetic leather that has need add defoamer makes its inside durable, surface-brightening; The product needed that has is added tinting material makes its color rich and varied.

The elastomer material that above-mentioned common soil is made after modification, multiple product be can produce, elastic sports floor (comprising the employed elastic planking materials of playground such as runway, basketball field, volleyball court, tennis court, table tennis court, swimming pool and recreation ground), flexibly wall brick, synthetic leather etc. for example made.

Below narrate the production method of several typical products of the present invention respectively.

One, elastic sports floor:

(1) modification earth, acrylic acid emulsion copolymers, (adding according to different product function needs) tinting material, flexibility agent, whipping agent, antifreezing agent, water etc. are carried out mechanically mixing, make it become uniform composite sludge;

(2) the gained composite sludge is coated on the template, baking constant temperature is 280 ℃ (± 80 ℃), and after moisture content volatilization was done, molding formed the elastic sports floor of all size, and the surface pattern that institute becomes product is determined by the texture of template.This product can be made the indoor and outdoor elastic sports floor, for example the surface layer of runway, basketball field, tennis court, squash court, court, table tennis court, volleyball court and other athletic ground and children's territory, safety movement place, swimming pool, amusement venue etc.

Two, wall brick flexibly:

(1) modification earth, acrylic acid emulsion copolymers, (adding according to different product function needs) tinting material, softening agent, whipping agent, antifreezing agent, water etc. are carried out mechanically mixing, make it become uniform composite sludge;

(2) the gained composite sludge is coated on the template, baking constant temperature is 280 ℃ (± 80 ℃), after the moisture content volatilization is done, molding, become flexibly wall brick, become product surface pattern by the texture decision of template, for example can be made into the indoor nonlocal wall brick of different texture such as wood grain, bag, dermatoglyph, porcelain facing.

Three, compound mud leather:

(1) modification earth, acrylic acid emulsion copolymers, (adding according to different product function needs) tinting material, softening agent, antifreezing agent, defoamer, water etc. are carried out mechanically mixing, make it become uniform composite sludge;

(2) the compound mud leather of no base cloth: the gained composite sludge is coated on the template that has decorative pattern or shiny surface, and thickness is 0.15mm to 3.0mm, and storing temperature is 80 ℃-285 ℃, until conjunctiva after the polishing back side, molding is cut edge, and produces the compound mud leather of no base cloth.The compound mud leather that base cloth is arranged: 1. composite sludge is coated on the template that has decorative pattern or shiny surface, thickness is 0.15mm to 3.0mm, and storing temperature is 80 ℃-285 ℃, fit behind conjunctiva base cloth, side cut; 2. composite sludge is coated on the base cloth, thickness is 0.15mm to 3.0mm, and storing temperature is 80 ℃-285 ℃, until conjunctiva, extrudes required decorative pattern on preheating or the embossing machine that is not preheated.

Advantage of the present invention:

The modifying common soil composite elastic runway plane materiel that present method is produced, every performance index such as its tensile strength, elongation at break, shock absorption, vertical deformation reach International Track and Field Association's runway standard fully.

Modifying common soil composite elastic court plane materiel that present method is produced and swimming pool, recreation ground plane materiel, its mechanical index can reach german standard din.

The modifying common soil that present method is produced is wall brick flexibly, its protection against the tide, anti-skidding, not yielding, fire-retardant, sense of touch is pliable and tough, more ageing-resistant, and cost is low.

The compound mud leather of modifying common soil that present method is produced is good springiness, anti-tear drawing not only, and cost is low, good permeability, fire-retardant, more ageing-resistant, uvioresistant.

The modifying common soil compound elastomer product that present method is produced water-soluble because additive therefor is, produces, mat formation, nonhazardous gas and organic solvent volatilization in the use, to the unusual close friend of environment.

The modifying common soil compound elastomer product that present method is produced utilizes the true qualities of mud, adds a small amount of paint-printing colour size as required and mixes colours, forms various also under intensive ultraviolet, shine for a long time not can variable color color variety.

The modifying common soil compound elastomer product that present method is produced, main raw material(s) is an earth, and is good with the water compatibility, and than great, heavy rain is met in the back of mating formation does not also have the foaming and the phenomenon that arches upward.

The modifying common soil compound elastomer product main raw material(s) that present method is produced is earth and acrylic polymer, is exposed to the sun at burning sun and also can not distribute poisonous and hazardous foreign odor flavor down, and more ageing-resistant, be easy to safeguard recyclable utilization again.

But the modifying common soil compound elastomer product once shaped that present method is produced, the material unanimity can not produce delamination, threshing phenomenon from bottom to top.

Description of drawings

Fig. 1 is a common soil surface modification technology synoptic diagram of the present invention.

Fig. 2 is a modifying common soil compound elastomer product structural representation of the present invention.

As shown in Figure 1: surface modification technology is that the common soil powder is carried out dynamic heat, under its at a high speed dynamic situation, adds above-mentioned surface modifier, and drying obtains modification earth.

As shown in Figure 2: the modifying common soil compound elastomer product can be bound up earth equably by the effect of acrylic emulsion copolymer, softening agent etc., and physical and chemical performance is highly stable. Among the figure, the 1st, mud particles, the 2nd, take the acrylic emulsion copolymer as main crosslinking agent.

