CN101790564A - Saturated polyester resin composition and hot melt adhesive composition - Google Patents
Saturated polyester resin composition and hot melt adhesive composition Download PDFInfo
- Publication number
- CN101790564A CN101790564A CN200880104587A CN200880104587A CN101790564A CN 101790564 A CN101790564 A CN 101790564A CN 200880104587 A CN200880104587 A CN 200880104587A CN 200880104587 A CN200880104587 A CN 200880104587A CN 101790564 A CN101790564 A CN 101790564A
- Authority
- CN
- China
- Prior art keywords
- saturated polyester
- polyester resin
- composition
- resin composition
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a saturated polyester resin composition which is excellent in sealing properties and adhesive strength to metal materials such as copper and aluminum as well as resin materials such as polyethylene terephthalate. This saturated polyester resin composition is particularly improved in adhesive strength at low temperatures. Specifically, the saturated polyester resin composition contains a saturated polyester resin, a crystalline polyolefin resin and a thermoplastic soft acrylic resin. The saturated polyester resin composition may further contain an epoxy resin. The thermoplastic soft acrylic resin preferably has a Shore A hardness of less than 90 and a melt index at 190 DEG C under a load of 2.16 kg of not less than 10 g/10 minutes.
Description
Technical field
The present invention relates to contain the saturated polyester resin composition of saturated polyester resin, crystalline polyolefin resinoid and thermoplastic soft acrylic resin and the hot-melt adhesive composition that provides by said composition.
Background technology
The electrical specification of saturated polyester resin and thermal property excellence, and because it is to plastic materials such as vibrin, the characteristic of the adaptation excellence of metallic substance such as copper, aluminium has been widely used as the polyethylene terephthalate resinoid of IC-card and the laminated hotmelt of using the suitable wirning harness in hotmelt and automobile, electric and electronic field etc. that the IC chip is installed sheet material.Above-mentioned IC-card and wirning harness are being popularized in recent years, on the other hand, are improving for the requirement of the bond strength of the hotmelt that uses.Particularly carried out maintenance in the bond strength of wide temperature range, in the winter time, summer etc. the applied temps scope the stripping strength of protective membrane of IC-card keep having become problem.
Therefore, so far, have been proposed in the saturated polyester resin hot-melt adhesive composition that adds, mixed various resinous principles.For example, proposed in saturated polyester resin, to add ldpe resin, high-density polyethylene resin, and added the saturated polyester class hot-melt adhesive composition (with reference to patent documentation 1) of Resins, epoxy.In addition, proposed in saturated polyester resin, to have added the saturated polyester class hot-melt adhesive composition (with reference to patent documentation 2) of resol.In addition, proposed to comprise the saturated polyester class hot-melt adhesive composition (with reference to patent documentation 3) of crystallinity polyester resin and amorphism polyester resin and Resins, epoxy.
Patent documentation 1: the spy opens the 2004-269654 communique
Patent documentation 2: the spy opens the 2003-327940 communique
Patent documentation 3: the spy opens the 2002-138269 communique
Summary of the invention
The problem that invention will solve
According to the method for record in patent documentation 1, patent documentation 2 and the patent documentation 3, improve because of saturated polyester resin monomer as main component with the stripping strength of tackiness agent.But, do not solve and peel off the poor reliability under the applied temps (10 ℃～80 ℃) in adhesive interface under the low temperature.
The objective of the invention is to formation, provide and can realize the composition of improvement the bond strength of resin material under low temperature (10 ℃～10 ℃) such as metallic substance such as copper, aluminium and polyethylene terephthalates by the improvement saturated polyester resin composition.
Be used to solve the means of problem
In view of above-mentioned problem, inventor's further investigation, found that by cooperation crystalline polyolefin resinoid and thermoplastic soft acrylic resin in saturated polyester resin, thereby improvement has been finished the present invention in the bond strength of wide temperature range (10 ℃～80 ℃).
The present invention is as described below.
1. saturated polyester resin composition is characterized in that, contains (A) saturated polyester resin, (B) crystalline polyolefin resinoid and (C) thermoplastic soft acrylic resin.
2. above-mentioned 1 described saturated polyester resin composition, the Shore A hardness of wherein said thermoplastic soft acrylic resin (C) are less than 90, and the melt index values under 190 ℃ of temperature and the load 21.2N is more than 10g/10 minute.
3. above-mentioned 2 described saturated polyester resin compositions, the Shore A hardness of wherein said thermoplastic soft acrylic resin (C) is 10～80.
4. above-mentioned 2 described saturated polyester resin compositions, the melt index values of wherein said thermoplastic soft acrylic resin (C) under 190 ℃ of temperature and load 21.2N is 10～100g/10 minute.
5. above-mentioned 1 described saturated polyester resin composition, wherein said thermoplastic soft acrylic resin (C) is a segmented copolymer.
6. above-mentioned 5 described saturated polyester resin compositions, the Shore A hardness of wherein said thermoplastic soft acrylic resin (C) are less than 90, and the melt index values under 190 ℃ of temperature and the load 21.2N is more than 10g/10 minute.
