CN101724307A - 环保安全性负离子内墙腻子 - Google Patents
环保安全性负离子内墙腻子 Download PDFInfo
- Publication number
- CN101724307A CN101724307A CN201010105510A CN201010105510A CN101724307A CN 101724307 A CN101724307 A CN 101724307A CN 201010105510 A CN201010105510 A CN 201010105510A CN 201010105510 A CN201010105510 A CN 201010105510A CN 101724307 A CN101724307 A CN 101724307A
- Authority
- CN
- China
- Prior art keywords
- putty
- kilogram
- powder
- interior wall
- wall putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提出的是环保安全性负离子内墙腻子。取生物胶5-10公斤,无机胶5-10公斤,氧化钙80-90公斤,方解石粉末80-90公斤,电气石粉3-5公斤,竹子短纤维1-3公斤,硝酸银0.01-0.1公斤,混合,通过研磨机研磨成为膏状腻子成品。本发明腻子由于以生物胶和无机胶作为胶结剂,以氧化钙作为具有胶结性能的体质材料,以方解石粉末作为分散剂,以电气石粉作为负离子发生材料,以竹子短纤维作为抗裂增韧材料,以硝酸银作为抗菌剂,所制成的建筑内墙腻子具有环保性和安全性,且生产容易,成本低,无气味,对人体无危害。适宜作为建筑内墙腻子使用。
Description
技术领域
本发明提出的是建材领域的墙体涂覆材料,具体地说是环保安全性负离子内墙腻子。
背景技术
墙体腻子广泛使用在墙体的涂饰上,通常用在墙体涂料打底,用于填平墙面。根据墙体腻子的使用功能,需要其具有易涂性,而且又易于打磨,与墙体保持足够的粘结力,且防止脱落。
目前所使用的腻子品种很多,但总体来说,通常是使用非金属矿石或金属氧化物粉末与胶结剂配合,经过研磨制成。
例如:专利号为02119525.0的发明专利的权利要求所要保护的产品,是一种复合滑石粉,特征在于该滑石粉是碳酸钙或白云石和膨润土组成,按比例混合粉碎研磨制成325目的复合滑石粉,作为腻子体质材料使用。
随着人们对腻子要求水平的提高,02123891.X的发明专利提出了一种能够产生空气负离子的建筑内墙涂料,其特征是在纯丙烯酸乳液、各种丙烯酸树脂、丙烯酸醇酸树脂、硅丙乳液、苯丙乳液中加入占涂料总重1%-30%的稀土激活高效产生空气负离子的电气石复合粉末。可作腻子使用。
目前,对于建筑腻子来说,通常是用非金属矿石粉末或金属氧化物粉末与有机胶体混合研磨制成的。其中,非金属矿石原料和金属氧化物粉碎与研磨耗费工时多,消耗能源大,造成材料成本的提高。而有机胶体中都含有化学物质,随着时间的推移,不断转化与扩散,尤其是对于内墙来说,更是时刻对生存环境产生危害,对人体健康不利。尤其是添加有功能性的材料,虽然产生了特定的效果,但或多或少地对人体不利。例如,在腻子中加入五氯酚钠,虽然起到抗霉的作用,但氯对人体有所损害。例如,在腻子中加入稀土和电气石,虽然说能够激发产生空气负离子,但稀土原料或多或少地会产生放射性,也对人体不利。
因而,如何制造出具有环保性能的内墙腻子是需要研究的课题。
发明内容
为了克服现有内墙腻子所存在的缺点,本发明提出了一种环保安全性负离子内墙腻子。该腻子采用生物胶和无机胶混合胶作为胶粘剂,采用具有胶结性的氧化钙作为体质材料,采用方解石粉末作为分散材料,采用电气石粉作负离子发生材料,采用竹短纤维作为抗裂材料,共同配合制成具有环保性和安全性的建筑内墙腻子。
