CN101831115A - Ethylene propylene rubber insulation material for longitudinal high-voltage watertight cable of ships and warships and production method thereof - Google Patents
Ethylene propylene rubber insulation material for longitudinal high-voltage watertight cable of ships and warships and production method thereof Download PDFInfo
- Publication number
- CN101831115A CN101831115A CN 201010159882 CN201010159882A CN101831115A CN 101831115 A CN101831115 A CN 101831115A CN 201010159882 CN201010159882 CN 201010159882 CN 201010159882 A CN201010159882 A CN 201010159882A CN 101831115 A CN101831115 A CN 101831115A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- insulation material
- tac
- terpolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an ethylene propylene rubber insulation material for longitudinal high-voltage watertight cables of ships and warships and a production method thereof. The method comprises the following steps: adding the ethylen e-propylene-diene mischpolymere, age resister and fire retardant into a banbury for banburying for 3.5min; adding argil, white carbon black and paraffin wax for continued banburying for 2min; adding active agent, and discharging after banburying for 1.5min; filtering the rubber compound with a three-layer filter screen (namely a 60 mesh filter screen, a 60 mesh filter screen and a 80 mesh filter screen) on a rubber filter; and beating into cornucopla on a double-roller mill, adding vulcanizer and co-crosslinker, then beating into cornucopla for 7 times, grinding and slicing after finishing the steps, and then cooling, wherein the materials are as follows in parts by weight: 100 parts of ethylen e-propylene-diene mischpolymere, 1-5 parts of vulcanizer, 1-4 parts of age resister, 15-70 parts of fire retardant, 0.5-10 parts of active agent, 10-20 parts of argil and 2-4 parts of paraffin. The prepared insulation material has the characteristics of low smoke, no halogen, fire resistance, high machinery strengthen, and high insulation resistance, good flexibility, elasticity and viscosity, and can be used for the ships and warships.
Description
Technical field
The present invention relates to the Insulation Material that a kind of power cable is used, particularly a kind of naval vessel longitudinal high-pressure watertight cable ethylene propylene rubber insulation material.
Background technology
Terpolymer EP rubber is widely used as the wire cable insulating material because of having characteristics such as electrical property excellence, heat-resisting ageing-resisting performance high and low temperature snappiness be good.
On May 20th, 2009, publication number is the Chinese invention patent application of CN101434728, a kind of ultraviolet light crosslinked EPT rubber cable insulation material and preparation method thereof is disclosed, feature is by weight 100 parts of terpolymer EP rubbers, 100~120 parts of mineral fillers, 0.5~5.0 part of ultraviolet initiator, 0.5~5.0 part of multi-group crosslink agent, 5.0~10.0 parts of tenderizers, 0.8~1.2 part of silane coupling agent and 0.01~1.0 part of composite antioxidant mixingly evenly to be extruded at 100~150 ℃, obtains the ultraviolet light crosslinked EPT rubber cable material; On conductor wire core, melt extrude then and be overmolding to insulation layer or restrictive coating; At wavelength 200~400NM, light intensity 400~2000MW/cm
2Cross-linking radiation under the UV-light.This Insulation Material does not possess fire retardation, and it is fire-retardant with the category-A bunchy of cable requirement to satisfy the naval vessel.
Summary of the invention
The technical problem to be solved in the present invention is that a kind of naval vessel longitudinal high-pressure watertight cable ethylene propylene rubber insulation material of superior performance is provided.
For solving above technical problem, naval vessel provided by the present invention longitudinal high-pressure watertight cable ethylene propylene rubber insulation material, feed composition and weight content are as follows: virgin rubber: 100 parts of terpolymer EP rubbers; Vulcanizing agent: dicumyl peroxide DCP, 3~5 parts; Triallyl trimerization hydrocyanic ester TAC, 1~3 part; Anti-aging agent: 2-thiol group benzimidazolyl MB, 2~4 parts; Alkylated diphenylamine compound XH-1,1~2 part; Fire retardant: aluminium hydroxide, 50~70 parts; Zinc borate, 15~30 parts; Promoting agent: Zinic stearas, 1~3 part; Stearic acid, 0.5~2 part; Zinc oxide, 5~10 parts; Strengthening agent: potter's clay, 10~20 parts.
