CN101696370A - Method for preparing metal part forming lubricant - Google Patents
Method for preparing metal part forming lubricant Download PDFInfo
- Publication number
- CN101696370A CN101696370A CN200910218775A CN200910218775A CN101696370A CN 101696370 A CN101696370 A CN 101696370A CN 200910218775 A CN200910218775 A CN 200910218775A CN 200910218775 A CN200910218775 A CN 200910218775A CN 101696370 A CN101696370 A CN 101696370A
- Authority
- CN
- China
- Prior art keywords
- soap
- forming lubricant
- additive
- lubricant
- metal part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing a metal part forming lubricant, which comprises the following steps: (1) cutting a soap into small pieces of which the volume is smaller than 15*20*30 to obtain small pieces of soap; (2) evenly mixing the small pieces of soap, an additive and pure water, standing for 24 hours, and obtaining mixed solution, wherein the weight ratio of the small pieces of soap to the additive to the pure water is 4:16:1; and (3) stirring the mixed solution for 10 to 20 seconds in a stirrer to obtain the forming lubricant. The additive consists of mineral oil, saponin powder and molybdenum disulfide of which the weight ratio is 8:4:1. The metal part forming lubricant has the advantages that: the metal part forming lubricant can replace oil lubricants, is favorable for protecting environment, greatly reduces metal forming processing cost, particularly can simplify metal cleaning process flow, and can be widely applied to all procedures for metal forming.
Description
Technical field:
The invention belongs to chemical field, relate to a kind of forming lubricant, forming lubricant of especially a kind of metallic element and preparation method thereof.
Background technology:
The forming lubricant of present metallic element belongs to oil lubricant, during use lubricant is coated in the material deformation surface, the effect of play cooling, lubricating.This technology extensively adopts in industrial production, and its deficiency mainly shows as:
(1) pollutes production on-site environment.
(2) purchase cost height.
(3) the matting difficulty is big.
Summary of the invention:
The objective of the invention is to overcome the shortcoming of above-mentioned prior art, a kind of preparation method of forming lubricant of metallic element be provided:
(1) soap is cut into the length and width height respectively less than 15 * 20 * 30 fritter, obtains fritter soap;
(2) fritter soap, additive and pure water were mixed and place after 24 hours obtain mixing solutions, wherein the weight ratio of fritter soap, pure water and additive is 4: 16: 1;
(3) mixing solutions is put into stirrer and stirred 10-20 after second, obtain forming lubricant.
Described additive is made up of mineral oil, spaonin powder and molybdenumdisulphide, and the weight ratio of mineral oil, spaonin powder and molybdenumdisulphide is 8: 4: 1.
Described mineral oil mainly is to contain the fewer hydrocarbons of carbonatoms, and many have tens carbon atoms, and majority is a unsaturated hydrocarbons, promptly contains the hydrocarbon of carbon-carbon double bond or three key.
The invention has the beneficial effects as follows:
Use the alternative oil lubricant of the present invention, help protecting environment, reduce the metal forming tooling cost significantly, especially can simplify the metal cleaning process flow, can be widely used in all process steps of metal forming.
Description of drawings:
Fig. 1 is lubricant applications figure of the present invention;
Embodiment:
Below in conjunction with accompanying drawing the present invention is done and to describe in further detail:
Referring to Fig. 1,
The forming lubricant that the purpose of this invention is to provide a kind of metallic element to substitute the oil lubricant that is using, is issued to the purpose of cheapness, environmental protection in the prerequisite that satisfies service requirements.
The technical solution adopted in the present invention is:
A. main component: soap, pure water, additive (main component is mineral oil, spaonin powder and molybdenumdisulphide).
B. ratio: carry out proportioning according to differing materials and thickness, adjust each component proportions of additive.
C. complete processing
(1) will cut with a knife fritter from the soap that storehouse is reclaimed less than 15 * 20 * 30.
(2) the fritter soap that cuts is put into the plastics casing that fills pure water and soak, (soap is 1: 4 with the ratio of pure water weight).Soak time is no less than 24 hours.Every box weight of solvent 20kg.
(3) stir (10-20) second with soaked solvent adding stirrer and after adding an amount of additive, pour in the clean plastics casing.Each add-on is no more than 600ml.
(4) stirred 1 box with stirrer after, hand mixing is packed into after evenly in the plastic tank, bung will seal, and carries out sign, indicates the name of an article " forming lubricant "; Weight " 20kg ".
The invention has the beneficial effects as follows:
Use the alternative oil lubricant of the present invention, help protecting environment, reduce the metal forming tooling cost significantly, especially can simplify the metal cleaning process flow, can be widely used in all process steps of metal forming.
Above content is to further describing that the present invention did in conjunction with concrete preferred implementation; can not assert that the specific embodiment of the present invention only limits to this; for the general technical staff of the technical field of the invention; without departing from the inventive concept of the premise; can also make some simple deduction or replace, all should be considered as belonging to the present invention and determine scope of patent protection by claims of being submitted to.
Claims (2)
1. the preparation method of the forming lubricant of a metallic element is characterized in that:
(1) soap is cut into the length and width height respectively less than 15 * 20 * 30 fritter, obtains fritter soap;
(2) fritter soap, additive and pure water were mixed and place after 24 hours obtain mixing solutions, wherein the weight ratio of fritter soap, pure water and additive is 4: 16: 1;
(3) mixing solutions is put into stirrer and stirred 10-20 after second, obtain forming lubricant.
2. a kind of preparation method of forming lubricant of metallic element according to claim 1, it is characterized in that: described additive is made up of mineral oil, spaonin powder and molybdenumdisulphide, and the weight ratio of mineral oil, spaonin powder and molybdenumdisulphide is 8: 4: 1.