CN101712846A - Raw ancient building decorative paint - Google Patents
Raw ancient building decorative paint Download PDFInfo
- Publication number
- CN101712846A CN101712846A CN200910219547A CN200910219547A CN101712846A CN 101712846 A CN101712846 A CN 101712846A CN 200910219547 A CN200910219547 A CN 200910219547A CN 200910219547 A CN200910219547 A CN 200910219547A CN 101712846 A CN101712846 A CN 101712846A
- Authority
- CN
- China
- Prior art keywords
- raw
- ancient building
- building decorative
- paint
- decorative paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a raw ancient building decorative paint, which is prepared from the following raw materials in percentage by mass: raw paint 50-70, modifier 30-50, dispersant 0.1-0.5, wherein the total mass of the raw materials is 100 percent. The raw ancient building decorative paint has good drying property, meets the requirements on humidity and temperature of raw paint drying, can resist acid, alkali, water oil and wear, has high glossiness and high adhesive force and can be directly coated and brushed on ancient buildings, antique furniture or indoor decorations, and the paint films are bright and have high waterproof, heat-resistance and chemical-resistance performance. The product of the invention is suitable to be used for decorating and painting ancient buildings and antique furniture and decorating or maintaining doors and windows of the ancient buildings.
Description
Technical field
The present invention relates to a kind of lacquer, particularly a kind of raw ancient building decorative paint, be mainly used in ancient building, pseudo-classic furniture decoration, coat with lacquer and be coated with and the decoration and the maintenance of ancient building door and window.This laccol antique building decorative coating is filmed and is had good decorate properties and optical property, can satisfy the ancient building reparation, coat with lacquer the inferior light requirement that is coated with, and ultraviolet resistance is strong, heat-resisting, water-fast, chemicals-resistant, wear-resisting, strong adhesion.
Background technology
The decoration that raw lacquer is used for utensil and article of furniture is history in 8000, but execution conditions are had relatively high expectations, need specific warm and humid environment, its application is restricted. for further improving drying property, the use properties of raw lacquer, enhancing and glorifying the unique cultural features of a nation and opening up the exhibition Lacquer Market all is a thing highly significant.
China's ancient building is gone through the development in thousands of years, and it is of a great variety, the form style varied, exquisite no human relations have high historical relic, history and artistic value, and she is not only the precious legacy of the Chinese nation, also being the rarity of world architecture art, is the data important in kind of research ancient history culture.Although many ancient buildings are destroyed in the natural and man-made calamities in successive dynasties, nowadays leave over preserve also many scarred.In one's early years excellent, magnificent paint colour painting, gloss dimness nowadays, the coat of paint be full of cracks is peeled off.Therefore it is repaired, protection has become an important research project.The Chinese lacquer culture is of long standing and well established, with China's conventional matter-raw lacquer it is carried out repair mode with old restoration of old ways, reappears the historical original appearance of ancient building, and this should can be described as combining of the most perfect, most complete culture and history.
Summary of the invention
The objective of the invention is to, on the basis that keeps the raw lacquer premium properties, provide a kind of raw ancient building decorative paint.
In order to realize above-mentioned task, the technical solution used in the present invention is:
A kind of raw ancient building decorative paint is characterized in that, this raw ancient building decorative paint that makes is made up of following raw materials according and mass percent thereof: raw lacquer: 50%～70%; Properties-correcting agent: 30%～50%, dispersion agent: 0.1%～0.5%, the per-cent sum of above-mentioned raw materials is 1.00%.
Described raw lacquer is one or more of Qi, city mouth Qi, hair dam Qi, Qin Ling Qi and other area lacquers that produce from peace health Qi, the Chinese, fries in shallow oil and coils mark more than 65%, and laccol content is more than 50%.
Described properties-correcting agent is one or more of vinylbenzene, tung oil, vegetables oil, methyl methacrylate.
Described dispersion agent is a polyethylene wax.
Raw ancient building decorative paint of the present invention has good drying property, and paint film has kept the premium properties of raw lacquer.Have excellent corrosion resistance, acidproof, water-fast, media-resistant, ageing-resistant performance are good, have good decoration effect and optical property.
Embodiment
The raw ancient building decorative paint that the present invention makes is made up of following raw materials according and mass percent thereof: raw lacquer: 50%～70%; Properties-correcting agent: 10%～50%, dispersion agent: 0.1%～0.5%, the per-cent sum of raw material is 100%.