With respect to prior art, the present invention has obtained following beneficial effect: the naval vessel longitudinal high-pressure watertight cable ethylene-propylene rubber(EPR) that uses this Insulation Material to make has the characteristics of low cigarette, Halogen, fire-retardant, high mechanical strength, high insulation resistance; Can guarantee the snappiness of cable, having solved the finished cable bending radius is the technical problem of 5 times of outside diameters of cable; Especially have elasticity and viscosity preferably, realize seal gum and the bonding one of insulation double-layer coextrusion that watertight cable requires, realize the difficult problem of the high pressure resistant water longitudinally water blocking of cable, can satisfy the naval vessel and use.
As preferred version of the present invention, described fire retardant also comprises antimonous oxide, and weight ratio is 15~30 parts; Described strengthening agent also comprises 6~9 parts of white carbon blacks.
As preferred version of the present invention, also comprise softening softening agent in the feed composition of described Insulation Material: 2~4 parts in paraffin.
As preferred version of the present invention, the feed composition and the weight content of Insulation Material are as follows: virgin rubber: 100 parts of terpolymer EP rubbers; Vulcanizing agent: dicumyl peroxide DCP, 3 parts; Triallyl trimerization hydrocyanic ester TAC, 1 part; Anti-aging agent: 2-thiol group benzimidazolyl MB, 2 parts; Alkylated diphenylamine compound XH-1,1.5 parts; Fire retardant: aluminium hydroxide, 65 parts; Zinc borate, 20 parts; Promoting agent: Zinic stearas, 1.5 parts; Stearic acid, 1 part; Zinc oxide, 5 parts; Strengthening agent: potter's clay, 15 parts; White carbon black, 7.5 parts; Softening softening agent: 3.5 parts in paraffin.
As preferred version of the present invention, the feed composition and the weight content of Insulation Material are as follows: virgin rubber: 100 parts of terpolymer EP rubbers; Vulcanizing agent: dicumyl peroxide DCP, 3.5 parts; Triallyl trimerization hydrocyanic ester TAC, 1 part; Anti-aging agent: 2-thiol group benzimidazolyl MB, 4 parts; Alkylated diphenylamine compound XH-1,1.5 parts; Fire retardant: aluminium hydroxide, 60 parts; Zinc borate, 15 parts; Promoting agent: Zinic stearas, 1.5 parts; Stearic acid, 0.5 part; Zinc oxide, 6.5 parts; Strengthening agent: potter's clay, 20 parts; White carbon black, 6 parts; Softening softening agent: 2 parts in paraffin.
As preferred version of the present invention, the feed composition and the weight content of Insulation Material are as follows: virgin rubber: 100 parts of terpolymer EP rubbers; Vulcanizing agent: dicumyl peroxide DCP, 4 parts; Triallyl trimerization hydrocyanic ester TAC, 2 parts; Anti-aging agent: 2-thiol group benzimidazolyl MB, 3 parts; Alkylated diphenylamine compound XH-1,1 part; Fire retardant: aluminium hydroxide, 70 parts; Zinc borate, 25 parts; Promoting agent: Zinic stearas, 3 parts; Stearic acid, 1 part; Zinc oxide, 6 parts; Strengthening agent: potter's clay, 15 parts; White carbon black, 7 parts; Softening softening agent: 3 parts in paraffin.
Another technical problem that the present invention will solve is, the production method of a kind of naval vessel longitudinal high-pressure watertight cable with ethylene propylene rubber insulation material is provided, the Insulation Material that this method is made, superior performance has the characteristics of low cigarette, Halogen, fire-retardant, high mechanical strength, high insulation resistance.