Embodiment

Below by embodiment the present invention is specifically described; be necessary to be pointed out that at this present embodiment can only further specify the present invention; can not be interpreted as limiting the scope of the invention, those skilled in the art can make some nonessential improvement and adjustment to the present invention according to foregoing.

Embodiment 1

Gather clean red soil, drying, pulverizing, mistake 100-800 mesh sieve are removed stone, gravel and foreign material, get the mud powder; Perhaps earth adds the water mixing, crosses the 100-800 mesh sieve and makes mud, and drying, pulverizing again gets the mud powder.Surface-modifying agent is selected 1 part of silane coupling agent vinyl trichlorosilane for use, and the polysiloxane with reactive functional groups adopts and contains-(CH ₂) the hydroxyl alkyl polysiloxane 3 (weight) part of n OH, fatty amide alkyl silane 1 (weight) part adds 96 (weight) part water and stirs and obtain surface-modifying agent; At first, the red soil powder is carried out dynamically (fluidized-bed) heating, during temperature to 80 ℃-130 ℃, under its at a high speed dynamic situation,, 30 (weight) part surface-modifying agent is added in the red soil powder with atomization according to the weight of 70 parts of red soil, should remain between 80-130 ℃, continuation is seethed with excitement at fluidized-bed, and the hold-time obtained surface modification earth powder at 2～6 minutes.

Embodiment 2

Gather clean yellow mud, drying, pulverizing, mistake 100-800 mesh sieve are removed stone, gravel and foreign material, get the mud powder; Perhaps earth adds the water mixing, crosses the 100-800 mesh sieve and makes mud, and drying, pulverizing again gets the mud powder.Surface-modifying agent is selected silane coupling agent β-(3 for use, the 4-epoxycyclohexyl) ethyl trimethoxy silane 2 (weight) part, polysiloxane with reactive functional groups adopts and to contain-(CH2) the hydroxyl alkyl polysiloxane 5 (weight) part of 3OCH (OH) CH2OH, fatty amide alkyl silane 0.5 (weight) part adds 92.5 parts of water stirrings and obtains surface-modifying agent; At first, the yellow mud powder is carried out dynamically (fluidized-bed) heating, during to 80 ℃-130 ℃ of temperature, under its at a high speed dynamic situation,, 20 (weight) part surface-modifying agent is added in the red soil powder with atomization according to the weight of 80 parts of yellow mud powder, should remain between 80-130 ℃, continuation is seethed with excitement at fluidized-bed, and the hold-time obtained surface modification yellow soil powder at 2～6 minutes.

Embodiment 3

Gather clean white clay, add water and mix, cross the 100-800 mesh sieve and make mud, drying, pulverizing again gets the mud powder; Perhaps earth adds the water mixing, crosses the 100-800 mesh sieve and makes mud, and drying, pulverizing again gets the mud powder.Surface-modifying agent is selected silane coupling agent 3-(methacryloxy) propyl trimethoxy silicane 0.8 (weight) part for use, polysiloxane with reactive functional groups adopts carboxyl polysiloxane 6 (weight) part, fatty amide alkyltrialkoxysilaneand 0.7 (weight) part adds 92.5 parts of water stirrings and obtains surface-modifying agent; At first, white clay is carried out dynamically (fluidized-bed) heating, during to 80 ℃-130 ℃ of temperature, under its at a high speed dynamic situation,, 20 (weight) part surface-modifying agent is added in the white clay powder with atomization according to the weight of 80 parts of white clay powder, should remain between 80-130 ℃, continuation is seethed with excitement at fluidized-bed, and the hold-time obtained surface modification white clay soil powder at 2～6 minutes.

Embodiment 4

Gather clean white clay, drying, pulverizing, mistake 100-800 mesh sieve are removed stone, gravel and foreign material, get the mud powder; Perhaps earth adds the water mixing, crosses the 100-800 mesh sieve and makes mud, and drying, pulverizing again gets the mud powder.Surface-modifying agent is selected silane coupling agent 3-(acryloxy) propyl trimethoxy silicane 2.5 (weight) part for use, polysiloxane with reactive functional groups adopts poly-octyl group methylsiloxane (POMS) 2 (weight) part, fatty amide alkyltrialkoxysilaneand 2 (weight) part adds 93.5 parts of water stirrings and obtains surface-modifying agent; At first, white clay is carried out dynamically (fluidized-bed) heating, during to 80 ℃-130 ℃ of temperature, under its at a high speed dynamic situation,, 50 (weight) part surface-modifying agent is added in the white clay powder with atomization according to the weight of 50 parts of white claies, should remain between 80-130 ℃, continuation is seethed with excitement at fluidized-bed, and the hold-time obtained surface modification earth powder at 2～6 minutes.

