CN101691480B - Environment friendly type snow melt agent - Google Patents
Environment friendly type snow melt agent Download PDFInfo
- Publication number
- CN101691480B CN101691480B CN2009102102210A CN200910210221A CN101691480B CN 101691480 B CN101691480 B CN 101691480B CN 2009102102210 A CN2009102102210 A CN 2009102102210A CN 200910210221 A CN200910210221 A CN 200910210221A CN 101691480 B CN101691480 B CN 101691480B
- Authority
- CN
- China
- Prior art keywords
- snow melt
- sodium
- melt agent
- weight
- environment friendly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to an environment friendly type snow melt agent, which comprises sodium chloride serving as a main component and various additives of sodium citrate, sodium dihydrogen phosphate, sodium metasilicate, urea, sodium carboxymethyl cellulose and the like, and may also comprises abscisic acid or indolylacetic acid or mixture thereof, sodium tartrate and humic acid or salt thereof. The snow melt agent of the invention has a high snow melt capacity and a wide application temperature range, is particular suitable for the ambient temperature of no less than 15 DEG C below zero and economy and environmental protection, and can effectively reduce the corrosion on metalized products and a concrete structure and effectively improve the anti-sallification ability of seeds, plants and soil. The invention also provides a method for using the snow melt agent. In the method, the finished product of the snow melt agent is unnecessarily prepared in advance, instead the main component and various additives are separately placed, and the snow melt agent is prepared in a construction site before using; therefore, the method can avoid the problems that the snow melt agent is wetted and hardened during storage and transportation, and also overcome the defects of high temperature energy consumption and possibly caused decomposition of additives in a process of preparing composite particles(such as coating granulation). The snow melt agent is simple in operation and low in cost and particularly suitable for mechanized spraying operation.
Description
Technical field
The present invention relates to a kind of is the environment friendly type snow melt agent of main component with sodium-chlor, contains multiple additives.
Background technology
The snowfall of winter-spring season and icing is made troubles often for city and communications and transportation, and is very easily caused traffic accident, and particularly motorway often because of snowfall and freezing sealing stoppage in transit, causes enormous economic loss to society.Use Snow Agent to remove road accumulated snow to have that cost is low, method is easy, ice and snow melts that speed is fast, traffic recovers fast advantage and extensively adopted by more and more countries institute.Quickening along with China's economic construction speed, China's motorway total kilometrage occupies prostatitis, the world, and be the fast-developing impetus, " national freeway net planning " is pointed out: 4.4 ten thousand kilometers on following China high speed highway yet to be built, China's motorway and economize the Class I highway total kilometrage and will reach 180,000 kilometers when the time comes is 90,000 kilometers one times more than in U.S. of present world motorway owning amount maximum.Yet because the usable floor area of China's Snow Agent is very limited, every year is very big because of the financial loss that ice and snow caused, low temperature sleet freezing weather has several times particularly appearred in recent years, attacked by four low temperature sleet freezing weather processes as the big portion of China at the beginning of 2008 especially southern area, range of influence relates to 2/3rds provinces, cities and autonomous regions, whole nation population suffered from disaster reaches more than 100,000,000, and direct economic loss reaches more than 1,500 hundred million yuan.
At present, there is tame Snow Agent more than 100 (containing industrial frostproofer) manufacturing enterprise in China, and the overwhelming majority is private small business, and these enterprise's production units and technology fall behind, more do not have technical research strength, and be raw material how with the villaumite, simply composite, kind is single, unstable product quality, and side effect is obvious.As using a class Snow Agent the most widely at present, villaumite has corrodibility to metal and concrete, and vegetation and soil are had hazardness, can greatly destroy highway foundation facility and highway periphery ecotope.For example, spring in 2005,8 cities, Beijing the withered situation of large quantities of vegetations occurred because of using sodium-chlor and calcium chloride as Snow Agent, more than 3,000 ten thousand yuan of direct economic losses.And for example, in anti-snow disaster relief process, highway maintenance department has used a large amount of Industrial Salts as Snow Agent in order to remove ice and snow on road surfaces as early as possible, and environment has been caused big disaster at the beginning of 2008.This negative effect becomes influences the bottleneck problem that villaumite type Snow Agent is promoted.To this, some experts and scholar have proposed many pertinent suggestions based on environment protection to the use of Snow Agent.Suggestion according to pretty academician of Chinese Academy of Sciences's week, Premier Wen Jiabao makes comments and instructions and requires to strengthen to using the monitoring of Snow Agent to environmental influence, and propose the environment friendly type snow melt agent that research and development have independent intellectual property right, thereby China's Snow Agent has been mentioned unprecedented height to the problem that influences of environment.