For solving above technical problem, the naval vessel provided by the present invention longitudinal high-pressure watertight cable production method of ethylene propylene rubber insulation material, may further comprise the steps: terpolymer EP rubber, 2-thiol group benzimidazolyl MB, triallyl trimerization hydrocyanic ester TAC, aluminium hydroxide, zinc borate are added Banbury mixer, banburying 3.5 minutes; Add potter's clay and white carbon black then, add paraffin again, continue banburying 2 minutes; Then add Zinic stearas, stearic acid, zinc oxide, banburying discharging after 1.5 minutes; Rubber unvulcanizate is being filtered on the rubber machine with 60 orders+60 orders+80 mesh filter screens, three metafiltration glue; In two roller mills, play the triangle bag at last and add dicumyl peroxide DCP, triallyl trimerization hydrocyanic ester TAC and co-crosslinker, and then play the triangle bag 7 times, grind page or leaf section and cooling after finishing; Each raw material weight ratio is terpolymer EP rubber: 100 parts; Dicumyl peroxide DCP:3~5 part; Triallyl trimerization hydrocyanic ester TAC:1~3 parts; 2-thiol group benzimidazolyl MB:2~4 parts; Alkylated diphenylamine compound XH-1:1~2 part; Aluminium hydroxide: 50~70 parts; Zinc borate: 15~30 parts; Zinic stearas: 1~3 part; Stearic acid: 0.5~2 part; Zinc oxide: 5~10 parts; Potter's clay: 10~20 parts; White carbon black: 6~9 parts; Paraffin: 2~4 parts.
With respect to prior art, the present invention has obtained following beneficial effect: the Insulation Material of using this method to make, be used to make naval vessel longitudinal high-pressure watertight cable ethylene-propylene rubber(EPR), and have the characteristics of low cigarette, Halogen, fire-retardant, high mechanical strength, high insulation resistance; Can guarantee the snappiness of cable, having solved the finished cable bending radius is the technical problem of 5 times of outside diameters of cable; Especially have elasticity and viscosity preferably, realize seal gum and the bonding one of insulation double-layer coextrusion that watertight cable requires, realize the difficult problem of the high pressure resistant water longitudinally water blocking of cable, can satisfy the naval vessel and use.
As preferred version of the present invention, the naval vessel longitudinal high-pressure watertight cable production method of ethylene propylene rubber insulation material, may further comprise the steps: terpolymer EP rubber, 2-thiol group benzimidazolyl MB, triallyl trimerization hydrocyanic ester TAC, aluminium hydroxide, zinc borate are added Banbury mixer, banburying 3.5 minutes; Add potter's clay and white carbon black then, add paraffin again, continue banburying 2 minutes; Then add Zinic stearas, stearic acid, zinc oxide, banburying discharging after 1.5 minutes; Rubber unvulcanizate is being filtered on the rubber machine with 60 orders+60 orders+80 mesh filter screens, three metafiltration glue; In two roller mills, play the triangle bag at last and add dicumyl peroxide DCP, triallyl trimerization hydrocyanic ester TAC and co-crosslinker, and then play the triangle bag 7 times, grind page or leaf section and cooling after finishing; Each raw material weight ratio is terpolymer EP rubber: 100 parts; 2-thiol group benzimidazolyl MB:2 part; Triallyl trimerization hydrocyanic ester TAC:1 part; Aluminium hydroxide: 65 parts; Zinc borate: 20 parts; Potter's clay: 15 parts; White carbon black: 7.5 parts; Paraffin: 3.5 parts; Zinic stearas: 1.5 parts; Stearic acid: 1 part; Zinc oxide: 5 parts; Dicumyl peroxide DCP:3 part; Triallyl trimerization hydrocyanic ester TAC:1 part; Aluminium hydroxide: 65 parts; Zinc borate: 20 parts.
As preferred version of the present invention, the naval vessel longitudinal high-pressure watertight cable production method of ethylene propylene rubber insulation material, may further comprise the steps: earlier with terpolymer EP rubber and 2-thiol group benzimidazolyl MB, alkylated diphenylamine compound XH-1, aluminium hydroxide, zinc borate drops into two roller mill mixings, add potter's clay and white carbon black behind the bag roller, add paraffin then, powder stirs evenly the back fully and adds Zinic stearas, stearic acid, zinc oxide, draw and play the triangle bag again after thin and add dicumyl peroxide DCP, triallyl trimerization hydrocyanic ester TAC and co-crosslinker grind page or leaf section and cooling after drawing logical 7 times; Each raw material weight ratio is: terpolymer EP rubber: 100 parts, dicumyl peroxide DCP:3.5 part; Triallyl trimerization hydrocyanic ester TAC:1 part, 2-thiol group benzimidazolyl MB:4 part, alkylated diphenylamine compound XH-1:1.5 part, aluminium hydroxide: 60 parts, zinc borate: 15 parts, Zinic stearas: 1.5 parts, stearic acid: 0.5 part, zinc oxide: 6.5 parts, potter's clay: 20 parts, white carbon black: 6 parts, paraffin: 2 parts.