7. above-mentioned 1 described saturated polyester resin composition, when wherein described saturated polyester resin (A), described crystalline polyolefin resinoid (B) and described thermoplastic soft acrylic resin (C) being added up to 100 quality %, the content of described thermoplastic soft acrylic resin (C) is 0.5～30 quality %.
8. above-mentioned 1 described saturated polyester resin composition wherein also contains (D) Resins, epoxy.
9. above-mentioned 8 described saturated polyester resin compositions, when wherein described saturated polyester resin (A), described crystalline polyolefin resinoid (B), described thermoplastic soft acrylic resin (C) and described Resins, epoxy (D) being added up to 100 quality %, the content of described Resins, epoxy (D) is 1～25 quality %.
10. hot-melt adhesive composition is characterized in that, contains above-mentioned 1 described saturated polyester resin composition.
11. hot-melt adhesive composition is characterized in that, contains above-mentioned 8 described saturated polyester resin compositions.
The effect of invention
Use the adhesive member of saturated polyester resin composition of the present invention, because the driving fit improved performance, therefore the bond strength of resin materials such as metallic substance such as copper, aluminium and polyethylene terephthalate is improved as hot-melt adhesive composition.Particularly improve by bond strength and the destruction form of low temperature to the pyritous wide temperature range.In addition, owing to improve tackiness agent and, therefore can obtain the adhesive member of stopping property excellence by the interface peel state of sticking material.
Embodiment
An embodiment of the invention are described as follows, but the present invention are not defined in this.In this specification sheets, " (methyl) vinylformic acid " expression vinylformic acid and methacrylic acid, " (methyl) acrylate " expression acrylate and methacrylic ester.
Saturated polyester resin composition of the present invention, it is characterized in that, comprise (A) saturated polyester resin (below be also referred to as " resinous principle (A) "), (B) crystalline polyolefin resinoid (below be also referred to as " resinous principle (B) ") and (C) thermoplastic soft acrylic resin (below be also referred to as " resinous principle (C) ").
Above-mentioned resinous principle (A) is not particularly limited, the saturated polyester resin that can use polycondensation by sour composition and polyhydroxy reactant etc. to obtain.
Monomeric sour composition and polyhydroxy reactant as forming above-mentioned resinous principle (A) are not particularly limited, and can use following each composition.
As above-mentioned sour composition, can enumerate aromatic acid, aliphatic dibasic acid and alicyclic diprotic acid etc.
As the specific examples of aromatic acid, can enumerate terephthalic acid, m-phthalic acid, Tetra hydro Phthalic anhydride, α-naphthalic acid, β-naphthalic acid and their ester organizer etc.
As the specific examples of aliphatic dibasic acid, can enumerate succsinic acid, pentanedioic acid, hexanodioic acid, pimelic acid, suberic acid, nonane diacid, sebacic acid, undecylenic acid, dodecanedioic acid and their ester organizer etc.
In addition, as the specific examples of alicyclic diprotic acid, can enumerate 1,4 cyclohexanedicarboxylic acid, Tetra Hydro Phthalic Anhydride, hexahydrophthalic anhydride etc.
Above-mentioned sour composition can only use a kind, also can will also use more than 2 kinds.
In the above-mentioned sour composition, preferred terephthalic acid and ester organizer thereof aspect bond strength, containing of terephthalic acid is proportional, is preferably 30 moles more than the % with respect to all acid composition.If the terephthalic acid composition is 30 moles more than the %, obtain enough resin cohesive force and hardness, bond strength is improved, so preferably.
In addition, as sour composition, in not damaging the gelation and the scope of bond strength of this saturated polyester resin (A) when synthetic, can be with unsaturated acid such as toxilic acid, fumaric acid, dimeracids, polycarboxylic acids such as trimellitic acid, pyromellitic acid etc. are also used, with respect to all acid composition, can use 5 moles of scopes below the %.
As above-mentioned polyhydroxy reactant, can enumerate dibasic alcohol and polyvalent alcohols such as aliphatic dihydroxy alcohol, alicyclic dibasic alcohol.
In the above-mentioned dibasic alcohol,, can enumerate ethylene glycol, 1 as the specific examples of aliphatic dihydroxy alcohol, 2-propylene glycol, 1, ammediol, 1,3 butylene glycol, 1,4-butyleneglycol, 1,5-pentanediol, 1,6-hexylene glycol, 1,8-ethohexadiol, 1,9-nonanediol, neopentyl glycol, 3-methyl pentanediol, 2,2,3-neopentyl glycol, glycol ether, triglycol, dipropylene glycol etc.
As the specific examples of alicyclic dibasic alcohol, can enumerate 1,4 cyclohexane dimethanol, Hydrogenated Bisphenol A etc.
Above-mentioned dibasic alcohol can only use a kind, also can will also use more than 2 kinds.
As above-mentioned dibasic alcohol, preferably use 1, the 4-butyleneglycol, 1, the 4-butyleneglycol is preferably 30 moles more than the % with respect to the ratio of whole polyhydroxy reactants.If 1, the 4-butyleneglycol is 30 moles more than the %, owing to obtain enough cohesive force, bond strength is improved, so obtain high heat resistance.
