CN101747819A - 一种膨胀型透明防火涂料的生产工艺 - Google Patents

一种膨胀型透明防火涂料的生产工艺 Download PDF

Info

Publication number
CN101747819A
CN101747819A CN200810080140A CN200810080140A CN101747819A CN 101747819 A CN101747819 A CN 101747819A CN 200810080140 A CN200810080140 A CN 200810080140A CN 200810080140 A CN200810080140 A CN 200810080140A CN 101747819 A CN101747819 A CN 101747819A
Authority
CN
China
Prior art keywords
component
formaldehyde
retardant coating
expansion
fire
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200810080140A
Other languages
English (en)
Inventor
张力
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN200810080140A priority Critical patent/CN101747819A/zh
Publication of CN101747819A publication Critical patent/CN101747819A/zh
Pending legal-status Critical Current

Abstract

一种膨胀型透明防火涂料的生产工艺是用磷酸二氢铵、甲醛、季戊四醇、尿素、三乙醇胶、氢氧化钠按一定配比制得A组分；用三聚氰胺、甲醛、硼砂按一定配比制得B组分，然后将A、B组分以1∶1-2重量配比混合搅拌得到膨胀型透明防火涂料。本发明具有产品成本低，较好的防火性能的优点。

Description

一种膨胀型透明防火涂料的生产工艺
技术领域
本发明属于涂料领域，具体涉及一种膨胀型透明防火涂料的生产工艺。
技术背景
防火涂料是用于可燃性基材表面，能降低被涂材料表面的可燃性、阻滞火灾的迅速蔓延，用以提高被涂材料耐火极限的一种特种涂料。防火涂料涂覆在基材表面，除具有阻燃作用以外，还具有防锈、防水、防腐、耐磨、耐热以及涂层坚韧性、着色性、黏附性、易干性和一定的光泽等性能。
燃烧是一种快速的有火焰发生的剧烈的氧化反应，反应非常复杂，燃烧的产生和进行必须同时具备三个条件，即可燃物质、助燃剂(如空气、氧气或氧化剂)和火源(如高温或火焰)。为了阻止燃烧的进行，必须切断燃烧过程中的三要素中的任何一个，例如降低温度、隔绝空气或可燃物。
防火涂料的组燃机理大致可分为如下几种：
(1)防火涂料本身具有难燃性或不燃性，使被保护基材不直接与空气接触，延迟物体着火和减少燃烧的速度。
(2)防火涂料除本身具有难燃性或不燃性外，它还具有较低的导热系数，可以延迟火焰温度向被保护基材的传递。
(3)防火涂料受热分解出不燃惰性气体，冲淡被保护物体受热分解出的可燃性气体，使之不易燃烧或燃烧速度减慢。
(4)含氮的防火涂料受热分解出NO、NH3等基团，与有机游离基化合，中断连锁反应，降低温度。
(5)膨胀型防火涂料受热膨胀发泡，形成碳质泡沫隔热层封闭被保护的物体，延迟热量与基材的传递，阻止物体着火燃烧或因温度升高而造成的强度下降。
膨胀型防火涂料的防火机理在于当防火涂料的饰面层暴露于火焰上时，涂膜中的发泡性成分即受热分解，形成隔热性的海绵状发泡层，从而阻止火焰的传播。涂料中的防火助剂主要是发泡成分，包括碳源、发泡剂和有机氮化合物等，它们可以配合使用。
透明油漆由于光泽好，透明性强，面广泛用于建筑，车辆及铁木制品表面作防腐饰面材料。但由于该漆一旦出现火情，就会在短时间内造成火灾隐患。为了提高该油漆的防火性能。近年来很多单位都进行了研究工作，但所得的产品仍然存在着防火性、固化性、耐磨性较差的缺点。
发明内容
本发明的目的是提供一种即能保证油漆的透明性能，又具有一定防火性能的膨胀型透明防火涂料。
本发明提供的生产工艺如下：
本发明的主要内容是用磷酸二氢铵、甲醛、季戊四醇、尿素、三乙醇胶、氢氧化钠按一定配比制得A组分；用三聚氰胺、甲醛、硼砂按一定配比制得B组分，然后将A、B组分以1∶1-2重量配比混合搅拌得到膨胀型透明防火涂料；
各物料组成为
       原料名称    浓度    重量份范围
A组份：磷酸        84％    135-168
       季虎四醇            84-97
       甲醛        36％    230-237
       尿素        45％    55-66
       三乙醇胺            21-29
       氢氧化钠    15％    0.5-1
B组份：三聚氰胺            35-45
       甲醛                210-240
       硼砂                1-1.5
经过测试，该涂料具有较好的防火性能，当涂层为0.3-0.4mm厚时，在600一850火焰下，耐火极限可达30分钟，符合我国专业标准一级要求；该产品成本也较低，尤其是使用后材料具有较好的防火性能。
具体实施方式
实施例1：
       原料名称    浓度    重量份
A组份  磷酸        85％    168
       季虎四醇            97
       甲醛        7％     237
尿素               46％    66
       三乙醇胺            29
       氢氧化钠    10％    1
B组份  三聚氰胺            45
       甲醛                240
       硼砂                1
组分A与组分B按1∶1重量比混合。
实施例2
       原料名称    浓度    重量
A组份  磷酸        85％    135
       季虎四醇            84
       甲醛        37％    230
       尿素        46％    55
       三乙醇胺            21
       氢氧化钠    10％    0.5
B组份  三聚氰胺            35
       甲醛                210
       硼砂                1.5
组分A与组分B按1∶2重量比混合。
实施例3
       原料名称    浓度    重量
A组分  磷酸        85％    150
       季虎四醇            90
       甲醛        37％    234
       尿素        46％    60
       三乙醇胺            25
       氢氧化钠    10％    0.8
B组分  三聚氰胺            40
       甲醛                230
       硼砂                1.2
组分A与组分B按1∶1.5重量比混合。

Claims (1)

1.一种膨胀型透明防火涂料的生产工艺，其特征在于包括如下步骤：
用磷酸二氢铵、甲醛、季戊四醇、尿素、三乙醇胶、氢氧化钠按一定配比制得A组分；用三聚氰胺、甲醛、硼砂按一定配比制得B组分，然后将A、B组分以1∶1-2重量配比混合搅拌得到膨胀型透明防火涂料；
各物料组成为
        原料名称    浓度        重量份范围
A组份： 磷酸        84％        135-168
        季虎四醇                84-97
        甲醛        36％        230-237
        尿素        45％        55-66
        三乙醇胺                21-29
        氢氧化钠    15％        0.5-1
B组份：三聚氰胺                 35-45
        甲醛                    210-240
        硼砂                    1-1.5。
CN200810080140A 2008-12-13 2008-12-13 一种膨胀型透明防火涂料的生产工艺 Pending CN101747819A (zh)