Embodiment 5

Gather clean black mud, drying, pulverizing, mistake 100-800 mesh sieve are removed stone, gravel and foreign material, get the mud powder; Perhaps earth adds the water mixing, crosses the 100-800 mesh sieve and makes mud, and drying, pulverizing again gets the mud powder.Surface-modifying agent is selected amino third Trimethoxy silane 1 (weight) part of silane coupling agent 3-for use, polysiloxane with reactive functional groups adopts polyphenyl methyl siloxane (PPhMS) 7 (weight) part, fatty amide alkyltrialkoxysilaneand 1 (weight) part adds 91 parts of water stirrings and obtains surface-modifying agent; At first, the black mud powder is carried out dynamically (fluidized-bed) heating, during to 80 ℃-130 ℃ of temperature, under its at a high speed dynamic situation,, 25 (weight) part surface-modifying agent is added in the black mud powder with atomization according to the weight of 75 parts of black mud powder, should remain between 80-130 ℃, continuation is seethed with excitement at fluidized-bed, and the hold-time obtained surface modification earth powder at 2～6 minutes.

Embodiment 6

Gather clean black mud, drying, pulverizing, mistake 100-800 mesh sieve are removed stone, gravel and foreign material, get the mud powder; Perhaps earth adds the water mixing, crosses the 100-800 mesh sieve and makes mud, and drying, pulverizing again gets the mud powder.Surface-modifying agent is selected 3-(acryloxy) propyl trimethoxy silicane coupling agent 1 (weight) part for use, fatty amide alkyltrialkoxysilaneand coupling agent 5 (weight) part, polydimethylsiloxane (PDMS) 4 (weight) part, 1 part of fatty amide alkyltrialkoxysilaneand adds 89 parts of water stirrings and obtains surface-modifying agent; At first, the black mud powder is carried out dynamically (fluidized-bed) heating, during to temperature (80 ℃-100 ℃), under its at a high speed dynamic situation,, 30 (weight) part surface-modifying agent is added in the black mud powder with atomization according to the weight of 70 parts of black mud powder, should remain between 80-100 ℃, continuation is seethed with excitement at fluidized-bed, and the hold-time obtained surface modification earth powder at 2～6 minutes.

Embodiment 7:

The modification yellow mud powder 56% of embodiment 1-6, acrylic ester high molecular type copolymer emulsion 44%, mechanically mixing makes it become uniform composite sludge; Mud is coated on the template that has sheepskin line or crocodile dermatoglyph, and coating thickness is 2mm, and molding after 280 ° of C (± 80 ℃) oven dry obtains flexibly wall brick product of sheepskin line or crocodile dermatoglyph yellow.Need to produce the flexibly wall brick product of different colours, add corresponding mill base or toner in mud, adopt identical method to make.Need to produce the flexibly wall brick product of different thickness, the increase and decrease coating thickness gets final product.Need to produce the flexibly wall brick product of different surfaces decorative pattern, change template and get final product.

Embodiment 8:

The modified white clay powder 50% of embodiment 1-6, polyethyl acrylate, butyl polyacrylate, hydroxymethyl acrylamide copolymer 42%, ethyleneamines antifreezing agent 4%, paint-printing colour size brown 1%, the emulsified body flexibility agent 3% of organosilicon and fatty amine, mechanically mixing makes it become uniform composite sludge; Mud is coated on the template that has bag or wood grain, and coating thickness is 6mm, and molding after 280 ℃ (± 80 ℃) oven dry obtains the flexibly wall brick product of brown bag or wood grain.Need to produce the bag of different thickness or the flexibly wall brick of wood grain, the increase and decrease coating thickness gets final product.Need the bag of other color or the flexibly wall brick of wood grain, add corresponding mill base or toner in mud, adopt identical method to make.Need to produce the brown ground wall brick of different surfaces decorative pattern, change template and get final product.

Embodiment 9:

The modification yellow mud powder 47% of embodiment 1-6, butyl acrylate (n-BA) and ethyl acrylate (Octyl acrylate, 2-EHA) multipolymer 46%, ethyleneamines antifreezing agent 3%, have the flexibility agent 4% of the polysiloxane of reactive functional groups, mechanically mixing makes it become uniform composite sludge; Mud is coated on the template that has bag or wood grain, and coating thickness is 5mm, and molding after 280 ℃ (± 80 ℃) oven dry obtains flexibly wall brick product of bag or wood grain yellow.The bag of needs production different thickness or wood grain be wall brick flexibly, and the increase and decrease coating thickness gets final product.Need flexibly wall brick of the bag of other color or wood grain, add corresponding mill base or toner in mud, adopt identical method to make.Need to produce the yellow ground wall brick of different surfaces decorative pattern, change template and get final product.

Embodiment 10:

The modification yellow mud powder 71% of embodiment 1-6, acrylic ester high molecular type copolymer emulsion 20%, water 9%, mechanically mixing stirs into uniform composite sludge.Composite sludge is coated on the template that has woven design or wood grain or bag, and coating thickness is 1.6mm, and baking constant temperature is 280 ℃ (± 80 ℃), after the moisture content volatilization is done, and molding, forming thickness is yellow woven design or wood grain or the compound mud ground wal ceramic tile of bag of 1.6mm.Need to produce woven design or the wood grain or the bag ground wall brick of different thickness, the increase and decrease coating thickness gets final product.Need the woven design of production same thickness different colours or the compound mud ground wal ceramic tile of wood grain or bag, add corresponding mill base or toner in mud, adopt identical method to make.