Current; purpose for environment protection; the domestic and international research staff development goes out diversified non-villaumite type Snow Agent product; but it is all former thereby can't promote the use of because of aspects such as cost and technology; cause and still use villaumite type Snow Agent at present both at home and abroad mostly, remain sodium-chlor and magnesium chloride as the snow melt material of the present usage quantity maximum of the U.S..Given this, developing a kind of is main component with the villaumite, but can effectively reduce the novel Snow Agent product to highway foundation facility and eco-environmental impact, has great importance and application and popularization value.
Summary of the invention
The invention provides a kind of environment friendly type snow melt agent, this Snow Agent is cheap, wide material sources, snow melt ability are strong, compare with existing Snow Agent, can significantly reduce, soil is had good improvement protective effect to metal and concrete corrosion and to the harm of peripheral vegetation and soil.
Described environment friendly type snow melt agent is a main component with sodium-chlor, contains multiple additives.It specifically contains following component:
Sodium-chlor 90-95 weight %
Trisodium Citrate 0.5-3 weight %
SODIUM PHOSPHATE, MONOBASIC 0.5-3 weight %
Starso 0.5-2 weight %
Urea 1-5 weight %
Xylo-Mucine 0.5-1.5 weight %.
Preferably, described environment friendly type snow melt agent also contains dormin, indolylacetic acid or its mixture, and its content is 0-0.02 weight %, preferred 0.01-0.02 weight %.
Preferably, described environment friendly type snow melt agent also contains sodium tartrate, and its content is 0-1 weight %, preferred 0.5-1 weight %.
Preferably, described environment friendly type snow melt agent also contains humic acid or its salt, and its content is 0-1 weight %, preferred 0.5-1 weight %, and described humate is sodium humate or potassium humate.
Except said components, Snow Agent of the present invention can also contain Snow Agent field other various supplementary additives commonly used.
Compare with the various villaumite type Snow Agent of present use, Snow Agent snow melt ability of the present invention is strong, the Applicable temperature scope is wide, especially be suitable for the envrionment temperature that is not less than-15 ℃, not only economy but also environmental protection, corrodibility can be effectively reduced, the anti-salinization ability of seed, plant and soil can be improved effectively metal object and concrete structure.
Snow Agent of the present invention can be used preparation method's preparation well known in the art; the commonly used blending method in this area or additive made coated granule or the like as the dressing composition for example, and the Snow Agent product of gained can use with usual manners such as composite particles or solution.
The present invention also provides a kind of new Snow Agent using method, it is characterized in that need not preparing in advance the Snow Agent finished product, but sodium-chlor and various additive is placed apart, and is compound at building-site again before needing to use.Concrete steps are: the sodium-chlor that described ratio is provided; The various additives of described ratio are provided, and mix; The mechanical dispersion sodium chloride particle is sprayed at the form of mixed additive with the aqueous solution on the particle simultaneously, forms the Snow Agent composite particles; The gained composite particles is directly used.
This method can avoid the finished product Snow Agent to occur in storing and transporting as problems such as making moist, harden, also can avoid high temperature power consumption and the defective that may cause additives decompose in the process of preparation composite particles (for example coating pelletizing), this method is simple to operate, with low cost, be particularly suited for on-the-spot mechanize and shed operation.
Embodiment
Below will the present invention will be described in detail with specific embodiment, but these embodiment should be interpreted as limiting the scope of the invention.
(1) environment friendly type snow melt agent prescription
Table 1 has been listed four kinds of representative formulations, and wherein said numerical value is meant the weight percent of each component in Snow Agent.
Table 1 environment friendly type snow melt agent prescription is formed
| Prescription is formed | Prescription 1 | Prescription 2 | Prescription 3 | Prescription 4 |
| Sodium-chlor | 94.48 | 90.48 | 91.49 | 90.99 |
| Sodium tartrate | 0 | 0.5 | 0 | 1 |
| Trisodium Citrate | 1.5 | 2.5 | 1.5 | 1 |
| SODIUM PHOSPHATE, MONOBASIC | 0.5 | 2 | 1 | 2.5 |
| Starso | 0.5 | 1 | 1 | 1.5 |
| Urea | 1 | 2 | 4 | 2 |
| Dormin | 0.02 | 0 | 0.01 | 0 |
| Indolylacetic acid | 0 | 0.02 | 0 | 0.01 |
| Sodium salts humic acids | 0.5 | 1 | 0 | 0 |
| Xylo-Mucine | 1.5 | 0.5 | 1 | 1 |
(2) snow melt ability test
According to the provincial standard DB 11/T161-2002 of Beijing, above-mentioned four kinds of environment friendly type snow melt agents are carried out snow melt ability determination test.Experimental technique is: Snow Agent is configured to the 0.2g/ml concentration of aqueous solution, gets 6ml (V
0), in thermostat container, pour in the ice cube cumulative volume (V of metering liquid behind the 30min under-10 ℃ of conditions into
Snow Agent), deduct Snow Agent solution 6ml (V
0), difference is ice-melt ability (representing the snow melt ability with the ice-melt ability) for the volume that melts water outlet, under equal conditions does the sodium-chlor simultaneous test, 90% of index request 〉=sodium-chlor snow melt ability.Experimental result sees Table 2.