As preferred version of the present invention, the naval vessel longitudinal high-pressure watertight cable production method of ethylene propylene rubber insulation material, may further comprise the steps: terpolymer EP rubber is mixing in Banbury mixer, with Zinic stearas, stearic acid, zinc oxide, 2-thiol group benzimidazolyl, alkylated diphenylamine compound XH-1, aluminium hydroxide, zinc borate, that potter's clay is mixed and made into compound is standby, it is mixing together to treat that terpolymer EP rubber after mixing 2 minutes adds this compound Banbury mixer; Mixingly in the Banbury mixer fully evenly down beat behind the triangle bag again pulling-on piece and filter rubber to mill.Beat then and on three-roller open mill, beat triangle Bao Wuci, draw and get back to Banbury mixer after thin and add fines, after the banburying 1 minute, added vulcanizing agent dicumyl peroxide DCP, triallyl trimerization hydrocyanic ester TAC and co-crosslinker mixing again 2 minutes, then cutting slice and cooling; Each raw material weight ratio is terpolymer EP rubber: 100 parts; Dicumyl peroxide DCP:4 part; Triallyl trimerization hydrocyanic ester TAC:2 part; 2-thiol group benzimidazolyl MB:3 part; Alkylated diphenylamine compound XH-1:1 part; Aluminium hydroxide: 70 parts; Zinc borate: 25 parts; Zinic stearas: 3 parts; Stearic acid: 1 part; Zinc oxide: 6 parts; Potter's clay: 15 parts.
Embodiment
Naval vessel provided by the present invention longitudinal high-pressure watertight cable ethylene propylene rubber insulation material, feed composition and weight content are as follows: virgin rubber: 100 parts of terpolymer EP rubbers; Vulcanizing agent: dicumyl peroxide DCP, 3~5 parts; Triallyl trimerization hydrocyanic ester TAC, 1~3 part; Anti-aging agent: 2-thiol group benzimidazolyl MB, 2~4 parts; Alkylated diphenylamine compound XH-1,1~2 part; Fire retardant: aluminium hydroxide, 50~70 parts; Zinc borate, 15~30 parts; Antimonous oxide, 15~30 parts; Promoting agent: Zinic stearas, 1~3 part; Stearic acid, 0.5~2 part; Zinc oxide, 5~10 parts; Strengthening agent: potter's clay, 10~20 parts; White carbon black, 6~9 parts; Softening softening agent: 2~4 parts in paraffin.
Embodiment one
The feed composition and the weight content of Insulation Material are as follows: virgin rubber: 100 parts of terpolymer EP rubbers; Vulcanizing agent: dicumyl peroxide DCP, 3 parts; Triallyl trimerization hydrocyanic ester TAC, 1 part; Anti-aging agent: 2-thiol group benzimidazolyl MB, 2 parts; Alkylated diphenylamine compound XH-1,1.5 parts; Fire retardant: aluminium hydroxide, 65 parts; Zinc borate, 20 parts; Promoting agent: Zinic stearas, 1.5 parts; Stearic acid, 1 part; Zinc oxide, 5 parts; Strengthening agent: potter's clay, 15 parts; White carbon black, 7.5 parts; Softening softening agent: 3.5 parts in paraffin.
Embodiment two
The feed composition and the weight content of Insulation Material are as follows: virgin rubber: 100 parts of terpolymer EP rubbers; Vulcanizing agent: dicumyl peroxide DCP, 3.5 parts; Triallyl trimerization hydrocyanic ester TAC, 1 part; Anti-aging agent: 2-thiol group benzimidazolyl MB, 4 parts; Alkylated diphenylamine compound XH-1,1.5 parts; Fire retardant: aluminium hydroxide, 60 parts; Zinc borate, 15 parts; Promoting agent: Zinic stearas, 1.5 parts; Stearic acid, 0.5 part; Zinc oxide, 6.5 parts; Strengthening agent: potter's clay, 20 parts; White carbon black, 6 parts; Softening softening agent: 2 parts in paraffin.
