CN101735695A - Nano insulating glass coating - Google Patents
Nano insulating glass coating Download PDFInfo
- Publication number
- CN101735695A CN101735695A CN200810180020A CN200810180020A CN101735695A CN 101735695 A CN101735695 A CN 101735695A CN 200810180020 A CN200810180020 A CN 200810180020A CN 200810180020 A CN200810180020 A CN 200810180020A CN 101735695 A CN101735695 A CN 101735695A
- Authority
- CN
- China
- Prior art keywords
- insulating glass
- glass coating
- coating
- methyl methacrylate
- nano insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses nano insulating glass coating which comprises the terpolymer of styrol, methyl methacrylate and methacrylic acidwhich and is prepared by dissolving the terpolymer of styrol, methyl methacrylate and methacrylic acid, which is used as the film forming matter, in organic mixed solvent according to the needed concentration and then adding and stirring evenly a proper amount of epoxy resin, curing agent and pigment to the solution. The insulating glass coating can be used for the cold coating of the large-area plate glass and the dip coating of the irregularly-shaped glass product and has the advantages of good gloss, high transparency, hard film, strong adhesion and heat insulation.
Description
Technical field
The present invention relates to a kind of nano insulating glass coating.
Background technology
Existing coating at present with phthalic resin coating use the most extensive, weak point is temperature of reaction up to 200-230 ℃, the reaction times reaches 12-18 hour, the product poor water resistance.Esters of acrylic acid coating transparency height, strong adhesion, but cost is too high.Polyacrylic acid and polyhexene alcohol sticking power are good, but poor water resistance; Thereby make its application be subjected to very big restriction.
Summary of the invention
The objective of the invention is to solve deficiency of the prior art, but a kind of cold spraying large-area flat-plate glass is provided, but also dip-coating special-shaped glass goods have that glossiness is good, transparency is high, paint film is hard, a strong adhesion, heat insulation coating.
The present invention is achieved in that a kind of nano insulating glass coating, and--methyl methacrylate--methacrylic acid ter-polymer 14-16% (weight percentage) that it is characterized in that adopting vinylbenzene and Resins, epoxy 5-7%, diformazan phenyl ring ketone in the sixth of the twelve Earthly Branches mixed solvent 77-80%, organic multicomponent amine are an amount of, colorant is mixed in right amount and stirs well.
Described nano insulating glass coating; it is characterized in that terpolymer is to get weight ratio to be: 5: 4.5: 0.5 vinylbenzene, methyl methacrylate, methacrylic acid; cause with Diisopropyl azodicarboxylate, under nitrogen protection, normal pressure 80-100 ℃ temperature copolyreaction preparation in 3-4 hour.
Described nano insulating glass coating is characterized in that Resins, epoxy can adopt E-44 or E-42.
But the present invention's cold spraying large-area flat-plate glass, but also dip-coating special-shaped glass goods have that glossiness is good, transparency is high, paint film is hard, a strong adhesion, heat insulation multiple advantage.
Embodiment
Embodiment 1
Terpolymer: vinylbenzene-methacrylic acid-methacrylic acid 14%, Resins, epoxy: E445%; Organic mixed solvent: dimethylbenzene pimelinketone 77%; Solidifying agent: organic multicomponent amine is an amount of; Colorant: all organic oil soluble dyes that can be dissolved in the mixed solvent are an amount of.Stir well even promptly getting and be transparent colored liquid through miscible, but but also dip-coating special-shaped glass goods of cold spraying large-area flat-plate glass.
Claims (3)
1. nano insulating glass coating,--methyl methacrylate--methacrylic acid ter-polymer 14-16% (weight percentage) that it is characterized in that adopting vinylbenzene and Resins, epoxy 5-7%, diformazan phenyl ring ketone in the sixth of the twelve Earthly Branches mixed solvent 77-80%, organic multicomponent amine are an amount of, colorant is mixed in right amount and stirs well.
2. nano insulating glass coating according to claim 1; it is characterized in that terpolymer is to get weight ratio to be: 5: 4.5: 0.5 vinylbenzene, methyl methacrylate, methacrylic acid; cause with Diisopropyl azodicarboxylate; under nitrogen protection, normal pressure 80-100 ℃ temperature copolyreaction preparation in 3-4 hour.
3. nano insulating glass coating according to claim 1 is characterized in that Resins, epoxy can adopt E-44 or E-42.