CN101760129A - 一种遮盖玻璃擦伤痕迹的有机硅油漆及其制备方法 - Google Patents
一种遮盖玻璃擦伤痕迹的有机硅油漆及其制备方法 Download PDFInfo
- Publication number
- CN101760129A CN101760129A CN200810160425A CN200810160425A CN101760129A CN 101760129 A CN101760129 A CN 101760129A CN 200810160425 A CN200810160425 A CN 200810160425A CN 200810160425 A CN200810160425 A CN 200810160425A CN 101760129 A CN101760129 A CN 101760129A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- emulsion
- organic silicon
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种遮盖玻璃擦伤痕迹的有机硅油漆及其制备方法，该油漆由聚甲基硅氧烷复合物2-6份，巴西棕榈蜡0.5-2份，蜂蜡0.5-2份，固态石蜡1-3份，石油溶剂汽油6-8份，缩水山梨糖醇单硬脂酸酯2-4份，POE山梨糖醇单硬脂酸酯(POE20mol)1-5份，其余为水。由上述组分混合制成的油漆由有机物构成，不含重金属含量，有效降低污染、利于环保。该产品漆膜质感丰富，摩擦不易产生静电，耐水性、弹性、柔韧性、耐化学性、耐磨损性能优良；且附着力强、遮盖率高、单位涂覆面积大，故使用成本低。
Description
技术领域：
本发明属于一种油漆及其制备方法.特别涉及一种遮盖玻璃擦伤痕迹的有机硅油漆及其制备方法。
背景技术：
目前的用于喷涂金属表面的油漆，喷涂的效果不理想，存在外观质量差、易划份、易磨损伤、光泽暗淡等缺陷，从而影响了金属板的外观质量和外观形象。
发明内容：
本发明的目的就在于克服上述现有技术中存在的不足，而提供一种易于喷涂，涂抹效果好，且喷涂后表面光亮的遮盖玻璃擦伤痕迹的有机硅油漆。本发明的技术方案是：一种遮盖玻璃擦伤痕迹的有机硅油漆及其制备方法，其特征在于：该油漆由有机硅乳液A和有机硅乳液B构成，其中按重量比，有机硅乳液A由α，ω-二羟基二甲基硅氧烷85份，γ-氨基丙基三乙氧基硅烷和γ-缩水甘油氧丙基三甲氧基硅烷的反应物15份，环状二甲基硅氧烷混合物(含六甲基环三硅氧烷8％，八甲基环四硅氧烷79％和十甲基环五硅氧烷13％)25份，二己基葵基二甲基氯化铵3份，氢氧化钾0.5份，醋酸水溶液若干，其余为水构成；有机硅乳液B由二甲基硅氧烷30份，山梨糖醇单月桂酸酯2份，聚氧化乙烯山梨糖醇单月桂酸酯2份，其余为水构成。
有机硅乳液A的制备方法为：将85份α，ω-二羟基二甲基硅氧烷与15份γ-氨基丙基三乙氧基硅烷和γ-缩水甘油氧丙基三甲氧基硅烷的反应物混合后，在80℃下加热30h，将10份上述物料于25份环状二甲基硅氧烷混合物(含六甲基环三硅氧烷8％，八甲基环四硅氧烷79％和十甲基环五硅氧烷13％)25份、3份二己基葵基二甲基氯化铵和水混合，再与0.5份氢氧化钾混合后，进行研磨，在75℃下搅拌3h，冷却至40℃，用醋酸水溶液中和后制得乳液A。
有机硅乳液B的制备方法为：将上述B组分进行研磨，制得乳液B。
将制得的A乳液和B乳液，以20∶80的比例进行混合，用水稀释10倍，制得油漆。
本发明的优点是：
1、因为本产品所选用的原料是有机化合物，不含重金属，无毒无污染。2、漆膜的质感丰富，摩擦不会产生静电，有优良的耐水性、弹性、柔韧性、耐化学性、耐磨损性。产品固含60％，遮盖率高、涂布面积大，单位使用量相对成本低。3、适用于金属表面喷涂，是安全防静电保护用漆。
具体实施方式：
将85kgα，ω-二羟基二甲基硅氧烷与15kgγ-氨基丙基三乙氧基硅烷和γ-缩水甘油氧丙基三甲氧基硅烷的反应物混合后，在80℃下加热30h，将10kg上述物料于25kg环状二甲基硅氧烷混合物(含六甲基环三硅氧烷8％，八甲基环四硅氧烷79％和十甲基环五硅氧烷13％)25kg、3kg二己基葵基二甲基氯化铵和水混合，再与0.5kg氢氧化钾混合后，进行研磨，在75℃下搅拌3h，冷却至40℃，用醋酸水溶液中和后制得乳液A。
二甲基硅氧烷30kg，山梨糖醇单月桂酸酯2kg，聚氧化乙烯山梨糖醇单月桂酸酯2kg，其余为水。将上述组分进行研磨，制得乳液B。
将制得的A乳液和B乳液，以20∶80的比例进行混合，用水稀释10倍，制得涂料。即可得遮盖玻璃擦伤痕迹的有机硅油漆。浸漆瓶于新瓶子外观相似、明亮、新颖。
将制得的油漆，用来浸涂擦伤的玻璃底材，浸渍3min后，将其在室温下干燥12h，涂膜固化，若用2％苛性苏打溶液在50℃下洗涤，可出去所涂胶漆。
Claims (4)
1.一种遮盖玻璃擦伤痕迹的有机硅油漆及其制备方法，其特征在于：该油漆由有机硅乳液A和有机硅乳液B构成，其中按重量比，有机硅乳液A由α，ω-二羟基二甲基硅氧烷85份，γ-氨基丙基三乙氧基硅烷和γ-缩水甘油氧丙基三甲氧基硅烷的反应物15份，环状二甲基硅氧烷混合物(含六甲基环三硅氧烷8％，八甲基环四硅氧烷79％和十甲基环五硅氧烷13％)25份，二己基葵基二甲基氯化铵3份，氢氧化钾0.5份，醋酸水溶液若干，其余为水构成；有机硅乳液B由二甲基硅氧烷30份，山梨糖醇单月桂酸酯2份，聚氧化乙烯山梨糖醇单月桂酸酯2份，其余为水构成。
2.依权利要求1所述的遮盖玻璃擦伤痕迹的有机硅油漆，其特征在于：有机硅乳液A的制备方法为：
将85份α，ω-二羟基二甲基硅氧烷与15份γ-氨基丙基三乙氧基硅烷和γ-缩水甘油氧丙基三甲氧基硅烷的反应物混合后，在80℃下加热30h，将10份上述物料于25份环状二甲基硅氧烷混合物(含六甲基环三硅氧烷8％，八甲基环四硅氧烷79％和十甲基环五硅氧烷13％)25份、3份二己基葵基二甲基氯化铵和水混合，再与0.5份氢氧化钾混合后，进行研磨，在75℃下搅拌3h，冷却至40℃，用醋酸水溶液中和后制得乳液A。
3.依权利要求1所述的遮盖玻璃擦伤痕迹的有机硅油漆，其特征在于：有机硅乳液B的制备方法为：将上述B组分进行研磨，制得乳液B。
4.依权利要求1所述的遮盖玻璃擦伤痕迹的有机硅油漆，其特征在于：将制得的A乳液和B乳液，以20∶80的比例进行混合，用水稀释10倍，制得油漆。