Embodiment three
The feed composition and the weight content of Insulation Material are as follows: virgin rubber: 100 parts of terpolymer EP rubbers; Vulcanizing agent: dicumyl peroxide DCP, 4 parts; Triallyl trimerization hydrocyanic ester TAC, 2 parts; Anti-aging agent: 2-thiol group benzimidazolyl MB, 3 parts; Alkylated diphenylamine compound XH-1,1 part; Fire retardant: aluminium hydroxide, 70 parts; Zinc borate, 25 parts; Promoting agent: Zinic stearas, 3 parts; Stearic acid, 1 part; Zinc oxide, 6 parts; Strengthening agent: potter's clay, 15 parts; White carbon black, 7 parts; Softening softening agent: 3 parts in paraffin.
The naval vessel provided by the present invention longitudinal high-pressure watertight cable production method of ethylene propylene rubber insulation material, may further comprise the steps: terpolymer EP rubber, 2-thiol group benzimidazolyl MB, triallyl trimerization hydrocyanic ester TAC, aluminium hydroxide, zinc borate are added Banbury mixer, banburying 3.5 minutes; Add potter's clay and white carbon black then, add paraffin again, continue banburying 2 minutes; Then add Zinic stearas, stearic acid, zinc oxide, banburying discharging after 1.5 minutes; Rubber unvulcanizate is being filtered on the rubber machine with 60 orders+60 orders+80 mesh filter screens, three metafiltration glue; In two roller mills, play the triangle bag at last and add dicumyl peroxide DCP, triallyl trimerization hydrocyanic ester TAC and co-crosslinker, and then play the triangle bag 7 times, grind page or leaf section and cooling after finishing; Each raw material weight ratio is terpolymer EP rubber: 100 parts; Dicumyl peroxide DCP:3~5 part; Triallyl trimerization hydrocyanic ester TAC:1~3 parts; 2-thiol group benzimidazolyl MB:2~4 parts; Alkylated diphenylamine compound XH-1:1~2 part; Aluminium hydroxide: 50~70 parts; Zinc borate: 15~30 parts; Zinic stearas: 1~3 part; Stearic acid: 0.5~2 part; Zinc oxide: 5~10 parts; Potter's clay: 10~20 parts; White carbon black: 6~9 parts; Paraffin: 2~4 parts.
Naval vessel of the present invention longitudinal high-pressure watertight cable ethylene propylene rubber insulation material has the characteristics of low cigarette, Halogen, fire-retardant, high mechanical strength, high insulation resistance, can satisfy the naval vessel and use.Its preparation technology is banburying, filter rubber, compressing tablet, cooling, and banburying needs to guarantee each component uniform mixing; Owing to may have some impurity in the refining glue, need filter glue at filter rubber machine behind the refining glue, remove impurity; The filter rubber is finished the back rubber is carried out compressing tablet, cutting, forms strip film; Then that the film cooling is inter-adhesive to prevent between each film.
Performance of the present invention and existing ethylene-propylene rubber(EPR) performance relatively see the following form:
Embodiment one
Terpolymer EP rubber, 2-thiol group benzimidazolyl MB, triallyl trimerization hydrocyanic ester TAC, aluminium hydroxide, zinc borate are added Banbury mixer, banburying 3.5 minutes; Add potter's clay and white carbon black then, add paraffin again, continue banburying 2 minutes; Then add Zinic stearas, stearic acid, zinc oxide, banburying discharging after 1.5 minutes; Rubber unvulcanizate is being filtered on the rubber machine with 60 orders+60 orders+80 mesh filter screens, three metafiltration glue; In two roller mills, play the triangle bag at last and add dicumyl peroxide DCP, triallyl trimerization hydrocyanic ester TAC and co-crosslinker, and then play the triangle bag 7 times, grind page or leaf section and cooling after finishing; Each raw material weight ratio is terpolymer EP rubber: 100 parts; 2-thiol group benzimidazolyl MB:2 part; Triallyl trimerization hydrocyanic ester TAC:1 part; Aluminium hydroxide: 65 parts; Zinc borate: 20 parts; Potter's clay: 15 parts; White carbon black: 7.5 parts; Paraffin: 3.5 parts; Zinic stearas: 1.5 parts; Stearic acid: 1 part; Zinc oxide: 5 parts; Dicumyl peroxide DCP:3 part; Triallyl trimerization hydrocyanic ester TAC:1 part.
