CN100514507C - Screening material for medium voltage rubber insulation cable - Google Patents

Screening material for medium voltage rubber insulation cable Download PDF

Info

Publication number
CN100514507C
CN100514507C CNB2004100890245A CN200410089024A CN100514507C CN 100514507 C CN100514507 C CN 100514507C CN B2004100890245 A CNB2004100890245 A CN B2004100890245A CN 200410089024 A CN200410089024 A CN 200410089024A CN 100514507 C CN100514507 C CN 100514507C
Authority
CN
China
Prior art keywords
cable
parts
shielding material
wax
rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CNB2004100890245A
Other languages
Chinese (zh)
Other versions
CN1783359A (en
Inventor
曾纪刚
刘旌平
陈佶民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Kaibo Cable Special Material Co ltd
Shanghai Electric Cable Research Institute
Original Assignee
Shanghai Electric Cable Research Institute
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Electric Cable Research Institute filed Critical Shanghai Electric Cable Research Institute
Priority to CNB2004100890245A priority Critical patent/CN100514507C/en
Publication of CN1783359A publication Critical patent/CN1783359A/en
Application granted granted Critical
Publication of CN100514507C publication Critical patent/CN100514507C/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

This invention relates to a shield material used in high soft medium pressure rubber insulation cables in the following proportion of mass: EPT rubber: 100, conductive carbon black: 50-100, age resister: 1-3, organ peroxidate: 2-4, coupler: 1-2, wax: 2-8 and processed oil: 5-20, which can solve the technological problem of preparing a cable with the bending diameter six times of the outer diameter.

