CN101724315B - UV snowflake printing ink - Google Patents
UV snowflake printing ink Download PDFInfo
- Publication number
- CN101724315B CN101724315B CN 200910189279 CN200910189279A CN101724315B CN 101724315 B CN101724315 B CN 101724315B CN 200910189279 CN200910189279 CN 200910189279 CN 200910189279 A CN200910189279 A CN 200910189279A CN 101724315 B CN101724315 B CN 101724315B
- Authority
- CN
- China
- Prior art keywords
- acrylic resin
- printing ink
- percent
- snowflake
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to UV snowflake printing ink which comprises the following raw material components in percentage by weight: 30-50 percent of amino acrylic resin, 10-15 percent of hydroxy acrylic resin, 5-16 percent of epoxy acrylic resin, 10-20 percent of alkyd, 2-10 percent of 1-hydroxycyclohexyl phenyl ketone and 5-18 percent of color ink. When the UV snowflake printing ink is used, only printing with one chromatic degree is needed, so that characters or patterns are well arranged and present remarkable stereoperception.
Description
Technical field
The invention belongs to printing ink, particularly a kind of UV snowflake printing ink that is used for silk screen printing.
Background technology
The ink for screen printing that generally is used for silk screen printing is being printed onto the stock surface, and in UV (i.e. ultraviolet ray) solidification process, the particle in the printing ink is because contact or close proximity cause to attract each other cohesion in the middle of entity fast, the plane of formation rule.Monochromatic time literal or pattern silk screen printing can only embody a plane effect, do not have tangible gradation sense and stereoscopic sensation, have only and adopt time above silk screen printing of 2 looks, just can embody stereoscopic sensation.So not only, also take resource, cause unnecessary waste overlapping the qualification rate that the position precision requires height but also influences product.
Summary of the invention
The objective of the invention is to the problems referred to above of existing to existing printing ink, the printing of of the same colour time of a kind of need is provided, just can make literal or pattern well arranged and demonstrate tangible relief UV snowflake printing ink.
The objective of the invention is to realize like this:
UV snowflake printing ink of the present invention; Its raw material is made up of following component, in weight percentage: aminoacrylic acid resin 30%~50%, Hydroxylated acrylic resin 10%~15%; Epoxy acrylic resin 5%~16%; Synolac 10%~20%, 1-hydroxy-cyclohexyl phenyl-acetone 2%~10%, look China ink 5%~18%.
Preferred version is: the raw material of UV snowflake printing ink is made up of following component, in weight percentage, and aminoacrylic acid resin 50%; Hydroxylated acrylic resin 12%, epoxy acrylic resin 10%, Synolac 15%; 1-hydroxy-cyclohexyl phenyl-acetone 5%, look China ink 8%.
Above-mentioned aminoacrylic acid resin, Hydroxylated acrylic resin, epoxy acrylic resin are formed the light ramming material that is connected.Light be connected ramming material be the general designation, by one or more light be connected the knot resin form.The light ramming material that is connected has two kinds of functions: 1. give printing ink with suitable flowability, when printing ink is printed onto printable fabric through press plate, can make printing ink shift (printability) smoothly; 2. after the printing, after drying, be transformed into solid film, make the look China ink anchor at (drying property) on the printing surface.Synolac is an auxiliary agent, can improve light be connected knot resin flow property and dispersiveness, quickens the curing of printing ink, shows good stereoscopic sensation.1-hydroxy-cyclohexyl phenyl-acetone is a UV photocuring light trigger.
The preparation method of UV snowflake printing ink of the present invention is following:
With raw materials such as aminoacrylic acid resin, Hydroxylated acrylic resin, epoxy acrylic resin, Synolac, 1-hydroxy-cyclohexyl phenyl-acetone, look China inks; Ratio in prescription is contained in the stainless steel vessel; Even through grinding stirrer thorough mixing under 2000 rev/mins condition; The sealing of cooling back is at room temperature preserved.