Embodiment two
Earlier terpolymer EP rubber and 2-thiol group benzimidazolyl MB, alkylated diphenylamine compound XH-1, aluminium hydroxide, zinc borate are dropped into two roller mill mixings, add potter's clay and white carbon black behind the bag roller, add paraffin then, powder stirs evenly the back fully and adds Zinic stearas, stearic acid, zinc oxide, draw and play the triangle bag again after thin and add dicumyl peroxide DCP, triallyl trimerization hydrocyanic ester TAC and co-crosslinker, grind page or leaf section and cooling after drawing logical 7 times; Each raw material weight ratio is: terpolymer EP rubber: 100 parts, dicumyl peroxide DCP:3.5 part; Triallyl trimerization hydrocyanic ester TAC:1 part, 2-thiol group benzimidazolyl MB:4 part, alkylated diphenylamine compound XH-1:1.5 part, aluminium hydroxide: 60 parts, zinc borate: 15 parts, Zinic stearas: 1.5 parts, stearic acid: 0.5 part, zinc oxide: 6.5 parts, potter's clay: 20 parts, white carbon black: 6 parts, paraffin: 2 parts.
Embodiment three
Terpolymer EP rubber is mixing in Banbury mixer, with Zinic stearas, stearic acid, zinc oxide, 2-thiol group benzimidazolyl, alkylated diphenylamine compound XH-1, aluminium hydroxide, zinc borate, that potter's clay is mixed and made into compound is standby, it is mixing together to treat that terpolymer EP rubber after mixing 2 minutes adds this compound Banbury mixer; Mixingly in the Banbury mixer fully evenly down beat behind the triangle bag again pulling-on piece and filter rubber to mill.Beat then and on three-roller open mill, beat triangle Bao Wuci, draw and get back to Banbury mixer after thin and add fines, after the banburying 1 minute, added vulcanizing agent dicumyl peroxide DCP, triallyl trimerization hydrocyanic ester TAC and co-crosslinker mixing again 2 minutes, then cutting slice and cooling; Each raw material weight ratio is terpolymer EP rubber: 100 parts; Dicumyl peroxide DCP:4 part; Triallyl trimerization hydrocyanic ester TAC:2 part; 2-thiol group benzimidazolyl MB:3 part; Alkylated diphenylamine compound XH-1:1 part; Aluminium hydroxide: 70 parts; Zinc borate: 25 parts; Zinic stearas: 3 parts; Stearic acid: 1 part; Zinc oxide: 6 parts; Potter's clay: 15 parts.
In addition to the implementation, the present invention can also have other embodiments.All employings are equal to the technical scheme of replacement or equivalent transformation formation, all drop on the protection domain of requirement of the present invention.
Claims (10)
1. naval vessel longitudinal high-pressure watertight cable ethylene propylene rubber insulation material is characterized in that the feed composition and the weight content of this Insulation Material are as follows:
Virgin rubber: 100 parts of terpolymer EP rubbers;
Vulcanizing agent: dicumyl peroxide DCP, 3~5 parts; Triallyl trimerization hydrocyanic ester TAC, 1~3 part;
Anti-aging agent: 2-thiol group benzimidazolyl MB, 2~4 parts; Alkylated diphenylamine compound XH-1,1~2 part;
Fire retardant: aluminium hydroxide, 50~70 parts; Zinc borate, 15~30 parts;
Promoting agent: Zinic stearas, 1~3 part; Stearic acid, 0.5~2 part; Zinc oxide, 5~10 parts;
Strengthening agent: potter's clay, 10~20 parts.
2. naval vessel according to claim 1 longitudinal high-pressure watertight cable ethylene propylene rubber insulation material is characterized in that described fire retardant also comprises antimonous oxide, and weight ratio is 15~30 parts; Described strengthening agent also comprises 6~9 parts of white carbon blacks.
3. naval vessel according to claim 1 longitudinal high-pressure watertight cable ethylene propylene rubber insulation material is characterized in that, also comprises softening softening agent in the feed composition of described Insulation Material: 2~4 parts in paraffin.