Description

The middle India-rubber cable of pressing is expected with shielding
Technical field
The present invention relates to insulation and conducing composite material technical field, refer to press in a kind of highly-flexible India-rubber cable especially with shielding material.
Background technology
In to press India-rubber cable be a product that generally uses, the regulation of relevant middle pressure India-rubber cable is all arranged as IEC60502 and IEC92-354 etc.In the wide range that its uses, land, water, civilian, military nothing can't be obtained.Ethylene-propylene rubber has wide serviceability temperature, can still keep performance at 150 ℃, and still pliable and tough under-40 ℃, temperature resistant grade is generally 105 ℃, and emergency is 140 ℃, this means to improve 7~8% ampacity.Ethylene-propylene rubber has excellent electric performance, and its dielectric constant and dielectric loss angle tangent are all very little, and outstanding water-resistance and corona-resistance property are arranged, stable anti-electric pulse intensity.The thermal expansion of ethylene-propylene rubber is low, can prevent that insulating barrier separation, joint or end retraction, the neutral line from embedding insulation, improves the matching of cable and preparation joint.Ethylene-propylene rubber has the excellent flexibility energy, makes cable have very little bending radius, and installation, joint and end-blocking are easier, and the defective patience is higher.So epr cable compound is the trend of power cable development.
The used ethylene-propylene rubber type of ethylene-propylene rubber cable has two kinds in common ethylene-propylene rubber and high-modulus ethylene-propylene rubber, and they have different physical properties and electric property regulation, the cable that moves or what have that the soft cable that requires adopts is exactly common ethylene-propylene rubber.Some special occasions have higher soft requirement to cable, and as magnetic suspension long stator cable etc., this just needs highly-flexible performance Insulation Material and shielding material.
Present domestic medium and high voltage cable mainly adopts the crosslinkable polyethylene Insulation Material, as: Chinese patent 02106022.3 stable middle voltage and high-voltage cable insulation composition, relate to a kind of polyethylene composition as the electric wire and cable insulating material, it has improved anti-incipient scorch, composition comprises: (a) polyethylene, (b) under atmospheric pressure fusing point is lower than 50 ℃ incipient scorch inhibitor and (c) organic peroxide.But this Insulation Material is because hardness own is big, and the cable bending property of making is bad, and the cable bending diameter is at least 20 times of outside diameters of cable.Satisfy the requirement of highly-flexible cable, as bending diameter is 6 times of outside diameters of cable, needs to adopt new Insulation Material, simultaneously, because medium and high voltage cable must adopt semiconductive shielding layer, so need to propose a kind of new shielding material to satisfy the actual needs of preparation highly-flexible cable.
Summary of the invention
In order to overcome the technical problem that prior art can not prepare the highly-flexible midium voltage cable, especially solving the preparation bending diameter is the technical problem of 6 times of outside diameters of cable, and the present invention proposes to press in a kind of highly-flexible India-rubber cable with shielding material.Calculate with the constituent mass proportioning, its concrete scheme is as follows: 100 parts of ethylene propylene diene rubbers, 50~100 parts of conductive blacks, 1~3 part of antiaging agent, 2~4 parts of organic peroxides, 1~2 part of coupling agent, 2~8 parts in wax, 5~20 parts of processing oils.
The preparation technology that the present invention shields material is relevant existing processes such as banburying or kneading, dispersion granulation or rolling page or leaf.Because the present invention shields material and is applied as the master with midium voltage cable, so the production environment of corresponding product needed cleaning could guarantee the electrical property of product fine.Preferably adopt ventilation equipment to send into cleaned air passes, keep the malleation of workshop.Concrete operations are seen as follows: 1. banburying, kneading, open the refining or other process for dispersing, mix as long as can guarantee each component.2. granulation or rolling page or leaf shield material and adopt single screw extrusion machine or miscellaneous equipment to make the particle of suitable size; Also can adopt page machine of rolling over or miscellaneous equipment calendering to cut into the suitable adhesive tape of size.3. no matter packing is adhesive tape or micelle, all will adopt moistureproof dustproof packing, prevents from storing, polluting when transporting.
Performance of the present invention is:
Pilot project The shielding material
Tensile strength, MPa 7~15
Elongation at break, MPa 400~700
Specific insulation, Ω m 0.1~50
Shore A hardness, H A 60~80
Tensile strength rate of change after the 135 ℃ * 168h heat ageing, % -15~+15
Elongation at break rate of change after the 135 ℃ * 168h heat ageing, % -15~+15
Embodiment
The present invention selects for use Ethylene Propylene Terpolymer (EPDM) rubber composition of soft, highly-flexible as Insulation Material, can reach the requirement of cable highly-flexible, and the ethylene propylene diene rubber good electric property, can satisfy the requirement of midium voltage cable fully.
Embodiment 1: Insulation Material and shielding material raw material components are as follows:
Figure C200410089024D00051
Wherein ethylene propylene diene rubber (EPDM) is the product that adopts Dutch States Mines (DSM), and the trade mark is Keltan 2470.Conductive black is the VXC-72 that Cabot Co.,Ltd (CABOT) produces.Calcinated argil is calcining and the surface treatment potter's clay Translink 37 that An Ge company (ENGELHARD) produces.Antiaging agent is 2,2,4-trimethyl-1,2-dihyaroquinoline (RD).Organic peroxide is that cumyl peroxide (DCP) coupling agent is vinyl three (methoxyethoxy) silane (A-172).Wax is paraffin.Processing oil is the SUNPAR 2280 that solar oil company (SUNOCO) produces.
The preparation method is as follows: earlier EPDM rubber and antiaging agent are dropped into banbury, add calcinated argil (Insulation Material) or conductive black (shielding material) behind the banburying 3min, add wax and processing oil again, continue to add coupling agent, discharging behind the banburying 1min behind the banburying 2min.After playing three triangle bags in the two roller mills, add organic peroxide, roll over page or leaf or granulation after the thin-pass 8 times.
Be pressed into after the test piece as follows with Insulation Material that processes and shielding material through recording its performance after the 160 ℃ * 40min heat cure:
Figure C200410089024D00061
Embodiment 2: Insulation Material and shielding material raw material components are as follows:
Figure C200410089024D00062
Figure C200410089024D00071
Wherein ethylene propylene diene rubber (EPDM) is the product that adopts JSR company, and the trade mark is EP21.Conductive black is the BP2000 that Cabot Co.,Ltd (CABOT) produces.Calcinated argil is calcining and the surface treatment potter's clay Translink 77 that An Ge company (ENGELHARD) produces.Antiaging agent is 1,2-mercaptobenzimidazole (MB).Organic peroxide is cumyl peroxide (DCP).Coupling agent is vinyltrimethoxy silane (A-171).Wax is Tissuemat E.Processing oil is the SUNPAR 2280 that solar oil company (SUNOCO) produces.
The preparation method is as follows: earlier EPDM rubber and antiaging agent are dropped into two roller mills, add calcinated argil (Insulation Material) or conductive black (shielding material) behind the bag roller, add wax and processing oil again, powder is eaten up the back and is added coupling agent, add organic peroxide again, roll over page or leaf or granulation after the thin-pass 8 times.
Be pressed into after the test piece as follows with Insulation Material that processes and shielding material through recording its performance after the 160 ℃ * 40min heat cure:
Figure C200410089024D00072
Embodiment 3: Insulation Material and shielding material raw material components are as follows:
Figure C200410089024D00081
Wherein ethylene propylene diene rubber (EPDM) is the product that adopts ExxonMobil company, and the trade mark is Vistalon 1703P.Conductive black is the N220 of Tianjin Carbon Black Factory.Calcinated argil is homemade calcining and surface treatment potter's clay Glc.Antiaging agent is 1,2-mercaptobenzimidazole (MB).Organic peroxide is that cumyl peroxide (DCP) coupling agent is vinyl three (methoxyethoxy) silane (A-172).Wax is paraffin.Processing oil is the SUNPAR 2280 that solar oil company (SUNOCO) produces.
The preparation method is as follows: the recipe ingredient branch is assembled in the corresponding hopper, adopts the diffusing granulation of continuous mixing dual-screw pelletizer component.
Be pressed into after the test piece as follows with Insulation Material that processes and shielding material through recording its performance after the 160 ℃ * 40min heat cure:
Figure C200410089024D00082
Technique effect of the present invention:
10/17.5 (20) the kV India-rubber cable of producing with Insulation Material of the present invention and shielding material satisfies related request the GB/T 12706.2 (adopting by equation IEC 60502-2) " rated voltage 1kV (Um=1.2kV) arrives extruding insulation power cable and annex the 2nd part thereof of 30kV (Um=36kV): the cable of specified cable from 1kV (Um=1.2kV) to 30kV (Um=36kV) " fully. Need to prove that especially cable minimum bend diameter of the present invention can reach 1.5D (D is the outside diameter of cable).
10/17.5 (20) the kV India-rubber cable of producing with Insulation Material of the present invention and shielding material is 1.5D bending front and back 24kV partial discharge test results at bending diameter:
 
