CN101775888B - Production technology of high brightness composite floor board - Google Patents
Production technology of high brightness composite floor board Download PDFInfo
- Publication number
- CN101775888B CN101775888B CN201010101278XA CN201010101278A CN101775888B CN 101775888 B CN101775888 B CN 101775888B CN 201010101278X A CN201010101278X A CN 201010101278XA CN 201010101278 A CN201010101278 A CN 201010101278A CN 101775888 B CN101775888 B CN 101775888B
- Authority
- CN
- China
- Prior art keywords
- paper
- floor board
- hot press
- high brightness
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to the technical field of the composite floor board, in particular to a production technology of a high brightness composite floor board, which comprises the following steps: a. firstly wear resistant paper, decorative paper and balance paper are steeped in viscose glue, and then the wear resistant paper, the decorative paper, a substrate and the balance paper are sequentially stacked from top to bottom; b. the well-stacked floor board is sent into a hot press to be hot pressed, the hot press temperature of the hot press is 130 to 150 DEG C, the pressure is 20 to 30 tons, the temperature and the temperature are maintained for 10 t 20 minutes, then the hot press is cooled to the room temperature within 25 to 35 minutes, the hot press releases the pressure, and the floor board is discharged. The brightness of the floor board which is produced by the production technology can reach more than 110 degrees, and the wear resistant property of the surface of the floor board can reach 10000 turns.
Description
Technical field
The present invention relates to the composite floor board technical field, especially a kind of production technology of high brightness composite floor board.
Background technology
The floor is divided into solid wooden floor board, solid wooden compound floor and reinforced composite floorboard, and wherein the surface of solid wooden floor board and solid wooden compound floor is paint coat, though the surface brightness height, clean mark, anti-wear performance is poor, very easily scratches.
The reinforced composite floorboard production technology be with in/high density fiberboard or particieboard are base material, the back side at base material installs balance layer additional, one deck dipping decorative paper of mating formation on the surface of base material, after on dipping decorative paper, installing one deck wearing coat paper again additional, the compound reinforced composite floorboard product that promptly can be made into by wearing layer, decorative paper layer, substrate layer and four layers of composite construction of balance layer of hot pressing.This reinforced composite floorboard is compared with solid wooden floor board has advantages such as wearability is strong and not yielding, but because reinforced composite floorboard is by cover the anti-wear performance that one deck wearing coat paper improves the surface separately on decorative paper layer, then by the quick hot pressing of HTHP hot press short time, adopt the floor of this heat pressing process, the wearing coat paper that it covered can reduce apparent glossiness of composite floor board and definition greatly, influence the vision aesthetic effect of complex intensifying floor, be difficult to satisfy the user demand of high-end user requirement high gloss and fine definition.In order to obtain all gratifying composite floor board of glossiness definition and wearability,
A kind of existing solution is that original conventional composite consolidated floor balance layer, substrate layer, decorative layer and four layers of composite construction of wearing layer are changed into balance layer, substrate layer and decorative layer three-layer composite structure, wherein decorative layer is surface coating or facing paper or the bunting that oozes intrinsic wear-resistant material, but, the life cycle and the life-span of this method steel template are very short, and a template is merely able to hundreds of backs of hot pressing and just must polishes or change.
Summary of the invention
Technical problem to be solved by this invention is: a kind of production technology of high brightness composite floor board is provided, and the requirement of high brightness and high abrasion can be taken into account in the floor of coming out by this explained hereafter.
The technical solution adopted for the present invention to solve the technical problems is: a kind of production technology of high brightness composite floor board, have following processing step,
A. at first with abrasion-proof paper, facing paper, balance paper dipping viscose glue, carry out stacked according to the layer structure that is abrasion-proof paper, facing paper, substrate, balance paper from top to bottom respectively then;
B. stacked good floor is entered hot press hot pressing, the hot pressing temperature of hot press is 130 ℃～150 ℃, and pressure is the 20-30 ton, insulation 10-20 minute keep-ups pressure, hot press was cooled to room temperature in 25-35 minute then, and hot press pressure release ejecting plate, hot press are the steam heat press.
In step b, preferred, insulation 15 minutes keep-ups pressure; Hot press was cooled to room temperature in 30 minutes.
Abrasion-proof paper is the high brightness abrasion-proof paper, and facing paper is the high brightness facing paper.
The invention has the beneficial effects as follows: change conventional high-temperature hot high pressure compression technology, adopt long-time low-temp low-pressure heat pressing process, make the brightness on the floor of coming out by this explained hereafter can reach more than 110 degree, its surperficial anti-wear performance reaches 10000 right sides of turning left.
The specific embodiment
A kind of production technology of high brightness composite floor board has following processing step,
A. at first with abrasion-proof paper, facing paper, balance paper dipping viscose glue, carry out stacked according to the layer structure that is abrasion-proof paper, facing paper, substrate, balance paper from top to bottom respectively then;
B. stacked good floor is entered hot press hot pressing, the hot pressing temperature of hot press is 130 ℃～150 ℃, and pressure is the 20-30 ton, the insulation 15 minutes that keep-ups pressure, and hot press was cooled to room temperature in 30 minutes then, hot press pressure release ejecting plate.
Hot press is the steam heat press.
Abrasion-proof paper is the high brightness abrasion-proof paper, and facing paper is the high brightness facing paper.
Claims (3)
1. the production technology of a high brightness composite floor board is characterized in that: have following processing step,
A. at first with abrasion-proof paper, facing paper, balance paper dipping viscose glue, carry out stacked according to the layer structure that is abrasion-proof paper, facing paper, substrate, balance paper from top to bottom respectively then;
B. stacked good floor is entered hot press hot pressing, the hot pressing temperature of hot press is 130 ℃～150 ℃, and pressure is the 20-30 ton, insulation 10-20 minute keep-ups pressure, hot press was cooled to room temperature in 25-35 minute then, and hot press pressure release ejecting plate, described hot press are the steam heat press.
2. the production technology of high brightness composite floor board according to claim 1 is characterized in that: in step b, insulation 15 minutes keep-ups pressure; Hot press was cooled to room temperature in 30 minutes.
3. the production technology of high brightness composite floor board according to claim 1, it is characterized in that: described abrasion-proof paper is the high brightness abrasion-proof paper, described facing paper is the high brightness facing paper.