Embodiment 11:

The modified white clay powder 50% of embodiment 1-6, selfing chain acrylate copolymer emulsion (unreacted monomer≤1%) 50%, mechanically mixing stirs into uniform white composite sludge.Composite sludge is coated on the template that has decorative pattern, and coating thickness is 8mm, and baking constant temperature is 280 ℃ (± 80 ℃), after moisture content volatilizes, and molding, forming thickness is the compound mud ground wal ceramic tile of white decorative pattern of 8mm.Need to produce the decorative pattern ground wall brick of different thickness, the increase and decrease coating thickness gets final product.The compound mud ground wal ceramic tile that needs the decorative pattern of production same thickness different colours adds corresponding mill base or toner in mud, adopts identical method to make.

Embodiment 12:

The modification black mud powder 35% of embodiment 1-6, the compound 65% of polyacrylic ester, mechanically mixing stirs into uniform black composite sludge.Composite sludge is coated on the template that has decorative pattern, and coating thickness is 2mm, and baking constant temperature is 280 ℃ (± 80 ℃), after the moisture content volatilization is done, and molding, forming thickness is the compound mud ground wal ceramic tile of black decorative pattern of 2mm.Need to produce the decorative pattern ground wall brick of different thickness, the increase and decrease coating thickness gets final product.The compound mud ground wal ceramic tile that needs the flower of production same thickness different colours is changed corresponding mill base of interpolation or toner in mud, adopts identical method to make.

Embodiment 13:

The modification yellow mud powder 35% of embodiment 1-6, compound emulsification system acrylic acid esters co-polymer 60%, ethyleneamines (ethyleneamines) antifreezing agent 5%, mechanically mixing stirs into uniform composite sludge.It is 1.22 meters that composite sludge is coated on width, and length is that coating thickness is 13mm on 22 meters the runway template that has ridge design, baking constant temperature is 280 ℃ (± 80 ℃), after the moisture content volatilization is done, molding, the formation specification is the yellow compound mud elasticity runway plane materiel of 1.22m * 22m * 13mm.Need to produce the yellow compound mud elasticity runway plane materiel of different size, change template and get final product.Need to produce the compound mud elasticity runway plane materiel of different colours, add corresponding mill base or toner in mud, adopt identical method to make.

Embodiment 14:

The modification red soil powder 54% of embodiment 1-6, the multi-copolymerization emulsion 35% of the acrylate copolymer of tool reactive group, paint-printing colour size bright red 2%, ethyleneamines antifreezing agent 3%, have the flexibility agent 6% of the polysiloxane of reactive functional groups, mechanically mixing stirs into uniform yellow composite sludge.It is 2.44 meters that composite sludge is coated on width, and length is that coating thickness is 13mm on 12 meters the runway template that has ridge design, baking constant temperature is 280 ℃ (± 80 ℃), after the moisture content volatilization is done, molding, the formation specification is the red compound mud elasticity runway plane materiel of 2.44m * 12m * 13mm.Need to produce the red compound mud elasticity runway plane materiel of different size, change template and get final product.Need to produce the compound mud elasticity runway plane materiel of different colours, add corresponding mill base or toner in mud, adopt identical method to make.

Embodiment 15:

The modified white clay powder 38% of embodiment 1-6, synthetic (styrene-butadiene emulsion) and natural polymer mixed emulsion 56%, paint-printing colour size indigo plant or ultramarine blue toner 1%, ethylene glycol and derivative antifreezing agent 4% thereof, two carboxylic acid amide derivative flexibility agents 1%, mechanically mixing stir into uniform blue composite sludge.Composite sludge is coated on the runway template that has ridge design, and coating thickness is 16mm, and baking constant temperature is 280 ℃ (± 80 ℃), and after the moisture content volatilization was done, molding formed blue compound mud elasticity runway plane materiel.Need to produce the compound mud elasticity runway plane materiel of different thickness, the increase and decrease coating thickness gets final product.Need the compound mud elasticity runway plane materiel of production same thickness different colours, add corresponding mill base or toner in mud, adopt identical method to make.Its plane materiel specification is determined by template.

Embodiment 16:

The modification yellow mud powder 40% of embodiment 1-6, the flexibility agent 2% that acrylic ester high molecular type copolymer emulsion 57%, paint-printing colour size be green 1%, have the polysiloxane of reactive functional groups, mechanically mixing stirs into uniform green composite sludge.Composite sludge is coated on the runway template that has ridge design, and coating thickness is 25mm, and baking constant temperature is 280 ℃ (± 80 ℃), and after the moisture content volatilization was done, molding formed blue compound mud elasticity runway plane materiel.Need to produce the compound mud elasticity runway plane materiel of different thickness, the increase and decrease coating thickness gets final product.Need the compound mud elasticity runway plane materiel of production same thickness different colours, add corresponding mill base or toner in mud, adopt identical method to make.Its plane materiel specification is determined by template.

