CN101788452A - 一种动态腐蚀试验方法及其设备 - Google Patents
一种动态腐蚀试验方法及其设备 Download PDFInfo
- Publication number
- CN101788452A CN101788452A CN200910231259A CN200910231259A CN101788452A CN 101788452 A CN101788452 A CN 101788452A CN 200910231259 A CN200910231259 A CN 200910231259A CN 200910231259 A CN200910231259 A CN 200910231259A CN 101788452 A CN101788452 A CN 101788452A
- Authority
- CN
- China
- Prior art keywords
- test
- test chamber
- medium
- inlet union
- media
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种动态腐蚀试验方法,它是在高于试验容器处设置一外置介质容器,并使试验介质在介质容器和试验容器间循环,保持试验容器中试验介质腐蚀性杂质浓度相对稳定进行试验的一种方法。本发明方法腐蚀试验数据更加准确、试验结果更为可靠,更接近于工业生产中的实际工况。其设备结构简单操作方便。
Description
技术领域:本发明涉及一种腐蚀试验的方法及其设备。特别是用于腐蚀性杂质含量较低的液化气体、液体、气体介质腐蚀试验的方法及其设备。
背景技术:许多气、液相工业产品及中间产品,其本身并无腐蚀性,腐蚀的发生主要是由其中含有的少量腐蚀性杂质引起的。由于生产工艺原因,生产过程中气、液相产品中含有少量腐蚀性杂质又是不可避免的,如石油、煤炭原料中均含硫,在以其为原料的化工产品中硫杂质常以硫化氢形式存在,硫化氢就具有腐蚀性,这是发生腐蚀的根本所在。而脱除这些杂质成本高昂,且难以完全脱除,这就造成了含少量杂质的工业产品的腐蚀问题。在实验室对工业过程中的腐蚀进行模拟试验时,由于实验容器/反应釜容积远小于工业储罐,随着试验中腐蚀进程的进行,介质中腐蚀性杂质含量随之降低,使腐蚀试验不能完全模拟工业储罐中介质的腐蚀性杂质含量基本不变的情况,从而影响实验的准确性。为解决这一问题,通常的是采用加大实验容器容积,以加大试验介质的量,以及采用较小的腐蚀试件的方法。但腐蚀分析要求试件必须满足一定尺寸,而不能减小,实验容器容积也常受限制,如慢应变腐蚀试验装置造价100余万元,其反应釜仅1.9升不可改变。
发明内容:本发明的目的是提供一种新的腐蚀试验方法及其设备,用以有效的克服现有腐蚀试验方法所存在的上述弊端。
本发明的目的是以如下技术方案实现的:
一、本发明的腐蚀试验方法,其实验步骤如下:
(一)采用可放入试件的广口试验容器,并设置密封盖,在试验容器的上部设试验介质出口接头,下部设进口接头;
(二)在相对高于试验容器处,设置一容积明显大于试验容器的外置式试验介质容器,在该容器的中部设介质进口接头,下部设出口接头,并分别用连接管将外置介质容器的介质出口接头与试验容器的介质进口接头连接,外置介质容器的介质进口接头与试验容器的介质出口接头连接,同时在介质容器的介质出口接头与试验容器的介质进口接头连接管上设一管道泵;
(三)先将试件放入试验容器,并将广口封闭,再向外置试验介质容器中通过加料口加入足够的试验介质,试验介质则同时经其介质出口接头与试验容器介质进口接头连接管流向试验容器,腐蚀试验即开始进行。
(四)开启介质容器介质出口接头与试验容器介质进口接头连接管上设置的管道泵,使试验介质在外置的介质容器和试验容器间循环,保持试验容器中试验介质腐蚀性杂质浓度相对稳定;如果腐蚀反应可产生热能,足以在反应热能的作用下实现介质的自然循环,或通过给试验容器加温,促使介质循环,可以不开启管道泵,专门用于这一工况的实验装置也可以不设置管道泵。
二、本发明试验方法的试验设备,它包括试验容器,其特征在于该试验容器为设有密封盖的广口容器,其上部设试验介质出口接头,下部设进口接头;在相对高于试验容器处,设置有一容积明显大于试验容器的外置介质容器,该介质容器的中部设有介质进口接头,下部设有出口接头,并分别用连接管将外置介质容器的介质出口接头与试验容器的介质进口接头连接,外置介质容器的介质进口接头与试验容器的介质出口接头连接,同时在介质容器的介质出口接头与试验容器的介质进口接头连接管上设有一管道泵。