4. naval vessel according to claim 1 longitudinal high-pressure watertight cable ethylene propylene rubber insulation material is characterized in that the feed composition and the weight content of described Insulation Material are as follows:
Virgin rubber: 100 parts of terpolymer EP rubbers;
Vulcanizing agent: dicumyl peroxide DCP, 3 parts; Triallyl trimerization hydrocyanic ester TAC, 1 part;
Anti-aging agent: 2-thiol group benzimidazolyl MB, 2 parts; Alkylated diphenylamine compound XH-1,1.5 parts;
Fire retardant: aluminium hydroxide, 65 parts; Zinc borate, 20 parts;
Promoting agent: Zinic stearas, 1.5 parts; Stearic acid, 1 part; Zinc oxide, 5 parts;
Strengthening agent: potter's clay, 15 parts; White carbon black, 7.5 parts;
Softening softening agent: 3.5 parts in paraffin.
5. naval vessel according to claim 1 longitudinal high-pressure watertight cable ethylene propylene rubber insulation material is characterized in that the feed composition and the weight content of described Insulation Material are as follows:
Virgin rubber: 100 parts of terpolymer EP rubbers;
Vulcanizing agent: dicumyl peroxide DCP, 3.5 parts; Triallyl trimerization hydrocyanic ester TAC, 1 part;
Anti-aging agent: 2-thiol group benzimidazolyl MB, 4 parts; Alkylated diphenylamine compound XH-1,1.5 parts;
Fire retardant: aluminium hydroxide, 60 parts; Zinc borate, 15 parts;
Promoting agent: Zinic stearas, 1.5 parts; Stearic acid, 0.5 part; Zinc oxide, 6.5 parts;
Strengthening agent: potter's clay, 20 parts; White carbon black, 6 parts;
Softening softening agent: 2 parts in paraffin.
6. naval vessel according to claim 1 longitudinal high-pressure watertight cable ethylene propylene rubber insulation material is characterized in that the feed composition and the weight content of this Insulation Material are as follows:
Virgin rubber: 100 parts of terpolymer EP rubbers;
Vulcanizing agent: dicumyl peroxide DCP, 4 parts; Triallyl trimerization hydrocyanic ester TAC, 2 parts;
Anti-aging agent: 2-thiol group benzimidazolyl MB, 3 parts; Alkylated diphenylamine compound XH-1,1 part;
Fire retardant: aluminium hydroxide, 70 parts; Zinc borate, 25 parts;
Promoting agent: Zinic stearas, 3 parts; Stearic acid, 1 part; Zinc oxide, 6 parts;
Strengthening agent: potter's clay, 15 parts; White carbon black, 7 parts;
Softening softening agent: 3 parts in paraffin.
7. a naval vessel longitudinal high-pressure watertight cable is with the production method of ethylene propylene rubber insulation material, may further comprise the steps: terpolymer EP rubber, 2-thiol group benzimidazolyl MB, triallyl trimerization hydrocyanic ester TAC, aluminium hydroxide, zinc borate are added Banbury mixer, banburying 3.5 minutes; Add potter's clay and white carbon black then, add paraffin again, continue banburying 2 minutes; Then add Zinic stearas, stearic acid, zinc oxide, banburying discharging after 1.5 minutes; Rubber unvulcanizate is being filtered on the rubber machine with 60 orders+60 orders+80 mesh filter screens, three metafiltration glue; In two roller mills, play the triangle bag at last and add dicumyl peroxide DCP, triallyl trimerization hydrocyanic ester TAC and co-crosslinker, and then play the triangle bag 7 times, grind page or leaf section and cooling after finishing;
Each raw material weight ratio is terpolymer EP rubber: 100 parts; Dicumyl peroxide DCP:3~5 part; Triallyl trimerization hydrocyanic ester TAC:1~3 parts; 2-thiol group benzimidazolyl MB:2~4 parts; Alkylated diphenylamine compound XH-1:1~2 part; Aluminium hydroxide: 50~70 parts; Zinc borate: 15~30 parts; Zinic stearas: 1~3 part; Stearic acid: 0.5~2 part; Zinc oxide: 5~10 parts; Potter's clay: 10~20 parts; White carbon black: 6~9 parts; Paraffin: 2~4 parts.