Embodiment 17:

Emulsified body flexibility agent 4%, the water 6% of modification yellow mud powder 60%, acrylic ester high molecular type copolymer emulsion 30%, organosilicon and the fatty amine of embodiment 1-6, mechanically mixing stirs into uniform composite sludge.It is 2 meters that composite sludge is coated on width, and length is that coating thickness is 8mm on 30 meters the smooth template, baking constant temperature is 280 ℃ (± 80 ℃), after the moisture content volatilization is done, molding, the formation specification is yellow compound mud elastic ball scene material or the recreation ground plane materiel of 2m * 30m * 8mm.Need to produce the yellow compound mud elastic ball scene material or the recreation ground plane materiel of different size or different surfaces decorative pattern, change template and get final product.Need to produce the compound mud elastic ball scene material or the recreation ground plane materiel of same size different colours, add corresponding mill base or toner in mud, adopt identical method to make.

Embodiment 18:

Emulsified body softening agent 3%, ethylene glycol and the derivative antifreezing agent 6% thereof of multi-copolymerization emulsion 56%, organosilicon and the fatty amine of the modification yellow mud powder 35% of embodiment 1-6, the acrylate copolymer of tool reactive group, mechanically mixing stir into uniform yellow mud look composite sludge.Composite sludge is coated on the template that has wood grain, and coating thickness is 8mm, and baking constant temperature is 280 ℃ (± 80 ℃), after moisture content volatilizes, and molding, forming thickness is the compound mud elastic ball of yellow wood grain scene material or the recreation ground plane materiel of 8mm.Need to produce the compound mud elastic ball of the yellow wood grain scene material or the recreation ground plane materiel of different thickness, the increase and decrease coating thickness gets final product.Need to produce the yellow compound mud elastic ball scene material or the recreation ground plane materiel of different size or different surfaces decorative pattern, change template and get final product.Need the compound mud elastic ball of the wood grain scene material or the recreation ground plane materiel of production same thickness different colours, add corresponding mill base or toner in mud, adopt identical method to make.

Embodiment 19:

The modified white clay powder 50% of embodiment 1-6, compound emulsification system acrylic acid esters co-polymer 43.5%, paint-printing colour size Huang 0.5%, two carboxylic acid amide derivatives and octadecyl ethylene urea flexibility agent one to one mixture 2%, ethylene glycol and derivative antifreezing agent 4% thereof, mechanically mixing stirs into uniform beige composite sludge.Composite sludge is coated on the template that has bag or wood grain, and coating thickness is 9mm, and baking constant temperature is 280 ℃ (± 80 ℃), and after moisture content volatilized, molding formed thickness and be the beige bag of 9mm or the compound mud elastic ball of wood grain scene material, recreation ground plane materiel.The beige wood grain of needs production different thickness or the compound mud elastic ball of bag scene material, recreation ground plane materiel, the increase and decrease coating thickness gets final product.When needing the bag of production same thickness different colours or the compound mud elastic ball of wood grain scene material, recreation ground plane materiel, add corresponding mill base or toner in mud, adopt identical method to make.Need to produce the compound mud elastic ball of the beige scene material or the recreation ground plane materiel of different size or different surfaces decorative pattern, change template and get final product.

Embodiment 20:

The modification black mud powder 42% of embodiment 1-6, methyl acrylate (MA) and ethyl propenoate (EA) and butyl acrylate (n-BA), ethyl acrylate (Octyl acrylate, 2-EHA) the emulsified body flexibility agent 2% of copolymer emulsion 56%, organosilicon and fatty amine, mechanically mixing stirs into uniform black composite sludge.Composite sludge is coated on the template that has woven design or wood grain, and coating thickness is 8mm, and baking constant temperature is 280 ℃ (± 80 ℃), after the moisture content volatilization is done, and molding, forming thickness is black woven design or the compound mud elastic ball of wood grain scene material or the recreation ground plane materiel of 8mm.Need to produce black woven design or the compound mud elastic ball of the wood grain scene material or the recreation ground plane materiel of different thickness, the increase and decrease coating thickness gets final product.The woven design or the compound mud elastic ball of wood grain scene material or the recreation ground plane materiel that need production same thickness different colours are changed mud look and the corresponding mill base of interpolation or toner in mud, adopt identical method to make.Need to produce the compound mud elastic ball of the black scene material or the recreation ground plane materiel of different size or different surfaces decorative pattern, change template and get final product.

Embodiment 21:

Modification yellow mud powder 47%, acrylic ester high molecular type copolymer emulsion 42%, water 4.5%, polysiloxane flexibility agent 3%, alkyl ether phosphate defoamer 0.5%, ethylene glycol and the derivative antifreezing agent 3% thereof of embodiment 1-6 are mixed into and are uniform composite sludge.Composite sludge is coated on the template that has decorative pattern or shiny surface, and thickness is 1.4mm, and storing temperature is 100 ℃ (± 20 ℃), after polishing, molding is cut edge, and produces the yellow compound mud leather of no base cloth until conjunctiva.Need the compound mud leather of no base cloth of other color, add corresponding mill base or toner in mud, adopt identical method to make.

Embodiment 22:

The modification black mud powder 44% of embodiment 1-6, negatively charged ion, nonionic phenotype deceive 1% from interlinkage acrylate copolymer emulsion (unreacted monomer≤0.5%) 45%, water 5%, organosilicon flexibility agent 4%, propanediol polyoxypropylene polyoxyethylene ether defoaming agent 1%, paint-printing colour size, are mixed into uniform composite sludge.Composite sludge is coated on the template that has decorative pattern or shiny surface, and thickness is 2mm, and storing temperature is 200 ℃ (± 30 ℃), after polishing, molding is cut edge, and produces the compound mud leather of black of no base cloth until conjunctiva.Need the compound mud leather of no base cloth of other color, add corresponding mill base or toner in mud, adopt identical method to make.