In addition, as above-mentioned polyvalent alcohol, can enumerate glycerine, trimethylolethane, TriMethylolPropane(TMP), tetramethylolmethane etc.They can only use a kind, also can will also use more than 2 kinds.Above-mentioned polyvalent alcohol can use 5 moles of scopes below the % with respect to whole polyhydroxy reactants.
The fusing point of saturated polyester resin of the present invention (A) is that the above main endotherm peak temperature of 1J/g is represented with the fusion heat that adopts differential scanning calorimeter (below be also referred to as DSC) to measure, preferably the fusing point of representing with this melting heat peak temperature is 50 ℃～200 ℃ a vibrin, more preferably 60 ℃～150 ℃ vibrin.If this fusing point is 50 ℃～200 ℃ scopes, because coating temperature and tack temperature become suitable temperature, be difficult to take place the thermal degradation when and the oxidation of adhesive substrate, therefore obtain excellent adhesion strength.
The melt viscosity of above-mentioned saturated polyester resin (A) is 10～500g/10 minute surveying periodic melt index values (below be also referred to as " MI value ") under the condition of 190 ℃ of temperature, load 21.2N preferably.This MI value more preferably 10～300g/10 minute, more preferably 10～100g/10 minute.If the MI value of this saturated polyester resin (A) is 10～500g/10 minute, then can easily mix with other resinous principles, obtain showing the more resin combination of excellent adhesion strength.
Above-mentioned saturated polyester resin (A) can adopt synthetic, the manufacturing of usual method.For example, charging feedstock and catalyzer are arranged, the melt phase polycondensation that under the temperature more than the fusing point of resultant, heats, at the following polymeric solid phase polymerization method of the fusing point of resultant, use the solution polymerization process of solvent etc., can adopt any method, polyester for the appropriate polymerization degree that obtains following the object of the invention, and from the economy aspect, the preferred molten polymerization adopts ester-interchange method, direct esterification manufactured.
In the saturated polyester resin composition of the present invention, the content of above-mentioned saturated polyester resin (A), total amount with respect to above-mentioned resinous principle (A), resinous principle (B) and resinous principle (C), be preferably 40～98.5 quality %, more preferably 50～95 quality % are preferably 60～90 quality % especially.Above-mentioned resinous principle (A) if ratio be the scope of 40～98.5 quality % owing to obtain enough peel adhesion strength, so preferably.
In addition, in the saturated polyester resin composition of the present invention, contain crystalline polyolefin resinoid (B).Above-mentioned resinous principle (B) plays and prevents in the concentrated effect of the peel stress at adhesive substrate interface.Above-mentioned resinous principle (B) is in the state that is dispersed in the binder composition with microgranular.This dispersed particle surface and low as the wettability at saturated polyester resin (A) interface of principal constituent.In addition, the high modulus of saturated polyester resin (A) owing to having because of crystallization than principal constituent can make the peel stress that puts on adhesive member be scattered in the interface of the dispersed particle of saturated polyester resin (A) and crystalline polyolefin resinoid (B).Its result can prevent the concentrating of peel stress at tackiness agent and adhesive substrate interface, and peel adhesion strength improves.
The degree of crystallinity of above-mentioned resinous principle (B), preferably surveying periodic melting heat with DSC is more than the 50J/g, perhaps heat of crystallization is more than the 50J/g.Especially, more preferably melting heat is more than the 80J/g, and perhaps heat of crystallization is 80J/g above (it is following to be generally 220J/g).That is, can make the melting heat of resinous principle (B) or heat of crystallization is 50～220J/g, also can be the 80J/g～220J/g of above-mentioned lower value.If melting heat or heat of crystallization are the scope of 50～220J/g, the difference of the modulus of resinous principle (A) and resinous principle (B) becomes big, and peel stress disperses.Its result can prevent the concentrating of peel stress at tackiness agent and adhesive substrate interface, and peel adhesion strength improves.
The composition that forms above-mentioned resinous principle (B) is to be selected from more than a kind or 2 kinds of vinyl monomer with unsaturated double-bond.For example, be the olefines vinyl monomer of ethene, propylene, carbon number 2～20.Above-mentioned resinous principle (B) is preferably with high-density polyethylene resin and the ldpe resin of ethene as principal constituent, more preferably density 0.910～0.925g/cm
3New LDPE (film grade).
The melt viscosity of above-mentioned resinous principle (B) is surveyed periodic MI value and is preferably 0.5～150g/10 minute, more preferably 1～120g/10 minute under the condition of 190 ℃ of temperature, load 21.2N.If 0.5～150g/10 minute scope of MI value, can with above-mentioned resinous principle (A) and (C) uniform mixing, obtain stable bond strength.In addition, because resin combination has the flexibility of appropriateness, so even also can obtain sufficient bond strength at low temperature.