The method of use of UV snowflake printing ink of the present invention is following:
1, with plastic component such as Vilaterm surface flame or corona treatment;
2, the UV gloss oil is uniformly coated on the plastic component surface through glazing device, and solidifies;
3, UV snowflake printing ink of the present invention is coated on the plastic component surface through screen process press, adopts the nylon wire half tone of 36 line/inches best;
4, printing ink UV is solidified.
Technique effect of the present invention is: UV snowflake printing ink of the present invention is in the UV solidification process, and the particle in the printing ink is radial flowing around entity fast, forms the special-effect of starlike snowflake; Use UV snowflake printing ink of the present invention, only need of the same colour time printing, just can make literal or pattern well arranged and demonstrate tangible stereoscopic sensation.
Embodiment
Embodiment one:
The raw material of UV snowflake printing ink is formed as follows among the embodiment one, in weight percentage:
Aminoacrylic acid resin 50%,
Hydroxylated acrylic resin 12%,
Epoxy acrylic resin 10%,
Synolac 15%,
1-hydroxy-cyclohexyl phenyl-acetone 5%,
Look China ink 8%, that the look China ink adopts is UVC-171.
Embodiment two:
The raw material of UV snowflake printing ink is formed as follows among the embodiment two, in weight percentage:
Aminoacrylic acid resin 35%,
Hydroxylated acrylic resin 15%,
Epoxy acrylic resin 15%,
Synolac 20%,
1-hydroxy-cyclohexyl phenyl-acetone 10%,
Look China ink 5%.
Embodiment three:
The raw material of UV snowflake printing ink is formed as follows among the embodiment three, in weight percentage:
Aminoacrylic acid resin 30%,
Hydroxylated acrylic resin 14%,
Epoxy acrylic resin 16%,
Synolac 20%,
1-hydroxy-cyclohexyl phenyl-acetone 2%,
Look China ink 18%.
Embodiment four:
The raw material of UV snowflake printing ink is formed as follows among the embodiment four, in weight percentage:
Aminoacrylic acid resin 50%,
Hydroxylated acrylic resin 10%,
Epoxy acrylic resin 5%,
Synolac 10%,
1-hydroxy-cyclohexyl phenyl-acetone 10%,
Look China ink 15%.
Aminoacrylic acid resin among above-mentioned each embodiment, epoxy acrylic resin, Synolac all are purchased from Asai Bussan in Japan, and 1-hydroxy-cyclohexyl phenyl-acetone, Hydroxylated acrylic resin are purchased from Schekolin AG.Look China ink among the present invention is selected one or more for use according to the needs of ink color, and the look China ink among above-mentioned each embodiment is all selected UVC palette China ink for use, available from the learned Industrial Co., Ltd. that receives in Shenzhen.
The preparation method of the UV snowflake printing ink of above-mentioned each embodiment is following:
With raw materials such as aminoacrylic acid resin, Hydroxylated acrylic resin, epoxy acrylic resin, Synolac, 1-hydroxy-cyclohexyl phenyl-acetone, look China inks; Ratio in prescription is contained in the stainless steel vessel; Even through grinding stirrer thorough mixing under 2000 rev/mins condition; The sealing of cooling back is at room temperature preserved.
Claims (2)
1. UV snowflake printing ink; It is characterized in that its raw material is made up of following component, in weight percentage: aminoacrylic acid resin 30%~50%, Hydroxylated acrylic resin 10%~15%; Epoxy acrylic resin 5%~16%; Synolac 10%~20%, 1-hydroxy-cyclohexyl phenyl-acetone 2%~10%, look China ink 5%~18%.
2. UV snowflake printing ink according to claim 1; It is characterized in that its raw material is made up of following component, in weight percentage: aminoacrylic acid resin 50%, Hydroxylated acrylic resin 12%; Epoxy acrylic resin 10%; Synolac 15%, 1-hydroxy-cyclohexyl phenyl-acetone 5%, look China ink 8%.