Embodiment 23:,

The multi-copolymerization emulsion 54% of the modification yellow mud powder 40% of embodiment 1-6, the acrylate copolymer of tool reactive group, two carboxylic acid amide derivative flexibility agent 3%, glycerin polyether defoamer 1%, paint-printing colour size palm fibre 1% are mixed into uniform composite sludge.Composite sludge is coated on the template that has decorative pattern or shiny surface, and thickness is 2.3mm, and storing temperature is 200 ℃ (± 50 ℃), after polishing, molding is cut edge, and produces the brown compound mud leather of no base cloth until conjunctiva.Need the compound mud leather of no base cloth of other color, add corresponding mill base or toner in mud, adopt identical method to make.

Embodiment 24:

The emulsification flexibility agent C 1.4% of multi-copolymerization emulsion 59%, organosilicon and the fatty amine of the modified white clay powder 38.5% of embodiment 1-6, the acrylate copolymer of tool reactive group, silicone antifoam agent 0.5%, paint-printing colour size indigo plant 0.6%, be mixed into uniform composite sludge.Composite sludge is coated on cotton or the chemical fibre grid cloth, and thickness is 0.15mm, and storing temperature is 100 ℃ (± 20 ℃), until conjunctiva, extrudes required decorative pattern on the embossing machine of 130 ℃ of preheatings, produces the light blue compound mud leather of base cloth.Need other color that the compound mud leather of base cloth is arranged, add corresponding mill base or toner, adopt identical method to make in mud.

Embodiment 25:

The modification red soil powder 43% of embodiment 1-6, negatively charged ion, nonionic phenotype are mixed into uniform composite sludge from interlinkage acrylate copolymer emulsion 52%, polysiloxane flexibility agent 3%, alkyl ether phosphate defoamer 1%, paint-printing colour size red 1%.Composite sludge is coated on cotton or the chemical fibre grid cloth, and thickness is 0.2mm, and storing temperature is 150 ℃ (± 20 ℃), until conjunctiva, extrudes required decorative pattern on the embossing machine of 130 ℃ of preheatings, produces the light blue compound mud leather of base cloth.Need other color that the compound mud leather of base cloth is arranged, add corresponding mill base or toner, adopt identical method to make in mud.

Embodiment 26:

The modified white clay powder 43% of embodiment 1-6, acrylate copolymer emulsion 49%, water 4%, two carboxylic acid amide and derivative flexibility agent 2.8% thereof, propanediol polyoxypropylene polyoxyethylene ether defoaming agent 0.6%, paint-printing colour size deceive 0.6%, are mixed into uniform composite sludge.Composite sludge is coated on cotton or the chemical fibre grid cloth, and thickness is 0.18mm, and storing temperature is 150 ℃ (± 20 ℃), until conjunctiva, extrudes required decorative pattern on the embossing machine of 130 ℃ of preheatings, produces the compound mud leather of light gray black of base cloth.Need other color that the compound mud leather of base cloth is arranged, add corresponding mill base or toner, adopt identical method to make in mud.

Embodiment 27:

The modification yellow mud powder 38% of embodiment 1-6, the copolymer emulsion 54% of all acrylic ester class, water 4%, quaternary sun lotus property flexibility agent 3%, alkyl ether phosphate defoamer 0.5%, paint-printing colour size are golden yellow 0.5%, are mixed into uniform composite sludge.Composite sludge is coated on cotton or the chemical fibre grid cloth, and thickness is 0.28mm, and storing temperature is 160 ℃ (± 20 ℃), until conjunctiva, extrudes required decorative pattern on the embossing machine of 130 ℃ of preheatings, produces the yellow compound mud leather of base cloth.Need other color that the compound mud leather of base cloth is arranged, add corresponding mill base or toner, adopt identical method to make in mud.

Embodiment 28:

The modified white clay powder 53% of embodiment 1-6, polyethyl acrylate, butyl polyacrylate, hydroxymethyl acrylamide copolymer 33%, water 10%, quaternary sun lotus property promoting agent flexibility agent 3%, glycerin polyether defoamer 1% are mixed into uniform composite sludge.Composite sludge is coated on the template that has decorative pattern or shiny surface, and thickness is 1mm, and storing temperature is 180 ℃ (± 50 ℃), fits behind conjunctiva and goes up base cloth, and molding is cut edge, and produces the white compound mud leather of base cloth.What need other color has a compound mud leather of base cloth, adds corresponding mill base or toner in mud, adopts identical method to make.

Embodiment 29:

The copolymerized macromolecule compound 50% of modification red soil powder 43.5%, vinylformic acid and the ester thereof of embodiment 1-6, water 3%, quaternary sun lotus property promoting agent flexibility agent 3%, glycerin polyether defoamer 0.5% are mixed into uniform composite sludge.Composite sludge is coated on the template that has decorative pattern or shiny surface, and thickness is 1mm, and storing temperature is 180 ℃ (± 50 ℃), fits behind conjunctiva and goes up base cloth, and molding is cut edge, and produces the red compound mud leather of mud of base cloth.What need other color has a compound mud leather of base cloth, adds corresponding mill base or toner in mud, adopts identical method to make.

