CN101725048A - 尼龙膜及其贴合的防水透湿布帛 - Google Patents
尼龙膜及其贴合的防水透湿布帛 Download PDFInfo
- Publication number
- CN101725048A CN101725048A CN200810171341A CN200810171341A CN101725048A CN 101725048 A CN101725048 A CN 101725048A CN 200810171341 A CN200810171341 A CN 200810171341A CN 200810171341 A CN200810171341 A CN 200810171341A CN 101725048 A CN101725048 A CN 101725048A
- Authority
- CN
- China
- Prior art keywords
- nylon
- nylon membrane
- film
- waterproof
- same
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种尼龙膜及其贴合的防水透湿布帛,尼龙膜以改性尼龙为主要成分。本发明的尼龙膜及其贴合防水透湿布帛,具有可回收再利用、环保、防水透湿等特性,在环保要求越来越高的今天有非常高的实用性。
Description
技术领域:
本发明涉及尼龙膜及其贴合的防水透湿布帛。
背景技术:
关于防水透湿的纺织品各种各样,有高密度组织的纺织品,有涂层加工的纺织品,也有贴合加工的纺织品,品种繁多。其中贴合加工的纺织品,在解决防水透湿这一对矛盾上做的相对较好,有较好的防水性,透湿性较涂层织物也有很大提高。而贴合品中膜的作用占到主导地位,关于防水透湿的膜的成果层出不穷,品种繁多,包括丙烯酸树脂类、聚氨酯类、聚氯乙烯、橡胶基树脂、聚四氟乙烯等。随着科技的进步,各种膜的防水透湿性能有了长足的发展。聚氨酯树脂的防水透湿性有较大空间和服用性能良好,且价格适中,所以市场上占据份额最大。聚四氟乙烯类,生产成本较大,价格较高,但由于其防水透湿性能最高,在市场上也占有很大比例。聚氨酯膜、聚四氟乙烯膜,也存在自身的不足,两者的生产过程对环境都有一定的污染,而且不能够回收再利用。
发明内容:
本发明的目的在于提供一种具有一定的防水透湿性,且能解决回收再利用的问题,无环境污染的尼龙膜及用其贴合的防水透湿布帛。
本发明的技术解决方案是:
一种尼龙膜及其贴合的防水透湿布帛,其特征是:尼龙膜的主要成分为改性尼龙,改性尼龙结构如下:
R2=-CH2OCH3或H,中的一种或几种。使用本原料生产的膜具有可以和尼龙织物一起回收的特性,整个服用过程对环境的污染较小。
添加有粒径为10nm~25μm的无机化合物粒子。无机化合物粒子的含量为1%~20%。膜的厚度为10μm~50μm。膜的伸长率在50%~400%之间。
一种尼龙膜,以改性尼龙为主要成分,添加无机化合物粒径为10nm~25μm。如果添加无机化合物的粒径大于25μm,那加工膜的厚度受到限制,而且手感偏硬,缺乏实用性;如果添加无机化合物的粒径小于10nm,那么膜的手感粘着性很强,手感差,服用舒适性低,所以添加无机化合物粒径为10nm~25μm。
一种尼龙膜,添加无机化合物的含量为1%~20%。如果含量在20%以上,膜变硬,伸缩性显著地下降,缺乏实用性;如果含量在1%以下,透湿度下降,同时,有粘着性,所以通常无机化合物含量在5~15%之间。
一种尼龙膜,厚度为10μm~50μm。既要有高的耐水压,又要有一定的透湿性,膜越厚耐水压越高,透湿度越低,膜越薄耐水压越低,透湿度越高,所以一般膜的厚度都在15~30μm之间,耐水压、透湿度平衡性最好。