In the resin combination of the present invention, the content of above-mentioned crystalline polyolefin resinoid (B), the total amount with respect to above-mentioned resinous principle (A), resinous principle (B) and resinous principle (C) is preferably 1～30 quality %, more preferably 3～25 quality %.Resinous principle (B) is if in the scope of 1～30 quality %, then as problem of the present invention from low temperature to pyritous wide region temperature under bond strength improve.
Above-mentioned thermoplastic soft acrylic resin (C) has adaptation, the particularly function of low temperature adhesion intensity of improvement to metal bases such as resin base materials such as polyethylene terephthalate and copper.As the means of improving the adaptation of adhesive substrate, improving tackiness agent is important to the wettability of adhesive substrate.In addition, utilize the flexibility of binder composition to prevent that the concentrating of peel stress at tackiness agent and adhesive substrate interface from also being important.This thermoplastic soft acrylic resin (C) is because at room temperature flexibility is also high, can prevent stress concentration at tackiness agent and adhesive substrate interface for peel stress.
Above-mentioned resinous principle (C) is characterised in that, is that high soft of flexibility is resin.Herein, so-called soft system is meant that the Shore A hardness of JIS K6253 regulation is less than 90.The Shore A hardness of above-mentioned resinous principle (C) is preferably 10～80 less than 90, and more preferably 30～70.Shore A hardness is 90 when above, because stress concentration at the interface of tackiness agent and adhesive substrate, therefore produces the unfavorable situation of peel adhesion strength reduction.
In addition, the melt viscosity of above-mentioned resinous principle (C) preferably has the melt viscosity that approaches above-mentioned resinous principle (A).The MI value of above-mentioned resinous principle (C) was preferably more than 10g/10 minute, and more preferably 15～100g/10 minute, more preferably 20～70g/10 minute.The MI value is during less than 10g/10 minute, because big with the melt viscosity difference of resinous principle (A), it is bad to produce the dispersion that resinous principle (C) takes place, and even can not make the unfavorable situation of composition.
The main monomer composition that forms above-mentioned resinous principle (C) is for being selected from (methyl) acrylate, for example, in the esterification set of monomers of the alkyl alcohol composition of carbon numbers 1～20 such as (methyl) methyl acrylate, (methyl) ethyl propenoate, (methyl) butyl acrylate and (methyl) acrylic component more than a kind or 2 kinds.Preferably, be principal constituent with methyl methacrylate, butyl acrylate.
In addition, in the scope of not damaging the object of the invention, can use olefin monomers such as ethene, propylene, the fragrant same clan such as vinylbenzene, alpha-methyl styrene vinyl monomer, Tetra hydro Phthalic anhydride, vinylformic acid etc. contain the monomer of carboxyl, and (methyl) glycidyl acrylate etc. contains the monomer of epoxy group(ing) etc.
Above-mentioned resinous principle (C) in the use temperature scope, intensity of resin (for example tensile strength etc.) and flexibility and to deposit be necessary.Therefore, the segmented copolymer that constitutes of the soft chain segment of wishing to serve as reasons hard segment and having flexibility with outspoken nature.The hard segment of segmented copolymer has the effect that keeps mechanical strength of resin in common use temperature scope, and soft chain segment has the effect of the flexibility of giving.Above-mentioned resinous principle (C) is under the situation of random copolymers, the balanced differences of the intensity of resin and flexibility in the use temperature scope, and the intensity of tackiness agent self reduces, and even causes the reduction of peel adhesion strength.
Make the method for the segmented copolymer of above-mentioned resinous principle (C), can use polymerization process arbitrarily.Preferably, can use the spy to open that 2000-44631 communique, spy are opened the 2001-158805 communique, the spy opens the manufacture method of putting down in writing in 2003-277574 communique and the Te Kai 2004-2844 communique.
In the saturated polyester resin composition of the present invention, the content of above-mentioned thermoplastic soft acrylic resin (C), total amount with respect to above-mentioned resinous principle (A), resinous principle (B) and resinous principle (C), be preferably 0.5～30 quality %, more preferably 1～25 quality %, more preferably 1～20 quality %.
Above-mentioned resinous principle (C) is during less than 0.5 quality %, can not realize as problem of the present invention from low temperature to pyritous wide region temperature the improvement of bond strength.On the other hand, when surpassing 30 quality %, the intensity of said composition self reduces, and bond strength also reduces.
Saturated polyester resin composition of the present invention can further contain (D) Resins, epoxy (below be also referred to as " resinous principle (D) ").
Above-mentioned Resins, epoxy (D) is adjusted the thermotolerance and the modulus of saturated polyester resin composition of the present invention as the adhesion imparting agent, is used to adjust the adaptation to adhesive substrate effectively.As above-mentioned resinous principle (D), for example, can use bisphenol-type epoxy resin, phenol aldehyde type epoxy resin, phenolic resin varnish type epoxy resin, cresols phenolic resin varnish type epoxy resin etc.Be preferably bisphenol-type epoxy resin.
The R﹠amp of preferred above-mentioned resinous principle (D); The B softening temperature is 50 ℃～180 ℃.Wherein, R﹠amp; The B softening temperature is the resin rerum natura by JIS K-6863-1994 regulation.