A few series products Performance Detection situation of the present invention is as follows:

One, embodiment 7-12 produces the flexibly wall brick obtain, and through provincial test section gate test, its performance is as follows after 10 days for shaping and drying:

1, water tolerance (3d) no change.

2, alkali resistance (3%NaOH, 7d) no change.

3, acid resistance (the hydrochloric acid soln .7d of pH=4) no change.

4, freeze-thaw resistance (10 circulations) no change.

5, anti-surface contamination (5 secondary reflection coefficient rate of descent)≤10%.

6, artificial ageing resistance (3000h).

The flexibly wall brick that embodiment 7-12 production obtains has carried out acute oral toxicity (LD ₅₀) experiment.Each dosage group mouse does not see untoward reaction after giving sample, and diet is movable normal, and laboratory animal does not have death in the observation period, obtains female, male its mouse oral LD ₅₀＞28.5g/Kg BW, submitted sample flexibly wall brick belong to nontoxic level material.The result is as follows:

This test basis GB15193.3-2003 " toxicological evaluation of food safety procedure and method "

The flexibly wall brick that embodiment 7-12 production obtains has carried out formaldehyde, total volatile organic compound, benzene series thing etc. and has detected, and the result is as follows:

Test item	Unit	Assay
			Formaldehyde	??mg/m 3	??0.001-0.002
??TVOC	??mg/m 3	??0.065-0.095
			Benzene	??mg/m 3	??0.004-0.006
Toluene	??mg/m 3	??0.001-0.002
			P-Xylol	??mg/m 3	??0.001-0.004
O-Xylol	??mg/m 3	??＜0.02
			Dissoluble lead	??mg/kg	??＜0.027
Soluble chromium	??mg/kg	??＜0.226
			Soluble cadmium	??mg/kg	??＜0.005
Soluble mercury	??mg/kg	??＜0.005

Detection is according to the method for inspection: formaldehyde (GB18580-2001 appendix A); Total volatile organic compound (GB18587-2001 appendix A); Benzene series thing (GB18587-2001 appendix A); Dissoluble lead, cadmium, chromium, mercury (GB18585-2001).

Two, embodiment 13-16 produces the compound mud elasticity runway obtain and measures through legal detection department science, and every technical indicator is as follows:

Test item	Detection method	Index	Detected value (23 ℃)
				Shock absorption %	??IAAF	??35％-50％	??37％-45％
Vertical deformation mm	??IAAF	??0.6-1.8mm	??0.9-1.1mm
				Tensile strength	??IAAF	??≥0.5MPa	??≥0.68MPa
Tensile yield	??IAAF	??≥40％	??200％-288％
				Coefficient of friction	??IAAF	??≥47BPN?20℃	??48-52BPN
Volatile organic matter	??ASTM?D?5116	The california standard	Qualified

Test item	Detection method	Index	Detected value (23 ℃)
				Critical radiant flux	??ASTM?E?648		??0.44-0.58W/cm 2, the I type
Optics smoke density value	??ASTM?E?662	The I level	＜450, the I level
				Hardness Shao Shi A	??ASTM?D?2240		??53-64
Colour stability			Very good
				Anti-chemical solvents			Good
Uvioresistant			Very good

Three, embodiment 17-20 produces the compound mud elastic ball scene material obtain or recreation ground plane materiel and measures through legal detection department science, and every technical indicator is as follows:

Test item	Detection method	Detected result
			Shao's formula hardness (A)	?ASTM?D?2240	??54-84
Ball rebound degree (%)	?DIN?18032-2	??≥95
			Tensile strength (N)	?DIN?53455	??1,290psi
Residual indentation (%)	?DIN?18032-2	??6％-10％
			Elongation at break (%)	?DIN?53455	??150％-280％
Shock absorption (%)	?DIN18032-2	??35％-55％
			Vertical deformation (mm)	?DIN18032-2	??0.9mm-2.41mm
Frictional coefficient	?DIN18032-2	??0.43-0.60
			The flame retardant resistance level	?DIN?51960	The I level

Four, to produce the average physical parameter of the compound mud leather obtain as follows for embodiment 21-29:

Stripping strength 88.7%, tensile strength 38%, tensile yield 36.5%.Reach the technical parameter of common sheep.

Claims (10)

1. the elastomer product of a modifying common soil, it is characterized in that: be to add additive after common red soil, common yellow mud, common black mud or the common white clay modification, make elastomer product, described additive is ACRYLIC EMULSION multipolymer, tinting material, flexibility agent, whipping agent or defoamer, antifreezing agent and water, and the composition and the parts by weight of various raw materials are as follows:

Modifying common soil 30-80;

ACRYLIC EMULSION multipolymer 20-70;

Flexibility agent 0-8;

Whipping agent 0-12;

Antifreezing agent 0-10;

Defoamer 0-2;

Tinting material 0-6;

Water 0-20.

