CN101705435A - 超硬高铬铸造磨球的生产工艺方法 - Google Patents
超硬高铬铸造磨球的生产工艺方法 Download PDFInfo
- Publication number
- CN101705435A CN101705435A CN200910130491A CN200910130491A CN101705435A CN 101705435 A CN101705435 A CN 101705435A CN 200910130491 A CN200910130491 A CN 200910130491A CN 200910130491 A CN200910130491 A CN 200910130491A CN 101705435 A CN101705435 A CN 101705435A
- Authority
- CN
- China
- Prior art keywords
- ball
- percent
- chromium
- abrading
- grinding ball
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及超硬高铬铸造磨球的生产工艺方法,本发明磨球化学成分如下:碳(C):1.8-3.2%,硅(Si):0.3-1.0%,锰(Mn):0.2-0.9%,铬(Cr):10.0-10.5%,磷(P):0.02-0.1%,硫(S):0.02-0.1%;铜(Cu):0.02-0.1%,钼(Mo):0.02-0.1%,镍(Ni):0.02-0.1%,钨(W):0.02-0.1%,稀土钇(Y-Re):0.1-0.2%,铁(Fe)80.1-83.7%。本发明采用钇稀土进行变质处理,使碳化物形状、分布改变,进而断网,同时使晶粒细化,组织致密,提高韧性。采用油介质淬火加回火热处理工艺,获得马氏体加断网的共晶碳化物,使高铬磨球硬度达到HRc64-66,显著提高高铬磨球的韧性和耐磨性。本发明磨球经在多家水泥行业的球磨机中试用,其磨耗同比降低20%-32%,显著降低球磨机的运行成本。
Description
技术领域
本发明涉及一种研磨介质即铸造磨球及生产工艺方法。
背景技术
磨球作为一种研磨介质广泛应用于建材水泥、矿山冶金、能源火电、非金属加工、水煤浆及磁性材料等行业的粉体工程。由于需满足各行业不同设备、不同工况条件的要求,制造磨球的材质多种多样,如锻制钢球、球墨铸铁磨球、铬合金铸造磨球等,规格亦从到甚至更大直径。
高铬铸造磨球是继普通锻制钢球、低铬铸造磨球发展起来的新一代高效磨球,其含铬量大于10%,公知热处理技术为空气淬火与低温回火。在这种条件下,高硬度的M7C3型碳化物几乎全部代替了M3C型碳化物。与呈网状连续分布的M3C型碳化物相比,大大增强了基体的连续性,因而磨球的硬度和韧性均显著提高。我国现行标准(GB/T17445-1998、JC/T533-2004及YB/T092-2005)中高铬铸造磨球的铬(Cr)含量范围为10%-30%,其淬火态硬度为HRc52-56。
近些年来,高铬铸造磨球虽然已在较大范围内得到广泛应用,但由于我国的铬矿贫乏,铬铁的价格是一涨再涨,钼、镍、钛、铜等贵重金属的价格亦不断攀升。再加上高铬合金铸造磨球的生产设备投入较大,生产工艺较为复杂,导致高铬铸造磨球的成本持续增长,给磨球的制造企业与使用企业都带来相当大的压力;另一方面在水泥、矿山等行业,球磨机的直径、功率及产能都朝着大型化、高效化发展,希望磨球的硬度更高、磨耗更低,以创造更好的经济、社会效益,目前国产高铬铸造磨球淬火态硬度仅为HRc52-56已远不能满足国内外市场的要求。
发明内容
为了节约铬(Cr)等稀缺贵重金属材料,同时提高磨球的硬度,降低制造成本,本发明的目的之一是提供一种铬含量10%-10.5%的超硬高铬铸造磨球,目的之二是提供前述超硬高铬铸造磨球的生产工艺方法。
实现上述的目的的技术解决方案如下:
超硬高铬铸造磨球,其特征在于:其化学成分如下:
碳(C):1.8-3.2%,硅(Si):0.3-1.0%,锰(Mn):0.2-0.9%,
铬(Cr):10.0-10.5%,磷(P):0.02-0.1%,硫(S):0.02-0.1%;
铜(Cu):0.02-0.1%,钼(Mo):0.02-0.1%,镍(Ni):0.02-0.1%,