Table 2 snow melt ability test result
| Sequence number | Kind | Snow melt can force rate K (%) |
| 1 | Prescription 1 | 98 |
| 2 | Prescription 2 | 104 |
| 3 | Prescription 3 | 102 |
| 4 | Prescription 4 | 105 |
The snow melt of Snow Agent and sodium-chlor can force rate K=(V
Snow Agent-V
0)/(V
Sodium-chlor-V
0) * 100%, V in the formula
Snow melt AgentBe the cumulative volume of liquid that Snow Agent is melted, V
Sodium-chlorBe the cumulative volume of liquid that sodium-chlor melts, V
0Be Snow Agent or sodium chloride solution volume 6ml, the result keeps integer.
(3) metal corrosion of carbon steel test
According to GB GB/T 10124-1988, above-mentioned four kinds of environment friendly type snow melt agents are carried out the test of metal corrosion of carbon steel, step is as follows:
(1) gets carbon steel metal sheet 50 * 25 * 2mm of punching (aperture is 3mm) in the middle of 5, soak 5min with 5% sulphuric acid soln, wash successively, alcohol flushing, acetone rinsing again, nitrogen blowing is carried out drying, be put into afterwards in the loft drier, be numbered, measure and weigh;
(2) in five 2000ml beakers, add the 1000ml pure water respectively, in first beaker, add sodium-chlor 200g, add Snow Agent prescription 1, Snow Agent prescription 2, Snow Agent prescription 3 and Snow Agent prescription 4 each 200g in other four beakers respectively;
(3) 5 carbon steel metal sheets are hung in the solution of five beakers with nylon rope respectively, the nylon rope the other end ties up on the glass stick, and with the glass stick frame the beaker mouth along on, make metal be in solution central authorities position on the lower side;
(4) after the carbon steel metal sheet soaks 48h continuously in solution, be placed in the hydrochloric acid of 3% concentration and soak 10min, take out the back and brush surperficial residual rust with brush, successively with alcohol, acetone rinsing, nitrogen blowing carries out being put in the loft drier after the drying, weighs one by one more again;
(5) corrosion mitigating effect evaluation.Test-results sees Table 3.
Table 3 metal corrosion of carbon steel test-results
| Sequence number | Kind | Initial mass M (g) | Erosion back mass M 1(g) | Corrosion inhibitor quality (g) | Erosion rate R (mm/a) | Corrosion ratio (%) * |
| 1 | Sodium-chlor | 19.5682 | 19.5065 | 0.0617 | 0.5123 | - |
| 2 | Prescription 1 | 20.1004 | 20.0938 | 0.0066 | 0.0548 | 10.70 |
| 3 | Prescription 2 | 19.0483 | 19.0463 | 0.0020 | 0.0166 | 3.24 |
| 4 | Prescription 3 | 20.5113 | 20.5061 | 0.0052 | 0.0432 | 8.43 |
| 5 | Prescription 4 | 19.1365 | 19.1315 | 0.0050 | 0.0415 | 8.10 |
The erosion rate of * corroding ratio (%) and be with sodium-chlor is 100%
Erosion rate R=[8760 * (M-M1)] ÷ STD * 10
S represents surface-area in the formula, and standard test piece numerical value is 28cm
2T represents soak time, and numerical value is 48h; D represents density, and numerical value is 7.85g/cm
38760 is the hourss in 1 year; The 10th, the unit conversion coefficient.
(4) concrete erosion test
According to U.S. ASTM designation C672-84 method, above-mentioned four kinds of environment friendly type snow melt agents are carried out concrete corrosion test.Test method is: (100 * 100 * 100mm) are immersed in the Snow Agent solution of 3% concentration the concrete blocks that will rest, freezing 16h under-20 ℃ the environment, the thawing process at room temperature continues 8h, carried out repeatedly 50 days, Snow Agent solution is changed once weekly, and the weight of weighing concrete blocks, calculates the concrete erosion rate according to mass loss, calculate the corrosion ratio with the sodium-chlor contrast again, test-results sees Table 4.
