CN101748403A - 耐磨板的复合强化方法 - Google Patents

耐磨板的复合强化方法 Download PDF

Info

Publication number
CN101748403A
CN101748403A CN200910245161A CN200910245161A CN101748403A CN 101748403 A CN101748403 A CN 101748403A CN 200910245161 A CN200910245161 A CN 200910245161A CN 200910245161 A CN200910245161 A CN 200910245161A CN 101748403 A CN101748403 A CN 101748403A
Authority
CN
China
Prior art keywords
laser
steel plate
wear
plate
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200910245161A
Other languages
English (en)
Inventor
魏振华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sichuan Geelong Environmental Technology Co. Ltd.
Original Assignee
TIANJIN HANS YQ LASER CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN HANS YQ LASER CO Ltd filed Critical TIANJIN HANS YQ LASER CO Ltd
Priority to CN200910245161A priority Critical patent/CN101748403A/zh
Publication of CN101748403A publication Critical patent/CN101748403A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种耐磨板的复合强化方法,实施步骤如下:选择普通Q235钢板作为耐磨板基板,钢板厚度按不同使用要求分别选用6~30mm范围;金属光泽的钢板待强化处理表面分别预喷涂或刷涂含纳米级WC、TiC,SiC,CrC碳化物粉剂和分别复合微米级Cr、Si、Ni金属粉末,纳米级粉与微米级粉质量比例:2∶1,涂层厚度为:0.2~0.3mm;激光表面强化处理使用GS~TFL~6000型横流CO2激光器;激光功率为5kW,激光束尺寸为30×2.5mm,焦距为320mm,激光束扫描速度为6mm/s;激光纳米-微米级强化处理在原钢板表面1.5~2.0mm深度原位形成碳化物强化相颗粒和固溶体组成的多相组织的金属陶瓷强化层。本发明有效提高了耐磨板耐磨零部件的耐磨损、耐腐蚀、耐高温交变疲劳等性能,操作简单,效果非常显著。