为了便于观察试验介质的流向及流速,上述所说外置介质容器的介质进口接头与试验容器的介质出口接头连接管上可串接一透明管。
在腐蚀试验过程中,为了能够随时采样检验并了解试验容器中介质的杂质浓度,所说外置介质容器的介质进口接头与试验容器的介质出口接头连接管上还可连接有一三通阀,在该三通阀的第三端接一用于取样的橡胶管。
本发明方法工艺步骤合理,通过设置外置介质容器,并建立外置容器和试验容器间的介质循环,实现实验容器中介质杂质浓度的动态平衡,从而使腐蚀试验数据更准确、试验结果更加可靠,更接近于工业生产中的实际工况。本发明设备,结构简单,操作方便,是目前用于模拟工业化腐蚀试验结果比较准确、更接近实际的一种比较理想的试验设备。
附图说明:附图是本发明试验方法试验设备的结构示意图。
具体实施方式:附图给出了本发明试验设备一个具体实施例,下面结合附图对本发明设备及本发明方法进行详细说明:根据附图所示,图中1是试验容器,该试验容器1为设有密封盖3的广口容器,其上部设试验介质出口接头4,下部设进口接头2;在相对高于试验容器1处,设置有外置介质容器10,该外置介质容器10容积明显大于试验容器1,其中部设有介质进口接头9,下部设有出口接头11,并分别用连接管12将外置介质容器10的介质出口接头11与试验容器1的介质进口接头2连接,用连接管5将外置介质容器10的介质进口接头9与试验容器1的介质出口接头4连接,同时在介质容器介质出口接头11与试验容器介质进口接头2的连接管12上设有一管道泵13。先将试件放入试验容器1,并将广口封闭,再向外置试验介质容器10中通过加料口加入足够的试验介质,试验介质则同时经其介质出口接头11与试验容器介质进口接头2的连接管12流向试验容器1,此时腐蚀试验即开始进行。开启介质容器介质出口接头11与试验容器介质进口接头2的连接管12上设置的管道泵13,使试验介质在外置的介质容器10和试验容器1间循环,保持试验容器1中试验介质腐蚀性杂质浓度相对稳定,则进入正常的腐蚀试验。如果腐蚀反应可产生热能,足以在反应热能的作用下实现介质的自然循环,或通过给试验容器加温,促使介质循环,也可以不开启管道泵。
Claims (5)
1.一种动态腐蚀试验方法,其特征在于它的试验步骤为:
(一)采用可放入试件的广口试验容器,并设置密封盖,在试验容器的上部设试验介质出口接头,下部设进口接头;
(二)在相对高于试验容器处,设置一容积明显大于试验容器的外置式试验介质容器,在该容器的中部设介质进口接头,下部设出口接头,并分别用连接管将外置介质容器的介质出口接头与试验容器的介质进口接头连接,外置介质容器的介质进口接头与试验容器的介质出口接头连接,同时在介质容器的介质出口接头与试验容器的介质进口接头连接管上设一管道泵;
(三)先将试件放入试验容器,并将广口封闭,再向外置试验介质容器中通过加料口加入足够的试验介质,试验介质则同时经其介质出口接头与试验容器介质进口接头连接管流向试验容器,腐蚀试验即开始进行。
(四)当腐蚀反应产生热能,足以在反应热能的作用下实现介质通过两连接管在介质容器和试验容器间的自然循环,或通过给试验容器加温,促使介质循环,保持试验容器中试验介质腐蚀性杂质浓度相对稳定时,即进入正常腐蚀试验。否则,开启介质容器介质出口接头与试验容器介质进口接头连接管上设置的管道泵,使试验介质在外置的介质容器和试验容器间循环,保持试验容器中试验介质腐蚀性杂质浓度相对稳定,即进入正常腐蚀试验。
2.一种用于权利要求1所述腐蚀试验方法的设备,它包括试验容器(1),其特征在于该试验容器(1)为设有密封盖(3)的广口容器,其上部设试验介质出口接头(4),下部设进口接头(2);在相对高于试验容器(1)处,设置有一容积明显大于试验容器(1)的外置介质容器(10),该介质容器(10)的中部设有介质进口接头(9),下部设有出口接头(11),并分别用连接管(12,5)将外置介质容器的介质出口接头(11)与试验容器的介质进口接头(2)连接,外置介质容器的介质进口接头(9)与试验容器的介质出口接头(4)连接。
3.根据权利要求2所述的设备,其特征在于所说外置介质容器的介质出口接头(11)与试验容器的介质进口接头(2)连接管(12)上设有一管道泵(13)。
4.根据权利要求2所述的设备,其特征在于所说外置介质容器的介质进口接头(9)与试验容器的介质出口接头(4)连接管(5)上串接一透明管(6)。
5.根据权利要求2所述的设备,其特征在于所说外置介质容器的介质进口接头(9)与试验容器的介质出口接头(4)连接管(5)上连接有一三通阀(8),在该三通阀(8)的第三端接一橡胶管(7)。