Table 4 concrete erosion test-results
| Sequence number | Kind | Concrete erosion rate (%) | Corrosion ratio (%) * |
| 1 | Sodium-chlor | 5.37 | - |
| 2 | Prescription 1 | 1.17 | 21.79 |
| 3 | Prescription 2 | 0.31 | 5.77 |
| 4 | Prescription 3 | 0.48 | 8.94 |
| 5 | Prescription 4 | 0.54 | 10.06 |
* the corrosion rate that corrodes ratio (%) and be with sodium-chlor is 100%
(5) plant salt tolerance test
According to the provincial standard DB 11/T161-2002 of Beijing, above-mentioned four kinds of environment friendly type snow melt agents are carried out the plant salt tolerance test.Test method is: 2m is marked as estimating herbaceous plant in the use lawn tuber of dwarf lilyturf
2* 5, each dosage 10g/m
2, weekly, the accumulation sprinkling amount before the phenomenon that occurs being injured is the salt tolerant amount, with g/m
2Expression, test-results sees Table 5.
Table 5 plant salt tolerance test-results
| Sequence number | Kind | Salt tolerant amount (g/m 2) |
| 1 | Sodium-chlor | 60 |
| 2 | Prescription 1 | 380 |
| 3 | Prescription 2 | 220 |
| 4 | Prescription 3 | 200 |
| 5 | Prescription 4 | 170 |
(6) the plant seed rate of being injured relatively detects test
Above-mentioned four kinds of environment friendly type snow melt agents are carried out the plant seed rate of being injured relatively detect test.Test method is: with the English grass seed after 10% superoxol soaks 5min, use 40 ℃ of warm water soaking 15min again, choose 100 * 5 seeds that uniform particles is full, put into the germination box, Snow Agent solution-wet seed and absorbent cotton with 5g/L concentration, cover the germination box cover, in 20 ℃ of constant incubators, cultivate, and in time add water to keep seed moistening, record seed germination quantity after 12 days, do controlled trial with distilled water, plant seed is injured rate≤70% relatively for criterion, and test-results sees Table 6.
The table 6 plant seed rate test-results of being injured relatively
| Sequence number | Kind | The plant seed rate RR (%) that is injured relatively |
| 1 | Prescription 1 | 15 |
| 2 | Prescription 2 | 27 |
| 3 | Prescription 3 | 22 |
| 4 | Prescription 4 | 34 |
Plant seed germination rate R=A/N * 100%, A is a number of shoots in the formula, and N is for cultivating seed number, and numerical value is 100;
The plant seed rate RR=(R that is injured relatively
Contrast-R
Snow Agent)/R
Contrast* 100%, R in the formula
ContrastBe the rate of emergence of handling with distilled water, R
Snow AgentBe the rate of emergence of handling with Snow Agent, the result keeps integer.
Comprehensive above-mentioned every index as can be seen, Snow Agent snow melt ability of the present invention is strong, to metal and concrete corrodibility and very little to the harm of peripheral vegetation and soil, is a kind of Snow Agent of very high-efficiency environment friendly.
Claims (9)
1. an environment friendly type snow melt agent is characterized in that, contains following component:
Sodium-chlor 90-95 weight %
Trisodium Citrate 0.5-3 weight %
SODIUM PHOSPHATE, MONOBASIC 0.5-3 weight %
Starso 0.5-2 weight %
Urea 1-5 weight %
Xylo-Mucine 0.5-1.5 weight %.
2. environment friendly type snow melt agent according to claim 1 is characterized in that: also contain dormin, indolylacetic acid or its mixture, its content is 0-0.02 weight %.
3. environment friendly type snow melt agent according to claim 2 is characterized in that: the content of dormin, indolylacetic acid or its mixture is 0.01-0.02 weight %.
4. according to each described environment friendly type snow melt agent among the claim 1-3, it is characterized in that: also contain sodium tartrate, its content is 0-1 weight %.
5. environment friendly type snow melt agent according to claim 4 is characterized in that: the content of sodium tartrate is 0.5-1 weight %.
6. environment friendly type snow melt agent according to claim 1 is characterized in that: also contain humic acid or its salt, its content is 0-1 weight %, and described humate is sodium humate or potassium humate.
7. environment friendly type snow melt agent according to claim 6 is characterized in that: the content of humic acid or its salt is 0.5-1 weight %.
8. the using method of each described environment friendly type snow melt agent among the claim 1-7 may further comprise the steps:
(1) provides the sodium-chlor of described ratio;
(2) provide other component except that sodium-chlor of described ratio, and mix;
(3) mechanical dispersion sodium chloride particle is sprayed at the mixture that obtains in the step (2) form with the aqueous solution on the sodium chloride particle simultaneously, forms the Snow Agent composite particles;
(4) the gained composite particles is directly used.
9. using method according to claim 8 is characterized in that: mechanical dispersion described in the step (3) is for stirring or vibrating dispersion.