本发明解决技术问题所采用的方案是:取生物胶5-10公斤,无机胶5-10公斤,氧化钙80-90公斤,方解石粉末80-90公斤,电气石粉3-5公斤,竹子短纤维1-3公斤,硝酸银0.01-0.1公斤,混合,通过研磨机研磨成为膏状腻子成品。
积极效果,由于以生物胶和无机胶作为胶结剂,以氧化钙作为具有胶结性能的体质材料,以方解石粉作为分散剂,以电气石粉作负离子发生材料,以竹子短纤维作为抗裂增韧材料,以硝酸银作为抗菌剂,所制成的建筑内墙腻子具有环保型和安全性,且生产容易,成本低,无气味,对人体无危害。适宜作为建筑内墙腻子使用。
具体实施方式
取生物胶5-10公斤,无机胶5-10公斤,氧化钙80-90公斤,方解石粉末80-90公斤,电气石粉3-5公斤,竹子短纤维1-3公斤,硝酸银0.01-0.1公斤,混合,通过研磨机研磨成为膏状腻子成品。
生物胶采用淀粉、蛋白胶或树胶,无机胶采用硅酸钠水溶液或磷酸胶,体质材料采用氧化钙和方解石粉末,增韧抗裂材料采用竹子短纤维,抗菌剂采用硝酸银。
其中,淀粉可是土豆淀粉、红薯淀粉、木薯淀粉、玉米淀粉、高梁淀粉、小麦淀粉以及淀粉植物提取的淀粉。
无机胶采用波美度在10-30度的硅酸钠水溶液。
氧化钙是石灰石煅烧完全后的粉末,其中过烧石灰不超过1%,粉碎目数在300-1250目之间。
方解石粉末是方解石粉碎后的粉末,粉碎目数在300-1250目之间。
电气石粉是将电气石进行超细粉磨所得到的1250目的粉状材料。
竹子短纤维是将竹子在质量比为40%以上烧碱溶液中蒸煮后,压滤出碱液,在水中搅拌分散的粉末状纤维粉。
抗菌剂是硝酸银粉末,能够溶于水。
淀粉水溶液和蛋白胶水溶液及树胶水溶液具有粘结性,再经过硅酸钠碱性物质的改性,使其胶粘性得以提高,分散性有所改善,使腻子胶结附着力达到技术要求。
氧化钙为金属氧化物,与水作用后,产生氢氧化钙胶体,所以对墙体也有附着性,同时,它不断吸收空气中的二氧化碳,转变为具有结构强度的碳酸钙,是腻子能够牢固地附着在墙体上。同时,其具有填平性,便于涂刮,施工性能好,并使腻子层强度高。
方解石粉末,能够缓解氧化钙的粘结性,使氧化钙易于分散,并且有利于砂磨,同时也是增厚的体质材料,起到充填墙体孔洞及凹陷部位的作用。
电气石粉能够产生空气负离子,释放到空气当中,对环境有利,同时对人体有益。
竹子短纤维,耐碱性强,纤维短,分散在腻子中后用于墙体涂刮,对涂刮层产生增强、增韧作用,而且更易于填平孔洞,在腻子层中起到相互拉扯的作用,使得腻子层强度提高,易于打磨,同时能够防止腻子层开裂,产生增韧抗裂的效果。
硝酸银中含有金属银,而银有抗菌的效果,银经过时间的延长后,能够分解成为金属银、氮气和氧气,对人体和环境无害。
由于本发明腻子采用植物性的生物胶和无机胶作为胶结剂,以安全常用的氧化钙和方解石粉作为体质材料,并通过电气石产生空气负离子,以竹子短纤维作为增韧抗裂材料,以安全的硝酸银作为抗菌材料,所以,无有害物质挥发,无气味释放,其原料对人体无害,所制成的腻子能够达到技术要求,并且,打磨性、填充性、抗裂性能优越。由于氧化钙和方解石容易粉碎,因此与其它原料配合容易,研磨需要消耗能源少,所以制造成本低,工序简单。
Claims (1)
1.环保安全性负离子内墙腻子,其特征是:取生物胶5-10公斤,无机胶5-10公斤,氧化钙80-90公斤,方解石粉末80-90公斤,电气石粉3-5公斤,竹子短纤维1-3公斤,硝酸银0.01-0.1公斤,混合,通过研磨机研磨成为膏状腻子成品;
所述生物胶为淀粉、蛋白胶或树胶;无机胶为波美度在10-30度的硅酸钠水溶液;氧化钙为300-1250目的粉末状材料;方解石为300-1250目的粉末;电气石粉为300-1250目的粉状物;竹子短纤维为竹子在40%碱煮后清洗分散的粉末状的纤维粉;硝酸银为能够溶于水的银的硝酸盐。