Described modifying common soil is with common soil drying, pulverizing, crosses the 100-800 mesh sieve, removes sandstone and foreign material, gets the mud powder, perhaps earth adds the water mixing, cross the 100-800 mesh sieve, remove sandstone and foreign material, get the mud powder, then the common soil powder is carried out dynamic heat, under dynamic situation, add following surface-modifying agent, drying, obtain modification earth, the composition and the mass fraction of described earth surfaces properties-correcting agent are as follows:

Coupling agent 0.6-6 part;

Polysiloxane 1-12 part with reactive functional groups;

Emulsified body 0-2 part of organosilicon and fatty amine;

All the other are water.

2. the elastomer product of modifying common soil according to claim 1 is characterized in that: to select functional group for use be the silane coupling agent of vinyl, epoxide group, methacryloxy, acryloxy, amino, urea groups, chloropropyl to the coupling agent of surface-modifying agent in the described modifying common soil.

3. the elastomer product of modifying common soil according to claim 1, it is characterized in that: the polysiloxane with reactive functional groups of surface-modifying agent is selected from hydroxyl alkyl polysiloxane, carboxyl polysiloxane, polysiloxane polyether copolymer, contains the polysiloxane of vinyl or epoxide group in the described modifying common soil, polydimethylsiloxane, poly-propyl group methylsiloxane, poly-octyl group methylsiloxane or polyphenyl methyl siloxane

4. the elastomer product of modifying common soil according to claim 1, it is characterized in that: the emulsified body of the organosilicon of surface-modifying agent and fatty amine is fatty amide alkyl silane, the fatty amide alkyltrialkoxysilaneand that carboxylic acid and amido substituted silane carry out condensation in the described modifying common soil.

5. the elastomer product of modifying common soil according to claim 1 is characterized in that: the combination of one or more below described ACRYLIC EMULSION multipolymer adopts: (1) methyl acrylate; (2) ethyl propenoate; (3) butyl acrylate; (4) ethyl acrylate; (5) polyethyl acrylate, butyl polyacrylate, hydroxymethyl acrylamide copolymer; (6) compound of polyacrylic ester.

6. the elastomer product of modifying common soil according to claim 1 is characterized in that: described flexibility agent adopts emulsified body, the organosilicon emulsion of organosilicon and fatty amine or has the polysiloxane of reactive functional groups, two carboxylic acid amide derivative or octadecyl ethylene urea.

7. the production method of the elastomer product of modifying common soil as claimed in claim 1, it is characterized in that: the manufacturing process that modifying common soil is made elastomer product is as follows: (1) carries out mechanically mixing with modification earth, water, ACRYLIC EMULSION multipolymer or tinting material, softening agent, whipping agent, antifreezing agent, water, makes it become uniform composite sludge; (2) above-mentioned composite sludge is coated with carries out on template, baking constant temperature is 280 ℃ ± 50 ℃, and after moisture content volatilized, molding formed the Resilient product of all size.

8. the production method of the elastomer product of modifying common soil as claimed in claim 1, it is characterized in that: the manufacturing process that modifying common soil is made elastic sports floor is as follows: (1) carries out mechanically mixing with modification earth, water, ACRYLIC EMULSION multipolymer or tinting material, softening agent, whipping agent, antifreezing agent, water, makes it become uniform composite sludge; (2) above-mentioned composite sludge is coated with carries out on template, baking constant temperature is 280 ℃ ± 50 ℃, and after moisture content volatilized, molding formed the elastic sports runway of all size, and the surface pattern that institute becomes product is determined by the texture of template.

9. the production method of the elastomer product of modifying common soil as claimed in claim 1, it is characterized in that: the manufacturing process that this composite elastic product is made the resiliently-mounted floor brick is as follows: (1) carries out mechanically mixing with modification earth, water, ACRYLIC EMULSION multipolymer or tinting material, softening agent, whipping agent, antifreezing agent, water, makes it become uniform composite sludge; (2) composite sludge is coated with carries out on template, molding after the drying becomes resiliently-mounted floor brick or wall tile goods.

10. modification earth according to claim 1 is made the production method of elastomer product, it is characterized in that: the manufacturing process that this composite elastic product is made synthetic leather is as follows: (1) carries out mechanically mixing with modification earth, water, ACRYLIC EMULSION multipolymer or tinting material, softening agent, whipping agent, antifreezing agent, water, makes it become uniform composite sludge; (2) make the compound mud leather of no base cloth or the compound mud leather of base cloth is arranged;

The compound mud leather method for making of described no base cloth is composite sludge to be coated with carry out on the template that has decorative pattern or shiny surface, and thickness is 0.15mm to 3.0mm, and storing temperature is 80 ℃-285 ℃, until conjunctiva after the polishing back side, molding is cut edge, and produces the compound mud leather of no base cloth;

Described the compound mud leather method for making of base cloth is arranged is composite sludge to be coated with carry out on the template that has decorative pattern or shiny surface, and thickness is 0.15mm to 3.0mm, and storing temperature is 80 ℃-285 ℃, and the base cloth of fitting behind conjunctiva is cut edge; Composite sludge is coated with carries out on base cloth, thickness is 0.15mm to 3.0mm, and storing temperature is 80 ℃-285 ℃, until conjunctiva, extrudes required decorative pattern on preheating or the embossing machine that is not preheated.

Images