8. the longitudinal high-pressure watertight cable production method of ethylene propylene rubber insulation material in naval vessel according to claim 5 may further comprise the steps:
Terpolymer EP rubber, 2-thiol group benzimidazolyl MB, triallyl trimerization hydrocyanic ester TAC, aluminium hydroxide, zinc borate are added Banbury mixer, banburying 3.5 minutes; Add potter's clay and white carbon black then, add paraffin again, continue banburying 2 minutes; Then add Zinic stearas, stearic acid, zinc oxide, banburying discharging after 1.5 minutes; Rubber unvulcanizate is being filtered on the rubber machine with 60 orders+60 orders+80 mesh filter screens, three metafiltration glue; In two roller mills, play the triangle bag at last and add dicumyl peroxide DCP, triallyl trimerization hydrocyanic ester TAC and co-crosslinker, and then play the triangle bag 7 times, grind page or leaf section and cooling after finishing;
Each raw material weight ratio is terpolymer EP rubber: 100 parts; 2-thiol group benzimidazolyl MB:2 part; Triallyl trimerization hydrocyanic ester TAC:1 part; Aluminium hydroxide: 65 parts; Zinc borate: 20 parts; Potter's clay: 15 parts; White carbon black: 7.5 parts; Paraffin: 3.5 parts; Zinic stearas: 1.5 parts; Stearic acid: 1 part; Zinc oxide: 5 parts; Dicumyl peroxide DCP:3 part; Triallyl trimerization hydrocyanic ester TAC:1 part; Aluminium hydroxide: 65 parts; Zinc borate: 20 parts.
9. the naval vessel according to claim 5 longitudinal high-pressure watertight cable production method of ethylene propylene rubber insulation material, may further comprise the steps: earlier with terpolymer EP rubber and 2-thiol group benzimidazolyl MB, alkylated diphenylamine compound XH-1, aluminium hydroxide, zinc borate drops into two roller mill mixings, add potter's clay and white carbon black behind the bag roller, add paraffin then, powder stirs evenly the back fully and adds Zinic stearas, stearic acid, zinc oxide, draw and play the triangle bag again after thin and add dicumyl peroxide DCP, triallyl trimerization hydrocyanic ester TAC and co-crosslinker grind page or leaf section and cooling after drawing logical 7 times;
Each raw material weight ratio is: terpolymer EP rubber: 100 parts, dicumyl peroxide DCP:3.5 part; Triallyl trimerization hydrocyanic ester TAC:1 part, 2-thiol group benzimidazolyl MB:4 part, alkylated diphenylamine compound XH-1:1.5 part, aluminium hydroxide: 60 parts, zinc borate: 15 parts, Zinic stearas: 1.5 parts, stearic acid: 0.5 part, zinc oxide: 6.5 parts, potter's clay: 20 parts, white carbon black: 6 parts, paraffin: 2 parts.
10. the naval vessel according to claim 5 longitudinal high-pressure watertight cable production method of ethylene propylene rubber insulation material, may further comprise the steps: terpolymer EP rubber is mixing in Banbury mixer, with Zinic stearas, stearic acid, zinc oxide, 2-thiol group benzimidazolyl, alkylated diphenylamine compound XH-1, aluminium hydroxide, zinc borate, that potter's clay is mixed and made into compound is standby, it is mixing together to treat that terpolymer EP rubber after mixing 2 minutes adds this compound Banbury mixer; Mixingly in the Banbury mixer fully evenly down beat behind the triangle bag again pulling-on piece and filter rubber to mill.Beat then and on three-roller open mill, beat triangle Bao Wuci, draw and get back to Banbury mixer after thin and add fines, after the banburying 1 minute, added vulcanizing agent dicumyl peroxide DCP, triallyl trimerization hydrocyanic ester TAC and co-crosslinker mixing again 2 minutes, then cutting slice and cooling;
Each raw material weight ratio is terpolymer EP rubber: 100 parts; Dicumyl peroxide DCP:4 part; Triallyl trimerization hydrocyanic ester TAC:2 part; 2-thiol group benzimidazolyl MB:3 part; Alkylated diphenylamine compound XH-1:1 part; Aluminium hydroxide: 70 parts; Zinc borate: 25 parts; Zinic stearas: 3 parts; Stearic acid: 1 part; Zinc oxide: 6 parts; Potter's clay: 15 parts.