钨(W):0.02-0.1%,稀土钇(Y-Re):0.1-0.2%,
铁(Fe)80.1-83.7%。
超硬高铬铸造磨球的生产工艺方法包括以下操作步骤,所用原料为废钢;
A、首先将废钢在中频感应电炉中熔化,升温至1520-1580℃,再加入铬(Cr)、铜(Cu)、钼(Mo)、镍(Ni)和钨(W)和稀土钇(Y-Re);
B、加入碎块状的稀土钇(Y-Re),铁水冲熔并静置5-7分钟;
D、用浇铸装置将铁水浇注到铸球模具或砂箱中,冷却后得铸球;
E、将铸球装入加热炉进行奥氏体化处理,第一阶段由常温升至350-400℃、时间2-3小时;第二阶段升温至550-600℃、时间2-3小时;第三阶段升温至800℃、时间2-3小时;第四阶段升温至950-980℃、时间2-4小时;出炉得磨球;
F、将磨球放入淬火油池进行淬火处理,淬火时间为6-20分钟,冷却到室温;
G、再通过低温回火处理,温度210-240℃,回火时间8小时;
H、最后进行掼制检验,得合格磨球;磨球硬度为HRc64-66,落球冲击试验次数超过15000次。
本发明超硬高铬铸造磨球经过多元微合金化、稀土复合变质及油淬及回火处理后,基体组织和碳化物状态均发生了较大的变化。主要表现在:
(1)、晶粒度由传统高铬白口铸铁的2-3级,提升到7-8级。
(2)、夹杂物不但在数量上有较大的减少而且形态上也出现了球状变化;
(3)、铸态组织避免和消除了网状碳化物,基体为细片状或短棱柱状马氏体;
(4)、力学性能和抗磨性能大幅度提高,硬度稳定在HRc64-66,落球冲击试验次数超过15000次。与现行国家标准相比,本发明磨球的铬含量平均降低14.6%,而硬度提高16.1%,落球冲击疲劳次数提高50%,破碎率降低50%,具体数据如表1(注)。
表1
(注):国家标准:《铸造磨球》GB/T17445-1998;
建材行业标准:《建材工业用铬合金铸造磨球》JC/T533-2004
冶金行业标准:《合金铸铁球》YB/T092-2005
本发明磨球经在多家水泥行业的球磨机中试用,其磨耗同比降低20%--32%,显著降低球磨机的运行成本。
本发明的有益技术效果还体现在:采用钇稀土进行变质处理,使碳化物形状、分布改变,进而断网,同时使晶粒细化,组织致密,提高韧性。采用油介质淬火加回火热处理工艺,获得马氏体加断网的共晶碳化物,使高铬磨球硬度达到HRc64--66,显著提高高铬磨球的韧性和耐磨性。在进一步提高磨球抗磨、抗破碎性能的前提下,减少了贵金属铬的含量,同比降低磨球制造成本,社会效益巨大。
具体实施方式
下面结合实施例对本发明作进一步地说明。
实施例1:
碳(C):2.98%, 硅(Si):0.61%,锰(Mn):0.46%,
铬(Cr):10.15%,磷(P):0.052%,硫(S):0.055%;
铜(Cu):0.062%,钼(Mo):0.033%,镍(Ni):0.027%,
钨(W):0.02%,稀土钇(Y-Re):0.121%,
铁(Fe)85.43%。
超硬高铬铸造磨球制造工艺如下:
首先将废钢在中频感应电炉中先行熔化,升温至1510-1550℃,再加入Cr、Cu、Mo、Ni、W合金达到所要求的化学成分。然后将稀土钇放入铁水包,用铁水冲熔并静置7分钟,以对铁水进行变质及孕育处理。处理后的铁水使用铸造直读光谱仪测定其化学元素含量,合格铁水则通过恒温浇铸装置浇注到砂箱中,铁水凝固后形成的铸态磨球检验合格后装入加热炉进行奥氏体化处理,经油介质淬火后,再通过低温回火工序,最终经掼制处理并检验合格后入库。
所述磨球采用DISA垂直分型砂模生产线浇铸,热处理工艺包括油淬工序和低温回火工序。
所述油淬工序的工艺条件为:
将磨球装入加热炉进行加热,第一阶段由常温升至350℃、用时2小时;第二阶段升温至550℃、用时2小时;第三阶段升温至800℃、用时2.5小时;第四阶段升温至950℃、用时2.5小时;然后将磨球出炉,放入淬火油池中进行淬火处理,淬火时间为6-8分钟。淬火后的磨球冷却到室温后再装入台车式回火炉中进行低温回火处理。
所述低温回火的工艺条件为:温度210℃,回火时间8小时。
回火后的磨球冷却到室温后再装入专用掼制设备中进行时效处理及缺陷检测。
磨球硬度HRc65.8,落球冲击试验次数≥15000次).