The content of the resinous principle in the saturated polyester resin composition of the present invention (D), total amount with respect to above-mentioned resinous principle (A), resinous principle (B), resinous principle (C) and resinous principle (D), be preferably 1～25 quality %, more preferably 2～20 quality %.Above-mentioned resinous principle (D) if the scope of content 1～25 quality %, then obtain enough adaptations to adhesive substrate, bond strength is improved.
In addition, in the scope of not damaging the object of the invention, can use the 2nd adhesion imparting agent.Can use for example terpine resin type adhesion imparting agents such as terpine resin, terpene phenolic resin, aromatic series modified terpene resin, hydrogenated terpene resin, modified rosin resin types such as rosin modified phenolic resin adhesion imparting agent, petroleum resin types such as aliphatic category petroleum resin, alicyclic ring same clan petroleum resin, fragrant same clan petroleum resin adhesion imparting agent etc.
In the saturated polyester resin composition of the present invention, can use weighting agent arbitrarily in the scope of not damaging purpose of the present invention.Weighting agent is used to adjust thermotolerance, modulus, anti-adhesive, productivity of saturated polyester resin composition of the present invention etc. effectively.
As above-mentioned weighting agent, can use for example mineral compound type weighting agents such as talcum, organic surface treatment talcum, clay, water-ground limestone, light calcium carbonate, silicon-dioxide, fumed silica, zinc oxide, magnesium hydroxide, aluminium hydroxide, titanium oxide, glass fibre, smectite type laminar silicic acid salt compound, organic process smectite type laminar silicic acid salt compound, organic compound type weighting agents such as carbon black, man-made fiber etc.The usage quantity of weighting agent with respect to 100 quality % saturated polyester resin composition of the present invention, is generally below the 30 quality %, is preferably below the 20 quality %, more preferably below the 10 quality %.
In saturated polyester resin composition of the present invention, can use the arbitrary stable agent in the scope of not damaging purpose of the present invention.Stablizer is used for the material of the stabilization adjustment of bond properties effectively for suppressing the thermolysis and the hydrolysis of saturated polyester resin composition of the present invention.As stablizer, can use anti hydrolysis agent, phenol antioxidant, phosphorous acid esters antioxidant, thioether class antioxidants etc. such as for example gathering carbodiimide.The usage quantity of stablizer with respect to 100 quality % saturated polyester resin composition of the present invention, is generally below the 10 quality %, is preferably below the 5 quality %.
In the saturated polyester resin composition of the present invention,, can use coupling agent arbitrarily in the scope of not damaging the object of the invention.Coupling agent is the adhesive substrate surface that acts on saturated polyester resin composition of the present invention, is used for the material of the adjustment of moisture-proof thermostability effectively.As coupling agent, can use alkyl such as dimethyldimethoxysil,ne for example is that aluminium such as the silane coupling agents such as silane coupling agent that contain vinyl such as the silane coupling agent that contains amino silane coupling agent, 3-Racemic glycidol oxygen propyl trimethoxy silicane etc. and contain epoxy group(ing) such as silane coupling agent, 3-aminopropyltriethoxywerene werene, vinyltriacetoxy silane, acetyl alkoxyl group diisopropoxy aluminium are that titanic acid ester such as coupling agent, sec.-propyl three isostearoyl base titanic acid ester are coupling agent etc.These coupling agents further improve feature of the present invention sometimes, can suitably use.The usage quantity of coupling agent with respect to 100 quality % saturated polyester resin composition of the present invention, is generally below the 5 quality %, is preferably below the 3 quality %, more preferably below the 2 quality %.
In the saturated polyester resin composition of the present invention,, can use other additives arbitrarily in the scope of not damaging the object of the invention.For example, can use fire retardants such as bromide fire retardant, phosphorus flame retardant, UV light absorber, softening agent and crystallization nucleating agent etc.
Saturated polyester resin composition of the present invention obtains by adopting arbitrary method hybrid resin composition (A), resinous principle (B), resinous principle (C) etc.For example, by utilize single screw extrusion machine, engagement type cocurrent and parallel axle twin screw extruder, engagement type anisotropic parallel axle twin screw extruder, the incorgruous inclined shaft twin screw extruder of engagement type, non-engagement type twin screw extruder, not exclusively engagement type twin screw extruder, the forcing machine of kneading type altogether, planet-shaped forcing machine, transmit each raw material of mixing such as extrusion shaping machines such as mixing forcing machine, plunger-type extruder, roll-type forcing machine or kneader and obtain.In addition, also can before above-mentioned mixing, use Henschel mixer, rotary drum etc. with the raw material pre-mixing.
Each material composition of saturated polyester resin composition of the present invention can use pellet shape, powder shape, arbitrary shape or proterties such as liquid.
The form of saturated polyester resin composition of the present invention can be used any form.For example, can use pellet shape, Powdered, sheet or membranaceous, bar-shaped, as to be dissolved in solvent solution shape etc.