Described raw lacquer is one or more of Qi, city mouth Qi, hair dam Qi, Qin Ling Qi and other area lacquers that produce from peace health Qi, the Chinese, fries in shallow oil and coils mark more than 65%, and laccol content is more than 50%.
Described properties-correcting agent is one or more of vinylbenzene, tung oil, vegetables oil, methyl methacrylate.
Described dispersion agent is a polyethylene wax.
Below in conjunction with specific embodiment the present invention is described in further detail.
Embodiment 1:
The raw ancient building decorative paint of present embodiment is made up of cashew resin, tung oil, polyethylene wax, and method preparation routinely gets final product, and its weight percent is filled a prescription as following table:
| The component title | Weight percent (%) |
| Raw lacquer | ??59.7 |
| Tung oil | ??40 |
| Polyethylene wax | ??0.3 |
Embodiment 2:
The raw ancient building decorative paint of present embodiment is made up of raw lacquer, tung oil, methyl methacrylate, polyethylene wax, and method preparation routinely gets final product, and its weight percent is filled a prescription as following table:
| The component title | Weight percent (%) |
| Raw lacquer | ??49.8 |
| Tung oil | ??30 |
| Methyl methacrylate | ??20 |
| Polyethylene wax | ??0.2 |
Embodiment 3:
The raw ancient building decorative paint of present embodiment is made up of raw lacquer, vegetables oil, vinylbenzene, polyethylene wax, and method preparation routinely gets final product, and its weight percent is filled a prescription as following table:
| The component title | Weight percent (%) |
| Raw lacquer | ??69.5 |
| Vegetables oil | ??20 |
| Vinylbenzene | ??10 |
| The component title | Weight percent (%) |
| Polyethylene wax | ??0.5 |
The foregoing description is wherein preferable example just, the invention is not restricted to these embodiment, certainly, as long as in the formula range that the present invention provides, all can make qualified raw ancient building decorative paint.
Brushing according to ancient building, ancient building door and window or pseudo-classic furniture, ornaments modelled after an antique requires construction, can be directly pseudo-classic furniture or ornaments modelled after an antique be brushed or sprayed paint, spontaneous curing is dry to get final product, and dried paint film is beautiful, glossiness is high, hardness is high, water-fast, heat-resisting, chemical resistance is strong.
The technical feature of the raw ancient building decorative paint of the foregoing description preparation is referring to table 1.
Table 1. raw ancient building decorative paint performance index
| Project | Index | The method of inspection |
| Paint film appearance | Reddish-brown | |
| Solid content, %, ≮ | ??40％ | ??GB/T6470 |
| No impression time of drying, h, ≯ | ??4 | ??GB/T6753.2 |
| Viscosity, (being coated with 4 glasss) ≮ | ??23 | ??GB/T1723 |
| Water tolerance, ≮ 90d | Paint film do not come off, non-foaming, do not chap | ??GB/T1733 |
| Anti-sulfuric acid, ≮ 90d | Paint film do not come off, non-foaming, do not chap | ??GB/T9274.1 |
| Resistance to salt water (sodium-chlor), ≮ 90d | Paint film do not come off, non-foaming, do not chap | ??GB/T10834 |
| Petrol-resistance, ≮ 90d | Paint film do not come off, non-foaming, do not chap | ??GB/T1734 |
| The UV resistant experiment | Paint film do not come off, non-foaming, do not chap | ??GB/T14522-93 |
Claims (4)
1. a raw ancient building decorative paint is characterized in that, this raw ancient building decorative paint that makes is made up of following raw materials according and mass percent thereof: raw lacquer: 50%～70%; Properties-correcting agent: 30%～50%, dispersion agent: 0.1%～0.5%, the per-cent sum of above-mentioned raw materials is 100%.
2. raw ancient building decorative paint as claimed in claim 1, it is characterized in that, described raw lacquer is one or more of Qi, city mouth Qi, hair dam Qi, Qin Ling Qi and other area lacquers that produce from peace health Qi, the Chinese, fries in shallow oil and coils mark more than 65%, and laccol content is more than 50%.
3. raw ancient building decorative paint as claimed in claim 1 is characterized in that, described properties-correcting agent is one or more of vinylbenzene, tung oil, vegetables oil, methyl methacrylate.
4. raw ancient building decorative paint as claimed in claim 1 is characterized in that, described dispersion agent is a polyethylene wax.