实施例2
碳(C):2.4%,硅(Si):0.62%,锰(Mn):0.32%,
铬(Cr):10.19%,磷(P):0.059%,硫(S):0.053%;
铜(Cu):0.041%,钼(Mo):0.045%,镍(Ni):0.031%,
钨(W):0.017%,稀土钇(Y-Re):0.128%,
铁(Fe)86.096%。
首先将废钢在中频感应电炉中先行熔化,升温至1520-1560℃,再加入Cr、Cu、Mo、Ni、W合金达到所要求的化学成分。然后将稀土钇放入铁水包,用铁水冲熔并静置6分钟,以对铁水进行变质及孕育处理。处理后的铁水使用铸造直读光谱仪测定其化学元素含量,合格铁水则通过恒温浇铸装置浇注到模具中,铁水凝固后形成的铸态磨球检验合格后装入加热炉进行奥氏体化处理,经油介质淬火后,再通过低温回火工序,最终经掼制处理并检验合格后入库。
所述磨球采用金属模浇铸,热处理工艺包括油淬工序和低温回火工序。
所述油淬工序的工艺条件为:
将磨球装入加热炉进行加热,第一阶段由常温升至400℃、用时2.5小时;第二阶段升温至600℃、用时2.5小时;第三阶段升温至800℃、用时3小时;第四阶段升温至970℃、用时3小时;然后将磨球出炉,放入淬火油池中进行淬火处理,淬火时间为12-14分钟。淬火后的磨球冷却到室温后再装入台车式回火炉中进行低温回火处理。
所述低温回火的工艺条件为:温度220℃,回火时间8小时。
回火后的磨球冷却到室温后再装入专用掼制设备中进行时效处理及缺陷检测。
磨球硬度HRc65.2,落球冲击试验次数≥15000次。
实施例3:
超硬高铬铸造磨球及生产工艺
碳(C):2.12%,硅(Si):0.59%,锰(Mn):0.47%,
铬(Cr):10.25%,磷(P):0.041%,硫(S):0.043%;
铜(Cu):0.052%,钼(Mo):0.032%,镍(Ni):0.029%,
钨(W):0.023%,稀土钇(Y-Re):0.13%,
铁(Fe)86.22%。
首先将废钢在中频感应电炉中先行熔化,升温至1540-1580℃,再加入Cr、Cu、Mo、Ni、W合金达到所要求的化学成分。然后将稀土钇放入铁水包,用铁水冲熔并静置5分钟,以对铁水进行变质及孕育处理。处理后的铁水使用铸造直读光谱仪测定其化学元素含量,合格铁水则通过恒温浇铸装置浇注到模具中,铁水凝固后形成的铸态磨球检验合格后装入加热炉进行奥氏体化处理,经油介质淬火后,再通过低温回火工序,最终经损制处理并检验合格后入库。
磨球硬度HRc64.6,落球冲击试验次数≥15000次。
所述磨球采用金属模浇铸,热处理工艺包括油淬工序和低温回火工序。
所述油淬工序的工艺条件为:
将磨球装入加热炉进行加热,第一阶段由常温升至400℃、用时3小时;第二阶段升温至600℃、用时3小时;第三阶段升温至800℃、用时3.5小时;第四阶段升温至980℃、用时3.5小时;然后将磨球出炉,放入淬火油池中进行淬火处理,淬火时间为18-20分钟。淬火后的磨球冷却到室温后再装入台车式回火炉中进行低温回火处理。
所述低温回火的工艺条件为:温度210℃,回火时间8小时。
回火后的磨球冷却到室温后再装入专用掼制设备中进行时效处理及缺陷检测。
本发明机理浅析如下:
高铬铸造磨球在合适的温度、合适的铁液基本成分的条件下,通过钇稀土变质及孕育处理、多元微合金化处理的过程中除充分发挥各自冶金处理作用外,还彼此互相影响。例如:
A、随着多元微合金元素的溶入改变了碳在奥氏体中的扩散系数,在凝固过程连续冷却条件下,扩散速度减小就意味着碳的析出量的减少;
B、由良好的孕育效果形成的一定量的异质形核质点将导致奥氏体脱溶的碳原子和因铁液中浓度起伏出现的碳原子集团优先向其扩散,从而使碳化物转向以异质形核为主的结晶方式;
C、稀土等活性元素吸附在新生碳化物表面,使其难以连结成网状;