Saturated polyester resin composition of the present invention is to the bond strength of various metals and plastic material, and especially the adaptation excellence can be used for various fields.For example, can be used for tackiness agent, sealing material, the packaged material of the parts in electronics, the machine field, in addition, in packaging field, can be used as the tackiness agent between laminate film, laminate film.Also can be used for the tackiness agent of the built-in material of automotive field, the sealing material of wirning harness etc.The using method of saturated polyester resin composition of the present invention is not particularly limited, and can fit to make hereinafter described hot melt process etc.
Hot-melt adhesive composition of the present invention is characterized in that, contains the saturated polyester resin composition of the invention described above.
Hot-melt adhesive composition of the present invention can become and contains resinous principle (A), (B) and (C), contains the composition of additive as required, and contains resinous principle (A), (B), (C) and (D), contains the composition of additive as required.Under any situation, can be that 60 ℃～200 ℃ temperature becomes molten state all, with bonding between the sticking material of the quilt that is same to each other or different to each other by making hot-melt adhesive composition of the present invention.
For using the bonding method of hot-melt adhesive composition of the present invention to be illustrated by sticking material.The shape of hot-melt adhesive composition of the present invention is under the membranaceous situation, can be present in each by between the sticking material by at room temperature making this film, and the limit adds flanging and is heated to 60 ℃～200 ℃ as required, thereby both are bonding.
Embodiment
Below enumerate embodiment, illustrate in greater detail the present invention, as long as but be no more than purport of the present invention, the present invention is not limited to described embodiment.
(manufacturing of saturated polyester resin)
In four-hole boiling flask with whipping appts, nitrogen ingress pipe, still tube, thermometer, 1 of 0.6mol dimethyl terephthalate (DMT), the 1.6mol that pack into, 1 of 4-butyleneglycol, 0.2mol, 6-hexylene glycol and 0.2 * 10
-2Mol is as the tetra-n-butyl titanic acid ester of catalyzer, the limit imports the nitrogen limit and heats up, after distillating methyl alcohol under 130 ℃～200 ℃, add 0.15mol m-phthalic acid and 0.25mol sebacic acid, after distillating water under 200 ℃～240 ℃, then slowly decompression the time, reaction is 3 hours under 250 ℃, the decompression of 1mmHg, obtains saturated polyester resin (A-1).The rerum natura of saturated polyester resin (A-1), the fusing point of measuring under 10 ℃/minute intensification condition with DSC is 135 ℃, and second-order transition temperature is-18 ℃.According to JIS K 7210, the MI value is 80g/10 minute under 190 ℃, the condition of load 21.2N.In addition, analyzed the monomer of this vibrin formed by NMR and analyze, the result is with molar ratio computing, terephthalic acid/isophthalic acid/sebacic acid/1,4-butyleneglycol/1,6-hexylene glycol=60/15/25/80/20.
(the formability evaluation of the manufacture method of composition 1, composition)
With 1440g as the saturated polyester resin (A-1) of resinous principle (A), 280g Japanese polyolefine society system new LDPE (film grade), trade(brand)name " ジ エ イ レ Star Network ス LD JM910 " (density: 0.918g/cm as resinous principle (B)
3Melting heat: 112J/g, MI value under 190 ℃ of temperature and the load 21.2N: 20g/10 minute, below be also referred to as " LDPE ") and 280g as the Kuraray society of resinous principle (C) system trade(brand)name " LA-2140E " (below be also referred to as " C-1 ") in advance behind the uniform mixing, drop in the Chi Beishe system 30mm twin screw extruder " PCM-30 ", 160 ℃ of following melting mixing.The molten resin cooling curing that will utilize forcing machine to extrude with line material shape in tank cuts into pellet shape with tablets press, obtains 1000g composition 1.This moment Visual Confirmation line material the state of extruding, extrusion capacity is stable, line material surface is also level and smooth, formability is judged as well.
Should illustrate that above-mentioned C-1 is the ternary block polymer of polymethylmethacrylate-butyl polyacrylate-polymethylmethacrylate.In addition, adopt the Shore A hardness of measuring C-1 according to the method for JIS K6253, the result is 32 (mensuration temperature: 23 ℃).
(making method of composition/copper bond test sheet)
Hot pressing under 180 ℃ condition (0.1MPa, 30 seconds) composition 1 is made the thick sheet material of about 100 μ m (80～120 μ m).The sheet cutting that obtains is become wide 25mm, long 50mm, make adhesive sheet.
The copper coin (material is C-1100P, and thick is 50 μ m) of adhesive substrate is cut into wide 25mm, long 75mm.
Adhesive sheet is clipped between 2 copper coins, makes the about 25mm of length residue between the stretching clamp, hot pressing is 30 seconds under 180 ℃, 0.1MPa, making composition 1/ bronze medal test film.