Description

耐磨板的复合强化方法
技术领域
本发明涉及一种耐磨板的制作方法,特别涉及一种耐磨板的复合强化方法。
背景技术
目前,钢铁企业中轧钢生产上使用导卫板,烧结和炼铁等炉中使用的料仓附板、料车、布料器、料斗、管道、出料槽、风机、振动筛等耐磨零部件。电力工业企业中使用的出灰管、料仓、风机叶片、燃烧器管线、输料槽和料斗内衬,破碎机部件、磨煤机部件,运输机等。水泥、煤炭、矿山等行业广泛应用各种类型的耐磨板等耐磨零部件。这些耐磨零部件在承受小能量冲击条件下使用,为了增加其耐磨性能,常规的方法是使用耐磨铸造合金材料,例如Cr15W2系列铸造合金,或者使用贝化体Mn、Si高强度系列耐磨钢,用以提高强度、高温性能及高温环境下的耐磨性。另一种提高防腐性能的方式是在普通钢板上增加一层耐磨合金,用以提高耐磨性等指标。
但是由于耐磨板等耐磨零部件使用在具有高磨损、高温度和腐蚀介质的各类环境中,承受磨损、腐蚀、疲劳的复杂冷热交变等恶劣服役工况条件,造成耐磨板的耐磨零部件耐用性下降,更换频繁,消耗量大,浪费材料,增加生产成本,影响生产效率。
因此,提供一种节能降耗、应用效果显著的耐磨板的复合强化方法,是该领域技术人员应着手解决的问题之一。
发明内容
本发明的目的在于克服上述不足之处,提供一种节能降耗、应用效果显著的耐磨板的复合强化方法。
为实现上述目的本发明所采用的技术方案是:一种耐磨板的复合强化方法,其特征在于:具体实施步骤如下:
选择普通Q235钢板作为耐磨板基板,钢板厚度按不同使用要求分别选用6~30mm范围;金属光泽的钢板待强化处理表面分别预喷涂或刷涂含纳米级Wc、TiC,SiC,CrC碳化物粉剂和分别复合微米级Cr、Si、Ni金属粉末,纳米级粉与微米级粉质量比例:2∶1,涂层厚度为:0.2~0.3mm;
激光表面强化处理使用GS~TFL~6000型横流CO2激光器;激光功率为5KW,激光束尺寸为30×2.5mm,焦距为320mm,激光束扫描速度为6mm/s;激光纳米-微米级强化处理在原钢板表面1.5~2.0mm深度原位形成碳化物强化相颗粒和固溶体组成的多相组织的金属陶瓷强化层。
本发明的有益效果是:本发明是在耐磨板原有材质基础上,分别采用激光纳米金属间陶瓷表面合金强化,激光纳米复合微米级表面合金强化及激光表面淬火,相变强化相结合技术工艺方法,实现并提高耐磨板耐磨零部件耐磨损、耐腐蚀、耐高温交变疲劳等性能。其工艺简单,应用效果非常显著;同时,有效降低生产加工成本,提高加工产品的质量。
具体实施方式
以下结合较佳实施例,对依据本发明提供的具体实施方式、特征详述如下:
一种耐磨板的复合强化方法,具体实施步骤如下:
选择普通Q235钢板作为耐磨板基板,钢板厚度按不同使用要求,可以分别选用6~30mm范围任一尺寸。金属光泽的钢板待强化处理表面分别预喷涂或刷涂含纳米级Wc、TiC,SiC,CrC碳化物粉剂和分别复合微米级Cr、Si、Ni金属粉末,纳米级粉与微米级粉质量比例:2∶1,涂层厚度为:0.2~0.3mm。
激光表面强化处理使用GS~TFL~6000型横流CO2激光器。激光功率为5KW,激光束尺寸为30×2.5mm,焦距为320mm,激光束扫描速度为6mm/s。激光纳米-微米级强化处理在原钢板表面1.5~2.0mm深度原位形成金属陶瓷强化层。形成的一定厚度超细化,高强韧性,高耐磨性金相组织和合金层,为超细化、超饱和、均匀分布的碳化物强化相颗粒和固溶体组成的多相组织。
应用实例:
某钢铁生产公司热轧带钢生产线上使用一种65Mn钢制耐磨钢板,连续生产24小时将轧机的一对两块耐磨板被磨损成15~20mm深,宽约8~10mm的带状凹沟报废。停产更换非常困难,影响轧制生产线正常连续工作。采用激光纳米和微米复合金属间陶瓷表面合金强化处理,在耐磨钢板工作表面形成约1.5~2.0mm强化层。投入生产线上使用,达到72小时工作时间,比原来耐磨钢板提高2倍使用寿命,降低了停机时间,提高了生产效率。
上述参照实施例对该耐磨板的复合强化方法进行的详细描述,是说明性的而不是限定性的;因此在不脱离本发明总体构思下的变化和修改,应属本发明的保护范围之内。

Claims (1)

1.一种耐磨板的复合强化方法,其特征在于具体实施步骤如下:
选择普通Q235钢板作为耐磨板基板,钢板厚度按不同使用要求分别选用6~30mm范围;金属光泽的钢板待强化处理表面分别预喷涂或刷涂含纳米级Wc、TiC,SiC,CrC碳化物粉剂和分别复合微米级Cr、Si、Ni金属粉末,纳米级粉与微米级粉质量比例:2∶1,涂层厚度为:0.2~0.3mm;
激光表面强化处理使用GS~TFL~6000型横流CO2激光器;激光功率为5KW,激光束尺寸为30×2.5mm,焦距为320mm,激光束扫描速度为6mm/s;激光纳米-微米级强化处理在原钢板表面1.5~2.0mm深度原位形成碳化物强化相颗粒和固溶体组成的多相组织的金属陶瓷强化层。
CN200910245161A 2009-12-28 2009-12-28 耐磨板的复合强化方法 Pending CN101748403A (zh)