D、在凝固过程中由于溶质元素再分配使添加的各种合金元素富集在奥氏体结晶前沿的液体中,提高了初晶奥氏体的形核率,使奥氏体基体细化;
E、经过钇稀土变质、孕育处理及多元微合金化后,增大了铁液过冷倾向,使冷却速度对结晶过冷度的影响减弱,从而表现为铸造磨球断面的组织、性能趋以一致;
F、铸造磨球在一定冷却速度条件下凝固时,合金元素对延缓奥氏体转变的作用,突出表现在能否进行或多大程度上可能发生马氏体相变上。A-p是碳浓度变化的扩散型转变;A-M是碳浓度不变的结构型转变,而对碳原子来讲则是视其是处在长程还是短程的运动状态。当这种作用使碳原子只能在晶体内作短程运动,依托相变驱动力所产生的高速的铁原子晶格切变,就会在瞬间形成马氏体。
本发明中各种化学元素的作用:
碳(C):在铸造磨球中是最基本、最重要的元素。其含量多少直接决定共晶碳化物和基体的相对量,提高含碳量,可提高硬度、耐磨性,含碳量降低,韧性增加,故含碳量控制在1.8-3.2%范围内是合适的。
铬(Cr):是最重要的合金元素,为了保证有足够数量且高耐磨性的(CrFe)7C3型碳化物,应控制铬的含量大于10%,但其含量增加,虽碳化物亦增多,但生产成本增加。本发明将铬控制在10-10.5%范围内。
锰(Mn)和硅(Si):锰是稳定奥氏体的元素,使Ms点下降使残余奥氏体增加.加入较高的Mn,主要用来脱硫、脱氧,以增加韧性,故控制锰含量在0.2-1.0%范围内。适量的硅主要用于脱氧,因为过高的硅将导致韧性下阵,会使磨球使用过程有剥落现象,故将硅置控制在0.3-1.0%范围内。
铜(Cu)、钼(Mo)、镍(Ni)、钨(W)等合金的作用是显著提高淬透性,且具有较强的促进马氏体相变的作用。该类合金既可固溶于铁素体或奥氏体中,强化基体,提高基体的硬度,又可形成复杂碳化物,还能明显细化碳化物。因此加入微量的Cu、Mo、Ni、W等合金元素能提高磨球的综合力学性能。
硫(S)与磷(P):为有害元紊,降低磨球的力学性能,硫与磷是炉料带入的,所以要严格控制炉料质量,并进行脱硫脱磷处理,使所生产磨球的硫、磷含量均控制在0.1%以下为宜。
稀土钇(Y-Re)对铁水有净化、变质和促进合金化作用,能脱氧、除气、净化铁水,所生成氧化物可作为异质形核核心,细化基体晶粒组织,改善碳化物的形态与分布,含量均控制在0.1-0.2%以内。
Claims (2)
1.超硬高铬铸造磨球,其特征在于:其化学成分如下:
碳(C):1.8-3.2%,硅(Si):0.3-1.0%,锰(Mn):0.2-0.9%,
铬(Cr):10.0-10.5%,磷(P):0.02-0.1%,硫(S):0.02-0.1%;
铜(Cu):0.02-0.1%,钼(Mo):0.02-0.1%,镍(Ni):0.02-0.1%,
钨(W):0.02-0.1%,稀土钇(Y-Re):0.1-0.2%,
铁(Fe)80.1-83.7%。
2.根据权利要求1所述的超硬高铬铸造磨球的生产工艺方法,所用原料为废钢,其特征在于包括以下操作步骤:
A、首先将废钢在中频感应电炉中熔化,升温至1520-1580℃,再加入铬(Cr)、铜(Cu)、钼(Mo)、镍(Ni)和钨(W)和稀土钇(Y-Re);
B、加入碎块状的稀土钇(Y-Re),铁水冲熔并静置5-7分钟;
D、用浇铸装置将铁水浇注到铸球模具或砂箱中,冷却后得铸球;
E、将铸球装入加热炉进行奥氏体化处理,第一阶段由常温升至350-400℃、时间2-3小时;第二阶段升温至550-600℃、时间2-3小时;第三阶段升温至800℃、时间2-3小时;第四阶段升温至950-980℃、时间2-4小时;出炉得磨球;
F、将磨球放入淬火油池进行淬火处理,淬火时间为6-20分钟,冷却到室温;
G、再通过低温回火处理,温度210-240℃,回火时间8小时;
H、最后进行掼制检验,得合格磨球;磨球硬度为HRc64-66,落球冲击试验次数超过15000次。