(to the adhesion test of copper base material)
Embodiment 1
Use tensile testing machine (society of Shimadzu Seisakusho Ltd. system " オ one ト グ ラ Off DSS-500 "), make composition 1/ bronze medal test film become the T font and be fixed in the anchor clamps of tension test, the peel adhesion strength when measuring tension load under the draw speed condition of 5 ℃ of temperature, 200mm/ minute is 113N/25mm.In addition, for the composition 1/ bronze medal test film of making under same condition, the peel adhesion strength when to make temperature condition be 23 ℃, 40 ℃ and 50 ℃ is respectively 108N/25mm, 76N/25mm and 50N/25mm.In addition, Visual Confirmation is peeled off form, and the result destroys form for cohesion under the temperature condition of 40 ℃ and 50 ℃.
Embodiment 2
Except the Kuraray society system trade(brand)name " LA-2250 " of using 280g (below be also referred to as " C-2 ") as the resinous principle (C), use with the same method of composition 1 and make composition 2.Good forming ability.In addition, under the condition same, make composition 2/ bronze medal test film with making composition 1/ bronze medal bond test sheet.And measure bond strength with similarly to Example 1 method.When its result, test temperature were 5 ℃, 23 ℃, 40 ℃ and 50 ℃, stripping strength separately was 128N/25mm, 96N/25mm, 69N/25mm and 44N/25mm.In addition, Visual Confirmation is peeled off form, and the result destroys form for cohesion under the temperature condition of 40 ℃ and 50 ℃.
Comparative example 1
With 1720g saturated polyester resin (A-1) with as the 280g of resinous principle (B) above-mentioned " ジ エ イ レ Star Network ス LD JM910 " uniform mixing, adopt with the same method of composition 1 and obtain composition 3.And formability is good.In addition, under the condition same, make composition 3/ bronze medal test film with making composition 1/ bronze medal bond test sheet.And measure bond strength with similarly to Example 1 method.When its result, test temperature were 5 ℃, 23 ℃, 40 ℃ and 50 ℃, stripping strength separately was 21N/25mm, 54N/25mm, 47N/25mm and 29N/25mm.In addition, Visual Confirmation is peeled off form, and the result destroys form for cohesion under 50 ℃ temperature condition.
Embodiment 1 compares with comparative example 1 with 2, finds high about 2～5 times degree of peel adhesion strength of 5 ℃～50 ℃ of temperature ranges, in addition, destroys form and also easily produces cohesion destruction.By this result as can be known, by add the thermoplastic soft acrylic resin in saturated polyester resin, to the adaptation raising of copper base material, bond properties and sealing property improve.
(manufacture method of composition 4～9, formability evaluation)
According to the composition proportioning of record in the table 1, prepare composition material, the same method of the manufacture method of employing and composition 1 obtains composition 4～9.In addition, the formability of all compositions is all good.Moreover the resinous principle in the table 1 uses resin as follows.
(1)LDPE
Used ldpe resin (Japanese polyolefine society system, trade(brand)name " ジ エ イ レ Star Network ス LD JM910 ").
(2)C-1
Used thermoplastic soft acrylic resin (Kuraray society system, trade(brand)name " LA-2140E ").
Shore A hardness (JIS K6253) under 23 ℃ of the temperature is 32, and the MI value under 190 ℃ of temperature and the load 21.2N is 31g/10 minute.
(3)C-2
Used thermoplastic soft acrylic resin (Kuraray society system, trade(brand)name " LA-2250 ").This C-2 is the ternary block polymer of polymethylmethacrylate-butyl polyacrylate-polymethylmethacrylate.
Shore A hardness (JIS K6253) under 23 ℃ of the temperature is 65, and the MI value under 190 ℃ of temperature and the load 21.2N is 25g/10 minute.
(4)C-3
Used thermoplastic soft acrylic resin (Kuraray society system, trade(brand)name " LA-4285 ").This C-3 is the ternary block polymer of polymethylmethacrylate-butyl polyacrylate-polymethylmethacrylate.
Shore A hardness (JIS K6253) under 23 ℃ of the temperature is 95, and the MI value under 190 ℃ of temperature and the load 21.2N is 1.5g/10 minute.
(5) soft acrylic rubber
Mitsubishi rayon society system, trade(brand)name " メ タ Block レ Application W-310 " have been used.
(6) Resins, epoxy
Used bisphenol A type epoxy resin as resinous principle (D).R﹠amp; The B softening temperature is 138 ℃.
Embodiment 3～4 and comparative example 2
Use composition 4～6, make composition/copper test film, implemented the mensuration of bond strength with method similarly to Example 1.It is the results are shown in the embodiment 3～4 and the comparative example 2 of table 2.Among the result of the destruction form in the table 2, " interface " is expressed as the interface peel of resin combination and adhesive substrate, and the cohesion of " cohesion " expression resin combination destroys.
Comparative example 2 is the examples that do not contain resinous principle (C) and used Resins, epoxy.
Comparative example 2 is compared with comparative example 1, and under 23 ℃～50 ℃ temperature condition, peel adhesion strength is high a lot.And there is not to find an improvement of the peel adhesion strength under 5 ℃ cold condition.