Shelf depreciation
Before the bending 2.5pC
After the bending 3.5pC
And the single-core cable minimum bend diameter of regulation is 24D among the GB/T 12706.2, and shelf depreciation requires to be not more than 20pC. As seen the India-rubber cable that adopts the present invention to produce is very soft, and crooked rear electrical property is still good.

Claims (1)

1. press in one kind India-rubber cable with the shielding material, calculate with constituent mass, its component is: 100 parts of ethylene propylene diene rubbers, 50~100 parts of conductive blacks, 1~3 part of antiaging agent, 2~4 parts of organic peroxides, 1~2 part of coupling agent, 2~8 parts in wax, 5~20 parts of processing oils;
Described antiaging agent is 2,2,4-trimethyl-1,2-dihyaroquinoline or 1,2-mercaptobenzimidazole; Organic peroxide is a cumyl peroxide, and coupling agent is vinyltrimethoxy silane or vinyl trimethoxy Ethoxysilane; Wax is paraffin or Tissuemat E;
Described shielding material is prepared by banburying or kneading, dispersion granulation or a rolling page or leaf operation by recipe ingredient in clean environment;
Need 160 ℃ * 40min heat cure to obtain design performance after the moulding of described shielding material, its Shore A hardness is 60~80.
CNB2004100890245A 2004-12-02 2004-12-02 Screening material for medium voltage rubber insulation cable Active CN100514507C (en)