一种尼龙膜,膜的伸长率在50%~400%之间。膜的伸长率,可以反应膜的强度,同时服用过程中,也需要有一定的伸长率,一般50%~400%之间,可以适应任何织物的贴合加工条件。
一种尼龙膜,具有防水透湿性,耐水压在6000mmH2O以上,透湿度在5000g/m2·24hr以上。为了保证好的服用性能,耐水压一般在10000mmH2O左右,而透湿度也一般能达到6000~8000g/m2·24hr。
以上所述添加的无机化合物是硅化合物。
一种用上述尼龙膜贴合的防水透湿布帛,其特征是:包括基布,基布上贴合有尼龙膜,其中基布是尼龙组分的机织物或针织物。
本发明旨在保证了膜具有一定的防水透湿性同时,能解决回收再利用的问题。本发明尼龙膜与尼龙织物贴合后,得到的面料具有防水透湿性能,且可以按照尼龙回收方式,循环利用,减少了对环境的污染,在环保要求越来越高的今天有着深远的意义。
下面结合实施例对本发明作进一步说明。
具体实施方式:
实施例1
一种尼龙膜,其加工方法:
将改性尼龙树脂100克、平均粒径为15μm的硅化合物20克、溶剂400克加入空的容器中,高速搅拌(500~1500rpm)搅拌均匀后加入助剂5克搅拌均匀。
将调好的溶液,使用涂层机均匀的涂在离型纸的表面,控制其厚度变化范围,经过50℃×2分钟,120℃×2分钟干燥后膜成型,使用专门剥离的机器将膜剥下测其性能。
上述步骤中使用涂层机将溶液均匀的涂在离型纸的表面,控制其厚度变化范围,可以得到不同厚度的膜,例得到各不同厚度的膜的平均厚度分别为18.0μm、29.6μm、38.0μm。膜的伸长率在50%~400%之间。
所述改性尼龙结构如下:
R2=-CH2OCH3或H,中的一种或几种。
本发明产品各性能与尼龙膜(表中称为膜)平均厚度的主要指标比较,见下表:
膜平均厚度(μm) | 耐水压(mmH2O) | 透湿度(g/m2·24h) | 伸长率(%) |
18.0 | 10000以上 | 11256 | 371.33 |
29.6 | 10000以上 | 9332 | 298.25 |
38.0 | 10000以上 | 6824 | 243.46 |
测试方法和标准
(1)耐水压根据JIS L1092的标准测试(膜上方加200目的过滤网作基材,控制膜的弹性变形)。
(2)透湿度根据JIS L1099的标准测试。
(3)膜的伸长率根据JIS L 1018的标准测试(试样的宽度更改为5cm测试,拉力为膜断裂强力的80%测试)
实施例2
一种尼龙膜贴合防水透湿布帛
将厚度18.0μm的尼龙膜与普通尼龙机织物,通过贴合机器的点状轧辊,均匀的将接着剂转到制作的膜上,再通过轧辊将尼龙布与尼龙膜贴合在一起。测得的性能见下表:
耐水压(mmH2O) | 透湿度(g/m2·24h) | 剥离强力(N/cm) |
17030 | 5187 | 3.20 |
本发明实施例1中的改性尼龙还可以是下列结构:
R2=-CH2OCH3或H,中的一种或几种。
Claims (8)
2.根据权利要求1所述的尼龙膜,其特征是:膜中添加有粒径为10nm~25μm的无机化合物粒子。
3.根据权利要求2所述的尼龙膜,其特征是:膜中无机化合物粒子的含量为1~20%。
4.根据权利要求1、2或3所述的尼龙膜,其特征是:膜的厚度为10~50μm。
5.根据权利要求1、2或3所述的尼龙膜,其特征是:膜的伸长率在50~400%之间。
6.根据权利要求2所述的尼龙膜,其特征是:无机化合物粒子是硅化合物。
7.根据权利要求1、2或3所述的尼龙膜,其特征是:具有防水透湿性,耐水压在6000mmH2O以上,透湿度在5000g/m2·24hr以上。
8.一种用权利要求1所述的尼龙膜贴合的防水透湿布帛,其特征是:包括基布,基布上贴合有尼龙膜,其中基布是尼龙组分的机织物或针织物。