On the other hand, embodiment 3 compares with comparative example 2 with comparative example 1 with 4,5 ℃～50 ℃ temperature, find about the high several times of peel adhesion strength, and cohesion also takes place and destroys in destruction form more than 40 ℃ easily, and to the adaptation height of copper base material, bond properties and sealing property improve.
Embodiment 5～7
Use composition 7～9, make composition/copper test film, implemented the mensuration of peel adhesion strength with method similarly to Example 1.With the embodiment 5～7 of its result in table 2.
In embodiment 5 and embodiment 6,, in 5 ℃～50 ℃ wide temperature range, confirm the improvement of peel adhesion strength and destruction form although the usage quantity of resinous principle (C) is respectively 5 quality %, 3 quality %.
(manufacturing of composition 10～11 and formability evaluation)
Use acrylic acid or the like thermoplastic resin C-3 as resinous principle (C), according to the composition shown in the table 1, use the operation manufacturing composition 10 same with the manufacture method of composition 1, line material half blocks as a result, can not obtain stable line material, fails to make composition.
Therefore, for Shore A hardness height, acrylic resin that the MI value is low excessively, we can say to obtain the composition shown in the present invention.
In addition, replace resinous principle (C) and the soft propylene acids rubber of use non-thermal plasticity, non-segmented copolymer, according to the composition shown in the table 1, use with the same operation of the manufacture method of composition 1 and make composition 11, countless concavo-convex of online material surface Visual Confirmation.
Therefore, used under the situation of soft propylene acids rubber of non-thermal plasticity since in resinous principle (A) homodisperse not, when for example providing as sheet or membranaceous tackiness agent, the possibility that produces unfavorable situations such as flake, fragment is big.
(to the adhesion test of polyethylene terephthalate film)
Embodiment 8 and comparative example 3
Except composition 6 shown in the use table 1 and composition 4 and use the thick polyethylene terephthalate film of 100 μ m (below be also referred to as " PET film ") as the adhesive substrate, with with the same method of copper test film situation, make the bond test sheet, implement and the same tension test of method shown in the embodiment 1.It is the results are shown in the table 3.Among the result of the destruction form in table 3, " interface " is expressed as the interface peel of resin combination and adhesive substrate, and the cohesion of " cohesion " expression resin combination destroys, in addition, and the destruction of " material damage " expression PET film.
According to table 3, to compare with having used the comparative example 3 that does not contain the thermoplastic soft acrylic resin and contain the composition of Resins, epoxy, embodiment 8 peel adhesion strength in wide temperature range is strong, forms the material damage of PET film easily.By this results verification, the composition that contains thermoplastic soft acrylic resin (C) contains Resins, epoxy with replacing the thermoplastic soft acrylic resin composition is compared, to the adaptation and the stopping property excellence of polyethylene terephthalate.
Utilize possibility on the industry
Saturated polyester resin composition of the present invention and to have used the hot-melt adhesive composition of said composition be bonding strength height to metal material and resin material, adaptation be excellent material also. Therefore, be suitable for the bonding of the encapsulant of electric-electronics, automotive field and encapsulating material or foreign material (metal/resin).
Claims (11)
1. saturated polyester resin composition is characterized in that, contains (A) saturated polyester resin, (B) crystalline polyolefin resinoid and (C) thermoplastic soft acrylic resin.
2. the described saturated polyester resin composition of claim 1, the Shore A hardness of wherein said thermoplastic soft acrylic resin (C) are less than 90, and the melt index values under 190 ℃ of temperature and the load 21.2N is more than 10g/10 minute.
3. the described saturated polyester resin composition of claim 2, the Shore A hardness of wherein said thermoplastic soft acrylic resin (C) is 10～80.
4. the described saturated polyester resin composition of claim 2, the melt index values of wherein said thermoplastic soft acrylic resin (C) under 190 ℃ of temperature and load 21.2N is 10～100g/10 minute.
5. the described saturated polyester resin composition of claim 1, wherein said thermoplastic soft acrylic resin (C) is a segmented copolymer.
6. the described saturated polyester resin composition of claim 5, the Shore A hardness of wherein said thermoplastic soft acrylic resin (C) are less than 90, and the melt index values under 190 ℃ of temperature and the load 21.2N is more than 10g/10 minute.
7. the described saturated polyester resin composition of claim 1, when wherein described saturated polyester resin (A), described crystalline polyolefin resinoid (B) and described thermoplastic soft acrylic resin (C) being added up to 100 quality %, the content of described thermoplastic soft acrylic resin (C) is 0.5～30 quality %.
8. the described saturated polyester resin composition of claim 1 wherein also contains (D) Resins, epoxy.
9. the described saturated polyester resin composition of claim 8, when wherein described saturated polyester resin (A), described crystalline polyolefin resinoid (B), described thermoplastic soft acrylic resin (C) and described Resins, epoxy (D) being added up to 100 quality %, the content of described Resins, epoxy (D) is 1～25 quality %.
10. hot-melt adhesive composition is characterized in that, contains the described saturated polyester resin composition of claim 1.
11. hot-melt adhesive composition is characterized in that, contains the described saturated polyester resin composition of claim 8.